CN101684221A - 负离子健康漆 - Google Patents

负离子健康漆 Download PDF

Info

Publication number
CN101684221A
CN101684221A CN200810166823A CN200810166823A CN101684221A CN 101684221 A CN101684221 A CN 101684221A CN 200810166823 A CN200810166823 A CN 200810166823A CN 200810166823 A CN200810166823 A CN 200810166823A CN 101684221 A CN101684221 A CN 101684221A
Authority
CN
China
Prior art keywords
parts
paint
sodium hydroxide
water
scattered kettle
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN200810166823A
Other languages
English (en)
Inventor
杨录真
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN200810166823A priority Critical patent/CN101684221A/zh
Publication of CN101684221A publication Critical patent/CN101684221A/zh
Pending legal-status Critical Current

Abstract

一种负离子健康漆,其重量份的组合原料为:净化水300份、羟丙基瓜尔胶1.5份、羟乙基纤维素2份、水性颜料润湿剂1份、水性分散剂4份、消泡剂3份、钛白粉200份、负离子涂料添加剂72份、微细煅烧高岭土50份、硅酸铝10份、硅灰石10份、重晶石10份、丙二醇8份、氢氧化钠稀释液1份、杀菌剂2份、滑石粉50份、微细重质碳酸钙60份、防霉粉13份、苯丙乳液200份、增稠剂2.5份。制备方法:将净化水置入到分散釜中,再分别将羟丙基瓜尔胶、纤维素加入到分散釜中,再加入稀释液、润湿剂、分散剂、杀菌剂、消泡剂、硅酸铝、滑石粉、高岭土、钛白粉、重钙、硅灰石、重晶石、防霉粉,经砂磨后在调漆釜中加入消泡剂、丙二醇、苯丙乳液、负离子添加剂、增稠剂、净化水,最后再加入氢氧化钠,经过滤灌装即可。

Description

负离子健康漆
技术领域
本发明涉及一种负离子健康漆,具体的说是涉及一种可以释放负离子的、具有环保作用的建筑物内墙涂料的生产制备方法,属于建筑材料领域。
背景技术
建筑物内墙使用的装饰涂料的种类较多,目前市场上现有的装饰涂料,其制备方法主要是采用钛白粉、碳酸钙、纤维素、增稠剂、PH值调节剂、分散剂、防腐剂、润湿剂等主要原料,按一定比例直接置入到分散釜(容器)中,进行分散、磨砂,然后再加入丙烯醇乳液,消泡剂、成膜助剂、乙二醇进行混合、过滤后,最后制成涂料。由于在这种涂料成分中含有大量的甲醛、苯胺、VOC等有毒物质,挥发后的异味刺鼻难闻,这些有毒气体对人类的健康会造成非常严重的后果。另外,房屋在装修的过程中,会使用大量的人造纤维板、三合板和各种粘合剂,这些材料中也含有大量的甲醛和苯酚等有毒物质,其毒气挥发后也会对人体的健康带米危害作用。随着人们对室内环保要求的日益提高,人们迫切需要一种环保无毒的,能够改善室内环境质量并有利于人体健康的装饰涂料。
发明内容
本发明的目的是为了提供一种负离子健康漆(墙体涂料),该漆(涂料)的成分中不含有成膜助剂和VOC,不仅无毒无害,并且漆(涂料)还具有持续释放负离子的功能,释放出的负离子可以分解祛除室内甲醛、氨、苯酚等有毒、有害气体,这样即可达到消除室内有毒异味、灭菌、净化空气,防止居民受到空气污染,保障居民健康的目的。
为了达到上述目的,本发明是采用如下技术方案实现的。
一种负离子健康漆,其重量份的组合原料为:
1、净化水            300份
2、羟丙基瓜尔胶      1.5份
3、羟乙基纤维素        2份
4、水性颜料润湿剂      1份
5、水性分散剂          4份
6、消泡剂              3份
7、钛白粉              200份
8、负离子涂料添加剂    72份
9、微细煅烧高岭土      50份
10、硅酸铝             10份
11、硅灰石             10份
12、重晶石             10份
13、丙二醇             8份
14、氢氧化钠稀释液     1份
15、杀菌剂             2份
16、滑石粉             50份
17、微细重质碳酸钙     60份
18、防霉粉             13份
19、苯丙乳液           200份
20、增稠剂             2.5份
所述的净化水可选用普通纯净水。
所述的羟丙基瓜尔胶的含水率为11%,水不溶物含量为7%,残渣为6%,PH值为7.0。
所述的羟乙基纤维素(HEC)其质量标准为:摩尔取代度(M.S)2.0;水份(%)≤10;水不溶物(%)≤0.5;PH值8.5;重金属(ug/g)≤20;灰分(%)≤5;粘度(mpa.s)2% 20℃水溶液60000;铅(%)≤0.001。
所述的水性颜料润湿剂为疏水长碳链-乙氧基化合物,无色透明液体,pH值为7.0±1(1wt%水溶液),固含量100%,可分散于水中。
所述的水性分散剂为TH-904型聚羧酸类阻垢分散剂,主要成分为阴离子型聚合物,固体含量%≥40.0,PH(2%水溶液)为11,密度(20℃)g/cm3≥1.20,粘度(25℃)mpa.s为600。
所述的消泡剂俗名为泡沫控制剂,主要成分为二氧化硅。
所述的钛白粉选用金红石型的超细钛白粉。
所述的负离子涂料添加剂选用浆料型的,其主要成分为:超细压电晶体、纳米无机搭载剂。产品性状为:白色或浅灰色无毒无味压电晶体乳液。
所述的微细煅烧高岭土的PH值为7.0,细度为4000目。
所述的硅酸铝、硅灰石、重晶石均为粉状,其颗粒细均为3000目。
所述的氢氧化钠稀释液是由氢氧化钠添加20%纯净水进行溶解后获取。
所述的杀菌剂其有效成分为:异噻唑啉酮衍生物,活性成份为5-氯-2-甲基-4-异噻唑啉-3-酮(CIT)、2-甲基-4-异噻唑啉-3-酮(MIT)。
所述的滑石粉的细度为2000目,其主要成分为矽酸镁。
所述的微细重质碳酸钙的含钙量为98%,细度为4000目。
所述的防霉粉的主要成分为硫化锌。
所述的苯丙乳液的主要成分是丙烯酸正丁酯/苯乙烯共聚物的水分散体,其固体含量为50±1%。
所述的增稠剂为疏水改性的丙烯酸酯共聚物。
本发明负离子健康漆的制备方法如下:
首先将净化水270份置入到分散釜中,将分散机的转速设定为300转/分钟,开启分散机,然后再分别将羟丙基瓜尔胶1.5份、羟乙基纤维素2份加入到分散釜中,待分散釜旋转5分钟后,再向分散釜中加入氢氧化钠稀释液,氢氧化钠稀释液的加入量以达到将分散釜中混合液体的PH值调整为8为标准;待所述分散釜中的溶液分散均匀,溶解10分钟后,然后在分散釜不停止转动搅拌的情况下,再分别缓缓的加入水性颜料润湿剂1份、水性分散剂4份、杀菌剂2份、消泡剂1份;然后在分别加入硅酸铝10份、滑石粉50份、微细煅烧高岭土50份、钛白粉200份、微细重质碳酸钙60份、硅灰石10份、重晶石10份、防霉粉13份;将分散机的转速调整到800转/分钟,进行高速分散20分钟后,再将分散机的转速调整到200转/分钟,低速分散5分钟后,关闭分散机,然后将分散釜中的浆液通过分散釜下部的管道和齿轮泵传输到砂磨罐中用砂磨机进行研磨;经研磨后的浆液通过管道和齿轮泵传输到调漆釜中,开启调漆釜上的电机进行低速旋转,然后在调漆釜不停止转动搅拌的情况下,再分别缓缓的向调漆釜中加入消泡剂2份、丙二醇8份、苯丙乳液200份、负离子涂料添加剂72份、增稠剂2.5份、净化水30份,调漆釜低速旋转搅拌25分钟;最后再向调漆釜中加入氢氧化钠稀释液,氢氧化钠稀释液的加入量以达到将调漆釜中混合乳液的PH值调整为8为标准,让调漆釜继保持低速旋转搅拌20分钟;然后将调漆釜中的乳液通过管道和隔膜泵传输到反冲袋式过滤器中进行过滤,再将过滤后的乳液通过自动灌装设备在生产线上进行20KG的计量灌装,即制成本发明所述的负离子健康漆。
采用本发明飞方法制备的负离子内墙漆(涂料),不含有成膜助剂和VOC,无毒无害,并且漆(涂料)还具有持续释放负离子的功能,释放出的负离子可以分解祛除室内甲醛、氨、苯酚等有毒有害气体。本发明飞方法制备的负离子内墙漆符合国标GB/-T97562001以及内墙涂料GB/18582-2001标准。
具体实施方式
实施例
下面结合实施例对本发明负离子健康漆及其生产制备方法做进一步的说明:
首先,选购生产原料并按比例进行搭配,本发明所使用的的组合原料其重量份数为:
净化水300份、羟丙基瓜尔胶1.5份、羟乙基纤维素2份、水性颜料润湿剂1份、水性分散剂4份、消泡剂3份、钛白粉200份、负离子涂料添加剂72份、微细煅烧高岭土50份、硅酸铝10份、硅灰石10份、重晶石10份、丙二醇8份、氢氧化钠稀释液1份、杀菌剂2份、滑石粉50份、微细重质碳酸钙60份、防霉粉13份、苯丙乳液200份、增稠剂2.5份。
所述的净化水可选用普通纯净水。
所述的羟丙基瓜尔胶的含水率为11%,水不溶物含量为7%,残渣为6%,PH值为7.0。
所述的羟乙基纤维素(HEC)其质量标准为:摩尔取代度(M.S)2.0;水份(%)≤10;水不溶物(%)≤0.5;PH值8.5;重金属(ug/g)≤20;灰分(%)≤5;粘度(mpa.s)2%  20℃水溶液60000;铅(%)≤0.001。
所述的水性颜料润湿剂为疏水长碳链-乙氧基化合物,无色透明液体,pH值为7.0±1(1wt%水溶液),固含量100%,可分散于水中。
所述的水性分散剂为TH-904型聚羧酸类阻垢分散剂,主要成分为阴离子型聚合物,固体含量%≥40.0,PH(2%水溶液)为11,密度(20℃)g/cm3≥1.20,粘度(25℃)mpa.s为600。
所述的消泡剂俗名为泡沫控制剂,主要成分为二氧化硅。
所述的钛白粉选用金红石型的超细钛白粉。
所述的负离子涂料添加剂选用浆料型的,其主要成分为:超细压电晶体、纳米无机搭载剂。产品性状为:白色或浅灰色无毒无味压电晶体乳液。
所述的微细煅烧高岭土的PH值为7.0,细度为4000目。
所述的硅酸铝、硅灰石、重晶石均为粉状,其颗粒细均为3000目。
所述的氢氧化钠稀释液是由氢氧化钠添加20%纯净水进行溶解后获取。
所述的杀菌剂其有效成分为:异噻唑啉酮衍生物,活性成份为5-氯-2-甲基-4-异噻唑啉-3-酮(CIT)、2-甲基-4-异噻唑啉-3-酮(MIT)。
所述的滑石粉的细度为2000目,其主要成分为矽酸镁。
所述的微细重质碳酸钙的含钙量为98%,细度为4000目。
所述的防霉粉的优选物为硫化锌。
所述的苯丙乳液的主要成分是丙烯酸正丁酯/苯乙烯共聚物的水分散体,其固体含量为50±1%,本发明优选产品为《安固力》牌S 559型。
所述的增稠剂为疏水改性的丙烯酸酯共聚物。
步骤一:首先将净化水270份置入到分散釜中,将分散机的转速设定为300转/分钟,开启分散机,然后再分别将羟丙基瓜尔胶1.5份、羟乙基纤维素2份加入到分散釜中,待分散釜旋转5分钟后,再向分散釜中加入氢氧化钠稀释液,氢氧化钠稀释液的加入量以达到将分散釜中混合液体的PH值调整为8为标准。
步骤二:在分散釜不停止转动搅拌的情况下,再分别缓缓的加入水性颜料润湿剂1份、水性分散剂4份、杀菌剂2份、消泡剂1份;然后在分别加入硅酸铝10份、滑石粉50份、微细煅烧高岭土50份、钛白粉200份、微细重质碳酸钙60份、硅灰石10份、重晶石10份、防霉粉13份。
步骤三:将分散机的转速调整到800转/分钟,进行高速分散20分钟后,再将分散机的转速调整到200转/分钟,低速分散5分钟后,关闭分散机,然后将分散釜中的浆液通过分散釜下部的管道和齿轮泵传输到砂磨罐中用砂磨机进行研磨。
步骤四:经研磨后的浆液通过管道和齿轮泵传输到调漆釜中,开启调漆釜上的电机进行低速旋转,然后在调漆釜不停止转动搅拌的情况下,再分别缓缓的向调漆釜中加入消泡剂2份、丙二醇8份、苯丙乳液200份、负离子涂料添加剂72份、增稠剂2.5份、净化水30份,调漆釜低速旋转搅拌25分钟。
步骤五:最后再向调漆釜中加入氢氧化钠稀释液,氢氧化钠稀释液的加入量以达到将调漆釜中混合乳液的PH值调整为8为标准,让调漆釜继保持低速旋转搅拌20分钟。
步骤六:最后再向调漆釜中加入氢氧化钠稀释液,氢氧化钠稀释液的加入量以达到将调漆釜中混合乳液的PH值调整为8为标准,让调漆釜继保持低速旋转搅拌20分钟。
步骤七:将调漆釜中的乳液通过管道和隔膜泵传输到反冲袋式过滤器中进行过滤,再将过滤后的乳液通过自动灌装设备在生产线上进行20KG的计量灌装,即制成本发明所述的负离子健康漆。

Claims (3)

1、一种负离子健康漆,其特征在于:其重量份的组合原料为:净化水300份、羟丙基瓜尔胶1.5份、羟乙基纤维素2份、水性颜料润湿剂1份、水性分散剂4份、消泡剂3份、钛白粉200份、负离子涂料添加剂72份、微细煅烧高岭土50份、硅酸铝10份、硅灰石10份、重晶石10份、丙二醇8份、氢氧化钠稀释液1份、杀菌剂2份、滑石粉50份、微细重质碳酸钙60份、防霉粉13份、苯丙乳液200份、增稠剂2.5份。
2、根据权利要求1所述的一种负离子健康漆,其特征在于:
所述的净化水可选用普通纯净水;
所述的羟丙基瓜尔胶的含水率为11%,水不溶物含量为7%,残渣为6%,PH值为7.0;
所述的羟乙基纤维素(HEC)其质量标准为:摩尔取代度(M.S)2.0;水份(%)≤10;水不溶物(%)≤0.5;PH值8.5;重金属(ug/g)≤20;灰分(%)≤5;粘度(mpa.s)2%20℃水溶液60000;铅(%)≤0.001;
所述的水性颜料润湿剂为疏水长碳链-乙氧基化合物,无色透明液体,pH值为7.0±1(1wt%水溶液),固含量100%,可分散于水中;
所述的水性分散剂为TH-904型聚羧酸类阻垢分散剂,主要成分为阴离子型聚合物,固体含量%≥40.0,PH(2%水溶液)为11,密度(20℃)g/cm3≥1.20,粘度(25℃)mpa.s为600;
所述的消泡剂俗名为泡沫控制剂,主要成分为二氧化硅;
所述的钛白粉选用金红石型的超细钛白粉;
所述的负离子涂料添加剂选用浆料型的,其主要成分为:超细压电晶体、纳米无机搭载剂,产品性状为:白色或浅灰色无毒无味压电晶体乳液;
所述的微细煅烧高岭土的PH值为7.0,细度为4000目;
所述的硅酸铝、硅灰石、重晶石均为粉状,其颗粒细均为3000目;
所述的氢氧化钠稀释液是由氢氧化钠添加20%纯净水进行溶解后获取;
所述的杀菌剂其有效成分为:异噻唑啉酮衍生物,活性成份为5-氯-2-甲基-4-异噻唑啉-3-酮(CIT)、2-甲基-4-异噻唑啉-3-酮(MIT);
所述的滑石粉的细度为2000目,其主要成分为矽酸镁;
所述的微细重质碳酸钙的含钙量为98%,细度为4000目;
所述的防霉粉的主要成分为硫化锌;
所述的苯丙乳液的主要成分是丙烯酸正丁酯/苯乙烯共聚物的水分散体,其固体含量为50±1%;
所述的增稠剂为疏水改性的丙烯酸酯共聚物;
3、根据权利要求1所述的一种负离子健康漆,其特征在于:制备方法如下:
(1)、首先将净化水270份置入到分散釜中,将分散机的转速设定为300转/分钟,开启分散机,然后再分别将羟丙基瓜尔胶1.5份、羟乙基纤维素2份加入到分散釜中,待分散釜旋转5分钟后,再向分散釜中加入氢氧化钠稀释液,氢氧化钠稀释液的加入量以达到将分散釜中混合液体的PH值调整为8为标准;
(2)、在分散釜不停止转动搅拌的情况下,再分别缓缓的加入水性颜料润湿剂1份、水性分散剂4份、杀菌剂2份、消泡剂1份;然后在分别加入硅酸铝10份、滑石粉50份、微细煅烧高岭土50份、钛白粉200份、微细重质碳酸钙60份、硅灰石10份、重晶石10份、防霉粉13份;
(3)、将分散机的转速调整到800转/分钟,进行高速分散20分钟后,再将分散机的转速调整到200转/分钟,低速分散5分钟后,关闭分散机,然后将分散釜中的浆液通过分散釜下部的管道和齿轮泵传输到砂磨罐中用砂磨机进行研磨;
(4)、经研磨后的浆液通过管道和齿轮泵传输到调漆釜中,开启调漆釜上的电机进行低速旋转,然后在调漆釜不停止转动搅拌的情况下,再分别缓缓的向调漆釜中加入消泡剂2份、丙二醇8份、苯丙乳液200份、负离子涂料添加剂72份、增稠剂2.5份、净化水30份,调漆釜低速旋转搅拌25分钟;
(5)、最后再向调漆釜中加入氢氧化钠稀释液,氢氧化钠稀释液的加入量以达到将调漆釜中混合乳液的PH值调整为8为标准,让调漆釜继保持低速旋转搅拌20分钟;
(6)、最后再向调漆釜中加入氢氧化钠稀释液,氢氧化钠稀释液的加入量以达到将调漆釜中混合乳液的PH值调整为8为标准,让调漆釜继保持低速旋转搅拌20分钟;
(7)、将调漆釜中的乳液通过管道和隔膜泵传输到反冲袋式过滤器中进行过滤,再将过滤后的乳液通过自动灌装设备在生产线上进行20KG的计量灌装,即制成本发明所述的负离子健康漆。
CN200810166823A 2008-09-26 2008-09-26 负离子健康漆 Pending CN101684221A (zh)