CN101817938A - 淀粉透明包装材料及其生产方法 - Google Patents
淀粉透明包装材料及其生产方法 Download PDFInfo
- Publication number
- CN101817938A CN101817938A CN 201010127456 CN201010127456A CN101817938A CN 101817938 A CN101817938 A CN 101817938A CN 201010127456 CN201010127456 CN 201010127456 CN 201010127456 A CN201010127456 A CN 201010127456A CN 101817938 A CN101817938 A CN 101817938A
- Authority
- CN
- China
- Prior art keywords
- flour
- tapioca
- parts
- packaging material
- starch
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及塑料加工领域,具体涉及一种包装材料及其生产方法。淀粉透明包装材料,包括下述重量份数的原料制成:木薯淀粉70~90份,丙三醇5~20份,蒸馏水1~3份,润滑剂3~5份。淀粉透明包装材料的生产方法,包括以下步骤:1)将木薯淀粉、丙三醇和蒸馏水加入到有加压装置的密炼机中,密炼到物料温度达到95℃~135℃时,继续密炼,使木薯淀粉出现熔融体,这时加入润滑剂,再密炼10分钟,直至木薯淀粉完全变成半透明的木薯淀粉熔融体;2)把半透明的木薯淀粉熔融体送入单螺杆挤出机中进行磨面热切、风冷包装。本发明具有价格低廉、可循环使用、降解能力强等优点。
Description
技术领域
本发明涉及塑料加工领域,具体涉及一种包装材料及其生产方法。
背景技术
在工业化进程日趋加快的21世纪,石油资源更趋紧张,构建节约型社会,走可持续性发展道路已成为全球关注焦点和世界各国追求的健康经济发展目标。为适应新时代的要求,应对环境资源问题及金融危机的严重挑战。塑料包装材料的发展已经开始向低能耗、绿色环保、可循环利用的方向转变。植物淀粉塑料是塑料包装材料中新兴起的一种绿色环保再生资源型材料,植物淀粉塑料自问世以来得到了迅速发展,先后经历了淀粉填充型塑料、接枝共聚型淀粉塑料和热塑性塑料三个阶段。
众多研究结果表明,早期发展的填充型淀粉塑料,接枝共聚型淀粉塑料,这些材料只是用在一次性可降解包装制品中。由于这些材料加工工艺都是在高速搅拌机搅拌、同向平行双螺杆挤出造粒而得产品,因此这种淀粉塑料在终端产品加工和应用性能上仍不稳定,制品无法回收利用。而聚乳酸(PLA)、聚己内酯(PCL)、聚丁二酸丁二醇酯(PBS)等热塑性塑料其价格比传统塑料高25~30%左右,大规模推广起来,实际的操作性上受到了很大的局限。
发明内容
本发明的目的在于,提供一种淀粉透明包装材料,解决上述技术问题。本发明的目的还在于,提供一种淀粉透明包装材料的生产方法,解决上述技术问题。
本发明所解决的技术问题可以采用以下技术方案来实现:
淀粉透明包装材料,其特征在于,包括下述相混合的多种原料,多种原料名称及重量份数如下:木薯淀粉70~90份,丙三醇5~20份,蒸馏水1~3份,润滑剂3~5份。
本发明的植物淀粉来源于可再生资源的木薯淀粉,水分含量为17%左右,绿色环保,可循环利用,采用木薯淀粉制成的塑料制品降解能力强,可补充、替代石油基塑料,且木薯淀粉价格低,可有效降低成本。
所述润滑剂为蓖麻油。蓖麻油是可再生性资源,绿色环保。
淀粉透明包装材料的生产方法,其特征在于,包括以下步骤:
1)将木薯淀粉、丙三醇和蒸馏水加入到有加压装置的密炼机中,密炼到物料温度达到95℃~135℃时,木薯淀粉中的水分开始向外蒸发,木薯淀粉在密炼机中继续密炼,使木薯淀粉出现熔融体,这时加入润滑剂,再密炼10分钟,直至木薯淀粉完全变成半透明的木薯淀粉熔融体;
采用加压、密封的密炼机可使木薯淀粉蒸发的水分与丙三醇相遇,并相容在一起对木薯淀粉增塑。这样的增塑剂可以明显降低木薯淀粉大分子间的相互作用力,破坏木薯淀粉的高结晶度,使木薯淀粉玻璃化转变温度降低而具有可塑性。
2)把所述半透明的木薯淀粉熔融体送入单螺杆挤出机中进行磨面热切、风冷包装,即为可塑性柔软的淀粉透明包装材料。
所述单螺杆挤出机的压缩比为3.2,螺杆长径比为1∶20。由于单螺杆挤出机大压缩比、螺杆长径比小,使得半透明的木薯淀粉熔融体二次高压增塑,制成的淀粉透明包装材料在加工和应用上具有很好的稳定性,采用淀粉透明包装材料所制成的塑料制品具有降解能力强、绿色环保、可循环利用等优点。
步骤1)中,所述木薯淀粉70~90份,所述丙三醇5~20份,所述蒸馏水1~3份,所述润滑剂3~5份。
所述润滑剂为蓖麻油。
有益效果:本发明主要成分为可再生资源的木薯淀粉,使本发明具有价格低廉、可循环使用、降解能力强等优点。采用本发明制成的植物淀粉塑料在加工和应用上具有很好的稳定性,且具有绿色环保、价格低廉、可循环使用等优点。本发明与生物降解材料如:聚乳酸(PLA)、聚己内酯(PCL)、聚丁二酸丁二醇酯(PBS)等共混改性,能制备出成本低廉、全生物降解塑料制品。
附图说明
图1为本发明生产方法的流程示意图。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体图示进一步阐述本发明。
参照图1,淀粉透明包装材料包括下述相混合的多种原料,多种原料名称及重量份数如下:木薯淀粉70~90份,丙三醇5~20份,蒸馏水1~3份,润滑剂3~5份。润滑剂为蓖麻油。
淀粉透明包装材料的生产方法,包括以下步骤:第1步:将木薯淀粉、丙三醇和蒸馏水加入到有加压装置的密炼机中11,密炼12,到物料温度达到95℃~135℃时,木薯淀粉中的水分开始向外蒸发,木薯淀粉在密炼机中继续密炼,使木薯淀粉出现熔融体,这时加入润滑剂13,再密炼10分钟14,直至木薯淀粉完全变成半透明的木薯淀粉熔融体;第2步:把半透明的木薯淀粉熔融体送入单螺杆挤出机中21,进行磨面热切22、风冷包装23,即为可塑性柔软的淀粉透明包装材料。单螺杆挤出机的压缩比为3.2,螺杆长径比为1∶20。第1步中,木薯淀粉70~90份,丙三醇5~20份,蒸馏水1~3份,润滑剂3~5份。润滑剂为蓖麻油。
实施例一:
取木薯淀粉70份,丙三醇25份,蒸馏水1.5份,润滑剂3.5份;将上述配比的木薯淀粉、丙三醇和蒸馏水加入到有加压装置的密炼机中,密炼到物料温度达到95℃时,木薯淀粉中的水分开始向外蒸发,木薯淀粉在密炼机中继续密炼,使木薯淀粉出现熔融体,此时加入润滑剂,再密炼10分钟,直至木薯淀粉完全变成半透明的木薯淀粉熔融体;把半透明的木薯淀粉熔融体送入压缩比为3.2,螺杆长径比为1∶20的单螺杆挤出机中进行磨面热切、风冷包装,即为可塑性柔软的淀粉透明包装材料。
实施例二:
取木薯淀粉85份,丙三醇8份,蒸馏水2份,润滑剂5份;将上述配比的木薯淀粉、丙三醇和蒸馏水加入到有加压装置的密炼机中,密炼到物料温度达到95℃时,木薯淀粉中的水分开始向外蒸发,木薯淀粉在密炼机中继续密炼,使木薯淀粉出现熔融体,此时加入润滑剂,再密炼10分钟,直至木薯淀粉完全变成半透明的木薯淀粉熔融体;把半透明的木薯淀粉熔融体送入压缩比为3.2,螺杆长径比为1∶20的单螺杆挤出机中进行磨面热切、风冷包装,即为可塑性柔软的淀粉透明包装材料。
实施例三:
取木薯淀粉90份,丙三醇6份,蒸馏水1份,润滑剂3份;将上述配比的木薯淀粉、丙三醇和蒸馏水加入到有加压装置的密炼机中,密炼到物料温度达到95℃时,木薯淀粉中的水分开始向外蒸发,木薯淀粉在密炼机中继续密炼,使木薯淀粉出现熔融体,此时加入润滑剂,再密炼10分钟,直至木薯淀粉完全变成半透明的木薯淀粉熔融体;把半透明的木薯淀粉熔融体送入压缩比为3.2,螺杆长径比为1∶20的单螺杆挤出机中进行磨面热切、风冷包装,即为可塑性柔软的淀粉透明包装材料。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (6)
1.淀粉透明包装材料,其特征在于,包括下述相混合的多种原料,多种原料名称及重量份数如下:木薯淀粉70~90份,丙三醇5~20份,蒸馏水1~3份,润滑剂3~5份。
2.根据权利要求1所述的淀粉透明包装材料,其特征在于:所述润滑剂为蓖麻油。
3.淀粉透明包装材料的生产方法,其特征在于,包括以下步骤:
1)将木薯淀粉、丙三醇和蒸馏水加入到有加压装置的密炼机中,密炼到物料温度达到95℃~135℃时,木薯淀粉中的水分开始向外蒸发,木薯淀粉在密炼机中继续密炼,使木薯淀粉出现熔融体,这时加入润滑剂,再密炼10分钟,直至木薯淀粉完全变成半透明的木薯淀粉熔融体;
2)把所述半透明的木薯淀粉熔融体送入单螺杆挤出机中进行磨面热切、风冷包装,即为可塑性柔软的淀粉透明包装材料。
4.根据权利要求3所述的淀粉透明包装材料的生产方法,其特征在于:所述单螺杆挤出机的压缩比为3.2、螺杆长径比为1∶20。
5.根据权利要求3或4所述的淀粉透明包装材料的生产方法,其特征在于:步骤1)中,所述木薯淀粉70~90份,所述丙三醇5~20份,所述蒸馏水1~3份,所述润滑剂3~5份。
6.根据权利要求5所述的淀粉透明包装材料的生产方法,其特征在于:所述润滑剂为蓖麻油。