CN101889333B - 基板和其制造方法 - Google Patents
基板和其制造方法 Download PDFInfo
- Publication number
- CN101889333B CN101889333B CN2008801197630A CN200880119763A CN101889333B CN 101889333 B CN101889333 B CN 101889333B CN 2008801197630 A CN2008801197630 A CN 2008801197630A CN 200880119763 A CN200880119763 A CN 200880119763A CN 101889333 B CN101889333 B CN 101889333B
- Authority
- CN
- China
- Prior art keywords
- copper
- barrier film
- substrate
- tungsten
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
Claims (11)