CN101704987A - Macromolecular vessel prepared by adopting coffee grounds as stuffing and preparation method thereof - Google Patents
Macromolecular vessel prepared by adopting coffee grounds as stuffing and preparation method thereof Download PDFInfo
- Publication number
- CN101704987A CN101704987A CN200910233141A CN200910233141A CN101704987A CN 101704987 A CN101704987 A CN 101704987A CN 200910233141 A CN200910233141 A CN 200910233141A CN 200910233141 A CN200910233141 A CN 200910233141A CN 101704987 A CN101704987 A CN 101704987A
- Authority
- CN
- China
- Prior art keywords
- coffee grounds
- macromolecular
- vessel
- coffee
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a manufacturing method of a macromolecular vessel which is prepared from 17-22 percent of coffee grounds, 60-65 percent of resin powder, 10-15 percent of alumina powder, 4-8 percent of coloring agents and 1-2 percent of wetting agents. Aiming at the problem of low utilization ratio of the traditional coffee grounds, the coffee grounds are taken as the stuffing of the macromolecular vessel, and the coffee grounds have good characteristics of light weight, low density, good granule shape, bright color and lustre and the like; in addition, the coffee grounds have the characteristics of insulation, heat insulation, heat preservation and foreign taste absorption, and therefore, the performance of the macromolecular vessel can be greatly improved; a melamine resin coffee cup adopting the coffee grounds as the stuffing has the function of enhancing coffee aroma.
Description
Technical field
The present invention relates to macromolecular vessel manufacture method technology.
Background technology
Coffee berry grinds through coffee machine, can brew out the coffee of delicious drifting fragrance, but coffee berry is comparatively expensive, 100 gram coffee berrys can only obtain 30 gram coffees and be used to infuse coffee, 70 remaining grams are coffee grounds and can only be outwelled, and have also polluted environment when forming waste, and existing coffee grounds is mainly used in the peculiar smell of removing in the life in kitchen or the refrigerator, the coffee grounds that this method consumes is also just a spot of, and a large amount of coffee groundss can only fall as the refuse treatment of no utility value.
Summary of the invention.
In order to overcome above-mentioned defective, the technical problem to be solved in the present invention is: at the low problem of existing coffee grounds utilization ratio, provide a kind of method that adopts coffee grounds to prepare macromolecular vessel as weighting agent.
In order to overcome the defective that exists in the background technology, the technical solution adopted for the present invention to solve the technical problems is: a kind of macromolecular vessel that adopts coffee grounds as the weighting agent preparation, adopt coffee grounds, resin-oatmeal, aluminum oxide powder, tinting material and wetting agent to make macromolecular vessel, wherein the mass percent of coffee grounds is 17%～22%, the mass percent of resin-oatmeal is 60%～65%, the mass percent of aluminum oxide powder is 10%～15%, the mass percent of tinting material is 4%～8%, and the mass percent of wetting agent is 1%～2%.
Resin-oatmeal described in the present invention is melmac powder, phenol-formaldehyde resin powder or polyimide resin powder, adopt the melmac powder to be applicable to the macromolecular vessel of preparation contacting foodstuff, adopt phenol-formaldehyde resin powder to be applicable to the general macromolecular vessel that uses of preparation, adopt the polyimide resin powder to prepare high temperature resistant vessel.
Wetting agent described in the present invention is the ethanolic soln of liquid phenolic resin 15% concentration, adopts ethanolic soln to improve
A kind of preparation method who adopts coffee grounds as the macromolecular vessel of weighting agent preparation has following steps:
A, coffee grounds pre-treatment: water cleans coffee grounds, again with the coffee grounds oven dry, crosses 35 mesh sieves earlier, after 230 mesh sieves, select for use particle at 35 orders to 230 purpose coffee grounds particles;
B, compound configuration: particle after 35 orders mix stirring to 230 purpose coffee grounds particles, resin-oatmeal, aluminum oxide powder, tinting material and wetting agent precentagewise, is sieved with 10 mesh sieves, obtain stand-by compound;
C, moulding.
Beneficial effect: adopt the stopping composition of coffee grounds among the present invention as macromolecular vessel, coffee grounds has lightweight density, good particle shape, beautiful high-quality characteristics such as color and luster, add that coffee grounds can insulate, heat insulation, insulation, absorb the characteristics of peculiar smell, can improve the performance of macromolecular vessel greatly, adopt the melmac coffee cup of coffee grounds seat stopping composition to have the effect that increases coffee aroma.
Description of drawings
The present invention is further described below in conjunction with drawings and Examples.
Fig. 1 is the preferred embodiments of the present invention schematic flow sheets.
Embodiment
The present invention is further detailed explanation with preferred embodiment in conjunction with the accompanying drawings now.These accompanying drawings are the synoptic diagram of simplification, basic structure of the present invention only is described in a schematic way, so it only show the formation relevant with the present invention.
Embodiment one:
Adopt the macromolecular vessel of coffee grounds as the weighting agent preparation, raw material adopts coffee grounds, melmac powder, aluminum oxide powder, tinting material and wetting agent to make macromolecular vessel, wherein the mass percent of coffee grounds is 17%, the mass percent of resin-oatmeal is 65%, the mass percent of aluminum oxide powder is 10%, the mass percent of tinting material is 7%, and the mass percent of wetting agent is 1%.
A kind of preparation method who adopts coffee grounds as the macromolecular vessel of weighting agent preparation has following steps:
A, coffee grounds pre-treatment: water cleans coffee grounds, again with the coffee grounds oven dry, crosses 35 mesh sieves earlier, after 230 mesh sieves, select for use particle at 35 orders to 230 purpose coffee grounds particles;
B, compound configuration: particle after 35 orders mix stirring to 230 purpose coffee grounds particles, melmac powder, aluminum oxide powder, tinting material and wetting agent precentagewise, is sieved with 10 mesh sieves, obtain stand-by compound;
C, moulding.
Embodiment two:
Adopt the macromolecular vessel of coffee grounds as the weighting agent preparation, raw material adopts coffee grounds, melmac powder, aluminum oxide powder, tinting material and wetting agent to make macromolecular vessel, wherein the mass percent of coffee grounds is 21%, the mass percent of resin-oatmeal is 60%, the mass percent of aluminum oxide powder is 13%, the mass percent of tinting material is 4%, and the mass percent of wetting agent is 2%.
Adopt the preparation method of coffee grounds, have following steps as the macromolecular vessel of weighting agent preparation:
A, coffee grounds pre-treatment: water cleans coffee grounds, again with the coffee grounds oven dry, crosses 35 mesh sieves earlier, after 230 mesh sieves, select for use particle at 35 orders to 230 purpose coffee grounds particles;
B, compound configuration: particle after 35 orders mix stirring to 230 purpose coffee grounds particles, melmac powder, aluminum oxide powder, tinting material and wetting agent precentagewise, is sieved with 10 mesh sieves, obtain stand-by compound;
C, moulding.
With above-mentioned foundation desirable embodiment of the present invention is enlightenment, and by above-mentioned description, the related work personnel can carry out various change and modification fully in the scope that does not depart from this invention technological thought.The technical scope of this invention is not limited to the content on the specification sheets, must determine its technical scope according to the claim scope.
Claims (4)
1. macromolecular vessel that adopts coffee grounds as weighting agent preparation, it is characterized in that: adopt coffee grounds, resin-oatmeal, aluminum oxide powder, tinting material and wetting agent to make macromolecular vessel, wherein the mass percent of coffee grounds is 17%～22%, the mass percent of resin-oatmeal is 60%～65%, the mass percent of aluminum oxide powder is 10%～15%, the mass percent of tinting material is 4%～8%, and the mass percent of wetting agent is 1%～2%.
2. employing coffee grounds as claimed in claim 1 is as the macromolecular vessel of weighting agent preparation, and it is characterized in that: described resin-oatmeal is melmac, resol or polyimide resin.
3. employing coffee grounds as claimed in claim 1 is characterized in that: have following steps as the preparation method of the macromolecular vessel of weighting agent preparation:
A, coffee grounds pre-treatment: water cleans coffee grounds, again with the coffee grounds oven dry, crosses 35 mesh sieves earlier, after 230 mesh sieves, select for use particle at 35 orders to 230 purpose coffee grounds particles;
B, compound configuration: particle after 35 orders mix stirring to 230 purpose coffee grounds particles, resin-oatmeal, aluminum oxide powder, tinting material and wetting agent precentagewise, is sieved with 10 mesh sieves, obtain stand-by compound;
C, moulding.
4. employing coffee grounds as claimed in claim 3 is as the preparation method of the macromolecular vessel of weighting agent preparation, and it is characterized in that: described resin-oatmeal is melmac, resol or polyimide resin.