CN101787155B - 饮料包装用蒸煮膜制备方法 - Google Patents
饮料包装用蒸煮膜制备方法 Download PDFInfo
- Publication number
- CN101787155B CN101787155B CN2010101295806A CN201010129580A CN101787155B CN 101787155 B CN101787155 B CN 101787155B CN 2010101295806 A CN2010101295806 A CN 2010101295806A CN 201010129580 A CN201010129580 A CN 201010129580A CN 101787155 B CN101787155 B CN 101787155B
- Authority
- CN
- China
- Prior art keywords
- density polyethylene
- medium
- high density
- film
- lldpe
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明为液体饮料包装领域提供了一种饮料包装用蒸煮膜制备方法,主要特点是对传统制备饮料包装用蒸煮膜的主原料配方加以改进,采用一定重量百分比的高密度聚乙烯,中密度聚乙烯,线性低密度聚乙烯和茂金属低密度聚乙烯,并按一定的重量百分比分三层靶向定位用料,与现有辅料混配,利用三螺杆挤出机,按传统工艺步骤,制备成复合层的饮料包装用蒸煮膜材料,与传统制备工艺相比,不仅产品总厚度有所减少,残废品损耗率显著降低,而且产品质量性能提高,适应和满足使用时耐高温、抗穿刺、热密封、抗污染的性能要求。
Description
技术领域
本发明属于包装领域,涉及食品包装材料,具体涉及一种饮料包装用蒸煮膜制备方法。
背景技术
液体饮料的包装袋,不仅需要耐高温,在120-126℃,0.012Mpa的条件下保证不熔化不粘连,而且还要达到一定强度、韧度,保证抗穿刺性能以及热封性能。
传统的液体饮料包装材料的制备方法,其主原料采用高密度聚乙烯(HDPE)和线型低密度聚乙烯(LLDPE),按7∶3的重量份比例混合,采用单螺杆挤出机吹制而成。由于传统方法采用的原料及工艺,虽然采用的高密度聚乙烯(HDPE)耐高温,线型低密度聚乙烯(LLDPE)有一定增强增韧作用,但是经混合单螺杆挤出后,难免有瑕疵和厚度不一,导致蒸煮膜质量性能较差,不仅浪费了材料,而且影响到包装袋制品的性能质量,漏包率、坏包率等损失率较高,有时高达5%。
发明内容
申请人在多年生产经营饮料包装用蒸煮膜的活动中,发现传统的饮料包装用蒸煮膜的制备方法存在着上述诸多的缺陷,组织技术人员经过调查研究,不断探索,目的在于提出一种饮料包装用蒸煮膜制备方法,能够较好地克服传统制备方法所存在的缺陷和问题。
本发明所采取的技术方案是:一种饮料包装用蒸煮膜制备方法,原料包括主原料和辅料,采用以下重量百分比主原料经过加工而成:高密度聚乙烯HDPE20-40%,中密度聚乙烯MDPE20-40%,线型低密度聚乙烯LLDPE10-20%,茂金属低密度聚乙烯MPE10-20%,将主原料分三层与辅料均分混合,依次相复合的外层、中层和内层,各层主原料分别采用以下重量百分比:外层中,高密度聚乙烯HDPE40-60%,中密度聚乙烯MDPE40-60%;中层中,高密度聚乙烯HDPE5-20%,中密度聚乙烯MDPE40-60%,线型低密度聚乙烯LLDPE20-40%;内层中,高密度聚乙烯HDPE15-30%,中密度聚乙烯MDPE15-30%,线型低密度聚乙烯LLDPE15-30%,茂金属低密度聚乙烯MPE25-40%,分别对应输送入三螺杆挤出机,按现有工艺经过加热、挤出、吹涨、定经、刨切、收卷、印刷、熟化、分切、成品包装入库。
经过以下工艺步骤制备而成:将上述各层主原料分外层、中层、内层的组方并均分掺入辅料分别配料,搅拌均匀,分别对应送入三螺杆挤出机,按现有工艺经过加热,熔融挤出,吹涨,定经,刨切,收卷,印刷,熟化,分切,包装,入库。
本发明根据所述四种主原料的不同特性,分中层、内层和外层三层配料加工,协同作用,由于饮料包装用蒸煮膜,在使用中需要耐高温,本发明所述外层中采用一定量的高密度聚乙烯和中密度聚乙烯,能确保在120-126℃,0.012Mpa的条件下不熔化不粘连;由于蒸煮膜在使用中需要有抗穿刺性能,本发明在所述中层中采用少量的高密度聚乙烯和较多的中密度聚乙烯和线型低密度聚乙烯,能起到增强、增韧、抗穿刺作用;由于蒸煮膜在使用中需要热封性能好,本发明在所述内层中采用一定量的高密度聚乙烯、中密度聚乙烯、线型低密度聚乙烯和较多的茂金属低密度聚乙烯,能起到提高产品的热封性、密闭性和抗污染性。这种采用靶向定位用料,不仅对产品的质量和性能起到很好的决定性作用,而且厚度可降低15-18%,废品破损率可降低近50倍,节约了原料成本,提高了工作效率。
具体实施方式
本发明饮料包装用蒸煮膜制备方法采用以下重量百分比主原料:高密度聚乙烯HDPE20-40%,中密度聚乙烯MDPE20-40%,线型低密度聚乙烯LLDPE10-20%,茂金属低密度聚乙烯MPE10-20%。
经过分三层配料组方,各层中主原料采用以下重量百分比:其中外层中,高密度聚乙烯HDPE40-60%,中密度聚乙烯MDPE40-60%;中层中,高密度聚乙烯HDPE5-20%,中密度聚乙烯MDPE40-60%,线型低密度聚乙烯LLDPE20-40%;内层中,高密度聚乙烯HDPE15-30%,中密度聚乙烯MDPE15-30%,线型低密度聚乙烯LLDPE15-30%,茂金属低密度聚乙烯MPE25-40%。
本发明饮料包装用蒸煮膜制备方法实施例1,各层中主原料采用以下重量百分比:外层中,高密度聚乙烯HDPE60%,中密度聚乙烯MDPE40%;中层中,高密度聚乙烯HDPE5%,中密度聚乙烯MDPE55%,线型低密度聚乙烯LLDPE40%;内层中,高密度聚乙烯HDPE15%,中密度聚乙烯MDPE30%,线型低密度聚乙烯LLDPE15%,茂金属低密度聚乙烯MPE40%。
将上述的每层主料和现有用量辅料均分混配,分别对应均匀送入三螺杆挤出机喂料斗,按传统工艺,加温,挤出,吹涨,定经,刨切,收卷,印刷,热化,分切,包装入库,产品的每层厚度相同,总厚度由原来的120微米降为100微米,残废品损耗率由5%降为1‰。
本发明饮料包装用蒸煮膜制备方法实施例2,各层中主原料采用以下重量百分比:外层中,高密度聚乙烯HDPE40%,中密度聚乙烯MDPE60%;中层中,高密度聚乙烯HDPE20%,中密度聚乙烯MDPE60%,线型低密度聚乙烯LLDPE20%;内层中,高密度聚乙烯HDPE30%,中密度聚乙烯MDPE30%,线型低密度聚乙烯LLDPE15%,茂金属低密度聚乙烯MPE25%。
本发明饮料包装用蒸煮膜制备方法实施例3,各层中主原料采用以下重量百分比:外层中,高密度聚乙烯HDPE50%,中密度聚乙烯MDPE50%;中层中,高密度聚乙烯HDPE10%,中密度聚乙烯MDPE50%,线型低密度聚乙烯LLDPE40%;内层中,高密度聚乙烯HDPE20%,中密度聚乙烯MDPE20%,线型低密度聚乙烯LLDPE20%,茂金属低密度聚乙烯MPE40%。
Claims (4)
1.一种饮料包装用蒸煮膜制备方法,原料包括主原料和辅料,经过加工而成,其特征是采用以下重量百分比主原料:高密度聚乙烯HDPE20-40%,中密度聚乙烯MDPE20-40%,线型低密度聚乙烯LLDPE10-20%,茂金属低密度聚乙烯MPE10-20%,将主原料分三层与辅料均分混合,依次相复合的外层、中层和内层,外层中含有高密度聚乙烯HDPE40-60%,中密度聚乙烯MDPE40-60%的主原料;中层中含有高密度聚乙烯HDPE5-20%,中密度聚乙烯MDPE40-60%,线型低密度聚乙烯LLDPE20-40%的主原料;内层中含有高密度聚乙烯HDPE15-30%,中密度聚乙烯MDPE15-30%,线型低密度聚乙烯LLDPE15-30%,茂金属低密度聚乙烯MPE25-40%的主原料,分别对应输送入三螺杆挤出机,按现有工艺经过加热、挤出、吹涨、定经、刨切、收卷、印刷、熟化、分切、成品包装入库。
2.如权利要求1所述的饮料包装用蒸煮膜制备方法,其特征是所述各层主原料采用以下重量百分比:外层中,高密度聚乙烯HDPE60%,中密度聚乙烯MDPE40%;中层中,高密度聚乙烯HDPE5%,中密度聚乙烯MDPE55%,线型低密度聚乙烯LLDPE40%;内层中,高密度聚乙烯HDPE15%,中密度聚乙烯MDPE30%,线型低密度聚乙烯LLDPE15%,茂金属低密度聚乙烯MPE40%。
3.如权利要求1所述的饮料包装用蒸煮膜制备方法,其特征是所述各层主原料采用以下重量百分比:外层中,高密度聚乙烯HDPE40%,中密度聚乙烯MDPE60%;中层中,高密度聚乙烯HDPE20%,中密度聚乙烯MDPE60%,线型低密度聚乙烯LLDPE20%;内层中,高密度聚乙烯HDPE30%,中密度聚乙烯MDPE30%,线型低密度聚乙烯LLDPE15%,茂金属低密度聚乙烯MPE25%。
4.如权利要求1所述的饮料包装用蒸煮膜制备方法,其特征是所述各层主原料采用以下重量百分比:外层中,高密度聚乙烯HDPE50%,中密度聚乙烯MDPE50%;中层中,高密度聚乙烯HDPE10%,中密度聚乙烯MDPE50%,线型低密度聚乙烯LLDPE40%;内层中,高密度聚乙烯HDPE20%,中密度聚乙烯MDPE20%,线型低密度聚乙烯LLDPE20%,茂金属低密度聚乙烯MPE40%。