CN101660328A - Building waterproof construction method, compound waterproof roll material and preparation method thereof - Google Patents
Building waterproof construction method, compound waterproof roll material and preparation method thereof Download PDFInfo
- Publication number
- CN101660328A CN101660328A CN200910176420A CN200910176420A CN101660328A CN 101660328 A CN101660328 A CN 101660328A CN 200910176420 A CN200910176420 A CN 200910176420A CN 200910176420 A CN200910176420 A CN 200910176420A CN 101660328 A CN101660328 A CN 101660328A
- Authority
- CN
- China
- Prior art keywords
- coiled material
- composite
- water
- layer
- waterproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a building waterproof construction method. The terylene non-woven fabrics of the upper and lower surfaces of compound waterproof roll materials are embedded and blended mutuallywith the polymer cement binding materials before curing to form a whole waterproof layer which tightly sticks to a building structure layer and a rigid waterproofing protective layer in double sides;the whole waterproof layer has favorable waterproof effect, is suitable for proofing water for the following buildings: basements, roofs, tunnels and pools and the like, and construction can also becarried out in overcast and rainy days or moisture base surface. The used compound waterproof roll material is polyethylene macromolecule compound waterproof roll material, and the preparation methodcomprises the following steps: (1) preheating equipment; (2) preparing materials; (3) carrying out extrusion molding; (4) reinforcing a bonding layer compositely; and (5) drawing, cutting edges and rolling to prepare the finished product. The invention also provides a compound waterproof roll material which has the structure that the middle part is a polyethylene film, the upper and lower surfacesare terylene non-woven fabrics; and the compound waterproof roll material comprises the following raw materials: linear low density polyethylene, black masterbatch and short-fiber needle-punched nonwovens. The material has good extensibility, long service life, simple preparation process and simple and convenient construction.
Description
Technical field
The present invention relates to the building waterproofing technique field, be specifically related to a kind of composite of water-proof coiled material of using and form composite of water-proof coiled material that uses in two-sided closely connected waterproofer's method and the described worker's method and preparation method thereof in building structure.
Background technology
Along with rapid economy development, building size enlarges, and the personalization of building, variation are more outstanding, and still, people still are accustomed to adopting waterproof method in the past, as using Ethylene Propylene Terpolymer, PVC or non-tar polyurethane coating.At present on waterproof market popular waterproofing materials, no matter be that coating or coiled material also are non-tar polyurethane coating, all there is the difficult problem that can not solve in these materials from beginning the later maintenance of constructing, and specifically comprise following several aspect:
(1) general waterproof roll, but how these good coiled materials are joined together, forming the waterproofing course that is waterproof together is a difficult problem, the processing of overlap joint, node has become the key point of waterproof roll construction.
(2) material of some waterproofing materialss is too soft, a bit hard thing is arranged slightly just easily material damage, as non-tar polyurethane, modified bitumen etc.If there are indivedual grains of sand in basic unit, be easy to by bursting after waterproofing course is done, and some utensils of job site just are corrupted to waterproofing course easily.The way of basement side wall topping particularly, the protective material that most of waterproofing materials adopts all is a cystosepiment, such topping is difficult to cement with waterproofing course.
(3) rigidity water-proofing material is prevented the crack that unknown malformation causes.
(4) traditional flexible waterproof material separates with structure substantially, does not have great adhesion stress, as long as a point is destroyed, water will be from entering the back side of waterproofing course here, and the leakage point of structure often is not the real damaged points of waterproofing course.The time be difficult to the leakage point that finds waterproofing course real in maintenance, almost can't keep in repair.
Summary of the invention
Technical problem to be solved by this invention is the shortcoming that exists at above prior art, provide a kind of can with building structure buildings waterproof worker closely connected, easy construction method, used composite of water-proof coiled material and preparation method thereof.
For achieving the above object, technical scheme provided by the present invention is:
A kind of buildings waterproof worker method; one polymer cement binding material of brushing on the building structure basal plane; lay the vinyl polymer composite of water-proof coiled material then; polymer cement binding material and waterproof roll are chimeric mutually, complementary, compatible; fit tightly the tack coat (enhancement layer) that forms deck and coiled material layer, form one with building structure layer and the two-sided closely connected integral waterproofing layer of rigid waterproofing topping.Smear cement mortar (topping) on waterproof roll, the terylene non-woven fabric of cement mortar (topping) and waterproof roll surface layer is chimeric mutually, fit tightly the skin that forms protection waterproof roll and waterproof compatibility, and it specifically may further comprise the steps:
(1) constructs a building structure layer;
(2) tack coat is set: evenly brushing thickness is the polymer cement binding material of 1.2mm on described building structure basal plane, constitutes tack coat;
(3) lay the composite of water-proof coiled material layer: prefabricated composite of water-proof coiled material is tiled on the cement-bonded material of the described bonding layer polymer surface; Combination between this coiled material and the adjacent coiled material is parallel docking or overlap joint, carries out node after big face installation of membrane finishes and strengthens handling, and constitutes the composite of water-proof coiled material layer.Described tower connects mode: tower is connect the position clean out, spread polymer cement at the waterproof roll upper and lower surface and paste material;
(4) topping is set: cover described composite of water-proof coiled material with concrete, floating, constitute described topping;
Said structure layer, tack coat (enhancement layer), waterproof roll layer, the common formation of topping be two-sided closely connected integral waterproofing layer together; Composite of water-proof coiled material upper and lower surface wherein and the cement-bonded material of bonding layer polymer mutually embed before curing and merge, and form together and building structure layer and the two-sided closely connected integral waterproofing layer of topping.
Above-mentioned tower connects mode, its lap width: long limit is not less than 80mm, minor face is not less than 100mm.
(5) repeat above-mentioned steps (2)～(4), can constitute dual waterproof construction.
A kind of preparation method of composite of water-proof coiled material of above-mentioned buildings waterproof worker method, it comprises screw injection molding machine, it comprises the steps:
(1) injection machine preheating: with screw rod, the heating earlier of die apparatus heating position 1.5～2.0 hours;
(2) batch mixes: polyethylene and black masterbatch are placed on stir mixing in the batch mixing pot, and dried moisture 10～20 minutes;
(3) extrusion molding: batch mixing is put into hopper, rotated by screw rod and inject raw material, raw material is squeezed into the polyvinyl resin film through the screw rod and the mould of heating;
(4) the compound enhancing tack coat of pressurization: the polyvinyl resin film is gone out to three roll-ins to prolong by the mould mouth, and calendering is rolled roller chopped fiber needle-punched non-weaving cloth is compound to polyvinyl resin film two sides, is extruded to shape through press roll, forms composite of water-proof coiled material;
Wherein, most importantly will regulate calendering and roll the pressure at two ends of roller and the rotating speed of pressure roller, pressure must keep the both sides balance, accomplishes that two sides bonding enhancement layer combined state is good, does not peel off waterproofing course, phozy, but does not injure the inner membrance position of coiled material
(5) traction cutting edge rolling, packing go out finished product.
Wherein, above-mentioned steps (1), the heating-up temperature of screw portion should be gradually high by hanging down: 130 ± 5 ℃ of (4) districts, 110 ± 5 ℃ of (3) districts, 100 ± 5 ℃ of (2) districts, (1) district 150 ± 5 ℃ (5) distinguish 190 ± 5 ℃ in 170 ± 5 ℃ (6) district.
In the above-mentioned steps (3), the propelling rotating speed of screw rod is 900～1150 rev/mins.
Above-mentioned steps (3) comprises that also the temperature at mould extruding and discharging place is controlled at 210 ± 5 ℃ in 205 ± 5 ℃ of (11) districts, 200 ± 5 ℃ of (10) districts, 205 ± 5 ℃ of (9) districts, 210 ± 5 ℃ of (8) districts, (7) district.The temperature on both sides is high slightly, guarantees the whole discharging speed uniformity of mould mouth, and the thickness of stopping coiled material inner membrance waterproofing course differs.
In the above-mentioned steps (4), the calendering roller bearing range of speed control is 250～450 rev/mins.
A kind of composite of water-proof coiled material that adopts method for preparing, it comprises internal layer waterproof film and outer tack coat, it is characterized in that, and the internal layer waterproof film is a polyethylene sheeting, and outer tack coat is the terylene non-woven fabric of described internal layer waterproof film upper and lower surface; Its raw material components comprises: LLDPE, black masterbatch, terylene non-woven fabric; Described black masterbatch is made up of pigment or dyestuff, carrier and three kinds of fundamentals of additive.
Above-mentioned composite of water-proof coiled material, the weight ratio of its raw material components is: LLDPE: black masterbatch is 99: 1; The internal layer waterproof film: the upper and lower surface terylene non-woven fabric is 350～450g/m
2: 100～120g/m
2
The invention has the beneficial effects as follows:
1, the good water-proof effect of buildings waterproof worker method of the present invention: the top terylene non-woven fabric of composite of water-proof coiled material and polymer cement are pasted material; embed mutually before solidifying and merge; complementary compatible, the hard and soft compound exterior waterproof coating of one coiled material of complementary formation and coating also plays protection main water barrier polyethylene sheeting simultaneously.Terylene non-woven fabric below the composite of water-proof coiled material and the cement mortar tabling that is layered on the building structure basal plane are combined closely composite of water-proof coiled material and building basal plane, can prevent " scurrying water " effectively.The waterproof method of building structure of the present invention adopts hard and soft composite water-proof structure, and it pastes material by polymer cement bonding force is bonded at flexible waterproof roll on the structure firmly.This coiled material uses polymer cement to paste material coiled material completely is attached on the structure, comprises node, and overlap edge all uses polymer cement to paste full sticking, the compacting of material, after do not have any leak source.Reliably bonding between coiled material and the basic unit, local location destroys, and water only can Anywhere, not overcome leveling layer and not play waterproof action around can not scurrying at ruined this point, in case coiled material leaks easy " scurrying water " not easy-to-maintain defective.The waterproof method of building structure of the present invention can be realized dual waterproof construction, strengthens waterproof effect.
2, buildings waterproof worker method employing polymer cement of the present invention is pasted and is expected to have one's face covered with cold mounting method construction, can construct on moist basal plane, as long as no open fire can be constructed; After having smeared leveling layer or having smash concrete, under the situation of people on the not sticking pin energy, also can construct; Even under the environment of occasional drizzles, all can construct, shorten the construction period.
3, economy: as tack coat, save traditional levelling Cen layer with cement mortar, reduce construction costs, do not need base treatment agent, reduce operation, save cost of labor.
4, embody the feature of environmental protection: general waterproof roll needs base treatment agent, and it generally has volatile solvent soln, contaminated environment, hot melt coiled material consume fuel resource.Composite of water-proof coiled material is owing to be two-sided closely connected, and in work progress, the employing cement mortar is bonding, pollution-free, the saving resource.
5, the construction technology of buildings waterproof worker method of the present invention is simple: basic unit does not need base treatment agent to handle, and is not high to the levelling processing requirements yet, and manually training can be constructed slightly.
6, composite of water-proof coiled material preparation technology of the present invention is simple, adopts the method for vertical compression heat seal, can realize the industrialization production application.
7, composite sheet material main water barrier polyethylene sheeting, the two sides is a terylene non-woven fabric, and the life-span is long, and favorable extensibility is arranged, and after deformation took place in building structure basic unit, the sizing material at place, crack was stretched, and the coiled material main body remains intact.The composite of water-proof coiled material performance is good: terylene non-woven fabric tensile strength is big, and the elongation per unit length height is corrosion-resistant good, and bonding is permanent, firm, endurable thorn.
For a better understanding of the present invention, below in conjunction with drawings and Examples the present invention is further set forth.
Description of drawings
Fig. 1 is the generalized section of waterproofing course of the buildings waterproof worker method of the embodiment of the invention 1;
Fig. 2 is the generalized section of composite of water-proof coiled material of the present invention;
Fig. 3 is the generalized section of dual waterproofing course of the buildings waterproof worker method of the embodiment of the invention 2.
Wherein: 1, the 3-terylene non-woven fabric, the 2-polyethylene sheeting, the 4-deck, 5, the 8-polymer cement is pasted material tack coat, 6,9-composite of water-proof coiled material layer, 7,10-cement mortar protective course.
The specific embodiment
Embodiment 1: referring to Fig. 1, and a kind of buildings waterproof worker method that present embodiment provides, it comprises the steps:
(1) construct a building structure layer 4: it is floating directly to carry slurry;
(2) tack coat 5 is set: evenly brushing thickness is the polymer cement binding material of 1.2mm on described building structure basal plane, constitutes tack coat;
(3) shop waterproof roll layer 6: the thick composite of water-proof coiled material of prefabricated 0.8mm is tiled on the cement-bonded material of the described bonding layer polymer surface; Combination between this coiled material and the adjacent coiled material is parallel docking or overlap joint, carries out node after big face installation of membrane finishes and strengthens handling, and constitutes the composite of water-proof coiled material layer.Described tower connects mode: tower is connect the position clean out, spread polymer cement at the waterproof roll upper and lower surface and paste material;
(4) topping 7 is set: cover described composite of water-proof coiled material with concrete, floating, constitute described topping;
Said structure layer, tack coat (enhancement layer), waterproof roll layer, the common formation of topping be two-sided closely connected integral waterproofing layer together; Composite of water-proof coiled material upper and lower surface wherein and the cement-bonded material of bonding layer polymer mutually embed before curing and merge, and form together and building structure layer and the two-sided closely connected integral waterproofing layer of topping.
Above-mentioned tower connects mode, its lap width: long limit is not less than 80mm, minor face is not less than 100mm.
The concrete operations step of present embodiment is: basic unit's face of handling building structure, make it solid, clean, and it is fully moistening, no ponding, brush 1.2mm thick polymer cement then and paste material, can spread composite of water-proof coiled material, embed mutually before one deck terylene non-woven fabric and polymer cement are pasted material and solidified below the waterproof roll and merge, complementary one coiled material and compatible, the hard and soft compound waterproofing course of coating complementation of forming.On coiled material, smear the cement mortar covering and do topping.Juncture between the composite of water-proof coiled material is that parallel docking or tower connect.Tower is connect the position clean out, spread cement at the waterproof roll upper and lower surface and paste material, compacting, floating; When tower connect, lap width: lap width: long limit was not less than 80mm, minor face is not less than 100mm.
The preparation method of the employed composite of water-proof coiled material of above-mentioned waterproof method may further comprise the steps:
(1) equipment preheating: screw rod, the heating earlier of die apparatus heating position 1.5～2.0 hours;
(2) batch mixes: will prepare burden (weight ratio, polyethylene/black masterbatch=99/1) is placed on stir mixing oven dry moisture (10～20 minutes) in the batch mixing pot;
(3) extrusion molding: batch mixing is put into hopper, rotate (900～1150 rev/mins) by screw rod and inject raw material, raw material is through the screw rod and the mould of heating, extrusion modling, wherein the heating-up temperature of screw portion should be gradually high by hanging down: 130 ± 5 ℃ of (4) districts, 110 ± 5 ℃ of (3) districts, 100 ± 5 ℃ of (2) districts, (1) district 150 ± 5 ℃ (5) distinguish 190 ± 5 ℃ in 170 ± 5 ℃ (6) district; The temperature at mould extruding and discharging place is controlled at: 205 ± 5 ℃ in 210 ± 5 ℃ of (8) districts, (7) district.(9) 205 ± 5 ℃ of (11) districts, 200 ± 5 ℃ of (10) districts, district are 210 ± 5 ℃;
(4) compound enhancing tack coat: two surfaces are compound with chopped fiber needle-punched non-weaving cloth (terylene non-woven fabric), are extruded to shape through press roll, wherein coiled material internal layer waterproof film: terylene non-woven fabric (upper and lower surface)=350～450g/m
2: 110 ± 10g/m
2
(5) traction cutting edge rolling, packing go out finished product.
Referring to Fig. 2, the composite of water-proof coiled material that said method makes, its structure is that the centre is that the internal layer waterproofing course 2 of polyethylene sheeting, coiled material upper and lower surface are terylene non-woven fabric 1,3.
Embodiment 2: referring to Fig. 3, and the buildings waterproof worker method that present embodiment provides, its basic technical scheme is identical with embodiment 1, and its difference is that it also comprises step (5): repeat described step (2)～(4), make up double-deck waterproofing course.
The concrete steps of present embodiment are successively: (1) building structure layer 4: it is floating directly to carry slurry; (2) tack coat 5 is set: brushing 1.2mm thick polymer cement is pasted the material tack coat; (3) shop waterproof roll layer 6: the thick prefabricated composite of water-proof coiled material of paving 0.8mm; (4) topping 7 is set: smear cement mortar and do topping; (5) tack coat 8 is set: brushing 1.2mm thick polymer cement is pasted the material tack coat; (6) shop waterproof roll layer 9: the thick prefabricated composite of water-proof coiled material of paving 0.8mm; (7) topping 10 is set: smear cement mortar and do topping.By above-mentioned steps, constitute a dual waterproof construction.
The preparation method of the employed composite of water-proof coiled material of present embodiment and goods are identical with embodiment's 1.
The invention is not restricted to the foregoing description, the above-mentioned same or similar method of every employing and the present invention realizes all embodiments of the object of the invention, all within protection scope of the present invention.
Claims (10)
1, a kind of buildings waterproof worker method, it comprises the building structure basal plane, it is characterized in that, it comprises the steps:
(1) constructs a building structure layer;
(2) tack coat is set: evenly brushing thickness is the polymer cement binding material of 1.2mm on the basal plane of described building structure layer, constitutes tack coat;
(3) lay the composite of water-proof coiled material layer: prefabricated composite of water-proof coiled material is tiled on the surface of polymer cement ramming material of described tack coat, combination between this coiled material and the adjacent coiled material is parallel docking or overlap joint, carry out node after big face installation of membrane finishes and strengthen handling, constitute the composite of water-proof coiled material layer;
(4) topping is set: cover described waterproof roll layer with concrete, floating, constitute topping;
Above-mentioned building structure layer, tack coat, composite of water-proof coiled material layer, the common formation of topping be two-sided closely connected integral waterproofing layer together; Composite of water-proof coiled material upper and lower surface wherein and the cement-bonded material of bonding layer polymer mutually embed before curing and merge, and form together and building structure layer and the two-sided closely connected integral waterproofing layer of topping.
2, buildings waterproof worker method according to claim 1 is characterized in that, repeating step (2)～(4) constitute dual waterproof construction.
3, buildings waterproof worker method according to claim 1 and 2, it is characterized in that, described tower connects mode: tower is connect the position clean out, spread polymer cement at the waterproof roll upper and lower surface and paste material, lap width: long limit is not less than 80mm, minor face is not less than 100mm.
4, a kind of preparation method who realizes the composite of water-proof coiled material of claim 1 or 2 described buildings waterproof worker methods, it comprises screw injection molding machine, it is characterized in that, it comprises the steps:
(1) injection machine preheating: with screw rod, the heating earlier of die apparatus heating position 1.5～2.0 hours;
(2) batch mixes: polyethylene and black masterbatch are placed on stir mixing in the batch mixing pot, and dried moisture 10～20 minutes;
(3) extrusion molding: batch mixing is put into the injection machine hopper, rotated by screw rod and inject raw material, raw material is squeezed into the polyvinyl resin film through the screw rod and the mould of heating;
(4) the compound enhancing tack coat of pressurization: the polyvinyl resin film is gone out to three roll-ins to prolong by the mould mouth, and calendering is rolled roller chopped fiber needle-punched non-weaving cloth pressurization is compound to polyvinyl resin film two sides, and is extruded to shape through press roll, forms composite of water-proof coiled material;
(5) traction cutting edge rolling, packing go out finished product.
5, the preparation method of composite of water-proof coiled material according to claim 4 is characterized in that, in the described step (3), the propelling rotating speed of screw rod is 900～1150 rev/mins.
6, the preparation method of composite of water-proof coiled material according to claim 4 is characterized in that, in the described step (4), the calendering roller bearing range of speed control is 250～450 rev/mins.
7, the preparation method of composite of water-proof coiled material according to claim 4, it is characterized in that, in the described step (1), the heating-up temperature of screw portion should be gradually high by hanging down: 130 ± 5 ℃ of (4) districts, 110 ± 5 ℃ of (3) districts, 100 ± 5 ℃ of (2) districts, (1) district 150 ± 5 ℃ (5) distinguish 190 ± 5 ℃ in 170 ± 5 ℃ (6) district.
8, according to the preparation method of the described composite of water-proof coiled material of claim 4, it is characterized in that, in the described step (3), the temperature at mould extruding and discharging place is controlled at 210 ± 5 ℃ in 205 ± 5 ℃ of (11) districts, 200 ± 5 ℃ of (10) districts, 205 ± 5 ℃ of (9) districts, 210 ± 5 ℃ of (8) districts, (7) district.
9, a kind of composite of water-proof coiled material that adopts the described method preparation of claim 4, it comprises internal layer waterproof film and the outer tack coat that strengthens, it is characterized in that its internal layer waterproof film is a polyethylene sheeting, outer enhancing tack coat is the terylene non-woven fabric of described internal layer waterproof film upper and lower surface; Its raw material is formed and is comprised: LLDPE, black masterbatch, terylene non-woven fabric; Described black masterbatch is made up of pigment or dyestuff, carrier and three kinds of fundamentals of additive.
10, composite of water-proof coiled material according to claim 9 is characterized in that, the weight ratio of its component is: LLDPE: black masterbatch is 99: 1; The internal layer waterproof film: the upper and lower surface terylene non-woven fabric is 350～450g/m
2: 100～120g/m
2