CN101824665A - 多功能远红外ptt扁平长丝的制备方法 - Google Patents

多功能远红外ptt扁平长丝的制备方法 Download PDF

Info

Publication number
CN101824665A
CN101824665A CN 201010168932 CN201010168932A CN101824665A CN 101824665 A CN101824665 A CN 101824665A CN 201010168932 CN201010168932 CN 201010168932 CN 201010168932 A CN201010168932 A CN 201010168932A CN 101824665 A CN101824665 A CN 101824665A
Authority
CN
China
Prior art keywords
ptt
infrared
far
mass percent
percent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201010168932
Other languages
English (en)
Inventor
席文杰
赵满才
秦志忠
徐醒我
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ZHANGJIAGANG LONGJIE SPECIAL CHEMICAL FIBER CO Ltd
Original Assignee
ZHANGJIAGANG LONGJIE SPECIAL CHEMICAL FIBER CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHANGJIAGANG LONGJIE SPECIAL CHEMICAL FIBER CO Ltd filed Critical ZHANGJIAGANG LONGJIE SPECIAL CHEMICAL FIBER CO Ltd
Priority to CN 201010168932 priority Critical patent/CN101824665A/zh
Publication of CN101824665A publication Critical patent/CN101824665A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种多功能远红外PTT扁平长丝的制备方法，其特征在于：包括如下步骤：将质量百分比为3％～10％的纳米级远红外功能微粒和质量百分比为2％～6％的香型微胶囊，以及质量百分比为1％～3％的粒径在1微米以下的电气石与质量百分比为81％～94％的PTT共混制备成母粒，然后将质量百分比为3～5％的母粒均匀分散在PTT切片中，经干燥、熔融挤压后，使熔体流经喷丝板制得成品，所述的喷丝板的喷丝孔为长宽比为5～10的矩形喷丝孔，喷丝板的孔数为12～144之间。本发明所制备的产品适用于制造内衣、晚礼服、玩具和绒类制品。

Description

多功能远红外PTT扁平长丝的制备方法
技术领域
本发明涉及纺织工程技术领域。
背景技术
聚对苯二甲酸丙二醇酯(简称PTT)纤维是由美国Shell Chemical(壳牌化学公司)于1995年研制成功的新型纺丝聚合物。PTT纤维与聚对苯二甲酸乙二醇酯(简称PET)纤维、聚对苯二甲酸1.4丁二醇酯(简称PBT)纤维同属聚酯纤维。PTT纤维作为一种新型合成聚酯纤维，具有以下特点：
(1)PTT纤维兼有PET纤维的稳定性和PBT纤维的柔软性，其织物手感柔软、飘逸；
(2)有优异的伸长恢复性，经过适当的拉伸后可回复到原状；
(3)在110℃～120℃范围内可染成深色，适宜于与纤维素或天然纤维混纺。
但是由于PTT晶体中大分子链构象，使得PTT的大分子链呈明显的“Z”字形构象，分子链具有如同线圈式弹簧一样变形的弹性，目前国内外厂家生产PTT长丝时，PTT切片经干燥、熔融挤压后，使熔体流经喷丝板制得成品，所述的喷丝板均采用圆形喷丝孔的喷丝板，此种PTT长丝所织造的服装悬垂性差、容易起球，不适用于内衣、晚礼服等产品。
随着社会经济发展水平和人民生活水平的不断提高，人们对服装面料的高档化、舒适化的要求越来越高。具有远红外功能和散发香味功能的长丝面料越来越受到人们的青睐。但是目前国内外市场尚未出现兼具远红外功能和散发香味功能的长丝。
发明内容
本发明所要解决的技术问题是：提供一种悬垂性好、抗起球，又兼具远红外功能和散发香味功能的多功能远红外PTT扁平长丝的制备方法。
为解决上述问题，本发明采用的技术方案是：多功能远红外PTT扁平长丝的制备方法，包括如下步骤：将质量百分比为3％～10％的纳米级远红外功能微粒和质量百分比为2％～6％的香型微胶囊，以及质量百分比为1％～3％的粒径在1微米以下的电气石与质量百分比为81％～94％的PTT共混制备成母粒，然后将质量百分比为3～5％的母粒均匀分散在PTT切片中，经干燥、熔融挤压后，使熔体流经喷丝板制得成品，所述的喷丝板的喷丝孔为长宽比为5～10的矩形喷丝孔，喷丝板的孔数为12～144之间。
所述的母粒制备工序中，对纳米级远红外功能微粒、香型微胶囊及电气石均进行表面稳定化处理。
本发明的有益效果是：多功能远红外PTT扁平长丝的物理性能指标：
  项目   数值
  断裂强度(CN/dtex)   3.96
  项目   数值
  断裂强度变异系数(％)   0.645
  断裂伸长(％)   38
  断裂伸长变异系数(％)   2.8
  含油(％)   1.2-1.6
  沸水收縮率(％)   6.3
  网络度(个/米   10
  远红外释放率(洗涤50次)   ＞96％
  香味释放率(洗涤50次)   ＞85％
  负氧离子释放率(洗涤50次)   ＞96％
用多功能远红外PTT扁平长丝织造的织物手感好、垂性好、抗起球、美观大方，经过轻轻摩擦可以释放出香味，使穿着者心情舒畅、愉快，可不断释放负氧离子和远红外波，具有保健功能。
具体实施方式
下面对本发明多功能远红外PTT扁平长丝的制备方法作进一步的详细描述。
实施例1
多功能远红外PTT扁平长丝的制备方法，包括如下步骤：将质量百分比为3％的纳米级远红外功能微粒和质量百分比为2％的香型微胶囊，以及质量百分比为1％的粒径在0.8微米的电气石与质量百分比为94％的PTT共混制备成母粒，所述的母粒制备工序中，对纳米级远红外功能微粒、香型微胶囊及电气石均进行表面稳定化处理，然后将质量百分比为3％母粒均匀分散在PTT切片中，经干燥、熔融挤压后，使熔体流经喷丝板制得成品，所述的喷丝板的喷丝孔为长宽比为6的矩形喷丝孔，喷丝板的孔数为100个。
实施例2
多功能远红外PTT扁平长丝的制备方法，包括如下步骤：将质量百分比为10％的纳米级远红外功能微粒和质量百分比为6％的香型微胶囊，以及质量百分比为3％的粒径在0.9微米的电气石与质量百分比为81％的PTT共混制备成母粒，所述的母粒制备工序中，对纳米级远红外功能微粒、香型微胶囊及电气石均进行表面稳定化处理，然后将质量百分比为4％母粒均匀分散在PTT切片中，经干燥、熔融挤压后，使熔体流经喷丝板制得成品，所述的喷丝板的喷丝孔为长宽比为7的矩形喷丝孔，喷丝板的孔数为50个。
实施例3
多功能远红外PTT扁平长丝的制备方法，包括如下步骤：将质量百分比为6％的纳米级远红外功能微粒和质量百分比为4％的香型微胶囊，以及质量百分比为2％的粒径在0.7微米的电气石与质量百分比为88％的PTT共混制备成母粒，所述的母粒制备工序中，对纳米级远红外功能微粒、香型微胶囊及电气石均进行表面稳定化处理，然后将质量百分比为5％母粒均匀分散在PTT切片中，经干燥、熔融挤压后，使熔体流经喷丝板制得成品，所述的喷丝板的喷丝孔为长宽比为7的矩形喷丝孔，喷丝板的孔数为90个。
本发明的有益效果是：多功能远红外PTT扁平长丝的物理性能指标：
  项目   数值
  断裂强度(CN/dtex)   3.96
  断裂强度变异系数(％)   0.645
  断裂伸长(％)   38
  断裂伸长变异系数(％)   2.8
  含油(％)   1.2-1.6
  沸水收縮率(％)   6.3
  网络度(个/米   10
  远红外释放率(洗涤50次)   ＞96％
  香味释放率(洗涤50次)   ＞85％
  负氧离子释放率(洗涤50次)   ＞96％
用多功能远红外PTT扁平长丝织造的织物手感好、垂性好、抗起球、美观大方，经过轻轻摩擦可以释放出香味，使穿着者心情舒畅、愉快，可不断释放负氧离子和远红外波，具有保健功能。

Claims (2)

1.多功能远红外PTT扁平长丝的制备方法，其特征在于：包括如下步骤：将质量百分比为3％～10％的纳米级远红外功能微粒和质量百分比为2％～6％的香型微胶囊，以及质量百分比为1％～3％的粒径在1微米以下的电气石与质量百分比为81％～94％的PTT共混制备成母粒，然后将质量百分比为3～5％的母粒均匀分散在PTT切片中，经干燥、熔融挤压后，使熔体流经喷丝板制得成品，所述的喷丝板的喷丝孔为长宽比为5～10的矩形喷丝孔，喷丝板的孔数为12～144之间。
2.根据权利要求1所述的多功能远红外PTT扁平长丝的制备方法，其特征在于：所述的母粒制备工序中，对纳米级远红外功能微粒、香型微胶囊及电气石均进行表面稳定化处理。
CN 201010168932 2010-05-06 2010-05-06 多功能远红外ptt扁平长丝的制备方法 Pending CN101824665A (zh)