CN101875788A - 水乳型防护蜡 - Google Patents
水乳型防护蜡 Download PDFInfo
- Publication number
- CN101875788A CN101875788A CN2009100831235A CN200910083123A CN101875788A CN 101875788 A CN101875788 A CN 101875788A CN 2009100831235 A CN2009100831235 A CN 2009100831235A CN 200910083123 A CN200910083123 A CN 200910083123A CN 101875788 A CN101875788 A CN 101875788A
- Authority
- CN
- China
- Prior art keywords
- percent
- wax
- water emulsion
- emulsion type
- type protection
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种水乳型防护蜡,其组分按重量百分比计:含氧石油蜡6~10%、含氧合成蜡0.5~2.0%、改性松香树脂2~6%、有机石油溶剂3~5%、有机膨润土(填料)0.5~1.5%、石油磺酸盐防锈剂5~15%、反应型乳化剂1~4%、高分子聚合物20~35%、硅烷类交联剂3~5%、异唑啉酮类杀菌剂0.5~1.5%和水20~55%;原料易得,生产工艺简单,产品造价低;产品成膜附着力强;优异的防锈及高低温适应性能,满足汽车的高低温使用要求;使用安全可靠,挥发物中有机物含量降低,减少环境污染,改善工作环境;优良的防锈性能和抗碎石击打性能,保证汽车具有较长的使用寿命等优异使用性能。
Description
技术领域
本发明涉及一种防护用蜡质材料,特别是在汽车生产过程中使用的水乳型防护蜡。
背景技术
随着汽车发动机增压度的提高,发动机各运动部件工作时的温度也有所提高,因此,对于车用防护腊的适应性要求越来越高。目前,采用有机溶剂作为分散介质的溶剂型防护蜡存在的问题是:在使用温度较高时,防护蜡容易从金属底材上剥落,抗流挂性差,易溶易燃,性能指标不能完全达到使用要求。热熔型防护蜡虽然改善了溶剂型防护蜡的不足,但仍然存在着施工条件苛刻,操作成本高的缺点。
水乳型汽车用防护蜡技术查新显示:国内有关于汽车内腔、底盘等保护蜡的文献,其中涉及到水基或乳剂型汽车内腔、底盘保护蜡的只是部分成分相同,与本课题有一定的区别,国外有关汽车防腐蜡研究的文献有10篇,但其内容均与本课题有一定的区别。
发明内容
本发明的目的在于提供一种以水为分散介质,附着力强、耐腐蚀、使用安全可靠的水乳型防护蜡。
本发明的技术解决方案:一种水乳型防护蜡,其组分和重量百分比为:含氧石油蜡6~10%、含氧合成蜡0.5~2.0%、改性松香树脂2~6%、有机石油溶剂3~5%、有机膨润土0.5~1.5%、石油磺酸盐防锈剂5~15%、反应型乳化剂1~4%、高分子聚合物20~35%、硅烷类交联剂3~5%、异唑啉酮类杀菌剂0.5~1.5%,水20~55%。
含氧石油蜡滴熔点不小于70℃,酸值不小于15mgKOH/g。
含氧合成蜡滴熔点不小于103℃,酸值在3-7mgKOH/g。
高分子聚合物是一种丙烯酸脂或甲基丙烯酸脂及官能单体的共聚物,PH值:7-9,粘度:500-2000CPS。
水可以是蒸馏水、去离子水、自来水或硬度小于1000ppm的其它水质。
本发明的配方中的石油蜡、合成蜡和改性植物树脂中均含有含氧基团,有利于乳化,保证乳化形成均匀稳定的乳化体系。含氧石油蜡的滴熔点不小于70℃,酸值不小于15mgKOH/g,旨在保证防护蜡的成膜性。含氧合成蜡的滴熔点不小于103℃,酸值在3-7mgKOH/g,旨在保证防护蜡膜的高温性能。水乳型的高分子聚合物和少量的硅烷类交联剂,旨在提高蜡膜的附着力和成膜性,保证水乳型防护蜡产品防护性能。乳化剂属于反应型的试剂,形成乳液后就失去乳化能力,以此确保乳液产品所成膜的耐湿热性能。石油溶剂即成膜助剂的作用是有利于高熔点材料的乳化,并形成均匀稳定的乳液。有机膨润土填料的作用是提高防护蜡的抗流淌,保证产品成膜均匀性。杀菌剂的加入有利于提高产品的抗菌性能。防锈剂为磺酸盐类产品,具有良好的防盐雾和耐湿热防锈性能。本发明克服以有机溶剂为分散介质存在火灾危险性大和热溶型产品使用不方便的不足,产品具有良好的附着力;高低温适应性和防锈性能强,能满足汽车的高低温使用要求。
发明的特点是:1、原料易得,生产工艺简单,产品造价低。2、产品蜡膜为弹性的硬膜,成膜附着力强。3、优异的防锈及高低温适应性能,满足汽车的高低温使用要求。4、采用水为分散介质,使用安全可靠,杜绝安全隐患,挥发物中有机物含量降低,减少环境污染,改善工作环境。5、优良的防锈性能和抗碎石击打性能,保证汽车具有较长的使用寿命等优异使用性能。
具体实施方式
实施例1
含氧石油蜡6.0%、含氧合成蜡2.0%、改性松香树脂2.0%、有机石油溶剂(成膜助剂)5.0%、有机膨润土填料0.5%、石油磺酸盐防锈剂5.0%、反应型乳化剂4.0%、丙烯酸脂聚合物20%、硅烷类交联剂3.0%、异唑啉酮类抗菌剂0.5%、水52%。
实施例2
含氧石油蜡7.0%、含氧合成蜡1.7%、改性松香树脂3.0%、有机石油溶剂(成膜助剂)4.5%、有机膨润土填料0.75%、石油磺酸盐防锈剂7.5%、反应型乳化剂3.25%、甲基丙烯酸脂聚合物23.75%、硅烷类交联剂3.5%、异唑啉酮类抗菌剂0.75%、水44.3%。
实施例3
含氧石油蜡8.0%、含氧合成蜡1.3%、改性松香树脂4.0%、有机石油溶剂(成膜助剂)4.0%、有机膨润土填料1.0%、石油磺酸盐防锈剂10%、反应型乳化剂2.5%、官能单体聚合物27.5%、硅烷类交联剂4.0%、异唑啉酮类抗菌剂1.0%、水36.7%。
实施例4
含氧石油蜡9.0%、含氧合成蜡0.9%、改性松香树脂5.0%、有机石油溶剂(成膜助剂)3.5%、有机膨润土填料1.25%、石油磺酸盐防锈剂12.5%、反应型乳化剂1.75%、官能单体聚合物31.25%、硅烷类交联剂4.5%、异唑啉酮类抗菌剂1.25%、水29.75%。
实施例5
含氧石油蜡10.0%、含氧合成蜡0.5%、改性松香树脂6.0%、有机石油溶剂(成膜助剂)3.0%、有机膨润土填料1.5%、石油磺酸盐防锈剂15.0%、反应型乳化剂1.0%、甲基丙烯酸脂聚合物35%、硅烷类交联剂5.0%、异唑啉酮类抗菌剂1.5%、自来水21.5%。
实施例6
含氧石油蜡6.0%、含氧合成蜡2.0%、改性松香树脂2.0%、有机石油溶剂(成膜助剂)3.0%、有机膨润土填料0.5%、石油磺酸盐防锈剂5.0%、反应型乳化剂3.0%、丙烯酸脂聚合物20%、硅烷类交联剂3.0%、异唑啉酮类抗菌剂0.5%、去离子水55%。
实施例7
含氧石油蜡10.0%、含氧合成蜡0.5%、改性松香树脂6.0%、有机石油溶剂(成膜助剂)3.0%、有机膨润土填料1.5%、石油磺酸盐防锈剂15.0%、反应型乳化剂2.5%、甲基丙烯酸脂聚合物35%、硅烷类交联剂5.0%、异唑啉酮类抗菌剂1.5%、蒸馏水20%。
上述实施例中含氧石油蜡滴熔点不小于70℃,酸值不小于15mgKOH/g。含氧合成蜡滴熔点不小于103℃,酸值在3-7mgKOH/g。高分子聚合物是一种丙烯酸脂、甲基丙烯酸脂及官能单体的共聚物,PH值:7-9,粘度:500-2000CPS。
工艺过程的实施步骤是:1.将含氧石油蜡、含氧合成蜡、改性松香树脂、有机石油溶剂和有机膨润土填料加入调合釜中加热至熔融;2.加石油磺酸盐防锈剂溶匀;3.加入反应型乳化剂及部分热水;4.加高分子聚合物,并加入剩余量的水;5.搅拌降温至常温时加入硅烷类交联剂和异唑啉酮类抗菌剂,搅拌均匀后过滤装桶。
Claims (4)
1.一种水乳型防护蜡,其特征在于:其组分按重量百分比计:由含氧石油蜡6~10%、含氧合成蜡0.5~2.0%、改性松香树脂2~6%、有机石油溶剂3~5%、有机膨润土0.5~1.5%、石油磺酸盐防锈剂5~15%、反应型乳化剂1~4%、高分子聚合物20~35%、硅烷类交联剂3~5%、异唑啉酮类杀菌剂0.5~1.5%和水20~55%组成。
2.根据权利要求1所述的一种水乳型防护蜡,其特征在于:含氧石油蜡滴熔点不小于70℃,酸值不小于15mgKOH/g。
3.根据权利要求1所述的一种水乳型防护蜡,其特征在于:含氧合成蜡滴熔点不小于103℃,酸值在3-7mgKOH/g。
4.根据权利要求1所述的一种水乳型防护腊,其特征在于:高分子聚合物是一种丙烯酸脂或甲基丙烯酸脂及官能单体的共聚物,PH值:7-9,粘度:500-2000CPS。