CN101760015A - 无卤防翘曲变形高光泽阻燃尼龙6及其制作工艺 - Google Patents
无卤防翘曲变形高光泽阻燃尼龙6及其制作工艺 Download PDFInfo
- Publication number
- CN101760015A CN101760015A CN200910235156A CN200910235156A CN101760015A CN 101760015 A CN101760015 A CN 101760015A CN 200910235156 A CN200910235156 A CN 200910235156A CN 200910235156 A CN200910235156 A CN 200910235156A CN 101760015 A CN101760015 A CN 101760015A
- Authority
- CN
- China
- Prior art keywords
- halogen
- nylon
- free
- flame
- retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种有机高分子复合材料，更具体地说，是涉及一种无卤防翘曲变形高光泽阻燃尼龙6及其制备方法，是由以下成分按重量比组成，尼龙6：45-70％；无卤阻燃母粒：5-20％；无卤辅助阻燃剂2-6％；无卤玻璃微珠：1-30％；增韧剂：1-5％；偶联剂：0.1-0.4％；其他助剂：0.1-5.5％，本发明的一种无卤防翘曲变形高光泽阻燃尼龙6及其制作工艺，在综合机械性能保持良好与防火阻燃的基础上增加了防翘曲变形好和高光泽的特征，且流动性好，生产采购方便，这样提高了竞争力。
Description
技术领域
本发明涉及一种有机高分子复合材料，更具体地说，是涉及一种无卤防翘曲变形高光泽阻燃尼龙6及其制备方法。
背景技术
尼龙6是目前应用最多的几种工程塑料之一，他的酰胺基团具有极性，在他的结构中具有结构牢固的氢键，使得尼龙6的熔点较高，具有很好的物理力学性能和耐磨性以及自润滑性，这些综合特点是其他塑料所不具备的。但是纯尼龙6的热变形温度较低，吸水性大，吸水前冲击强度偏低，吸水后刚性又大幅下降，同时尺寸不稳定等缺点，从而限制了尼龙6的应用，进而又缩小了下游行业设计工程师的选材余地。因此，展开了对尼龙6进行复合改性的研究。而目前欧洲/日本等等发达国家出于种种原因，掀起了对外国进口产品种种限制，设立了一系列的壁垒，其中，对电子电器产品的材质无卤要求，就是其中之一。因此造成对我国较多出口企业严重困扰。而尼龙6又是结晶型材料，容易在成型时产生较大内应力，从而导致产成品翘曲变形。
目前市场中已有生产防翘曲的阻燃尼龙6材料具有强度低，防翘曲效果不充分，产品外观光泽不够好，材料流动性不好的系列缺点。本技术发明就是为了有效克服这种现象而产生的。
发明内容
本发明的目的在于克服现有技术的缺陷，提供一种在综合机械性能保持良好与防火阻燃的基础上增加了防翘曲变形好和高光泽的特征的无卤防翘曲变形高光泽阻燃尼龙6原料。
本发明提供的技术方案如下：本发明的一种无卤防翘曲变形高光泽阻燃尼龙6，是由以下成分按重量比组成，尼龙6：45-70％；无卤阻燃母粒：5-20％；无卤辅助阻燃剂2-6％；无卤玻璃微珠：1-30％；增韧剂：1-5％；偶联剂：0.1-0.4％；其他助剂：0.1-5.5％。
本发明所述的无卤防翘曲变形高光泽阻燃尼龙6的制备工艺是：先将尼龙6与无卤阻燃母粒分别烘干，然后先将烘干后的尼龙6、无卤玻璃微珠、增韧剂、偶联剂、其他助剂按照比例称量后在混料机中低速混合10分钟，再经双螺杆挤出机在中等强度剪切的螺杆组合情况下由侧面按比例加入烘干后的无卤阻燃母粒和无卤辅助阻燃剂，低转速混炼挤出，水冷拉条切粒经过筛分脱水制得无卤防翘曲变形高光泽阻燃尼龙6材料。
本发明有效的克服了现有技术的缺陷，具有以下优点：
本发明的一种无卤防翘曲变形高光泽阻燃尼龙6及其制作工艺，在综合机械性能保持良好与防火阻燃的基础上增加了防翘曲变形好和高光泽的特征，且流动性好，生产采购方便，这样提高了竞争力。
具体实施方式
以下是本发明所述的无卤防翘曲变形高光泽阻燃尼龙6原料的最佳实施例，并不因此限定本发明的保护范围。
实施例一，提供一种无卤防翘曲变形高光泽阻燃尼龙6，由以下成分按重量比组成，尼龙6：53％，尼龙6载体高色素黑色母：1.5％；无卤阻燃母粒：13％；无卤辅助阻燃剂：5％；无卤玻璃微珠：22％：增韧剂：3％；偶联剂：0.3％；其他助剂：2.2％；
先将尼龙6与无卤阻燃母粒分别烘干，然后烘干后的尼龙6、尼龙6载体高色素黑色母、无卤玻璃微珠、增韧剂、偶联剂、其他助剂按照比例称量后在混料机中低速混合10分钟，混料机采用低速混合，搅拌叶应与筒壁间隙小于0.5厘米，原辅料混合效果应目视各种粒子和粉末基本均匀，没有明显团块或集聚；双螺杆挤出机使用36长径比，中等强度剪切螺杆组合，设置不高于300转/分钟的转速；无卤阻燃母粒与无卤辅助阻燃剂由侧面按比例加入；采用水冷拉条切粒方式，经过筛分脱水即制得无卤防翘曲变形高光泽阻燃尼龙6材料。
Claims (2)
1.一种无卤防翘曲变形高光泽阻燃尼龙6，其特征在于：是由以下成分按重量比组成，尼龙6：45-70％；无卤阻燃母粒：5-20％；无卤辅助阻燃剂2-6％；无卤玻璃微珠：1-30％；增韧剂：1-5％；偶联剂：0.1-0.4％；其他助剂：0.1-5.5％。
2.一种制备无卤防翘曲变形高光泽阻燃尼龙6的方法，其特征在于：包括如下步骤：先将尼龙6与无卤阻燃母粒分别烘干，然后先将烘干后的尼龙6、无卤玻璃微珠、增韧剂、偶联剂、其他助剂按照比例称量后在混料机中低速混合10分钟，再经双螺杆挤出机在中等强度剪切的螺杆组合情况下由侧面按比例加入烘干后的无卤阻燃母粒和无卤辅助阻燃剂，低转速混炼挤出，水冷拉条切粒经过筛分脱水制得无卤防翘曲变形高光泽阻燃尼龙6材料。