CN101798686A - 一种显示invar钢及其焊接接头金相组织的化学侵蚀剂及制备方法 - Google Patents

一种显示invar钢及其焊接接头金相组织的化学侵蚀剂及制备方法 Download PDF

Info

Publication number
CN101798686A
CN101798686A CN 201010126650 CN201010126650A CN101798686A CN 101798686 A CN101798686 A CN 101798686A CN 201010126650 CN201010126650 CN 201010126650 CN 201010126650 A CN201010126650 A CN 201010126650A CN 101798686 A CN101798686 A CN 101798686A
Authority
CN
China
Prior art keywords
chemical erosion
invar steel
chromium trioxide
erosion agent
hydrochloric acid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201010126650
Other languages
English (en)
Inventor
王晓荣
顾青妹
廖祎
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hudong Zhonghua Shipbuilding Group Co Ltd
Original Assignee
Hudong Zhonghua Shipbuilding Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hudong Zhonghua Shipbuilding Group Co Ltd filed Critical Hudong Zhonghua Shipbuilding Group Co Ltd
Priority to CN 201010126650 priority Critical patent/CN101798686A/zh
Publication of CN101798686A publication Critical patent/CN101798686A/zh
Pending legal-status Critical Current

Abstract

本发明涉及到一种显示INVAR钢及其焊接接头金相组织的化学侵蚀剂及其制备方法,每一份该种化学侵蚀剂包括如下成份:三氧化铬CrO3 3~10g;盐酸HCL(分析纯) 30~100ml;水H2O 30~100ml;其方法包括如下步骤:①按照每份侵蚀剂的配方称量所需原料;②先将所述的三氧化铬加入到水中,搅拌至其完全溶解,形成混合溶液;然后将分析纯盐酸缓慢地加入至上述混合溶液中,并搅拌均匀,制成所需的化学侵蚀剂。本发明的用于显示INVAR钢及其焊接接头金相组织的化学侵蚀剂具有良好的侵蚀效果且侵蚀速度快、效率高、能长期放置,对于INVAR钢及其焊接接头金相检验具有极高的推广应用价值。

Description

一种显示INVAR钢及其焊接接头金相组织的化学侵蚀剂及制备方法
技术领域
本发明涉及化学侵蚀剂,特别是涉及到一种显示INVAR钢及其焊接接头金相组织的化学侵蚀剂及其制备方法。
背景技术
金相检验是现代工业中常用的一种试验方法,是控制机械产品质量,新材料、新工艺、新产品研究开发中的重要手段。它是指通过显微镜对金属材料的金相组织进行观察并作出定性鉴别和定量测量的过程,如确定合金中各组成相的尺寸、形状和分布特征、晶粒度、夹杂物类型和数量,以及表面处理层的组织等。它能提供有关金属材料的基体组织、晶粒度、第二相等参数的定性或定量的试验结果,也能提供关于各种材料缺陷的信息。
金相检验技术的最基础要求是使金属材料显示出清晰、准确的金相组织,以便通过显微镜观察。应用最早和最广泛的金相组织显示方法是化学侵蚀法,也是目前显示金属金相组织的主要办法。化学侵蚀实际上是一个电化学反应过程,它是将抛光好的金相试样磨面浸入化学侵蚀剂中或用化学侵蚀剂擦拭试样磨面,使之显示出金相组织的一种方法。它的原理是:在化学侵蚀剂的作用下,试样表面有选择性地溶解掉某些部分,使金相试样表面上的不同部分和组织成分,具有不同的反光能力,在用金相显微镜观察时出现反差,从而显示出金相组织。因此,在金相检验时,要根据不同金属材料的类别以及检验目的选取最合适的化学侵蚀剂。
INVAR钢是一种含Ni 36%的特殊合金,是薄膜型液化天然气运输船液货舱专用内衬材料。其用于结构件的厚度<1mm,工作温度为-196℃,具有从室温至工作温度范围内膨胀系数值小、膨胀系数变化小,低温强度高、不变脆,成型及焊接性能良好,能吸收冲击疲劳和振动等特点。
根据薄膜型液化天然气运输船液货舱建造规范要求,对INVAR钢焊接结构必须进行焊接接头金相组织的检测。由于INVAR钢材料特殊,常用化学侵蚀剂无法使之显示出金相组织;而国外技术文件GTT No.96Contatinment System for LNG Carrier(External document No1096-1))提供的INVAR钢浸蚀剂配方:50毫升蒸馏水、50毫升94%-95%酒精、50毫升盐酸、20克含5个结晶水的硫酸铜,在实际应用中存在着以下不足:1.侵蚀速度慢,侵蚀时间需十分钟以上甚至更长。2.侵蚀剂有效期短、无法久置使用,需始终使用新配置试剂。3.侵蚀结果不稳定,无法稳定获得能清晰观察的金相组织。
发明内容
本发明的目的在于克服上述现有技术存在的不足,提供一种显示INVAR钢及其焊接接头金相组织的化学侵蚀剂及其制备方法。该种新配方的化学侵蚀剂侵蚀速度快、有效期长、侵蚀效果良好稳定,适应企业生产中快速金相检验的需要。
为了达到上述发明目的,本发明提供如下技术方案:
一种显示INVAR钢及其焊接接头金相组织的化学侵蚀剂,其特征在于,每一份该种化学侵蚀剂包括如下成份:
三氧化铬CrO3                3~10g
盐酸HCL(分析纯)             30~100ml
水H2O                       30~100ml。
所述的化学侵蚀剂包括如下优化成份:
三氧化铬CrO3                5~8g
盐酸HCL(分析纯)              50~80ml
水H2O                        30~80ml
一种制备上述的显示INVAR钢及其焊接接头金相组织的化学侵蚀剂的方法,该方法包括如下步骤:
①按照每份侵蚀剂的配方称量所需原料,包括三氧化铬、分析纯盐酸和水;
②先将所述的三氧化铬加入到水中,搅拌至其完全溶解,形成混合溶液;
③然后将分析纯盐酸缓慢地加入至上述混合溶液中,并搅拌均匀,制成所需的化学侵蚀剂。
当需要侵蚀时,只需将抛光好的金相试样检验面浸入该化学侵蚀剂中或用该化学侵蚀剂擦拭试样检验面,至试样检验面光泽变成灰暗即可,时间约为5~30秒,侵蚀温度15~25℃。
基于上述技术方案,本发明的化学侵蚀剂较现有技术具有如下技术优点:
①本发明是一种具有快速侵蚀速度的化学侵蚀剂,将其应用于INVAR钢及其焊接接头能够清晰地显示金相组织结构。
②本发明存放期限为六个月左右,期间内不会发生侵蚀剂失效的问题,能随时使用。
具体实施方式
下面我们结合具体的实施例来对本发明的化学侵蚀剂及其制备方法做进一步的详细阐述,但不能以此来限制本发明的保护范围。
一种显示INVAR钢及其焊接接头金相组织的化学侵蚀剂,其特征在于,每一份该种化学侵蚀剂包括如下成份:
三氧化铬CrO3           3~10g
盐酸HCL(分析纯)        30~100ml
水H2O                  30~100ml。
实施例1:
三氧化铬CrO3           3g
盐酸HCL(分析纯)        30ml
水H2O                  30ml。
实施例2:
三氧化铬CrO3           5g
盐酸HCL(分析纯)        50ml
水H2O                  50ml。
实施例3:
三氧化铬CrO3           10g
盐酸HCL(分析纯)        100ml
水H2O                  100ml。
上述实施例的配制及使用方法
制备上述的显示INVAR钢及其焊接接头金相组织的化学侵蚀剂的方法,该方法包括如下步骤:
①按照每份侵蚀剂的配方称量所需原料,包括三氧化铬、分析纯盐酸和水;
②先将所述的三氧化铬加入到水中,搅拌至其完全溶解,形成混合溶液;
③然后将分析纯盐酸缓慢地加入至上述混合溶液中,并搅拌均匀,制成所需的化学侵蚀剂。
当侵蚀时,只需将抛光好的金相试样检验面浸入该化学侵蚀剂中或用该化学侵蚀剂擦拭试样检验面,至试样检验面光泽变成灰暗即可,时间为5~30秒,侵蚀温度15~25℃。
具体实施效果详细说明如下:
经侵蚀后的焊接试样,能清晰的显示焊接接头的外观质量、焊缝与母材之间的熔合线、母材区内的热影响区、焊缝内焊道与焊道之间的界线以及焊缝的枝晶分布状况,能十分方便地测量焊缝高度(包括公称焊缝高度和最小焊缝厚度),且结果精确有效。
经使用证明,本发明的用于显示INVAR钢及其焊接接头金相组织的化学侵蚀剂具有良好的侵蚀效果且侵蚀速度快、效率高、能长期放置,对于INVAR钢及其焊接接头金相检验具有极高的推广应用价值。

Claims (3)

1.一种显示INVAR钢及其焊接接头金相组织的化学侵蚀剂,其特征在于,每一份该种化学侵蚀剂包括如下成份:
三氧化铬CrO3             3~10g
盐酸HCL(分析纯)          30~100ml
水H2O                    30~100ml。
2.根据权利要求1所述的一种显示INVAR钢及其焊接接头金相组织的化学侵蚀剂,其特征在于,所述的化学侵蚀剂包括如下优化成份:
三氧化铬CrO3            5~8g
盐酸HCL(分析纯)         50~80ml
水H2O                   30~80ml。
3.一种制备权利要求1所述的显示INVAR钢及其焊接接头金相组织的化学侵蚀剂的方法,其特征在于,该方法包括如下步骤:
①按照每份侵蚀剂的配方称量所需原料,包括三氧化铬、分析纯盐酸和水;
②先将所述的三氧化铬加入到水中,搅拌至其完全溶解,形成混合溶液;
③然后将分析纯盐酸缓慢地加入至上述混合溶液中,并搅拌均匀,制成所需的化学侵蚀剂。
CN 201010126650 2010-03-17 2010-03-17 一种显示invar钢及其焊接接头金相组织的化学侵蚀剂及制备方法 Pending CN101798686A (zh)