CN101914877B - 炊蒸原纸生产方法 - Google Patents
炊蒸原纸生产方法 Download PDFInfo
- Publication number
- CN101914877B CN101914877B CN2010102369224A CN201010236922A CN101914877B CN 101914877 B CN101914877 B CN 101914877B CN 2010102369224 A CN2010102369224 A CN 2010102369224A CN 201010236922 A CN201010236922 A CN 201010236922A CN 101914877 B CN101914877 B CN 101914877B
- Authority
- CN
- China
- Prior art keywords
- paper
- pulp
- strength agent
- base paper
- steaming base
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及造纸工艺领域。本发明的炊蒸原纸生产方法的工艺流程为:采用立式水力将纸浆的碎浆疏解成浆,疏解后的浆料进入叩前贮浆池贮存备用;采用双盘磨浆机打浆,打浆疏解后的浆料进入叩后贮浆池;先加入干强剂后加湿强剂,搅拌;经除砂、精选,经精选后的纸浆送入高位箱稳流除气;通过一道立式离心筛后进入纸机流浆箱上网;纸页在成形网上成形,经脱水、压榨后,在圆筒卷纸机上卷取,然后放置以均衡水分,然后经湿润机湿润,送入压光机热压光后即成为炊蒸原纸。本发明采用如上技术方案,实现了一种具有高的紧度和透明度,且具有较高的干强度和湿强度的炊蒸原纸。
Description
技术领域
本发明涉及造纸工艺领域,尤其涉及一种炊蒸原纸生产方法,炊蒸原纸为薄型类特种纸,可以作为轻工日用品、食品、药品、水果等食品包装材料,经离型剂涂布加工后,成为食品炊蒸原纸。
背景技术
纯净的植物纤维素纤维是无色透明的,其密度为1.5g/cm3,就是说由纯净的植物纤维素纤维密集地组成的纸张(如玻璃纸),可以完全透射可见光,是无色透明的。而一般纸张的紧度(表观密度)为0.5g/cm3,这说明植物纤维组成纸张时,纸张中有2/3左右的孔隙。也就是说,一般的纸张中除植物纤维素纤维本身透射可见光外,在孔隙和纤维交界处,光线会被反射,因此我们看到的常为白色不透明的纸张。所以,如何实现高的紧度和透明度的炊蒸用纸是业界需要解决的问题。
另外一个问题就是,普通的半透明纸主要用于高档商品的包装,只要求其透明性指标,对纸的干强度只需要有一般要求即可,而不要求纸的湿强度指标,而针对于炊蒸用纸,不仅需要解决上述的高的紧度和透明度问题,也还需解决纸的干、湿强度的问题。
发明内容
本发明的目的在于提供一种炊蒸原纸生产方法,能实现具有高的紧度和透明度,并具有较高的干强度和湿强度的要求。
本发明的炊蒸原纸生产方法,包括如下步骤:
a.采用立式水力将纸浆的碎浆疏解成浆;
b.疏解后的浆料进入叩前贮浆池贮存备用;
c.进行打浆处理;
d.打浆疏解后的浆料进入叩后贮浆池;
e.加入干强剂后再加湿强剂,然后搅拌;
f.进行除砂处理和精选;
g.经精选后的纸浆送入高位箱稳流除气;
h.通过一道立式离心筛后进入纸机流浆箱上网;
i.纸页在成形网上成形;
j.进行脱水处理和压榨处理;
k.在圆筒卷纸机上卷取;
l.放置以均衡水分处理;
m.经湿润机进行湿润处理;
n.送入压光机热压光处理后即成为炊蒸原纸。
进一步的,所述的干强剂的添加比例是相对于绝干的纸浆质量百分比为2%。
更进一步的,所述的干强剂是含阳离子型干强剂或者两性多糖的干强剂。
进一步的,所述的湿强剂的添加比例是相对于绝干的纸浆质量百分比为2%。
更进一步的,所述的湿强剂是阳性聚丙烯酰胺。
进一步的,所述的打浆处理是采用双盘磨浆机打浆。
进一步的,所述的成形网是聚酯网。
本发明采用如上技术方案,实现了一种具有高的紧度和透明度,且具有较高的干强度和湿强度的炊蒸原纸。
具体实施方式
本发明的炊蒸原纸生产方法的工艺流程为:采用立式水力将纸浆的碎浆疏解成浆,疏解后的浆料进入叩前贮浆池贮存备用;采用双盘磨浆机打浆,打浆疏解后的浆料进入叩后贮浆池;先加入干强剂后加湿强剂,搅拌;经除砂、精选,经精选后的纸浆送入高位箱稳流除气;通过一道立式离心筛后进入纸机流浆箱上网;纸页在成形网上成形,经脱水、压榨后,在圆筒卷纸机上卷取,然后放置以均衡水分,然后经湿润机湿润,送入压光机热压光后即成为炊蒸原纸。
以下为本发明的一个最佳实施例的流程:
采用立式水力将100%漂白针叶木浆碎解成4%生浆→疏解后的浆料进入叩前贮浆池贮存备用→采用双盘磨浆机串联磨浆→添加相对于绝干的纸浆质量百分比为2%的含阳离子型干强剂或者两性多糖的干强剂,再添加相对于绝干的纸浆质量百分比为2%的阳性聚丙烯酰胺的湿强剂→成浆→进行除砂处理和精选→经精选后的纸浆送入高位箱稳流除气→调和成0.2%浓度并通过一道立式离心筛后进入纸机流浆箱上网→纸机抄造使纸页在成形网上成形→进行脱水处理和压榨处理→在圆筒卷纸机上卷取→放置以均衡水分处理→经湿润机进行湿润处理,使纸页水份达到20%→送入超级压光机热压处理→制作完成炊蒸原纸。
尽管结合优选实施方案具体展示和介绍了本发明,但所属领域的技术人员应该明白,在不脱离所附权利要求书所限定的本发明的精神和范围内,在形式上和细节上可以对本发明做出各种变化,均为本发明的保护范围。
Claims (3)
1.炊蒸原纸生产方法,其特征是,包括如下步骤:
a.采用立式水力将纸浆的碎浆疏解成浆;
b.疏解后的浆料进入叩前贮浆池贮存备用;
c.进行打浆处理;
d.打浆疏解后的浆料进入叩后贮浆池;
e.加入干强剂后再加湿强剂,然后搅拌;所述的干强剂的添加比例是相对于绝干的纸浆质量百分比为2%,所述的干强剂是含阳离子型干强剂或者两性多糖的干强剂;所述的湿强剂的添加比例是相对于绝干的纸浆质量百分比为2%,所述的湿强剂是阳性聚丙烯酰胺;
f.进行除砂处理和精选;
g.经精选后的纸浆送入高位箱稳流除气;
h.通过一道立式离心筛后进入纸机流浆箱上网;
i.纸页在成形网上成形;
j.进行脱水处理和压榨处理;
k.在圆筒卷纸机上卷取;
l.放置以均衡水分处理;
m.经湿润机进行湿润处理;
n.送入压光机热压光处理后即成为炊蒸原纸。
2.根据权利要求1所述的炊蒸原纸生产方法,其特征是:所述的打浆处理是采用双盘磨浆机打浆。
3.根据权利要求1所述的炊蒸原纸生产方法,其特征是:所述的成形网是聚酯网。