CN101830091A - Manufacturing method of novel aluminum or stainless steel coated high-grade composite board - Google Patents
Manufacturing method of novel aluminum or stainless steel coated high-grade composite board Download PDFInfo
- Publication number
- CN101830091A CN101830091A CN201010188920A CN201010188920A CN101830091A CN 101830091 A CN101830091 A CN 101830091A CN 201010188920 A CN201010188920 A CN 201010188920A CN 201010188920 A CN201010188920 A CN 201010188920A CN 101830091 A CN101830091 A CN 101830091A
- Authority
- CN
- China
- Prior art keywords
- stainless steel
- composite board
- aluminum
- substrate
- manufacturing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a manufacturing method of a novel aluminum or stainless steel coated high-grade composite board. The manufacturing method comprises the following steps of: (1) taking magnesium oxide or magnesium chloride as an inorganic gelled material, mixing and stirring, mechanically molding, demolding and maintaining to manufacture a baseplate; and (2) compounding an aluminum or stainless steel membrane with a baseplate together by adopting a hot coating membrane method of a hot-pressing roller through combining an aluminum or stainless steel membrane with a high polymer material at the outer surface of the baseplate to form the composite board. The composite board has the characteristics of light weight, high strength, heat resistance, combustion proofness, no toxicity and harms, environmental protection, water resistance, long service life, low cost as well as simple and convenient construction and is a novel product for manufacturing high-grade floors, imitation stones, furniture, cabinets, aluminum-magnesium boards, and the like.
Description
Technical field
The present invention relates to a kind of novel aluminum or stainless steel coated high-grade composite board and manufacture method thereof.
Background technology
The composite decorating board sold on the market at present as aluminium-plastic panel, plastic veneer, polyvinyl chloride decorative plate etc., though have light weight, surface smoothing, bright and clean characteristics, has certain decorative effect.But its maximum defective be high energy consumption, construction technology complexity, long in time limit, cost is high.And do not prevent fires,, discharge toxic and harmful, be absolutely unsafe if the chance fire also can decompose if serviceability temperature greater than 70 ℃, also can be out of shape.
Given this, for addressing the above problem, the inventor groping for many years and accumulating according to oneself, uses institute and gains knowledge, after deliberation, exploitation and the generation of this invention is arranged eventually.
Summary of the invention
The technical issues that need to address of the present invention just are to overcome the defective of prior art, a kind of novel aluminum or stainless steel coated high-grade composite board are provided, it have light weight, intensity height, heat-resisting, do not fire, nontoxic, harmless, environmental protection, waterproof, long service life, cost are low, the characteristics of easy construction, are the novel products of making high-grade floor, imitative stone material, furniture, cabinet, magnalium plate etc.
For addressing the above problem, the present invention adopts following technical scheme:
The manufacture method of a kind of novel aluminum of the present invention or stainless steel coated high-grade composite board, described manufacture method comprises the following steps:
1), with magnesia or magnesium chloride as inorganic coagulation material, through the batch mixing mix, substrate is made in mechanical-moulded, the demoulding and maintenance;
2), at the outer surface of substrate, the hot film covering method that combines with macromolecular material by the hot pressing roller with aluminium or stainless steel membrane is laminated with aluminium or stainless steel membrane and substrate together, forms composite plate.
Described aluminium or stainless steel membrane are laminated with the positive and negative two sides in substrate.
Perhaps, described aluminium or stainless steel membrane are laminated with a single face in substrate.
The present invention is made into substrate with inorganic coagulation materials such as magnesia, magnesium chlorides, substrate have light weight, intensity height, heat-resisting, do not fire, nontoxic, harmless, environmental protection.Again with substrate through with aluminium or clad stainless steel membrane process, make its outer surface be covered with the aluminium film of one deck different-thickness, different colours or stainless steel membrane and make, this product has characteristics such as waterproof, fire prevention, environmental protection, safety, intensity height, with safety, long service life, easy construction, low-carbon (LC), advantage such as energy-conservation.Alternative aluminium-plastic panel is to make high-grade floor, imitative stone material, furniture board, the first-class good merchantable brand of products such as cabinet plate.
Characteristics of the present invention are:
1, with inorganic coagulation materials such as magnesia, magnesium chloride, through the batch mixing mix, operations such as mechanical-moulded, the demoulding, maintenance, make the soleplate of different-thickness and specification, because of magnesia energy high temperature resistant (2800 ℃), magnesium chloride at high temperature can decompose chlorine, the flame that can suffocate, the Gu Te fire prevention.
2, at the outer surface of substrate, combine with macromolecular material by the hot coating technique of hot pressing roller with aluminium or stainless steel membrane and to be laminated with together, common outer surface of substrate is taken on an entirely new look immediately, beautiful colourful, and take into account the two advantage.
Technology of the present invention is simple, and advantage is: fire prevention, waterproof, environmental protection, safety, light weight, intensity height, simple, the low-carbon (LC), energy-conservation of construction, alternative traditional aluminium-plastic panel reduces the consumption of aluminium.It is the regeneration product of making furniture, cabinet plate, decorating inner and external walls plate, floor, imitative stone material etc.
Description of drawings
Fig. 1 is the inventive method step schematic diagram.
The specific embodiment
As shown in Figure 1, comprise the following steps:
1, with inorganic coagulation materials such as magnesia, magnesium chloride, through the batch mixing mix, operations such as mechanical-moulded, the demoulding, maintenance, make the soleplate 1 of different-thickness and specification, because of magnesia energy high temperature resistant (2800 ℃), magnesium chloride at high temperature can decompose chlorine, the flame that can suffocate, the Gu Te fire prevention.
2, at the outer surface of substrate, combine with macromolecular material 3 by hot pressing roller 4 hot coating techniques with aluminium or stainless steel membrane 2 and to be laminated with together, common outer surface of substrate is taken on an entirely new look immediately, beautiful colourful, and take into account the two advantage.
The making of aluminium of the present invention or stainless steel coated composite plate can all be carried out on factory's streamline, working specification, rigorous, quality control is strict, accurate.Various product, specification, kind, meticulous superior.
In sum, aluminium of the present invention or stainless steel coated high-grade composite board have overcome aluminium-plastic panel, plastic veneer, and the high energy consumption of polyvinyl chloride decorative plate is not prevented fires, if catch fire, also easily produce defectives such as toxic and harmful, cost height, construction complexity.The present invention adopts light weight, intensity height, the extremely excellent glass magnesium inorganic material of fire protecting performance to make substrate, pass through streamline hot pressing layer of aluminum or stainless steel coated at substrate surface then, make it obtain high-quality decorative layer, fast light, wear-resisting, fire prevention, waterproof, long service life, cost are low, environmental protection, safe fire-fighting, low-carbon energy-saving.Cost is low, effective, safe, reliable, has practical value, meets the patent of invention condition, so propose application for a patent for invention in accordance with the law.
It should be noted that at last: obviously, the foregoing description only is for example of the present invention clearly is described, and is not the qualification to embodiment.For those of ordinary skill in the field, can also make other changes in different forms on the basis of the above description.Here need not also can't give exhaustive to all embodiments.And conspicuous variation of being extended out thus or change still are among protection scope of the present invention.
Claims (3)
1. a novel aluminum or the manufacture method of stainless steel coated high-grade composite board and the range of application of product, it is characterized in that: described manufacture method comprises the following steps:
1., with magnesia and magnesium chloride inorganic coagulation material as main raw material(s), through the batch mixing mix, substrate is made in mechanical-moulded, the demoulding and maintenance;
2., at the outer surface of substrate, the hot film covering method that combines with macromolecular material by the hot pressing roller with aluminium or stainless steel membrane is laminated with aluminium or stainless steel membrane and substrate together, forms composite plate.
3., this product external surfaces is by the UV photocuring technology, stamps textured patterns such as various different colours, stone material, timber.Be used for indoor and outdoor and decorate, make furniture, cabinet etc.
2. the manufacture method of novel aluminum as claimed in claim 1 or stainless steel coated high-grade composite board is characterized in that: described aluminium or stainless steel membrane are laminated with positive and negative two sides or the single face in substrate.
3. the product that produces of novel aluminum as claimed in claim 1 or stainless steel coated high-grade composite board is characterized in that: the outer surface of product is printed on various different colours by the UV photocuring technology; Be printed on textured patterns such as stone material or timber, be used for indoor and outdoor and decorate, make furniture, cabinet etc.