CN101942261A - 一种紫外光固化涂料 - Google Patents

一种紫外光固化涂料 Download PDF

Info

Publication number
CN101942261A
CN101942261A CN 201010263927 CN201010263927A CN101942261A CN 101942261 A CN101942261 A CN 101942261A CN 201010263927 CN201010263927 CN 201010263927 CN 201010263927 A CN201010263927 A CN 201010263927A CN 101942261 A CN101942261 A CN 101942261A
Authority
CN
China
Prior art keywords
parts
ultraviolet
curing paint
ultraviolet curing
coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201010263927
Other languages
English (en)
Inventor
顾卫星
杜丽娜
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Adash Superior Paint Co., Ltd.
The new building materials (Shanghai) Co., Ltd. astec
Original Assignee
SHANGHAI ADASH SUPERIOR PAINT CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANGHAI ADASH SUPERIOR PAINT CO Ltd filed Critical SHANGHAI ADASH SUPERIOR PAINT CO Ltd
Priority to CN 201010263927 priority Critical patent/CN101942261A/zh
Publication of CN101942261A publication Critical patent/CN101942261A/zh
Pending legal-status Critical Current

Abstract

本发明涉及建筑涂料技术领域，尤其是涉及一种广泛用于涂装板、墙面装饰板、水泥纤维板等建筑装饰板的紫外光固化涂料。它含有的组分及重量份数为：它含有的组分及重量份数为：紫外光固化树脂20～90，活性稀释剂3～40，活性胺5～20，光引发剂3～10。本发明由于采用上述技术方案，在涂料成膜固化后，膜层中不含有耐磨性能差的丙烯酸酯单体，得到的膜层具有优异的耐磨性、硬度和附着力。同时该涂料合理调整活性稀释剂的种类及用量，消除了现有技术固化形成的漆膜表面粗糙、出现气泡、针眼、缩孔、流平不良等现象。

Description

一种紫外光固化涂料
技术领域
本发明涉及建筑涂料技术领域，尤其是涉及一种广泛用于涂装板、墙面装饰板、水泥纤维板等建筑装饰板的紫外光固化涂料。
背景技术
紫外光固化涂料是一种近年来发展起来的光固化涂料，与传统的光固化涂料相比，紫外光固化涂料具有较高的固含量，因而生产效率高。同时，其干燥时间也较短。上述紫外光固化涂料虽然可以作为木器、皮革和金属等的面漆使用，但将其运用于涂装板、墙面装饰板、水泥纤维板等建筑装饰板上，存在着易发生划伤、耐磨性差、硬度和附着力低等缺陷，使得固化形成的漆膜表面粗糙、出现气泡、针眼、缩孔、流平不良等现象。
发明内容
本发明所要解决的技术问题是提供一种克服现有技术缺陷的紫外光固化涂料。本发明解决其技术问题采用的技术方案是：一种紫外光固化涂料，它含有的组分及重量份数为：一种紫外光固化涂料，其特征是它含有的组分及重量份数为：紫外光固化树脂20～90，活性稀释剂3～40，活性胺5～20，光引发剂3～10。本发明所要解决的技术问题还可进一步通过如下技术方案加以解决：它还含有消泡剂，其重量份数为0.1～2；它还含有分散剂，其重量份数为0.3～5；它还含有滑石粉，其重量份数为1～50；紫外光固化树脂为环氧丙烯酸酯或丙烯酸聚氨酯，活性稀释剂为三丙二醇二丙烯酸酯或三羟甲基丙烷丙烯酸酯，活性胺为三乙醇胺，光引发剂为安息香双甲醚或二苯丙酮；消泡剂的型号为D002，制造厂商为深圳鼎好光化科技有限公司；分散剂为聚醚改性三硅氧烷；滑石粉粒径为1000～12000目，优选1250目。本发明中的紫外光固化树脂为成膜主体材料，活性稀释剂既可降低粘度，又可成膜，活性胺能促进光引发剂引发紫光固化树脂聚合而固化成膜，光引发剂能引发紫光固化树脂聚合而固化成膜，消泡剂起消泡作用，分散剂起到降低粘度作用、滑石粉能促进漆膜具有良好的打磨性。本发明中的所有组分均可在国内购得。本发明的制备方法为：在配料缸中加入20～90份紫外光固化树脂，在600转/分钟的转速下加入3～40份活性稀释剂，5～20份活性胺，后在1200～2000转/分钟的转速下加入3～10份光引发剂，1～50份滑石粉，0.1～2份消泡剂，0.3～5份分散剂，搅拌20～30分钟，即可得到本发明。本发明由于采用上述技术方案，在涂料成膜固化后，膜层中不含有耐磨性能差的丙烯酸酯单体，得到的膜层具有优异的耐磨性、硬度和附着力。同时该涂料合理调整活性稀释剂的种类及用量，消除了现有技术固化形成的漆膜表面粗糙、出现气泡、针眼、缩孔、流平不良等现象。
具体实施方式
  组分(单位：kg)  实施例1  实施例2  实施例3  实施例4  实施例5
  紫外光固化树脂   20   38   55   72   90
  活性稀释剂   40   30   21   12   3
  活性胺   5   9   12   16   20
  光引发剂   10   8   7   5   3
  组分(单位：kg)   实施例6   实施例7   实施例8   实施例9   实施例10
  紫外光固化树脂   20   38   55   72   90
  活性稀释剂   40   30   21   12   3
  活性胺   5   9   12   16   20
  光引发剂   10   8   7   5   3
  消泡剂   0.1   0.6   1   1.5   2
  组分(单位：kg)   实施例11   实施例12   实施例13   实施例14   实施例15
  紫外光固化树脂   20   38   55   72   90
  活性稀释剂   40   30   21   12   3
  活性胺   5   9   12   16   20
  光引发剂   10   8   7   5   3
  分散剂   0.3   1.5   2.7   3.8   5
  组分(单位：kg)   实施例16   实施例17   实施例18   实施例19   实施例20
  紫外光固化树脂   20   38   55   72   90
  活性稀释剂   40   30   21   12   3
  活性胺   5   9   12   16   20
  光引发剂   10   8   7   5   3
  消泡剂   0.1   0.6   1   1.5   2
  分散剂   5   3.8   2.7   1.5   0.3
  组分(单位：kg)   实施例21   实施例22   实施例23   实施例24   实施例25
  紫外光固化树脂   20   38   55   72   90
  活性稀释剂   40   30   21   12   3
  活性胺   5   9   12   16   20
  光引发剂   10   8   7   5   3
  分散剂   5   3.8   2.7   1.5   0.3
  滑石粉   1   15   30   45   50
  组分(单位：kg)   实施例26   实施例27   实施例28   实施例29   实施例30
  紫外光固化树脂   20   38   55   72   90
  活性稀释剂   40   30   21   12   3
  活性胺   5   9   12   16   20
  光引发剂   10   8   7   5   3
  消泡剂   0.1   0.6   1   1.5   2
  分散剂   5   3.8   2.7   1.5   0.3
  滑石粉   1   15   30   45   50

Claims (8)

1.一种紫外光固化涂料，其特征是它含有的组分及重量份数为：紫外光固化树脂20～90、活性稀释剂3～40、活性胺5～20和光引发剂3～10。
2.根据权利要求1所述的一种紫外光固化涂料，其特征是：它还含有消泡剂，其重量份数为0.1～2。
3.根据权利要求1或2所述的一种紫外光固化涂料，其特征是：它还含有分散剂，其重量份数为0.3～5。
4.根据权利要求3所述的一种紫外光固化涂料，其特征是：它还含有滑石粉，其重量份数为1～50。
5.根据权利要求1所述的一种紫外光固化涂料，其特征是：紫外光固化树脂为环氧丙烯酸酯或丙烯酸聚氨酯，活性稀释剂为三丙二醇二丙烯酸酯或三羟甲基丙烷丙烯酸酯，活性胺为三乙醇胺，光引发剂为安息香双甲醚或二苯丙酮。
6.根据权利要求2所述的一种紫外光固化涂料，其特征是：消泡剂的型号为D002。
7.根据权利要求3所述的一种紫外光固化涂料，其特征是：分散剂为聚醚改性三硅氧烷。
8.根据权利要求4所述的一种紫外光固化涂料，其特征是：滑石粉粒径为1000～12000目。
CN 201010263927 2010-08-24 2010-08-24 一种紫外光固化涂料 Pending CN101942261A (zh)