CN101734079A - Dieless controllable metal fusion cast molding method - Google Patents
Dieless controllable metal fusion cast molding method Download PDFInfo
- Publication number
- CN101734079A CN101734079A CN 200810122100 CN200810122100A CN101734079A CN 101734079 A CN101734079 A CN 101734079A CN 200810122100 CN200810122100 CN 200810122100 CN 200810122100 A CN200810122100 A CN 200810122100A CN 101734079 A CN101734079 A CN 101734079A
- Authority
- CN
- China
- Prior art keywords
- metal
- dieless
- medium
- molding method
- cast molding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a dieless controllable metal fusion cast molding method. The traditional metal casting techniques all use die casting without exception and shapes are not flexible and variable. The method of the invention comprises: firstly fusing the metal in a crucible, pouring the fused metal to a medium, naturally flowing the fused metal in the medium, controlling the condensing rate of the fused metal according to the need of finished products, coloring and welding the condensed metal. The raw materials of the method in the invention are derived from the residual leftover material after metal materials are processed so as to save cost. The metal ornaments cast by using the method of the invention have peculiar shapes and abundant colors and realize the artistic effect of combining abstract with reality.
Description
Technical field
The invention belongs to the metal casting technical field, relate to a kind of method of Dieless controllable metal fusion cast molding.
Background technology
Metal ornament occupies critical role in decoration industry.Metallic decoration all the time mainly is the casting ornaments, as the figure of buddha, incense burner etc.And traditional foundry engieering is the main flow technology of metal processing always, and this technology generally adopts moulds such as mud mould, sand mo(u)ld, resin mold, paraffin wax mould, metal pattern.Mold casting forming is traditional indispensable process means of metal carving, and traditional metal carving technology adopts die casting bar none, and the moulding underaction is changeable.
Summary of the invention
The purpose of this invention is to provide a kind of Dieless controllable metal fusion cast molding method.
The inventive method at first melts metal material in crucible, then the molten metal liquation is poured in the medium, and molten metal is trickling naturally in medium, and according to finished product needs control condensation rate, the metal that will condense carries out painted and soldering again.Medium wherein is gaseous state or liquid material, and temperature is 0～100 ℃, also can add flocculation aid in the medium.Medium can be an inactive state, also can be flow regime.When pouring into molten metal in the medium, crucible can be to be in the horizontal stationary state, also can pass through step motor control, makes it be in horizontal movement state.Flocculation aid among the present invention is dry ice, liquid nitrogen etc.
Fusing in the inventive method, method painted, soldering adopt ripe existing method, and inventive point of the present invention is to make finished product have more naturality by molten metal is poured out naturally, solidified in medium by this method.
The raw material sources of the inventive method have been saved cost in the remaining tailing of metal material processing.Utilize the inventive method can cast the new type of metal ornament, enlarge the workmanship frontier.The inventive method peculiar image occurs by welding and chemical treatment, has accomplished the abstract artistic effect that combines with reality.
The specific embodiment
With the metallic copper is that example is described further Dieless controllable metal fusion cast molding method of the present invention.
At first copper billet is melted in crucible, then the copper liquid of fusing is poured in the WATER AS FLOW MEDIUM, copper liquid is trickling naturally in WATER AS FLOW MEDIUM, partial accession flocculation aid in the WATER AS FLOW MEDIUM, according to finished product needs control condensation rate, can obtain the copper spare of forms such as heaped-up, sheet, strip, bulk, again copper spare be carried out painted and soldering.
When copper carries out painted processing, controlling color temperature and painted time according to the needs of finished product, wherein the relation such as the table 1 of temperature and molten coppery coloured silk:
| Temperature (℃) | ??15 | ??25 | ??35 | ??45 |
| Color | Light yellow | Brown | Dark-brown | Black |
Table 1
Along with the rising of temperature, color from shallow to deep.This is owing under different temperatures, the degree of oxidation difference, thereby obtain different colors.The relation such as the table 2 of painted time and molten coppery coloured silk:
| The painted time | ??30″ | ??1′ | ??1′30″ | ??3′ | ??5′ |
| Color | Pale yellow | Pale brown | Brown | Dark brown | Black |
Table 2
Under the normal temperature, for certain density coloring liquid, along with the increase of time, color is deepened gradually, and promptly the thickness of coloring film is increasing.After reaching certain hour, color no longer changes and becomes black.
Select for use sulfide as coloring liquid, the relation such as the table 3 of its concentration and molten coppery coloured silk:
| ??CuSO 4(g/L) | ??80 | ??90 | ??100 | ??110 | ??120 |
| Color | Shallow palm fibre | Brown | Dark-brown | Brownish black | Black |
Table 3
Above-mentioned color change rule is because Cu
2+It is the main component of coloring liquid.Its content how much, can change the thickness of film, thereby make the color difference of coloring film.
This method adopts no mould founding, and peculiarly shaped, rich color can be made the molten copper of different shapes such as sand grains, bulk, honeycomb.
Claims (4)
1. Dieless controllable metal fusion cast molding method, it is characterized in that: at first solid metal material is melted in crucible, then the molten metal liquation is poured in the medium, molten metal is trickling naturally in medium, according to the condensation rate of finished product needs control molten metal, the metal that will condense carries out painted and soldering again; Described medium is gaseous state or liquid, and temperature is 0～100 ℃.
2. a kind of Dieless controllable metal fusion cast molding method as claimed in claim 1 is characterized in that described medium is inactive state or flow regime.
3. a kind of Dieless controllable metal fusion cast molding method as claimed in claim 1, crucible is in horizontal stationary state or horizontal movement state when it is characterized in that pouring into molten metal in the medium.
4. a kind of Dieless controllable metal fusion cast molding method as claimed in claim 1 is characterized in that adding flocculation aid in the described medium.