CN101831845A - 废纸脱墨浆生产薄页包装纸的制造方法 - Google Patents
废纸脱墨浆生产薄页包装纸的制造方法 Download PDFInfo
- Publication number
- CN101831845A CN101831845A CN 201010194681 CN201010194681A CN101831845A CN 101831845 A CN101831845 A CN 101831845A CN 201010194681 CN201010194681 CN 201010194681 CN 201010194681 A CN201010194681 A CN 201010194681A CN 101831845 A CN101831845 A CN 101831845A
- Authority
- CN
- China
- Prior art keywords
- pulp
- paper
- bleached chemical
- wrapping paper
- slurry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开一种废纸脱墨浆生产薄页包装纸的制造方法,包括漂白化学针叶浆、漂白化学阔叶浆和废纸脱墨浆预处理热磨机械浆,经分别打浆后配用抄造,并经烘干机干燥及表面压光处理,打浆后浆料叩解度:漂白化学针叶浆30-40°SR,漂白化学阔叶浆25-35°SR,废纸脱墨浆50-62°SR;制得的薄页包装纸定量为16-20g/m2,白度不低于75%。本发明利用废纸脱墨浆加漂白化学针叶浆、漂白化学阔叶浆加工制得的薄页包装纸,采用特定的打浆工艺对浆料进行横向和纵向处理,提高了纸张的物理强度,在保持纸张高强度的要求下,使废纸脱墨浆和针叶浆、漂白化学阔叶浆科学配合,不但能节约资源还能降低生产成本。
Description
技术领域
本发明公开一种薄页包装纸的制造方法,按国际专利分类表(IPC)划分属于造纸行业中薄页纸生产制造技术领域,尤其是涉及一种废纸脱墨浆生产薄页包装纸。
背景技术
薄页纸,定量在22g/m2以下的一类纸的统称,纸质薄而柔软,有的还有一定的透明度,其中薄页包装纸,一般是应用于高级商品的内衬包装。薄页包装纸的生产与普通的造纸工艺流程基本相同,其工艺流程包括:浆板准备--浆板碎解--打浆或磨浆--配浆--净化--筛浆--流浆箱出浆--网部脱水--压榨脱水--干燥--压光--取卷--复卷--包装。但,薄页纸作为高档纸张,其要求要比普通纸张更为严格。
常见造纸所使用的原料一般为木材、芦苇、稻草等纤维质原料,造纸工艺主要是将原料蒸煮、打浆后进行抄纸,上述造纸工艺能耗高、污染大,特别是一些小型造纸厂污染处理能力差,致使对厂区周围环境造成严重的污染,而造纸过程的废纸浆回收率低,原料利用率得不到提高,一定程度上造成资源的浪费。而本发明申请利用废纸脱墨浆代替纤维质原料进行薄页包装纸生产,对原料利用率及能耗方面都有很大的进步。
发明内容
针对现有技术的不足,本发明提供了一种能耗低的废纸脱墨浆生产薄页包装纸的制造方法。
为达到上述目的,本发明是通过以下技术方案实现的:
一种废纸脱墨浆生产薄页包装纸的制造方法,包括漂白化学针叶浆、漂白化学阔叶浆和废纸脱墨浆预处理热磨机械浆,经分别打浆后配用抄造,并经烘干机干燥及表面压光处理,其中:
浆料重量配比:漂白化学针叶浆、漂白化学阔叶浆和废纸脱墨浆预处理热磨机械浆为10-20∶10-20∶30-50;
打浆后浆料叩解度:漂白化学针叶浆30-40°SR,漂白化学阔叶浆25-35°SR,废纸脱墨浆50-62°SR;
制得的薄页包装纸定量为16-20g/m2,白度不低于75%。
进一步,所述的薄页包装纸定量为16-18g/m2,白度不低于80%,且纸面裂断长纵横平均不小于4000m,撕裂度纵横平均不小于80mN。
进一步,所述的薄页包装纸紧度不小于0.45g/m3,水份在6±1%。
本发明利用废纸脱墨浆加漂白化学针叶浆、漂白化学阔叶浆加工制得的薄页包装纸,是一种环保新型的薄页纸加工工艺,采用特定的打浆工艺对浆料进行横向和纵向处理,提高了纸张的物理强度,在保持纸张高强度的要求下,使废纸脱墨浆和针叶浆、漂白化学阔叶浆科学配合,具有节约资源、降低生产成本、环保等优点。
附图说明
图1是本发明工艺流程图。
具体实施方式
下面结合附图对本发明作进一步说明:
实施例:请参阅图1,一种废纸脱墨浆生产薄页包装纸的制造方法,包括漂白化学针叶浆、漂白化学阔叶浆和废纸脱墨浆预处理热磨机械浆,经分别打浆后配用抄造,并经烘干机干燥及表面压光处理,其中:
浆料重量配比:漂白化学针叶浆、漂白化学阔叶浆和废纸脱墨浆预处理热磨机械浆为10-20∶10-20∶30-50;
打浆后浆料叩解度:漂白化学针叶浆30-40°SR,漂白化学阔叶浆25-35°SR,废纸脱墨浆50-62°SR;
制得的薄页包装纸定量为16-20g/m2,白度不低于75%。
优选的,所述薄页包装纸定量为16-18g/m2,白度不低于80%,且纸面裂断长纵横平均不小于4000m,撕裂度纵横平均不小于80mN。
优选的,所述薄页包装纸紧度不小于0.45g/m3,水份在6±1%。
本发明利用废纸脱墨浆加漂白化学针叶浆、漂白化学阔叶浆加工制得的薄页包装纸,是一种环保新型的薄页纸加工工艺,采用特定的打浆工艺对浆料进行横向和纵向处理,提高了纸张的物理强度,在保持纸张高强度的要求下,使废纸脱墨浆和针叶浆、漂白化学阔叶浆科学配合,具有节约资源、降低生产成本、环保等优点。
以上所记载,仅为利用本创作技术内容的实施例,任何熟悉本项技艺者运用本创作所做的修饰、变化,皆属本创作主张的专利范围,而不限于实施例所揭示者。
Claims (3)
1.一种废纸脱墨浆生产薄页包装纸的制造方法,其特征在于:包括漂白化学针叶浆、漂白化学阔叶浆和废纸脱墨浆预处理热磨机械浆,经分别打浆后配用抄造,并经烘干机干燥及表面压光处理,其中:
浆料重量配比:漂白化学针叶浆、漂白化学阔叶浆和废纸脱墨浆预处理热磨机械浆为10-20∶10-20∶30-50;
打浆后浆料叩解度:漂白化学针叶浆30-40°SR,漂白化学阔叶浆25-35°SR,废纸脱墨浆50-62°SR;
制得的薄页包装纸定量为16-20g/m2,白度不低于75%。
2.根据权利要求1所述的废纸脱墨浆生产薄页包装纸的制造方法,其特征在于:所述的薄页包装纸定量为16-18g/m2,白度不低于80%,且纸面裂断长纵横平均不小于4000m,撕裂度纵横平均不小于80mN。
3.根据权利要求1或2所述的废纸脱墨浆生产薄页包装纸的制造方法,其特征在于:所述的薄页包装纸紧度不小于0.45g/m3,水份在6±1%。