CN101922225A - Laminate plate floor and preparation method thereof - Google Patents
Laminate plate floor and preparation method thereof Download PDFInfo
- Publication number
- CN101922225A CN101922225A CN201010256177XA CN201010256177A CN101922225A CN 101922225 A CN101922225 A CN 101922225A CN 201010256177X A CN201010256177X A CN 201010256177XA CN 201010256177 A CN201010256177 A CN 201010256177A CN 101922225 A CN101922225 A CN 101922225A
- Authority
- CN
- China
- Prior art keywords
- layer
- laminate plate
- plate floor
- top layer
- twine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a laminate plate floor which is characterized by comprising a balancing layer (6), a bottom layer (1), lower enhanced net wires (2), an intermediate layer (3), upper enhanced net wires (4), a top layer (5) and a wear-resisting decorating layer (7), wherein the bottom layer (1), the intermediate layer (3) and the top layer (5) are prepared by settling and drying raw material mixture prepared according to certain proportion. The method for preparing the laminate plate floor comprises the following steps of: firstly, respectively and tightly sticking and pressing the balancing layer (6), the bottom layer (1), the lower enhanced net wires (4), the intermediate layer (3), the upper enhanced net wires (4) and the top layer (5) into an integral structure; then, settling the laminate plate floor at the environmental temperature of higher than 20 DEG C for at least 10h; and finally, sticking the wear-resisting decorating layer (7) on the upper surface of the top layer (5). The laminate plate floor manufactured by the method has the advantages of low cost, high hardness, water resistance, bacterium resistance, deodorization and other functions.
Description
Technical field
The present invention relates to a kind of floor, especially a kind of material environment friendly, manufacture craft is simple, has sandwich construction, possesses far infrared radiation and laminate plate floor antibiotic, deodorization functions, and the method for preparing this laminate plate floor.
Background technology
Raising along with people's living standard, requirement to employed floor in the various occasions is also more and more higher, not only require the floor to possess anti-water logging, hardness height, characteristics such as indeformable, simultaneously also to possess environmental protection, to advantages such as health are useful, there are wooden floor, composite floor board in traditional floor now, and their main raw material(s) all is a timber, and not only cost is higher, when making this floor, need cut down a large amount of trees simultaneously, destroy the green resource of the earth; And traditional wood floors also exist to meet water distortion, shortcoming such as mouldy inevitably, and the intensity of sheet material is also lower.
Summary of the invention
The present invention is in order to solve existing in prior technology the problems referred to above, provides a kind of sandwich construction, intensity height, cost low, has laminate plate floor of far infrared radiation and antibiotic, deodorization functions and preparation method thereof.
Concrete solution of the present invention is: a kind of laminate plate floor, it is characterized in that: described laminate plate floor by balance layer 6, bottom 1, down strengthen twine 2, intermediate layer 3, on strengthen twine 4, top layer 5 and wear-resisting decorative layer 7 and form, wherein bottom 1, intermediate layer 3 and top layer 5 be by the mixed material that following proportioning is made leave standstill, dry back obtains:
Loess or mica or charcoal 35%-45%
Magnesia 33%-45%
Concentration is the magnesium chloride solution 14%-20% of 20%-28%
Resin 5%-6%
A kind of method for preparing aforesaid laminate plate floor is characterized in that: described method is carried out according to following steps:
A, successively with balance layer 6, bottom 1, down strengthen twine 2, intermediate layer 3, on strengthen twine 4 and top layer 5 is closely pressed to integrative-structure,
B, with laminate plate floor under the environment more than 20 degrees centigrade, left standstill at least 10 hours,
C, wear-resisting decorative layer 7 is bonded in the upper surface of top layer 5.
The present invention compares with prior art, has following advantage:
The laminate plate floor that utilizes method of the present invention to be prepared from, can be widely used in family, office, public place etc., owing to its heating in manufacturing process without any need for form, therefore kept with the function of loess (mica, charcoal), met the requirement of modern the healthy aspect of constructional materials as releasing far infrared, the antibiotic and deodorizing that laminated plates was possessed of basic material; It can replace traditional wood floors, has protected limited green resource, energy-conserving and environment-protective; Its intensity height of while, cost is low, can be applicable to multiple environment, possesses extensive market prospects, very helps applying in the art.
Description of drawings
Fig. 1 is a structural representation of the present invention.
The specific embodiment
Below the specific embodiment of the present invention will be described.As shown in Figure 1, the laminate plate floor of the embodiment of the invention is made up of seven-layer structure, be followed successively by balance layer 6, bottom 1, down strengthen twine 2, intermediate layer 3, on strengthen twine 4, top layer 5 and wear-resisting decorative layer 7, wherein bottom 1, intermediate layer 3 and top layer 5 are with a kind of material, after promptly fully mixing, leave standstill by loess, magnesia, magnesium chloride solution and resin, dry back obtains.
Embodiment one:
At first according to following proportioning configuration mixed material:
Loess 43%
Magnesia 35%
Concentration is 27% magnesium chloride solution 17%
Resin 5%
At first balance layer 6 is placed on the panel machining, the above-mentioned raw materials of mud shape is smeared the upper surface of balance layer 6, as bottom 1, cover thereon then and strengthen twine 2 down, smear one deck above-mentioned raw materials again,, cover again and go up enhancing twine 4 as intermediate layer 3, smear one deck above-mentioned raw materials at last, as top layer 5; Then the laminated plates of these six layers of structures is cut, cuts into the sheet material of required size and shape, in 23 degrees centigrade environment, leave standstill 8 hours after, paste wear-resisting decorative layer 7 at the upper surface of top layer 5, finally finish the making of laminate plate floor.
Embodiment two
At first according to following proportioning configuration mixed material:
Charcoal 36%
Magnesia 42%
Concentration is 22% magnesium chloride solution 16%
Resin 6%
At first balance layer 6 is placed on the panel machining, the above-mentioned raw materials of mud shape is smeared the upper surface of balance layer 6, as bottom 1, cover thereon then and strengthen twine 2 down, smear one deck above-mentioned raw materials again,, cover again and go up enhancing twine 4 as intermediate layer 3, smear one deck above-mentioned raw materials at last, as top layer 5; Then the laminated plates of these six layers of structures is cut, cuts into the sheet material of required size and shape, in 20 degrees centigrade environment, leave standstill 12 hours after, paste wear-resisting decorative layer 7 at the upper surface of top layer 5, finally finish the making of laminate plate floor.
Claims (2)
1. laminate plate floor, it is characterized in that: described laminate plate floor by balance layer (6), bottom (1), down strengthen twine (2), intermediate layer (3), on strengthen twine (4), top layer (5) and wear-resisting decorative layer (7) and form, wherein bottom (1), intermediate layer (3) and top layer (5) be by the mixed material that following proportioning is made leave standstill, dry back obtains:
Loess or mica or charcoal 35%-45%
Magnesia 33%-45%
Concentration is the magnesium chloride solution 14%-20% of 20%-28%
Resin 5%-6%
2. method for preparing laminate plate floor as claimed in claim 1, it is characterized in that: described method is carried out according to following steps:
A, successively with balance layer (6), bottom (1), down strengthen twine (2), intermediate layer (3), on strengthen twine (4) and top layer (5) is closely pressed to integrative-structure,
B, with laminate plate floor under the environment more than 20 degrees centigrade, left standstill at least 10 hours,
C, wear-resisting decorative layer (7) is bonded in the upper surface of top layer (5).