CN101704067A - 解决用消失模工艺生产干式缸体水道中缺陷的方法 - Google Patents
解决用消失模工艺生产干式缸体水道中缺陷的方法 Download PDFInfo
- Publication number
- CN101704067A CN101704067A CN200910075633A CN200910075633A CN101704067A CN 101704067 A CN101704067 A CN 101704067A CN 200910075633 A CN200910075633 A CN 200910075633A CN 200910075633 A CN200910075633 A CN 200910075633A CN 101704067 A CN101704067 A CN 101704067A
- Authority
- CN
- China
- Prior art keywords
- cylinder body
- water channel
- core
- sealing
- dry type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种解决用消失模工艺生产干式缸体水道中缺陷的方法,其特征是它的具体步骤如下:(1)先将刷涂、烘干好的缸体消失模侧面孔用质量好的玻璃丝布胶粘封好;(2)在台式震实台上从缸体上面孔中往进填70~140目硅砂,含SiO2≥98%的天然砂,或混制好的覆膜用树脂砂,一边填,一边震,一边塞,确保水道上部犄角旮旯亦填充紧实;(3)将缸体上面孔用质量好的玻璃丝布胶粘封好。本发明省去了做芯盒,制芯、下芯的工艺,这样避免了制芯、下芯和漂芯出现的缺陷,降低了成本。
Description
技术领域
本发明属于消失模铸造工艺,具体涉及一种解决用消失模工艺生产干式缸体水道中缺陷的方法。
背景技术
用潮型等砂型铸造缸体下芯子多,工艺复杂,废品率高,成本高,且表面粗糙,尺寸精度差。消失模工艺因可以不下芯子或少下芯子便可生产出多孔腔的产品,非常适宜于生产顶级铸件缸体和缸盖。但在生产实践中发现,由于缸体、特别是干式缸体,水道形状异常复杂,有时水隙只有3-4mm,由于在震实台上埋箱时,水道上部难以填实,大量出现铁瘤、铁包砂、粘砂和铸不出窄水隙等缺陷。采取下芯的方法,窄水隙芯不好制,亦不好下,同时,芯子无法固定常常漂芯报废。
发明内容
本发明所要解决的技术问题是提供一种解决用消失模工艺生产干式缸体水道中缺陷的方法,这种方法工艺简单,成本低,省去了做芯盒的工艺,消除了制芯、下芯和漂芯出现的缺陷。
本发明的技术方案:一种解决用消失模工艺生产干式缸体水道中缺陷的方法,它的具体步骤如下:
(1)先将刷涂、烘干好的缸体消失模侧面孔用质量好的玻璃丝布胶粘封好;
(2)在台式震实台上从缸体上面孔中往进填70~140目硅砂,含SiO2≥98%的天然砂,或混制好的覆膜用树脂砂,一边填,一边震,一边塞,确保水道上部犄角旮旯亦填充紧实;
(3)将缸体上面孔用质量好的玻璃丝布胶粘封好。
本发明与现有技术相比具有以下有益效果:省去了做芯盒,制芯、下芯的工艺,若水道上部有的地方没有孔洞,为了便于将砂填满、填实,可在水道上部做一个工艺孔,填完砂后用加工好的等厚、等直径钢或同材质生铁柱状塞将工艺孔堵好,这样避免了制芯、下芯和漂芯出现的缺陷,降低了成本。
具体实施方式
一种解决用消失模工艺生产干式缸体水道中缺陷的方法,它的具体步骤如下:
(1)先将刷涂、烘干好的缸体消失模侧面孔用质量好的玻璃丝布胶粘封好;
(2)在台式震实台上从缸体上面孔中往进填70~140目硅砂,含SiO2≥98%的天然砂,或混制好的覆膜用树脂砂,一边填,一边震,一边塞,确保水道上部犄角旮旯亦填充紧实;
(3)将缸体上面孔用质量好的玻璃丝布胶粘封好。
为了便于将砂填满、填实,可在水道上部做一个工艺孔,填完砂后用加工好的等厚、等直径钢或同材质生铁柱状塞将工艺孔堵好.
Claims (1)
1.一种解决用消失模工艺生产干式缸体水道中缺陷的方法,其特征是它的具体步骤如下:
(1)先将刷涂、烘干好的缸体消失模侧面孔用质量好的玻璃丝布胶粘封好;
(2)在台式震实台上从缸体上面孔中往进填70~140目硅砂,含SiO2≥98%的天然砂,或混制好的覆膜用树脂砂,一边填,一边震,一边塞,确保水道上部犄角旮旯亦填充紧实;
(3)将缸体上面孔用质量好的玻璃丝布胶粘封好。