CN101629286B - 一种陶化剂及其制备方法 - Google Patents

一种陶化剂及其制备方法 Download PDF

Info

Publication number
CN101629286B
CN101629286B CN2009100415992A CN200910041599A CN101629286B CN 101629286 B CN101629286 B CN 101629286B CN 2009100415992 A CN2009100415992 A CN 2009100415992A CN 200910041599 A CN200910041599 A CN 200910041599A CN 101629286 B CN101629286 B CN 101629286B
Authority
CN
China
Prior art keywords
parts
water
fluozirconate
solution
add
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2009100415992A
Other languages
English (en)
Other versions
CN101629286A (zh
Inventor
覃秋兰
谭富
岑添祥
陆耀权
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2009100415992A priority Critical patent/CN101629286B/zh
Publication of CN101629286A publication Critical patent/CN101629286A/zh
Application granted granted Critical
Publication of CN101629286B publication Critical patent/CN101629286B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种陶化剂，其由下述质量组成份数的原材料制成：氟锆酸钾或氟锆酸钠：20～30份，氟化物：5～10份，络合剂：5～10份，水：40～60份。通过本工艺制作出来的陶化剂稳定性好，无沉渣，不含磷酸盐，可以在钢铁、锌和铝的表面上形成一层陶化层，其与各型号的涂料结合力强，适合常温的喷淋和浸泡处理，无须加热设备，达到节约能源、易于生产的目的。

Description

一种陶化剂及其制备方法 
技术领域
本发明涉及一种用于金属表面涂漆前进行陶化处理的陶化剂，特别是一种陶化剂及其制备方法。 
背景技术
目前许多钢铁制品加工企业，在进行金属制品加工涂漆前对金属表面只作简单的除油、除锈处理，没有做细致的化学加工，为钢铁材料今后的使用埋下了隐患，即经过半年到一年的使用就开始出现锈蚀现象，严重的影响了钢材的使用寿命。于是市面上出现了一种用于金属材料的表面涂漆前的磷化处理剂，其主要是将金属材料放入含有锰、铁、锌的磷酸盐溶液中进行化学处理，使金属表面生成一层难溶于水的磷酸盐保护膜，但是该磷化技术存在使用温度高，槽液不稳定，成本高，易出现沉渣降低了磷化膜的防腐性能。 
发明内容
为了克服现有技术的不足，本发明提供一种防锈效果好、制作成本低的陶化剂及其制备方法。 
本发明解决其技术问题所采用的技术方案是： 
一种陶化剂，其由下述质量组成份数的原材料制成：氟锆酸钾或氟锆酸钠：20～30份，氟化物：5～10份，络合剂：5～10 份，水：40～60份。 
一种制备上述陶化剂的方法，其步骤如下： 
1)按比例称取各种原料； 
2)在占称取原料重量2/3的水内加入氟锆酸钾或氟锆酸钠搅拌至溶解状态； 
3)在步骤2制得的溶液内加入氟化物搅拌至溶解状态； 
4)在步骤3制得的溶液内加入络合剂搅拌至溶解状态； 
5)在步骤4制得的溶液内加入占称取原料重量1/3的水搅拌10～20分钟即可。 
本发明的有益效果是：通过本工艺制作出来的陶化剂稳定性好，无沉渣，不含磷酸盐，可以在钢铁、锌和铝的表面上形成一层陶化层，其与各型号的涂料结合力强，适合常温的喷淋和浸泡处理，无须加热设备，达到节约能源、易于生产的目的。 
具体实施方式
一种陶化剂，其由下述质量组成份数的原材料制成：氟锆酸钾或氟锆酸钠：20～30份，氟化物：5～10份，络合剂：5～10份，水：40～60份。 
该陶化剂的最佳重量组成份数为：氟锆酸钾或氟锆酸钠：25份，氟化物：7份，络合剂：7份，水：50份。 
本发明使用的氟化物可以是：氢氟酸、氟化钠等，络合剂采用酒石酸。 
一种制备上述陶化剂的方法，其步骤如下： 
1)按比例称取各种原料； 
2)在占称取原料重量2/3的水内加入氟锆酸钾或氟锆酸钠搅拌至溶解状态； 
3)在步骤2制得的溶液内加入氟化物搅拌至溶解状态； 
4)在步骤3制得的溶液内加入络合剂搅拌至溶解状态； 
5)在步骤4制得的溶液内加入占称取原料重量1/3的水搅拌10～20分钟即可。 
为便于对本发明进一步理解，现结合具体实施例对本发明进行详细描述。 
实施例1： 
一种制备上述陶化剂的方法，其步骤如下： 
1)称取氟锆酸钾：20份，氟化钠：5份，酒石酸：5份，水：40份。 
2)在27份水内加入氟锆酸钾搅拌2～3分钟至溶解状态； 
3)在步骤2制得的溶液内加入氟化钠搅拌2～3分钟至溶解状态； 
4)在步骤3制得的溶液内加入酒石酸搅拌2～3分钟至溶解状态； 
5)在步骤制得的溶液内加入13份的水搅拌10～20分钟即可。 
实施例2： 
一种制备上述陶化剂的方法，其步骤如下： 
1)称取氟锆酸钠：25份，氢氟酸：7份，酒石酸：7份，水：50份。 
2)在34份水内加入氟锆酸钠搅拌2～3分钟至溶解状态； 
3)在步骤2制得的溶液内加入氢氟酸搅拌2～3分钟至溶解状态； 
4)在步骤3制得的溶液内加入酒石酸搅拌2～3分钟至溶解状态； 
5)在步骤4制得的溶液内加入16份的水搅拌10～20分钟即可。 
实施例3： 
一种制备上述陶化剂的方法，其步骤如下： 
1)称取氟锆酸钾：30份，氢氟酸：10份，酒石酸：10份，水：60份。 
2)在40份水内加入氟锆酸钾搅拌2～3分钟至溶解状态； 
3)在步骤2制得的溶液内加入氢氟酸搅拌2～3分钟至溶解状态； 
4)在步骤3制得的溶液内加入酒石酸搅拌2～3分钟至溶解状态； 
5)在步骤4制得的溶液内加入20份的水搅拌10～20分钟即可。 
通过本工艺制作出来的陶化剂稳定性好，无沉渣，不含磷酸盐，可以在钢铁、锌和铝的表面上形成一层陶化层，其与各 型号的涂料结合力强，适合常温的喷淋和浸泡处理，无须加热设备，达到节约能源、易于生产的目的。 

Claims (3)

1.一种陶化剂，其特征在于：由下述质量组成份数的原材料制成：氟锆酸钾或氟锆酸钠：20～30份，氟化物：5～10份，酒石酸：5～10份，水：40～60份。
2.根据权利要求1所述的一种陶化剂，其特征在于：氟锆酸钾或氟锆酸钠：25份，氟化物：7份，酒石酸：7份，水：50份。
3.一种生产权利要求1或2所述陶化剂的方法，其特征在于：步骤如下：
1)按比例称取各种原料；
2)在占称取原料重量2/3的水内加入氟锆酸钾或氟锆酸钠搅拌至溶解状态；
3)在步骤2制得的溶液内加入氟化物搅拌至溶解状态；
4)在步骤3制得的溶液内加入酒石酸搅拌至溶解状态；
5)在步骤4制得的溶液内加入占称取原料重量1/3的水搅拌10～20分钟即可。
CN2009100415992A 2009-07-29 2009-07-29 一种陶化剂及其制备方法 Expired - Fee Related CN101629286B (zh)