CN101758010A - Digging machine structural element coating method - Google Patents

Digging machine structural element coating method Download PDF

Info

Publication number
CN101758010A
CN101758010A CN200910199038A CN200910199038A CN101758010A CN 101758010 A CN101758010 A CN 101758010A CN 200910199038 A CN200910199038 A CN 200910199038A CN 200910199038 A CN200910199038 A CN 200910199038A CN 101758010 A CN101758010 A CN 101758010A
Authority
CN
China
Prior art keywords
structural element
digging machine
machine structural
carrying
coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN200910199038A
Other languages
Chinese (zh)
Other versions
CN101758010B (en
Inventor
郑可文
李强
高柏元
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
LONKING (SHANGHAI) EXCAVATOR CO Ltd
LONKING (SHANGHAI) EXCAVATOR MANUFACTURING Co Ltd
Lonking Shanghai Machinery Manufacturing Co Ltd
Original Assignee
LONKING (SHANGHAI) EXCAVATOR CO Ltd
LONKING (SHANGHAI) EXCAVATOR MANUFACTURING Co Ltd
Lonking Shanghai Machinery Manufacturing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by LONKING (SHANGHAI) EXCAVATOR CO Ltd, LONKING (SHANGHAI) EXCAVATOR MANUFACTURING Co Ltd, Lonking Shanghai Machinery Manufacturing Co Ltd filed Critical LONKING (SHANGHAI) EXCAVATOR CO Ltd
Priority to CN2009101990385A priority Critical patent/CN101758010B/en
Publication of CN101758010A publication Critical patent/CN101758010A/en
Application granted granted Critical
Publication of CN101758010B publication Critical patent/CN101758010B/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention relates to a digging machine structural element coating method, which comprises the following steps: firstly, hanging a digging machine structural element for carrying out ball blasting treatment on the digging machine structural element; carrying out spraying supplementing treatment on the surface of the digging machine structural element after the ball blasting treatment; carrying out primer coating; subsequently, carrying out putty scrapping and baking the primer; carrying out fine grinding after the completion of the putty scrapping and the primer baking; coating finish paint; intensively cooling the finish paint after the casting baking; and finally, taking the digging machine structural element down from a frame. The invention is characterized in that the surface of the digging machine structural element after the spraying supplementing treatment carries out coarse grinding. The invention has the advantages that the phenomena of roughness, collision, scratch, oxide coating and the like can be solved, and the operating efficiency of the production line is improved.

Description

A kind of digging machine structural element coating method
Technical field
The present invention relates to a kind of digging machine structural element coating method, belong to excavator Coating Pretreatment technical field.
Background technology
The digging machine structural element surface make and operation process in can produce unavoidably coarse, collide with, phenomenons such as scuffing and oxide skin, priming last as employing ball blast and the above-mentioned defective of blasting treatment.But that Shot Blasting can not thoroughly solve is coarse, oxide skin, collide with, problem such as projection.In order to address the above problem, increase the attractive in appearance of structural member outward appearance, digging machine structural element can carry out large tracts of land usually and scrape greasy and fine grinding after adopting priming paint.Though scraping the greasy decorative appearance that can improve the coated article surface coating, can not improve the protective value of filming, and putty layer lacks flexibility, easy to crack, thus cause whole film easily destroyed.Simultaneously, scraping greasy and fine grinding inefficiency, is a big bottleneck of the smooth and easy operation of streamline.
Summary of the invention
The purpose of this invention is to provide a kind of can solve coarse, collide with, the coating process of phenomenons such as scuffing and oxide skin and improve the operational efficiency of streamline.
In order to achieve the above object, technical scheme of the present invention has provided a kind of digging machine structural element coating method, the steps include:
Step 1, digging machine structural element is hung up, it is carried out Shot Blasting;
Step 2, to the processing that fills spray of the digging machine structural element surface behind the ball blast;
Step 4, carry out primer painting, scrape greasy subsequently and priming paint is toasted fine grinding after finishing;
Step 5, coating finish to cold by force after the baking of finish paint levelling, with the digging machine structural element undercarriage, is characterized in that having at last between step 2 and step 4:
Step 3, roughly ground on the digging machine structural element surface of handling to carrying out filling spray.
The present invention increases before structural member priming paint and roughly grinds technology together.Roughly grind before adopting priming paint, can control the structural member surface quality, cause structural member rough surface, uneven, residual oxide skin, greasy dirt, the burr of not removing, welding slag etc. to polish at ball blast and after filling spray, this saves the extensive work time for back operation fine grinding comprehensively.Structural member is through after roughly grinding before the priming paint, and the surface is smooth, and is no coarse, do not have oxide skin and greasy dirt etc., can directly carry out the priming paint spraying.Can behind priming paint, do slightly to mend among a small circle after evenly roughly grinding at serious pit.
Advantage of the present invention be can solve coarse, collide with, phenomenon such as scuffing and oxide skin and improved the operational efficiency of streamline.
Description of drawings
Fig. 1 is the flow chart of a kind of digging machine structural element coating method provided by the invention.
The specific embodiment
Specify the present invention below in conjunction with embodiment.
Embodiment
As shown in Figure 1, the flow chart for a kind of digging machine structural element coating method provided by the invention the steps include:
Step 1, digging machine structural element is hung up, it is carried out Shot Blasting;
Step 2, to the processing that fills spray of the digging machine structural element surface behind the ball blast;
Step 3, roughly ground on the digging machine structural element surface of handling to carrying out filling spray;
Step 4, carry out primer painting, scrape greasy subsequently and priming paint is toasted fine grinding after finishing;
Step 5, coating finish are to cold by force after the baking of finish paint levelling, at last with the digging machine structural element undercarriage.
As shown in the table in the parameter comparison of implementing a kind of digging machine structural element coating method provided by the invention front and back:
Figure G2009101990385D00021

Claims (1)

1. a digging machine structural element coating method the steps include:
Step 1, digging machine structural element is hung up, it is carried out Shot Blasting;
Step 2, to the processing that fills spray of the digging machine structural element surface behind the ball blast;
Step 4, carry out primer painting, scrape greasy subsequently and priming paint is toasted fine grinding after finishing;
Step 5, coating finish to cold by force after the baking of finish paint levelling, with the digging machine structural element undercarriage, is characterized in that having at last between step 2 and step 4:
Step 3, roughly ground on the digging machine structural element surface of handling to carrying out filling spray.
CN2009101990385A 2009-11-19 2009-11-19 Digging machine structural element coating method Expired - Fee Related CN101758010B (en)