CN101864823B - 利用去除重金属后的碳酸锰尾渣生产的加气混凝土砌块及其制造方法 - Google Patents
利用去除重金属后的碳酸锰尾渣生产的加气混凝土砌块及其制造方法 Download PDFInfo
- Publication number
- CN101864823B CN101864823B CN2010101962443A CN201010196244A CN101864823B CN 101864823 B CN101864823 B CN 101864823B CN 2010101962443 A CN2010101962443 A CN 2010101962443A CN 201010196244 A CN201010196244 A CN 201010196244A CN 101864823 B CN101864823 B CN 101864823B
- Authority
- CN
- China
- Prior art keywords
- still
- manganese carbonate
- heavy metal
- tailings
- building block
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
Claims (1)