CN101826765A - 高强度玻璃纤维布引拔槽楔 - Google Patents
高强度玻璃纤维布引拔槽楔 Download PDFInfo
- Publication number
- CN101826765A CN101826765A CN201010146025A CN201010146025A CN101826765A CN 101826765 A CN101826765 A CN 101826765A CN 201010146025 A CN201010146025 A CN 201010146025A CN 201010146025 A CN201010146025 A CN 201010146025A CN 101826765 A CN101826765 A CN 101826765A
- Authority
- CN
- China
- Prior art keywords
- slot wedge
- high intensity
- glass fiber
- fiber cloth
- alkali
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种高强度玻璃纤维布引拔槽楔，由重量比32％-34％无碱玻璃布和无碱玻璃纤维，以及重量比为66％-68％胶粘剂组成。由于引进无碱玻璃布，改进了胶粘剂，增加了槽楔的横向机械强度，使槽楔在高温下具有优异的机械性能和耐溶剂、化学药品性，尤其是在高温下保持较高的抗劈强度，抗劈强度可以达到3000N/10mm以上。完全可以满足电机的运行要求。
Description
技术领域
本发明涉及一种用于电机的部件，尤其涉及一种高强度引拔槽楔，由玻璃纤维布和玻璃纤维纱浸胶后引拔制成，能使引拔槽楔机械强度和抗劈强度大大提高。
背景技术
交、直流电机在正常运行时，固定线圈的槽楔，尤其是转子槽楔，在电磁力作用下需要承受巨大的离心力。此外，由于要求槽楔和槽型紧密配合，所以几何尺寸正确，还要同时具有更高的机械强度，特别是抗劈强度。
发明专利CN101295894公开了一种磁性槽楔及其生产方法，该磁性槽楔包括943不饱和聚酯树脂18％-20％、内脱模剂0.5％-1％、过氧化苯甲酸叔丁酯0.2％-0.5％、过氧化二苯甲酰0.1％-0.3％、增磁材料54％-57％和无碱玻璃纤维24％-25％。其生产方法是按比例把不饱和聚酯树脂、内脱模剂、过氧化物引发剂配制成胶粘剂，加热模具升温至150℃-200℃，引拔速率0.8-1.40r/min，把浸渍胶粘剂的无碱玻璃纤维通过模具拉挤成型后冷却和切割，对切割好的槽楔进行磨头，对槽楔表面油漆处理，使之光洁无毛刺，晾干检测包装。磁性槽楔导磁率高、抗劈强度高、抗弯强度大，其生产方法简单。
目前使用的磁性槽楔多用于电机的定子当中，而电机转子即受到电磁力又受到离心力的作用，因此，现有槽楔难以满足实际要求。
发明内容
本发明的目的是提供一种高强度玻璃纤维布引拔槽楔，以克服现有磁性槽楔用于电机转子时抗机械强度不够的问题。
本发明高强度玻璃纤维布引拔槽楔，由无碱玻璃布和无碱玻璃纤维和胶粘剂组成。其中，无碱玻璃布和无碱玻璃纤维的总和所占的重量比为32％-34％，胶粘剂所占的重量比为66％-68％。
胶粘剂组成，按重量比(％)为：
酚醛环氧改性乙烯基树脂 83-85
低收缩添加剂 2.0-2.5
偶联剂 1.3-1.9
脱模剂 1.5-1.55
助剂 1.6-1.7
拉挤引发剂为本领域常用引发剂，可以参见周承祥发表于《玻璃钢/复合材料》2001(5)的期刊，题为：拉挤的引发系统。
优选的，偶联剂为KH560，化学名称为γ-环氧丙氧基丙基三甲氧基硅烷或γ-缩水甘油醚氧丙基三甲氧基硅烷。
优选的，内脱模剂为TK-4，购自上海松亚化工有限公司。
7.根据权利要求1所述的高强度玻璃纤维布引拔槽楔，其特征是所述的填料为CaCO3、BaSO4或其组合。
本发明高强度玻璃纤维布引拔槽楔制造方法为：将无碱玻璃布和无碱玻璃纤维叠成适当厚度，浸胶后经模具引拔成型。引拔的挤拉速度控制在线速度50-250r/min。引拔温度分三段控制分别为145℃-150℃、165℃-180℃、135℃-145℃，每个温度段时间为1.0-1.5分钟。
本发明技术方案实现的有益效果：
本发明公开的一种高强度玻璃纤维布引拔槽楔，由无碱玻璃布和无碱玻璃纤维和胶粘剂组成。由于引进无碱玻璃布，改进了胶粘剂，增加了槽楔的横向机械强度，使槽楔在高温下具有优异的机械性能和耐溶剂、化学药品性，尤其是在高温下保持较高的抗劈强度，抗劈强度可以达到3000N/10mm以上。完全可以满足电机的运行要求。
具体实施方式
以下详细描述本发明的技术方案。
实施例高强度玻璃纤维布引拔槽楔
将重量比为32％无碱玻璃布和无碱玻璃纤维相叠后浸胶，使胶粘剂占总重量的68％。然后在线速度100r/min挤拉下，温度于145℃-150℃、165℃-180℃和135℃-145℃，每个温度段时间为1.0分钟，最后制得引拔槽楔。
经测试，制得的引拔槽楔的抗劈强度为4200N/10mm。
Claims (7)
1.一种高强度玻璃纤维布引拔槽楔，其特征是由无碱玻璃布、无碱玻璃纤维和胶粘剂组成。
2.根据权利要求1所述的高强度玻璃纤维布引拔槽楔，其特征是所述的无碱玻璃布和所述的无碱玻璃纤维总和所占的重量比为32％-34％。
3.根据权利要求1所述的高强度玻璃纤维布引拔槽楔，其特征是所述的胶粘剂的重量比为66％-68％。
4.根据权利要求1所述的高强度玻璃纤维布引拔槽楔，其特征是所述的胶粘剂，按重量百分比的组成为：
酚醛环氧改性乙烯基树脂 83-85
拉挤引发剂 2.0-2.5
偶联剂 1.3-1.9
内脱模剂 1.5-1.55
颜料 1.6-1.7
填料 8.0-8.5。
5.根据权利要求1所述的高强度玻璃纤维布引拔槽楔，其特征是所述的偶联剂为KH560。
6.根据权利要求1所述的高强度玻璃纤维布引拔槽楔，其特征是所述的内脱模剂为TK-4。
7.根据权利要求1所述的高强度玻璃纤维布引拔槽楔，其特征是所述的填料为CaCO3、BaSO4或其组合。