CN101875814A - 一种耐高温防腐蚀涂料底漆 - Google Patents

一种耐高温防腐蚀涂料底漆 Download PDF

Info

Publication number
CN101875814A
CN101875814A CN 201010250683 CN201010250683A CN101875814A CN 101875814 A CN101875814 A CN 101875814A CN 201010250683 CN201010250683 CN 201010250683 CN 201010250683 A CN201010250683 A CN 201010250683A CN 101875814 A CN101875814 A CN 101875814A
Authority
CN
China
Prior art keywords
base coat
parts
temperature resistant
high temperature
coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201010250683
Other languages
English (en)
Inventor
李新跃
张敬雨
李明田
喻兰英
张先银
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zigong Tuoli Chemical Co Ltd
Original Assignee
Zigong Tuoli Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zigong Tuoli Chemical Co Ltd filed Critical Zigong Tuoli Chemical Co Ltd
Priority to CN 201010250683 priority Critical patent/CN101875814A/zh
Publication of CN101875814A publication Critical patent/CN101875814A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种耐高温防腐蚀涂料底漆，它由如下质量份数的组分组成：环氧树脂改性有机硅树脂为25～55；锌铬黄为3～8；铁红为15～45；硫酸钡为7～18；滑石粉为6～16；有机膨润土为0.2～1.0；聚乙烯蜡防沉剂为0.05～0.45；防流挂剂为0.2～0.8；二甲苯适量。本发明底漆可耐400℃高温，72h内涂层表面没有裂皮现象，可以在300℃以下使用2年，具有较强防腐能力，耐候性及对外界起屏蔽作用、附着力良好。通过金像显微镜观察形貌图及扫描探针观察涂层表面结构表明，底漆涂层中填料分散均匀，填料与基料结合效果好。

Description

一种耐高温防腐蚀涂料底漆
技术领域
本发明涉及一种涂料，具体指一种耐高温防腐蚀涂料底漆。
背景技术
涂料广泛应用在国民经济各个部门，涂刷在物体表面对各种材料起保护和装饰作用。涂料在基体材料表面形成的固体膜状物称为涂层，也称涂膜。涂层起到覆盖基体材料和隔离介质的作用。单一一种涂料组成的涂层一般很少被采用，因为单一品种涂料不可能满足所有的要求。有的附着力好而耐候性或耐腐蚀性能差，有的耐腐蚀性能好，但与钢铁表面附着力很差。如某些高分子聚合物形成的涂层，由于附着力不良，涂膜下的金属仍然会锈蚀，使用后，不久涂层会大面积剥落，所以多采用复合涂层——由底层、中间层和面层构成，对应的涂料就有涂料底漆、中间漆和面漆之分。
在石油、化工生产中，涂料不仅起到保护、标志和装饰的作用，而且也常用作设备内壁及构筑物的耐高温防腐蚀涂层，广泛地应用于烟囱、高温蒸汽管道、热交换器、高温炉、石油裂解设备、发动机部位及排气管甚至飞机、导弹、宇航器等。随着航空、航天、能源、石化等工业的迅速发展，对于金属材料的使用性能要求也越来越高，如它们需要在更高的使用温度及更苛刻的腐蚀环境下作业，因此，耐高温防腐蚀涂料的研究是一项非常迫切的工作。如何提供一种行之有效的耐高温防腐蚀涂料（包括组成涂料的底漆、中间漆和面漆）就成了业内研究的方向。
发明内容
针对现有技术存在的上述不足，本发明的目的是提供一种耐高温、耐候性及对外界起屏蔽作用、附着力良好、有阻蚀作用的涂料底漆。
本发明的技术方案是这样实现的：一种耐高温防腐蚀涂料底漆，它由如下质量份数的组分组成：环氧树脂改性有机硅树脂为25~55；锌铬黄为3~8；铁红为15~45；硫酸钡为7~18；滑石粉为6~16；有机膨润土为0.2~1.0；聚乙烯蜡防沉剂为0.05~0.45；防流挂剂为0.2~0.8；二甲苯适量。
本发明底漆可耐400℃高温，72h内涂层表面没有裂皮现象，可以在300℃以下使用两年以上，具有较强防腐能力，耐候性及对外界起屏蔽作用、附着力良好。通过金像显微镜观察形貌图及扫描探针观察涂层表面结构表明，底漆涂层中填料分散均匀，填料与基料结合效果好。
具体实施方式
下面结合实施例对本发明进行详细说明。
本发明耐高温防腐蚀涂料底漆，它由如下质量份数的组分组成：环氧树脂改性有机硅树脂为25~55；锌铬黄为3~8；铁红为15~45；硫酸钡为7~18；滑石粉为6~16；有机膨润土为0.2~1.0；聚乙烯蜡防沉剂为0.05~0.45；防流挂剂为0.2~0.8；二甲苯适量，以使涂料黏度适中即可，通常为3~25。
以下给出一个较佳的具体实施例配方：环氧树脂改性有机硅树脂（具体型号为HG43）为40；锌铬黄为4；铁红为30；硫酸钡为10；滑石粉为10；有机膨润土为0.5；聚乙烯蜡防沉剂（具体型号为202P）为0.2；防流挂剂（具体型号为275）为0.5；二甲苯为15。
环氧树脂改性有机硅树脂HG43具有改善漆膜耐候、耐热、耐水性及电绝缘等性能，提高基料树脂与颜填料的复合性，同时提高涂料对基材的附着力，改善漆膜综合性能。
锌铬黄的主要成分是铬酸锌，习惯上常以三氧化铬(CrO3)的含量作为主要指标，一般锌铬黄中CrO3的含量为35~45%，本发明就是通常的锌铬黄。铁红就是三氧化二铁的别名，但作为涂料只能称呼铁红。锌铬黄和铁红的加入能够增加涂膜的致密性，降低腐蚀介质的渗透率，对腐蚀性介质起着屏蔽作用，而且锌铬黄还具有防锈性能，铁红颜料对漆膜的抗渗性影响较大，往往使漆膜助透气性和透水性增加，而且对钢铁的防锈以至阴极均无缓蚀作用。
在涂料中，滑石粉作为填料，可起到骨架作用，降低制造成本，同时提高涂料的漆膜硬度，增加涂料的细度。
硫酸钡具有较好的耐候性、耐酸碱、耐盐雾性和耐高温性。
添加有机膨润土可使涂料具有防沉效果，能够有效改善涂料的触变性、流变性等涂刷性，增强涂膜的防腐性及耐水性，还可以节省成本。
防流挂剂275的使用主要是防止涂料在垂直面上涂装时，涂料下垂。
二甲苯是溶剂。二甲苯用量不可过多，否则可能导致生产出的涂料黏度过低，用玻璃棒蘸取溶液观测黏度，并酌情加入二甲苯控制黏度，使黏度适中即可。

Claims (2)

1.一种耐高温防腐蚀涂料底漆，其特征在于，它由如下质量份数的组分组成：环氧树脂改性有机硅树脂为25~55；锌铬黄为3~8；铁红为15~45；硫酸钡为7~18；滑石粉为6~16；有机膨润土为0.2~1.0；聚乙烯蜡防沉剂为0.05~0.45；防流挂剂为0.2~0.8；二甲苯适量。
2.根据权利要求1去所述耐高温防腐蚀涂料底漆，其特征在于，所述环氧树脂改性有机硅树脂为40；锌铬黄为4；铁红为30；硫酸钡为10；滑石粉为10；有机膨润土为0.5；聚乙烯蜡防沉剂为0.2；防流挂剂为0.5；二甲苯为15。
CN 201010250683 2010-08-11 2010-08-11 一种耐高温防腐蚀涂料底漆 Pending CN101875814A (zh)