CN101812256A - Preprinted oil polish for high-temperature resistant carton - Google Patents
Preprinted oil polish for high-temperature resistant carton Download PDFInfo
- Publication number
- CN101812256A CN101812256A CN 200910037352 CN200910037352A CN101812256A CN 101812256 A CN101812256 A CN 101812256A CN 200910037352 CN200910037352 CN 200910037352 CN 200910037352 A CN200910037352 A CN 200910037352A CN 101812256 A CN101812256 A CN 101812256A
- Authority
- CN
- China
- Prior art keywords
- preprinted
- temperature resistant
- oil polish
- percent
- carton
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to the technical field of ink, in particular to preprinted oil polish for a high-temperature resistant carton. The preprinted oil polish comprises the following components in percentage by weight: 50 to 80 percent of acrylic resin emulsion, 5 to 20 percent of alkaline solubility colloid, 0.1 to 1 percent of defoaming agent, 0.1 to 1 percent of levelling agent, 1 to 10 percent of wax, 1 to 10 percent of ethanol and water. The preprinted oil polish has good lustrousness, ensures the corrugated compounding and using performance, and improves the high-temperature resistance by a higher level compared with similar high-temperature resistant ink prepared by acrylic resin; and the preprinted oil polish can resist high temperature of 240 DEG C maximally, can meet the requirement of high-grade printing, and has the advantages of simple preparation, low cost, environment friendliness, innocuity, stable performance, light air pollution, no residue of toxic solvent, and contribution to safe production and environmental protection.
Description
Technical field:
The present invention relates to technical field of ink, relate in particular to a kind of Preprinted oil polish for high-temperature resistant carton.
Background technology:
The colored Corrugated Box of traditional mode of production is directly to utilize the flexographic printing technology to print on the good carton of cross cutting, the carton pattern that this technology makes is simple, color is dirty, gorgeous inadequately, and because pressure is excessive, rough corrugation phenomenon also might appear in the carton surface, and this technology generally is applied in the lower packing of class.
The offset lithography technology then occurs and produce carton, on individual carton facial tissue, adopt offset printing, utilize facing machine that the facial tissue and the fluting board that print is bonding then, pass through shape by die-cutting again.The carton pattern that this method makes is abundanter, bright in luster, saturated, but production efficiency is still lower, and the stability of product batches be cannot say for sure to demonstrate,prove, because offset printing belongs to paste printing ink, on-the-spot adjustment form and aspect difficulty is bigger.
Along with development of science and technology, occur gentle version carton in recent years and preprinted technology, mainly be to adopt large-scale set type flexible printing machine, reel is to web printing, the rolled paper that prints directly goes up corrugated paper production line as the carton facial tissue and corrugation is combined into cardboard, again shape by die-cutting.This method is compared with preceding two kinds has remarkable advantages: the production efficiency height, stability is high between same batch, carton intensity height.Preprint in the technology because the printing ink difference that adopts can be divided into water-based and solvent-borne type at gentle version carton, wherein water color ink to little many of human injury, meets the trend of present global environmental protection than solvent-borne type; Simultaneously at printing effect, the color and luster degree, vividness, saturation ratio substantially all can reach the solvent-borne type effect.
The carton that aqueous flexible plate carton Preprinted ink cooperates the waterborne preprinting gloss oil to make has splendid effect, and cost is also lower with respect to flexographic ink, and is less to the influence of surrounding environment, and human body is not had injury substantially, is real environmentfriendly products.
At present, Chinese patent, application number is: 200610062147.9 application for a patent for invention file discloses a kind of aqueous flexible plate printing ink and preparation method thereof, it comprises film-forming resin emulsion 8.7-47.2%, water soluble acrylic acid mill base 40-50%, defoamer 0.1-0.3%, water-based wax slurry 0.2-2.0%, Virahol 2-8%, ethylene glycol 10-30%, thanomin 0.5-1%, surplus is a water; The disclosed aqueous flexible plate printing ink of this file has advantages such as trace is clear, low production cost; This printing ink is for good to halftone paper printing adaptability, but the poor effect on cardboard box printing.Chinese patent, application number is: 200710075177.8 application for a patent for invention file, disclose a kind of aqueous flexible plate printing ink, comprised pigment 30～35%, acrylic resin 25～32%, defoamer 0.2～0.5%, ethylene glycol monomethyl ether 2～5%, wax slurry 1.0～2.5%, flow agent 0.9～1.5%, water 23～30%; But non-refractory in the higher occasion of temperature, phenomenons such as welding decolouring occur easily.
Summary of the invention:
The objective of the invention is at the deficiencies in the prior art, and disclose a kind of good glossiness that not only has, and environment-protecting asepsis, especially can tolerate the carton Preprinted ink of comparatively high temps.
The objective of the invention is to be achieved by the following method:
A kind of Preprinted oil polish for high-temperature resistant carton; Comprise following raw materials by weight percent:
Emulsion acrylic resin 50%～80%
Caustic solubility colloid 5%～20%
Defoamer 0.1%～1%
Flow agent 0.1%～1%
Wax 1%～10%
Ethanol 1%～10%
Water 1%～20%.
A kind of Preprinted oil polish for high-temperature resistant carton; Comprise following raw materials by weight percent:
Emulsion acrylic resin 60%～70%
Caustic solubility colloid 10%～15%
Defoamer 0.2%～0.5%
Flow agent 0.5%～1%
Wax 2%～4%
Ethanol 1%～2%
Water 7%～12%.
Wherein, described caustic solubility colloid is an acrylic copolymer.
Described defoamer is a mineral oil antifoam agent.
Described flow agent is the polyacrylic flow agent.
Described defoamer is a dimethylsilicone oil.
The preparation method of Preprinted ink for high-temperature resistant carton is as follows: the caustic solubility colloid of aforementioned proportion amount is added entry, adding defoamer, flow agent and ethanol again stirs, add acrylic resin, wax and vinylformic acid mill base after fully stirring evenly again, stir and get final product.
The invention has the beneficial effects as follows, the present invention includes Emulsion acrylic resin, caustic solubility colloid, defoamer, flow agent, wax, second alcohol and water, is primary solvent with water, has good glossiness, the highest can anti-240 ℃ of high temperature, guarantee the compound and use properties of corrugation.The present invention is with respect to the high temperature resistant printing ink of other waterborne preprinting; degree ability that it is high temperature resistant has improved a higher level; this not only can satisfy the requirement of high-grade printing; and preparation is simple, cost is lower, environment-protecting asepsis, stable performance, low to topsoil; no noxious solvent is residual, helps safety in production and environment protection.
Embodiment:
The invention will be further described below in conjunction with example, and the following examples can be used for making those skilled in the art more fully to understand the present invention, but do not limit the present invention in any way.
Embodiment 1
A kind of Preprinted oil polish for high-temperature resistant carton; Comprise following raw materials by weight percent: 50% Emulsion acrylic resin, 20% acrylic copolymer, 1% dimethylsilicone oil, 0.1% flow agent, 1% wax, 1% second alcohol and water.
The preparation method of Preprinted ink for high-temperature resistant carton is as follows: the caustic solubility colloid of aforementioned proportion amount is added entry, adding defoamer, flow agent and ethanol again stirs, add acrylic resin, wax and vinylformic acid mill base after fully stirring evenly again, stir and get final product.
Embodiment 2
A kind of Preprinted oil polish for high-temperature resistant carton; Comprise following raw materials by weight percent: 60% Emulsion acrylic resin, 10% acrylic copolymer, 0.2 defoamer, 1% flow agent, 10% wax, 5% second alcohol and water.
The preparation method is with embodiment 1.
Embodiment 3
A kind of Preprinted oil polish for high-temperature resistant carton; Comprise following raw materials by weight percent: 70% Emulsion acrylic resin, 12% acrylic copolymer, 0.2% defoamer, 0.5% flow agent, 2% wax, 1% second alcohol and water.
The preparation method is with embodiment 1.
Embodiment 4
A kind of Preprinted oil polish for high-temperature resistant carton; Comprise following raw materials by weight percent: 80% Emulsion acrylic resin, 5% acrylic copolymer, 0.1% defoamer, 0.5% flow agent, 4% wax, 2% second alcohol and water.
The preparation method is with embodiment 1.
Embodiment 5
A kind of Preprinted oil polish for high-temperature resistant carton; Comprise following raw materials by weight percent: 60% Emulsion acrylic resin, 15% acrylic copolymer, 0.3% defoamer, 0.8% flow agent, 3% wax, 1% second alcohol and water.
The preparation method is with embodiment 1.
Embodiment 6
A kind of Preprinted oil polish for high-temperature resistant carton; Comprise following raw materials by weight percent: 55% Emulsion acrylic resin, 10% acrylic copolymer, 0.5% defoamer, 0.5% flow agent, 2% wax, 1% second alcohol and water.
The preparation method is with embodiment 1.
Embodiment 7
A kind of Preprinted oil polish for high-temperature resistant carton; Comprise following raw materials by weight percent: 65% Emulsion acrylic resin, 5% acrylic copolymer, 0.1% defoamer, 0.1% flow agent, 10% wax, 10% second alcohol and water.
The preparation method is with embodiment 1.
Claims (6)
1. Preprinted oil polish for high-temperature resistant carton; It is characterized in that: comprise following raw materials by weight percent:
Emulsion acrylic resin 50%～80%
Caustic solubility colloid 5%～20%
Defoamer 0.1%～1%
Flow agent 0.1%～1%
Wax 1%～10%
Ethanol 1%～10%
Water 1%～20%.
2. a kind of Preprinted oil polish for high-temperature resistant carton according to claim 1; It is characterized in that: comprise following raw materials by weight percent:
Emulsion acrylic resin 60%～70%
Caustic solubility colloid 10%～15%
Defoamer 0.2%～0.5%
Flow agent 0.5%～1%
Wax 2%～4%
Ethanol 1%～2%
Water 7%～12%.
3. according to any described a kind of Preprinted oil polish for high-temperature resistant carton among the claim 1-2; It is characterized in that: described caustic solubility colloid is an acrylic copolymer.
4. according to any described a kind of Preprinted oil polish for high-temperature resistant carton among the claim 1-2; It is characterized in that: described defoamer is a mineral oil antifoam agent.
5. according to any described a kind of Preprinted oil polish for high-temperature resistant carton among the claim 1-2; It is characterized in that: described flow agent is the polyacrylic flow agent.
6. a kind of Preprinted oil polish for high-temperature resistant carton according to claim 4; It is characterized in that: described defoamer is a dimethylsilicone oil.