CN101830139A - Manufacturing method of puffing paint decorative surface - Google Patents
Manufacturing method of puffing paint decorative surface Download PDFInfo
- Publication number
- CN101830139A CN101830139A CN 201010198659 CN201010198659A CN101830139A CN 101830139 A CN101830139 A CN 101830139A CN 201010198659 CN201010198659 CN 201010198659 CN 201010198659 A CN201010198659 A CN 201010198659A CN 101830139 A CN101830139 A CN 101830139A
- Authority
- CN
- China
- Prior art keywords
- puffing
- paint
- resin
- unsaturated
- decorative surface
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a manufacturing method of a puffing paint decorative surface, belonging to the technical field of furniture materials. The manufacturing method comprises the following steps of: (1) sufficiently uniformly stirring unsaturated resin, a promoter, a paint diluent, a colorant and a pearlescent product, and placing for 1-24 hours to sufficiently dissolve all the materials so as to obtain resin oil; (2) fast uniformly stirring the resin oil by adding a curing agent, then uniformly laying the resin oil which is uniformly stirred on the surface of a manufactured article, then uniformly dispersing a diffusant on the laid oil surface in a dripping way according to the size of manufactured patterns, and waiting for curing; (3) burnishing; (4) brushing gloss oil; and (5) grinding with water to obtain a finished product. The manufactured puffing paint decorative surface has the advantages of clear outline, good light sensitivity, strong stereoscopic sensation and high vividness and better meets the visual requirements of people on the luxury of home decorations.
Description
Technical field
The invention belongs to furniture decoration materials technical field, be specifically related to a kind of preparation method of puffing paint decorative surface.
Background technology
Along with the raising of living standard, people pursue also more and more stronger to the luxurious vision of household ornaments, because natural materials processing and carve difficultly costs an arm and a leg, so now to have occurred on the market be the furniture decoration materials product of base material with the unsaturated-resin.
Application number is the manufacture method that a kind of Scagliola and Scagliola have been introduced in the invention of 00134990.2 China, comprise matrix, be attached with simulation layer on the surface of matrix, the raw material of making simulation layer contain unsaturated-resin gel coat or unsaturated-resin glue, curing agent, promoter and stone grain, and it is the following natural or artificial stone grains of 20 orders that the stone grain adopts fineness.But such Scagliola, its texture is based on lines or irregular grain, and third dimension is relatively poor.
In addition, also having occurred is the bulb of fritillary stone of base material with the unsaturated-resin, and this product flower likeness in form bean curd slag specimen lacks fresh and alive property; With the unsaturated-resin is the colorful pattern of base material, and its flower shape slightly is bordering on snuff oil (phoenix antelope stone), but its product third dimension extreme difference, decorative pattern does not have fresh and alive property.
Summary of the invention
One of purpose of the present invention provides the preparation method of a kind of sharp outline, speed is good, third dimension is strong puffing paint decorative surface.
The object of the present invention is achieved like this.
A kind of preparation method of puffing paint decorative surface, it comprises and is prepared as follows step:
(1) unsaturated-resin, promoter, paint thinner, colouring agent and pearly-lustre product are stirred, deposited 1-24 hour, allow all materials fully dissolve, promptly obtain resinon;
(2) resinon is added curing agent and stir fast, the resinon after will stirring again evenly is tiled in the surface of made object, after with diffusant by the size of made decorative pattern evenly point be dispersed on the pasta of tiling, wait to solidify;
(3) polishing: the pasta after will thoroughly solidifying thoroughly polishes flat the top layer on the pasta with sand paper, again with the sand trace polishing of sand paper with buffed surface;
(4) brushing oil: the object that will polish is removed surface dirt, unsaturated-resin is added promoter, curing agent, liquid wax again, and the flat surface that is applied to this object, the back that stirs waits to solidify;
(5) water mill: the object surface that will thoroughly be cured adds water uniform grinding firmly back and forth with sand paper, till the object top layer does not have sand trace seal, with polishing ball top liquid feeding wax uniform grinding one time, gets product again.
In step (1), can also add reflective powder or fluorescent material.
The surface area of making object with respect to every square metre, below the consumption of each component be:
Unsaturated-resin 1-15kg
Diffusant 1g-20g.
With respect to every kilogram unsaturated-resin, below the consumption of each component be:
Promoter 1-40g
Curing agent 0.1g-15g
Colouring agent 0.1g-20g
Pearly-lustre product 1g-40g
Liquid wax 1g-10g
Paint thinner 5g-100g.
Described unsaturated-resin is a unsaturated polyester resin.
Described promoter is cobalt water.
Described curing agent is a MEK.
Described colouring agent is a kind of in toner, look essence or the printing ink.
Described diffusant comprises poly-second methylsiloxane, water and auxiliary agent.
Described paint thinner is a Tianna solution.
Beneficial effect of the present invention is: puffing paint decorative surface sharp outline, the speed that the present invention makes is good, third dimension is strong, has very strong fresh and alive property, satisfies people better the luxurious vision of household ornaments is pursued.
The specific embodiment
The invention will be further described below by embodiment, but practical range of the present invention is not limited to this.
Embodiment 1.
A kind of preparation method of puffing paint decorative surface, it comprises and is prepared as follows step:
(1) unsaturated-resin, promoter, paint thinner, colouring agent and pearly-lustre product are stirred, deposited 1 hour, allow all materials fully dissolve, promptly obtain resinon;
(2) resinon is added curing agent and stir fast, the resinon after will stirring again evenly is tiled in the surface of made object, after with diffusant by the size of made decorative pattern evenly point be dispersed on the pasta of tiling, wait to solidify;
(3) polishing: the pasta after will thoroughly solidifying is with 80
#Sand paper thoroughly polishes flat the top layer on the pasta, uses 240 again
#Sand paper is with the sand trace polishing of buffed surface;
(4) brushing oil: the object that will polish is removed surface dirt, unsaturated-resin is added promoter, curing agent, liquid wax again, and the flat surface that is applied to this object, the back that stirs waits to solidify;
(5) water mill: the object surface that will thoroughly be cured is with 120
#-2400
#Sand paper adds water uniform grinding firmly back and forth, till the object top layer does not have sand trace seal, with polishing ball top liquid feeding wax uniform grinding one time, gets product again.
The surface area of making object with respect to every square metre, below the consumption of each component be:
Unsaturated-resin 1kg
Diffusant 1g.
With respect to every kilogram unsaturated-resin, below the consumption of each component be:
Promoter 1g
Curing agent 0.1g
Colouring agent 0.1g
Pearly-lustre product 1g
Liquid wax 1g
Paint thinner 5g.
Described unsaturated-resin is a unsaturated polyester resin, promptly the chain macromolecule compound that is formed by saturated or unsaturated binary acid and saturated or unsaturated dihydroxylic alcohols polycondensation is dissolved in the liquid of the thickness that forms in the styrene, and used unsaturated-resin is the vinyl unsaturated polyester resin in the present embodiment.
Described promoter is cobalt water.
Described curing agent is a MEK.
Described colouring agent is a toner.
Described diffusant comprises poly-second methylsiloxane, water and auxiliary agent, and auxiliary agent plays and increases capillary effect.
Described paint thinner is a Tianna solution.
The snuff oil that present embodiment makes (phoenix antelope stone) facing sharp outline, speed is good, third dimension is strong, has very strong fresh and alive property.
Embodiment 2.
A kind of preparation method of puffing paint decorative surface, it comprises and is prepared as follows step:
(1) with unsaturated-resin, promoter, paint thinner, colouring agent, pearly-lustre product and reflective powder, stirs, deposited 10 hours, allow all materials fully dissolve, promptly obtain resinon;
(2) resinon is added curing agent and stir fast, the resinon after will stirring again evenly is tiled in the surface of made object, after with diffusant by the size of made decorative pattern evenly point be dispersed on the pasta of tiling, wait to solidify;
(3) polishing: the pasta after will thoroughly solidifying is with 80
#Sand paper thoroughly polishes flat the top layer on the pasta, uses 240 again
#Sand paper is with the sand trace polishing of buffed surface;
(4) brushing oil: the object that will polish is removed surface dirt, unsaturated-resin is added promoter, curing agent, liquid wax again, and the flat surface that is applied to this object, the back that stirs waits to solidify;
(5) water mill: the object surface that will thoroughly be cured is with 120
#-2400
#Sand paper adds water uniform grinding firmly back and forth, till the object top layer does not have sand trace seal, with polishing ball top liquid feeding wax uniform grinding one time, gets product again.
The surface area of making object with respect to every square metre, below the consumption of each component be:
Unsaturated-resin 8kg
Diffusant 12g.
With respect to every kilogram unsaturated-resin, below the consumption of each component be:
Promoter 20g
Curing agent 8g
Colouring agent 12g
Pearly-lustre product 20g
Liquid wax 6g
Paint thinner 50g.
Described unsaturated-resin is a unsaturated polyester resin, promptly the chain macromolecule compound that is formed by saturated or unsaturated binary acid and saturated or unsaturated dihydroxylic alcohols polycondensation is dissolved in the liquid of the thickness that forms in the styrene, and used unsaturated-resin is the bisphenol A-type unsaturated polyester resin in the present embodiment.
Described promoter is cobalt water.
Described curing agent is a MEK.
Described colouring agent is the look essence.
Described diffusant comprises poly-second methylsiloxane, water and auxiliary agent, and auxiliary agent plays and increases capillary effect.
Described paint thinner is a Tianna solution.
The snuff oil that present embodiment makes (phoenix antelope stone) facing sharp outline, speed is good, third dimension is strong, has very strong fresh and alive property.
Embodiment 3.
A kind of preparation method of puffing paint decorative surface, it comprises and is prepared as follows step:
(1) with unsaturated-resin, promoter, paint thinner, colouring agent, pearly-lustre product, fluorescent material, stirs, deposited 24 hours, allow all materials fully dissolve, promptly obtain resinon;
(2) resinon is added curing agent and stir fast, the resinon after will stirring again evenly is tiled in the surface of made object, after with diffusant by the size of made decorative pattern evenly point be dispersed on the pasta of tiling, wait to solidify;
(3) polishing: the pasta after will thoroughly solidifying is with 80
#Sand paper thoroughly polishes flat the top layer on the pasta, uses 240 again
#Sand paper is with the sand trace polishing of buffed surface;
(4) brushing oil: the object that will polish is removed surface dirt, unsaturated-resin is added promoter, curing agent, liquid wax again, and the flat surface that is applied to this object, the back that stirs waits to solidify;
(5) water mill: the object surface that will thoroughly be cured is with 120
#-2400
#Sand paper adds water uniform grinding firmly back and forth, till the object top layer does not have sand trace seal, with polishing ball top liquid feeding wax uniform grinding one time, gets product again.
The surface area of making object with respect to every square metre, below the consumption of each component be:
Unsaturated-resin 15kg
Diffusant 20g.
With respect to every kilogram unsaturated-resin, below the consumption of each component be:
Promoter 40g
Curing agent 15g
Colouring agent 20g
Pearly-lustre product 40g
Liquid wax 10g
Paint thinner 100g.
Described unsaturated-resin is a unsaturated polyester resin, promptly the chain macromolecule compound that is formed by saturated or unsaturated binary acid and saturated or unsaturated dihydroxylic alcohols polycondensation is dissolved in the liquid of the thickness that forms in the styrene, and used unsaturated-resin is the halo unsaturated polyester resin in the present embodiment.
Described promoter is cobalt water.
Described curing agent is a MEK.
Described colouring agent is a printing ink.
Described diffusant comprises poly-second methylsiloxane, water and auxiliary agent, and auxiliary agent plays and increases capillary effect.
Described paint thinner is a Tianna solution.
The snuff oil that present embodiment makes (phoenix antelope stone) facing sharp outline, speed is good, third dimension is strong, has very strong fresh and alive property.
The above only is a better embodiment of the present invention, so all equivalences of doing according to the described structure of patent claim of the present invention, feature and principle change or modify, is included in the patent claim of the present invention.
Claims (10)
1. the preparation method of a puffing paint decorative surface is characterized in that: it comprises and is prepared as follows step:
(1) unsaturated-resin, promoter, paint thinner, colouring agent and pearly-lustre product are stirred, deposited 1-24 hour, allow all materials fully dissolve, promptly obtain resinon;
(2) resinon is added curing agent and stir fast, the resinon after will stirring again evenly is tiled in the surface of made object, after with diffusant by the size of made decorative pattern evenly point be dispersed on the pasta of tiling, wait to solidify;
(3) polishing: the pasta after will thoroughly solidifying thoroughly polishes flat the top layer on the pasta with sand paper, again with the sand trace polishing of sand paper with buffed surface;
(4) brushing oil: the object that will polish is removed surface dirt, unsaturated-resin is added promoter, curing agent, liquid wax again, and the flat surface that is applied to this object, the back that stirs waits to solidify;
(5) water mill: the object surface that will thoroughly be cured adds water uniform grinding firmly back and forth with sand paper, till the object top layer does not have sand trace seal, with polishing ball top liquid feeding wax uniform grinding one time, gets product again.
2. the preparation method of a kind of puffing paint decorative surface according to claim 1 is characterized in that: can also add reflective powder or fluorescent material in step (1).
3. the preparation method of a kind of puffing paint decorative surface according to claim 1 is characterized in that: the surface area of making object with respect to every square metre, below the consumption of each component be:
Unsaturated-resin 1-15kg
Diffusant 1g-20g.
4. the preparation method of a kind of puffing paint decorative surface according to claim 1 is characterized in that: with respect to every kilogram unsaturated-resin, below the consumption of each component be:
Promoter 1-40g
Curing agent 0.1g-15g
Colouring agent 0.1g-20g
Pearly-lustre product 1g-40g
Liquid wax 1g-10g
Paint thinner 5g-100g.
5. the preparation method of a kind of puffing paint decorative surface according to claim 1, it is characterized in that: described unsaturated-resin is a unsaturated polyester resin.
6. the preparation method of a kind of puffing paint decorative surface according to claim 1, it is characterized in that: described promoter is cobalt water.
7. according to the preparation method of a kind of puffing paint decorative surface according to claim 1, it is characterized in that: described curing agent is a MEK.
8. the preparation method of a kind of puffing paint decorative surface according to claim 1 is characterized in that: described colouring agent is a kind of in toner, look essence or the printing ink.
9. the preparation method of a kind of puffing paint decorative surface according to claim 1 is characterized in that: described diffusant comprises poly-second methylsiloxane, water and auxiliary agent.
10. the preparation method of a kind of puffing paint decorative surface according to claim 1, it is characterized in that: described paint thinner is a Tianna solution.