CN101684589B - Process for producing wool product - Google Patents
Process for producing wool product Download PDFInfo
- Publication number
- CN101684589B CN101684589B CN2008101572943A CN200810157294A CN101684589B CN 101684589 B CN101684589 B CN 101684589B CN 2008101572943 A CN2008101572943 A CN 2008101572943A CN 200810157294 A CN200810157294 A CN 200810157294A CN 101684589 B CN101684589 B CN 101684589B
- Authority
- CN
- China
- Prior art keywords
- wool
- matrix
- sheet
- soap lye
- product
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to a process for manufacturing a non-woven fabric product, in particular to a process for producing a wool product. The invention overcomes the defects of hard texture, poor comfort and unattractive appearance of the prior wool product and provides the process for producing the wool product. The process integrally moulds wool by rubbing and rolling the wool totally soaked with soap water, and the wool product produced by the process has soft texture, good handfeel, no suture line, attractive appearance and comfortable use.
Description
Technical field
The present invention relates to a kind of manufacture craft of non-weaving cloth series products, specifically a kind of manufacture craft of wool product.
Background technology
Wool has advantages such as good springiness, hygroscopicity is strong, warmth retention property is good as the important source material of textile industry.But, therefore concerning the production of non-weaving cloth, use also few because its price is higher.Along with improving constantly of people's living standard, wool product is with its elasticity and warmth retention property preferably, and comfort feel is subjected to people's favor gradually.Our wool product of using always at present, as wool footwear, wool felt, woolen socks etc., all be to adopt the method for acupuncture to carry out production and processing, but the wool product quality that makes is harder, feel is coarse, and people use uncomfortable, and wool footwear in the market, woolen socks etc. all have suture, influence the attractive in appearance of wool product on the one hand, also reduced the comfort of wool product on the other hand.
Summary of the invention
The objective of the invention is to overcome that existing wool product quality is hard, comfortableness difference and inaesthetic defective, a kind of manufacture craft of wool product has been proposed, the wool product quality softness that goes out by this explained hereafter, good hand touch, and one-body molded, there is not suture, good looking appearance uses comfortable.
The present invention adopts following technical scheme to realize: a kind of manufacture craft of wool product, and this technology mainly may further comprise the steps:
(1) tiling wool sheet: with ready wool five equilibrium, part wool wherein is tiled into uniform wool sheet anyhow alternately;
(2) prepare soap lye water: soap or soap powder are prepared according to the weight ratio between 1: 60～1: 90 with hot water, and temperature remains between 70～90 ℃;
(3) deployed soap lye water is sprayed at equably on the good wool sheet of tiling, and pats with have gentle hands and to beat, make soap lye water evenly fused with the wool sheet fully by the wool sheet of soap lye water saturates;
(4) matrix is put to the wool sheet, the wool sheet is turned up according to the shape of matrix, guarantees when turning up that the wool sheet is close on the matrix;
(5) remain wool in the tiling alternately anyhow in a side that does not have the wool sheet on the matrix, until the consistency of thickness of its thickness with the wool sheet of having completed, and the shape according to matrix is rolled well, makes it identical with the shape of matrix, sprays soap lye water and beating gently afterwards on the wool sheet;
(6) rub and roll the wool sheet: according to the shape of matrix, wool to the matrix both sides is rubbed from outside to inside repeatedly, rub in the process of rolling and constantly on wool, to spray above-mentioned soap lye water, and guarantee that wool presses close to matrix all the time, rub be one and shape moulding to wool according to matrix till;
(7) as required with integral type shear opening, take out matrix, then the goods mould is put between two wool layers, continue on wool, to spray above-mentioned soap lye water, and rub and roll wool, be adjacent to until itself and goods mould;
(8) the goods mould is taken out, wool is rinsed well, and dry with clear water;
(9) the goods mould is inserted in the wool once more, is placed on the shady and cool ventilation place and dries and get final product.
When needing to add some decorative patterns on the above-mentioned wool product, at first the wool that will have a corresponding pattern color by needling process stings to wool product, and sting out the pattern form that needs, employing is rubbed the method for rolling and is made this pattern and wool product formation one then.Described matrix can by plastics for example nylon make, also can possess water proofing property and softer material is made by other.
Rub when rolling the wool sheet, can earlier plastic film or air bubble film be overlayed on the wool sheet, rub then.The wool product of producing by this method has wool footwear, wool felt, wool felt, wool bag, wool wallet, wool socks and wool rope etc., according to actual needs, can make various wool products by difform matrix and goods mould.
The method of the making of different wool products is also slightly different: when producing the wool footwear, tailor corresponding matrix according to the shape and size of footwear, with wool rub be integral after, clip in position, and the shoe tree of respective shapes and size put into integrated wool; When producing flat-shaped wool product such as wool socks, then do not need to use the goods mould, according to the shape of matrix with wool rub be integral after, get final product at correct position clip; When producing wool felt or wool felt, only need at a side lay wool of matrix and rub and roll moulding, cut the limit at last and can obtain wool felt; The making of wool rope then need not matrix, directly wool is rubbed and is rolled moulding.
This method is applicable to the wool of all kinds and length, and the wool that also is applicable to simultaneously polytype and length mixes and uses, and in order to guarantee the quality of wool product, preferably adopts more than 40, the wool of length more than 2cm.Raw material of the present invention both can be the wool tops through combing, also can be the diffusing wool of cleaning, and its color can be primary colors and shades of colour.
The invention has the beneficial effects as follows: by the wool product quality softness that method of the present invention is made, can not produce stiff and sense of touch thorn, comfortableness is better; And this product without any suture, therefore need not to sew up operation, one-body molded, simplified production process, and the wool product good looking appearance of producing, use comfortable.
The specific embodiment
Embodiment 1
The step of making the 15cm playshoes by the present invention is as described below:
At first, prepare raw material, i.e. wool 100g, this wool can adopt through the wool tops of combing or clean diffusing wool, soap 100g, and temperature is 70 ℃ water 6kg, soap is poured in the water, and fully dissolving and evenly mix with water is mixed with weight ratio and is 1: 60 soap lye water;
Next, one of the panel of preparation 45cm * 30cm, use the air bubble film of 50cm * 40cm that panel is wrapped, and the one side that is surrounded by air bubble film on the panel is upwards placed, the 100g wool is divided into 8 parts, take out about 3/4 part wool wherein, be tiled on the panel size of the wool sheet after the tiling and the size basically identical of matrix anyhow alternately equably;
The 3rd step was that 70 ℃ soap lye water is sprayed on the good wool sheet of tiling with the temperature for preparing, and till soap lye water irrigates wool, and patted the wool sheet gently, and soap lye water is fully fused with the wool sheet;
In the 4th step, the footwear matrix of tailoring in advance is placed on sprinkling to be had on the wool sheet of soap lye water, according to the shape of matrix the wool sheet is turned up then, and assurance matrix and wool sheet are close to all the time when turning up;
The 5th step, the wool of remaining about 1/4 part is tiled in a side that does not have wool on the matrix,, and on this wool sheet, sprays above-mentioned soap lye water until the consistency of thickness of its thickness with the wool sheet of having completed, pat gently simultaneously, in case of necessity the wool sheet is rolled well according to the shape of matrix;
The 6th step, all tiled behind the wool in the both sides of matrix, on wool, lay the air bubble film of 20cm * 20cm, shape according to matrix is constantly rubbed the wool of rolling the matrix both sides from outside to inside, rubbing needs in the process of rolling constantly to spray soap lye water on wool, and guarantees that the wool sheet is close to matrix all the time, and to be the shape of one and its shape and matrix to wool identical when rubbing, promptly when grabbing wool, grab phozy and during smooth surface, rub the process of rolling and finish with hand;
The 7th step, the wool of rubbing after the end is the complete closed shape, cut off welt in position, matrix is taken out, and penetrating shoe tree accordingly in former matrix position, spray temperature is 70 ℃ a soap lye water on wool then, and continues wool rubbed and roll, till wool and shoe tree are close to, the first one-step forming of wool footwear this moment;
The 8th step, shoe tree is taken out, and, till not having soap lye water, dry then with the first wool footwear of one-step forming of flushing with clean water, make the wool footwear put on shoe tree once more afterwards, and be placed on the shady and cool ventilation place and dry;
At last, shoe tree is taken out from the wool footwear that dry, the ox-hide sole all corresponding shape and size is fixed on the wool sole with the glue rifle, bored the awl eye that spacing is 0.9cm with awl then, and sole has been sewn on the wool footwear wool footwear final molding with the footwear line.In the time of need on vamp, making some decorative patterns, by acupuncture with the wool of respective color thorn on the surface of wool footwear, and the shape that pricks out the pattern is one by rubbing to roll this pattern and wool footwear are rubbed then.
Timesharing such as wool can be divided into several portions with wool according to actual needs, are not limited to 8 parts in the present embodiment.In the above-mentioned preparation method, soap can replace with soap powder, can serve the same role; Above-mentioned air bubble film can be by replacements such as plastic films; Described pad has water proofing property by plastics or nylon etc. and soft material is made.Roll technology and make wool around the both sides of matrix and one-body molded owing to adopt to rub, need not to adopt sewing process, therefore compare with existing wool footwear manufacture craft, simplified manufacture craft, and do not had sutural wool footwear good looking appearance, comfortableness is good.
By changing the shape and size of matrix and corresponding shoe tree, and cutting welt in position, can produce the wool footwear of difformity and different size.In addition, except can making light household shoe, can also produce the wool footwear of other kinds, as wool slippers, wool boots etc.
This invention is applicable to various types of wools, when the concentration of soap lye water between 1: 60～1: 90, temperature can both satisfy production requirement between 70～90 ℃.
Embodiment 2
The step of wool felt that by manufactured size of the present invention is 45cm * 45cm is as follows:
At first, prepare raw material, i.e. wool 125g, this wool can adopt through the wool tops of combing or clean diffusing wool, soap 100g, and temperature is 80 ℃ water 7kg, soap is poured in the water, and fully dissolving and evenly mix with water is mixed with weight ratio and is 1: 70 soap lye water;
Next, one of the panel of preparation 50cm * 50cm, and use the air bubble film of 60cm * 60cm that panel is wrapped, and make and be surrounded by one of the air bubble film placement that faces up on the panel, wool is divided into several portions, anyhow be tiled on the panel equably alternately, and the size of the wool sheet after the tiling and the size basically identical of matrix;
The 3rd step was that 80 ℃ soap lye water is sprayed on the good wool sheet of tiling with the temperature for preparing, and till soap lye water irrigates wool water, and patted the wool sheet gently, made soap lye water fused with wool fully;
In the 4th step, the matrix of tailoring in advance is placed on to spray to be had on the wool sheet of soap lye water, with matrix and the upset of wool sheet, the wool sheet is placed up then, and guarantees that matrix and wool sheet be close to all the time;
The 5th step, on the wool sheet, lay the air bubble film of 50cm * 50cm, constantly rub from outside to inside according to the shape of matrix and to roll wool, rubbing also needs constantly to spray soap lye water on the wool sheet in the process of rolling, and assurance wool sheet is close to matrix all the time, rub when wool and to be integral, promptly when grabbing wool, grab phozy and during smooth surface, the kneading process finishes with hand;
The 6th step, according to the shape of matrix the wool of rubbing after rolling is pruned, make its shape identical, the wool felt moulding with the shape of matrix;
In the 7th step,, till it does not have soap lye water, be placed on the shady and cool ventilation place after the drying and dry and to make wool felt with the wool felt of normal temperature flushing with clean water moulding.
According to above-mentioned technology,, can make the wool felt of different size by changing the shape and size of matrix; Also can make thicker wool felt according to said method in addition.
Other are with embodiment 1.
Embodiment 3
The step of wool bag that by manufactured size of the present invention is 15.5cm * 11.5cm is as follows:
At first, prepare raw material, i.e. wool 30g, this wool can adopt through the wool tops of combing or clean diffusing wool, soap 100g, and temperature is 90 ℃ water 8kg, soap is poured in the water, and fully dissolving and evenly mix with water is mixed with weight ratio and is 1: 80 soap lye water;
Next, one of the panel of preparation 20cm * 15cm, use the air bubble film of 25cm * 20cm that panel is wrapped, and make and be surrounded by one of the air bubble film placement that faces up on the panel, the 30g wool is divided into several portions, take out the wool of about 3/4 part wherein, be tiled on the panel size of the wool sheet after the tiling and the size basically identical of matrix anyhow alternately equably;
The 3rd goes on foot, and is that 90 ℃ soap lye water is sprayed on the good wool sheet of tiling by watering can with the temperature for preparing, and till soap lye water irrigates wool, and pats the wool sheet gently, makes soap lye water evenly soak into the wool sheet;
In the 4th step, the bag matrix of tailoring in advance is placed on to spray to be had on the wool sheet of soap lye water, according to the shape of matrix the wool sheet is turned up then, will guarantee when turning up that matrix and wool sheet be close to all the time;
The 5th step, the wool of remaining about 1/4 part is tiled in a side that does not have wool on the matrix,, on the wool sheet, sprays soap lye water until the consistency of thickness of its thickness with the wool sheet of having completed, and pat gently, in case of necessity the wool sheet is rolled well according to the shape of matrix;
The 6th step, after all there is wool the both sides of matrix, on matrix, lay the air bubble film of 20cm * 20cm, shape according to matrix is constantly rubbed the wool of rolling the matrix both sides from outside to inside, rubbing in the process also needs constantly to spray soap lye water on wool, and guarantees that wool is close to matrix all the time, and to rub the shape that is one and its shape and matrix identical when wool, promptly when grabbing wool, grab phozy and during smooth surface, the kneading process finishes with hand;
The 7th step, rub the wool of rolling after the end and be the complete closed shape, to wrap the mouth cut off after, take out matrix, when the wool bag need have certain shape, Bao Mo accordingly packed in former matrix position, spray temperature is 90 ℃ a soap lye water on wool then, and continue wool rubbed and roll, until the first one-step forming of wool bag, till promptly wool and Bao Mo are close to; When producing flat-shaped wool bag, only need the matrix taking-up is got final product;
The 8th step, will wrap mould and take out, and with the first wool bag of one-step forming of flushing with clean water, till it does not have soap lye water, drying then, the Bao Mo that packs into once more in the wool bag afterwards, and be placed on the shady and cool ventilation place and dry.
According to said method, can produce the wool bag of all size and shape by the size and dimension that changes matrix and Bao Mo.
Other are with embodiment 1.
Embodiment 4
Making length by the present invention is that the technical process of wool socks of 40cm is as follows:
At first, prepare raw material, i.e. wool 100g, this wool can adopt through the wool tops of combing or clean diffusing wool, soap 100g, and temperature is 70 ℃ water 9kg, soap is poured in the water, and fully dissolving and evenly mix with water is mixed with weight ratio and is 1: 90 soap lye water;
Next, one of the panel of preparation 50cm * 30cm, use the air bubble film of 60cm * 40cm that panel is wrapped, and make and be surrounded by one of the air bubble film placement that faces up on the panel, the 100g wool is divided into several portions, take out the wool of about 3/4 part wherein, be tiled on the panel size of the wool sheet after the tiling and the size basically identical of matrix anyhow alternately equably;
The 3rd step was that 70 ℃ soap lye water is sprayed on the good wool sheet of tiling with the temperature for preparing, and till soap lye water irrigates wool, and patted the wool sheet gently, made soap lye water fused with the wool sheet fully;
In the 4th step, the socks matrix of tailoring in advance is placed on to spray to be had on the wool sheet of soap lye water, according to the shape of matrix the wool sheet is turned up then, will guarantee when turning up that matrix and wool sheet be close to all the time;
The 5th step, the wool of remaining about 1/4 part is tiled in a side that does not have wool on the matrix,, and on the wool sheet, sprays soap lye water until the consistency of thickness of its thickness with the wool sheet of having completed, pat gently simultaneously, in case of necessity the wool sheet is rolled well according to the shape of matrix;
The 6th step, after all there is wool the both sides of matrix, on matrix, lay the air bubble film of 45cm * 25cm, shape according to matrix is constantly rubbed the wool of rolling the matrix both sides from outside to inside, rub in the process and constantly spray soap lye water on the wool sheet, and guarantee that the wool sheet is close to matrix all the time, to roll the shape that is one and its shape and matrix identical when wool is rubbed, promptly when grabbing wool, grab phozy and during smooth surface, rub the process of rolling and finish with hand;
In the 7th step, the wool of rubbing after rolling is the complete closed shape, after stocking blank is cut off, takes out matrix, uses the flushing with clean water of normal temperature then, till it does not have soap lye water, is placed on the shady and cool ventilation place after the drying and dries the woolen socks that can obtain final molding.
According to said method, can produce the woolen socks of all size and shape by the size and dimension that changes matrix.
Other are with embodiment 1.
Embodiment 5
The step of wool rope of making long 2m, thick 0.5cm by the present invention is as follows:
At first, prepare raw material, promptly long for 2.5m, weight are the wool of 13g, this wool can adopt through the wool tops of combing or clean diffusing wool, soap powder 50g, and temperature is 80 ℃ water 3.5kg, and soap powder is poured in the water, is made into weight ratio and is 1: 70 soap lye water.
Second step, one of the panel of preparation 45cm * 30cm, use the air bubble film of 50cm * 40cm to wrap, and make panel be surrounded by the upwards placement of one side of air bubble film, wool is equally divided into several portions, and evenly be tiled on the panel, evenly spray soap lye water, till irrigating, on panel, rub repeatedly then, phozy and smooth surface is even until the hair rope grip that is twisted into, guarantee that simultaneously its diameter reaches till the 0.5cm substantially.
At last, the flushing with clean water with normal temperature till it does not have soap lye water, is placed on the shady and cool ventilation place and dries the wool rope that can obtain final molding after the drying.
Other are with embodiment 1.
Claims (10)
1. the manufacture craft of a wool product is characterized in that this technology may further comprise the steps:
(1) tiling wool sheet: with the wool five equilibrium, the part wool of getting wherein is tiled into uniform wool sheet anyhow alternately;
(2) prepare soap lye water: soap or soap powder are prepared according to the weight ratio between 1: 60～1: 90 with hot water, and temperature is between 70～90 ℃;
(3) deployed soap lye water is sprayed at equably on the good wool sheet of tiling, pats gently then, make soap lye water evenly fused with wool fully by the wool sheet of soap lye water saturates;
(4) matrix is put to the wool sheet, the wool sheet is turned up, guarantee when turning up that the wool sheet is close on the matrix according to the shape of matrix;
(5) at a side that does not have the wool sheet on the matrix remaining wool in the tiling alternately anyhow, until the consistency of thickness of its thickness, and roll well according to the shape of matrix with the wool sheet completed, on the wool sheet, spray soap lye water afterwards and pat gently;
(6) rub and roll the wool sheet: according to the shape of matrix, wool to the matrix both sides is rubbed from outside to inside repeatedly, rub in the process of rolling and constantly on wool, to spray above-mentioned soap lye water, and guarantee that wool is close to matrix all the time, rub be one and shape moulding to wool according to matrix till;
(7) with the shear opening of first one-step forming, take out matrix, then the goods mould is put between two wool layers, on wool, spray above-mentioned soap lye water, and continue to rub and roll wool, be adjacent to until itself and goods mould;
(8) the goods mould is taken out, wool is rinsed well, and dry with the normal temperature clear water;
(9) the goods mould is inserted in the wool once more, being positioned over that the shady and cool ventilation place dries is moulding.
2. the manufacture craft of wool product according to claim 1, it is characterized in that: when processing has the wool product of decorative pattern, by acupuncture the wool of respective color is stung surface to wool product, and sting out corresponding shape, rub and be integral constituting the wool of pattern and wool product by gently rubbing then.
3. the manufacture craft of wool product according to claim 1, it is characterized in that: described matrix is made of plastics.
4. the manufacture craft of a wool product is characterized in that this technology may further comprise the steps:
(1) tiling wool sheet: with the wool five equilibrium, the part wool of getting wherein is tiled into uniform wool sheet anyhow alternately;
(2) prepare soap lye water: soap or soap powder are prepared according to the weight ratio between 1: 60～1: 90 with hot water, and the temperature of hot water is between 70～90 ℃;
(3) deployed soap lye water is sprayed at equably on the good wool sheet of tiling, pats gently then, make soap lye water evenly fused with wool fully by the wool sheet of soap lye water saturates;
(4) matrix is put to the wool sheet, the wool sheet is turned up, will guarantee when turning up that the wool sheet is close on the matrix according to the shape of matrix;
(5) at a side that does not have the wool sheet on the matrix remaining wool in the tiling alternately anyhow, until the consistency of thickness of its thickness, and roll well according to the shape of matrix with the wool sheet completed, on the wool sheet, spray soap lye water afterwards and pat gently;
(6) rub and roll the wool sheet: according to the shape of matrix, wool to the matrix both sides is rubbed from outside to inside repeatedly, rub in the process of rolling and constantly on wool, to spray above-mentioned soap lye water, and guarantee that wool is close to matrix all the time, rub be one and shape moulding to the wool sheet according to matrix till;
(7) with the shear opening after the moulding, take out matrix, with clear water the wool product of moulding is cleaned drying, be positioned over the shady and cool ventilation place and dry.
5. the manufacture craft of wool product according to claim 4, it is characterized in that: when processing has the wool product of decorative pattern, by acupuncture the wool of respective color is stung surface to wool product, and sting out corresponding shape, rub and be integral constituting the wool of pattern and wool product by gently rubbing then.
6. the manufacture craft of wool product according to claim 4, it is characterized in that: described matrix is made of plastics.
7. the manufacture craft of a wool product is characterized in that this technology may further comprise the steps:
(1) tiling wool sheet:, and be tiled into uniform wool sheet anyhow alternately with the wool five equilibrium;
(2) prepare soap lye water: soap or soap powder are prepared according to the weight ratio between 1: 60～1: 90 with hot water, and temperature is between 70～90 ℃;
(3) deployed soap lye water is sprayed at equably on the good wool sheet of tiling, pats gently then, make soap lye water evenly fused with wool fully by the wool sheet of soap lye water saturates;
(4) rub and roll the wool sheet: according to the shape of matrix, the wool sheet is rubbed from outside to inside repeatedly, is rubbed in the process of rolling the constantly soap lye water of spray temperature between 70～90 ℃, and guarantee that wool is close to matrix all the time, rub be one to wool till;
(7) according to the shape of matrix integrated wool is pruned, the wool product of moulding is cleaned drying, be positioned over the shady and cool ventilation place and dry with clear water.
8. the manufacture craft of wool product according to claim 7, it is characterized in that: when processing has the wool product of decorative pattern, by acupuncture the wool of respective color is stung surface to wool product, and sting out corresponding shape, rub and be integral constituting the wool of pattern and wool product by gently rubbing then.
9. the manufacture craft of wool product according to claim 7, it is characterized in that: described matrix is made of plastics.
10. the manufacture craft of a wool product is characterized in that this technology may further comprise the steps:
(1) tiling wool sheet: with the wool five equilibrium and be tiled into uniform wool sheet;
(2) prepare soap lye water: soap or soap powder are prepared according to the weight ratio between 1: 60～1: 90 with hot water, and temperature is between 70～90 ℃;
(3) deployed soap lye water is sprayed at equably on the good wool sheet of tiling, pats gently then, make soap lye water evenly fused with wool fully by the wool sheet of soap lye water saturates;
(4) rub and roll the wool sheet: rub wool, be one and reach the size of regulation until wool;
(5) with clear water the wool product of moulding is cleaned drying, be positioned over the shady and cool ventilation place and dry.