CN101798489B - 易撕性玻纤铝箔复合胶带 - Google Patents
易撕性玻纤铝箔复合胶带 Download PDFInfo
- Publication number
- CN101798489B CN101798489B CN 201010114481 CN201010114481A CN101798489B CN 101798489 B CN101798489 B CN 101798489B CN 201010114481 CN201010114481 CN 201010114481 CN 201010114481 A CN201010114481 A CN 201010114481A CN 101798489 B CN101798489 B CN 101798489B
- Authority
- CN
- China
- Prior art keywords
- thickness
- aluminum foil
- tear
- adhesive tape
- easy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明提供一种用于建筑及汽车工业、军火工业之管道、电缆线之捆扎及控制电磁波信号干扰的易撕性玻纤铝箔复合胶带,具有超软性、服贴性好,可再重复使用,可以防水、防潮、防火、抗电磁波干扰。本发明在甲基型硅胶涂层之上表面附加玻纤布,在玻纤布之上表面附加接着剂涂层,在接着剂涂层之上表面附加回火铝箔,复合胶带厚度为0.15~0.25mm,甲基型硅胶涂层厚度为0.02~0.05mm,玻纤布厚度为0.02~0.06mm,接着剂涂层厚度为0.1~0.15mm,回火铝箔厚度为0.02~0.05mm。本发明具有高抗张强度且能有易撕性效果,有特殊抗热性、水煮性、抗湿热性,超软性、服贴性好,可再重复使用。
Description
技术领域
本发明涉及一种工程对象加工用胶带,尤其涉及一种用于建筑及汽车工业、军火工业之管道、电缆线之捆扎及控制电磁波信号干扰的玻纤铝箔复合胶带。
背景技术
目前,各种用途的胶带种类较多,用于工程领域的也有不少,特别在工程对象加工流程中,需要对管道、电缆线等进行捆扎,以便于工程施工。大多数工作条件均同时要求绝缘及耐受一定温度,对其要求比普通胶带要高,现有的胶带机械强度较低,极易被撕裂,无法达到正常的保护效果。
发明内容
针对现有技术存在的问题,本发明所要解决的技术问题是要提供一种用于建筑及汽车工业、军火工业之管道、电缆线之捆扎及控制电磁波信号干扰的易撕性玻纤铝箔复合胶带,具有超软性、服贴性好,可再重复使用,可以防水、防潮、防火、抗电磁波干扰。
为达上述目的,本发明水性干式覆膜胶通过下述技术方案予以实现:
一种易撕性玻纤铝箔复合胶带,在甲基型硅胶涂层之上表面附加玻纤布,在玻纤布之上表面附加接着剂涂层,在接着剂涂层之上表面附加回火铝箔,复合胶带厚度为0.15~0.25mm,甲基型硅胶涂层厚度为0.02~0.05mm,玻纤布厚度为0.02~0.06mm,接着剂涂层厚度为0.1~0.15mm,回火铝箔厚度为0.02~0.05mm。
进一步,所述接着剂涂层其基本组成为二液型PU(聚氨酯)接着剂,用于合成PU(聚氨酯)的单体是芳香族异氰酸盐或饱和族二元异氰酸盐;甲基型硅胶涂层其配方的成分质量比为:
聚硅氧烷树脂 100
二甲基硅树脂(MQ硅树脂) 50~100
催化剂 1.5~3
溶剂 100~300。
进一步,所述玻纤布为易撕玻璃纤维布:
密度: 60×26
基重: 60±2g/m2
厚度: 0.06mm
织法: 平织;
进一步,所述回火铝箔的基材采用金属铝箔,金属铝箔经有铝锭经冷轧、退火、张力整平等制程产出,其:
拉力强度 120N/μm2
伸长率 2%
弯曲半径 厚度×0.5倍。
回火铝箔和玻纤布的复合加工条件,
接着剂固含量 30%
涂布湿量在 20±5g/m2
贴合加工压力 60PSF(磅/平方英尺)
贴合温度 80±10℃。
本发明可以广泛地应用在建筑工程及汽车工业中,其接着剂能抗高温及低温性,玻纤布具有高抗张强度且能有易撕性效果,接着剂的选用为二液型PU聚氨酯(聚氨酯+聚异氰脲酯)或环氧树脂,使胶带具有特殊抗热性、水煮性、抗湿热性,玻纤布利用经纬纱的应力平衡及粗细度来控制其撕裂性。本发明解决了上述现有的技术问题,并比传统的胶带相比,具有如下优点:(一)、超软性、服贴性好,可再重复使用;(二)、本产品易撕,不需在操作中使用刀具;(三)、具防水、防潮、防火、抗电磁波干扰特性;(四)、适用于-70℃~200℃环境中使用。
附图说明
图1是本发明的结构示意图。
具体实施方式
为能进一步了解本发明的特征、技术手段以及所达到的具体目的、功能,下面结合附图与具体实施方式对本发明作进一步详细描述。
本发明相关结构主要包括以下部件:甲基型硅胶涂层1、玻纤布2、接着剂涂层3、回火铝箔4。
复合胶带厚度为0.15~0.25mm,甲基型硅胶涂层厚度为0.02~0.05mm,玻纤布厚度为0.02~0.06mm,接着剂涂层厚度为0.1~0.15mm,回火铝箔厚度为0.02~0.05mm。
易撕性玻纤铝箔复合胶带的回火铝箔4基材用金属铝箔,把金属铝箔经有铝锭经冷轧、退火、张力整平等制程产出,其:
拉力强度 120N/μm2
伸长率 2%
弯曲半径 厚度×0.5倍。
接着剂涂层3其基本组成为二液型PU聚氨酯接着剂,PU聚氨酯是一种功能性高分子,其结构由胺脂基作为连结,其组成含羧基,又有胺基,两者皆是具极性的官能基,故其对材质密着力很好。用于合成聚胺酯的单体是:芳香族异氰酸盐或饱和族二元异氰酸盐;二液型PU聚氨酯接着剂能产生高强度及高韧性之接着效果,具有高的贴合强度,渗透性佳特性,产质量软、黏性强、耐水洗、接着性优良。
玻纤布2的易撕玻璃纤布:
规格: 450×150
密度: 60×26
基重: 60±2g/m2
厚度: 0.06mm
织法: 平织。
玻纤布2需利用热处理加工的技术来控制其易撕,使其张力强度不超过15±3kg/IN2撕裂强度;玻纤布2的制造需要定型处理,在多层次加工中,仍保留经纬纱不走样,使胶带在操作、撕断线能整齐,并保持水平方向;玻纤布2具有防水,耐水压,通气透湿,阻燃防污以及遮光反射等特殊功能。
其回火铝箔4和玻纤布2的复合加工条件:
接着剂固含量 30%
涂布湿量在 20±5g/m2
贴合加工压力: 60PSF(磅/平方英尺)
贴合温度: 80±10℃。
甲基型硅胶涂层1其原料基本质量比:
聚硅氧烷树脂 100
二甲基硅树脂(MQ硅树脂) 50~100
催化剂 1.5~3
溶剂 100~300。
甲基型硅胶涂层1其反应原理:
Si-CH3→Si-CH2 -
2Si-CH2 -→SiCH2-CH2-Si;
其反应催化剂:
缩合反应:过氧二(2-氯苯甲酰)
附加反应:白金触媒;
其加工条件
75℃×2分钟→
180℃×2分钟。
以上所举实施例仅用为方便举例说明本发明,并非对本发明作任何形式上的限制,任何所属技术领域中具有通常知识者,若在不脱离本发明所提技术特征的范围内,利用本发明所揭示技术内容所作出局部更动或修饰的等效实施例,并且未脱离本发明的技术特征内容,均仍属于本发明技术特征的范围内。
Claims (5)
2.根据权利要求1所述的易撕性玻纤铝箔复合胶带,其特征在于:所述回火铝箔(4)的基材采用金属铝箔,金属铝箔由铝锭经冷轧、退火、张力整平程序制成,其:
拉力强度 120N/μm2
伸长率 2%
弯曲半径 厚度×0.5倍。
3.根据权利要求1所述的易撕性玻纤铝箔复合胶带,其特征在于:所述接着剂涂层(3)其基本组成为二液型聚氨酯接着剂,用于合成聚 氨酯的单体是:芳香族异氰酸盐或饱和族二元异氰酸盐。
4.根据权利要求1所述的易撕性玻纤铝箔复合胶带,其特征在于: 所述玻纤布(2)为易撕玻璃纤维布,其:
密度:60×26
基重:60±2g/m2
厚度:0.06mm
织法:平织。