CN101628787A - 无砷低铁荧光灯用玻璃 - Google Patents

无砷低铁荧光灯用玻璃 Download PDF

Info

Publication number
CN101628787A
CN101628787A CN200810063484A CN200810063484A CN101628787A CN 101628787 A CN101628787 A CN 101628787A CN 200810063484 A CN200810063484 A CN 200810063484A CN 200810063484 A CN200810063484 A CN 200810063484A CN 101628787 A CN101628787 A CN 101628787A
Authority
CN
China
Prior art keywords
glass
percent
arsenic
fluorescent lamps
iron
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN200810063484A
Other languages
English (en)
Inventor
江涛
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang Super Lighting Electric Appliance Co Ltd (CN)
Original Assignee
Zhejiang Super Lighting Electric Appliance Co Ltd (CN)
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhejiang Super Lighting Electric Appliance Co Ltd (CN) filed Critical Zhejiang Super Lighting Electric Appliance Co Ltd (CN)
Priority to CN200810063484A priority Critical patent/CN101628787A/zh
Publication of CN101628787A publication Critical patent/CN101628787A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种无砷低铁荧光灯用玻璃，其以重量百分比计，含有SiO2：60－75％、Al2O3：0.5－5.0％、Na2O+K2O：12.0－22.0％、CaO+MgO：4.0－20.0％、B2O3：0.5－5.0％、CeO2：0.2－0.5％、Fe2O3：0.02－0.05％，该玻璃与普通荧光灯用钠钙玻璃性能接近，适合低气压放电灯的玻管及其它部件生产，其不含有砷，环保性好，并且玻璃中铁氧化物成分的含量低，光线透过率高、用其生产的荧光灯光效可提高2％。

Description

无砷低铁荧光灯用玻璃
技术领域
本发明涉及一种玻璃，特别是一种无砷低铁荧光灯用玻璃。
背景技术
目前，在荧光灯用的普通钠钙玻璃中，一般都包含有砷氧化物As2O3和铁氧化物Fe2O3。并且所述的铁氧化物成分含量在0.1％左右，铁氧化物使玻璃的颜色呈现淡绿色，在玻璃中对光透过率性能负面影响较大，低铁氧化物含量是荧光灯用玻璃的理想选择。砷是一种有毒物质，含有砷的玻璃在生产、加工和使用过程中，对环境和人身都非常有害。因此，人们希望生产和采用的荧光灯用玻璃不含有砷。
发明内容：
本发明要解决的技术问题主要是提供一种无砷低铁荧光灯用玻璃，使玻璃光透过率性能好，以及其它性能与普通荧光灯用钠钙玻璃相近，且不含有砷。
本发明提供的一种无砷低铁荧光灯用玻璃，其特征是：所述玻璃含有以下成份(以重量百分比计)：
SiO2        60.0-75.0
Al2O3       0.5---5.0
Na2O+K2O    12.0---22.0
CaO+MgO     4.0---20.0
B2O3       0.5---5.0
CeO2       0.2---0.5
Fe2O3      0.02-0.05
所述无砷低铁荧光灯用玻璃成分优选方案为：
SiO2       71.7
Al2O3      1.5
Na2O+K2O   17.6
CaO+MgO    7.75
B2O3       1.0
CeO2       0.22
Fe2O3      0.04
本发明中SiO2为玻璃组成的主体，较佳含量为60％--75％重量。若SiO2含量少于60％重量，所制作出的玻璃膨胀系数较大，粘度降低，不利于荧光灯的制作；若SiO2含量大于75％重量，将导致玻璃的软化温度过大升高和析晶倾向增加，而玻璃工作温度点的升高，将不利于荧光灯的制作加工。
Al2O3是为增强玻璃耐候性和失透性的组分，当含量小于0.5％重量时无法取得该效果，当含量大于5.0时，会降低玻璃的熔化效果，使玻璃缺陷增多。
R2O(Na2O+K2O)是调整玻璃膨胀系数使之能够与其他玻璃及金属封接在一起的组分，R2O还具有降低玻璃液粘度的作用，使之更有利于的玻璃的加工成型。当R2O含量小于12％时，上述效果无法体现；当R2O含量大于22％重量时，玻璃的膨胀系数过大，影响荧光灯的制作，同时因Na2O组分的升高会增大玻管析碱倾向，从而影响荧光灯的透光性。
R2O(CaO+MgO)是降低高温玻璃粘度、提高玻璃硬度的组分，同时可以降低玻璃成本。RO大于20％重量时，会使玻璃的料性变短，脆性增加，同时在玻璃的熔制过程中易于失透，玻璃的析晶倾向增加，耐化学侵蚀降低。
Fe2O3作为一种杂质成分的引入，Fe2O3的含量会直接影响荧光灯的光通。
为了降低紫外线的透射率，提高紫外线的屏蔽能力，CeO2作为一种基本组分引入，同时在玻璃熔制过程中起澄清剂的作用。当含量低于0.1％重量时达不到所期望的效果，超过0.5％重量时会影响可见光的光通，用CeO2代替As2O3作为澄清剂，可避免玻璃光透过率性能的下降。
本发明由于在玻璃组份中去除了砷氧化物As2O3，以及控制铁氧化物Fe2O3在0.02-0.05％重量间，使得玻璃的光透过率性能好，以及其它性能与普通荧光灯用钠钙玻璃相近，且不含有砷。
具体实施方式
下表列出了本发明两实施例，以及相比较的普通钠钙玻璃组份和相关性能比较情况。
  玻璃组份及参数  本发明实施例1  本发明实施例2  本发明实施例3   普通钠钙玻璃
  SiO2   75   60   71.7   72
  Al2O3   0.5   5.0   1.5   1.7
Na2O+K2O 15.0 12.0 17.6 15.6
  CaO+MgO   4.0   21.0   7.75   8
  B2O3   5.0   0.5   1.0   1.6
  As2O3   0.26
  CeO2   0.2   0.5   0.22
  Fe2O3   0.02   0.05   0.04   0.1
  膨胀系数x10-7   91   96   93   93
  软化温度(C)   716   680   689   710
  密度(Kg/dm3)   2.65   2.50   2.60   2.50
由上表可知，本发明提供的一种无砷低铁荧光灯用玻璃，其膨胀系数、软化温度和密度的性能均与普通荧光灯用钠钙玻璃相近，且铁含量较低、不含有砷，是一朝环保型高品质荧光灯用玻璃。

Claims (2)

1：一种无砷低铁荧光灯用玻璃，其特征是：所述玻璃含有以下成份(以重量百分比计)：
SiO2        60.0-75.0
Al2O3       0.5---5.0
Na2O+K2O    12.0---22.0
CaO+MgO     4.0---20.0
B2O3        0.5---5.0
CeO2        0.2---0.5
Fe2O3       0.02-0.05
2.根据权利要求1所述的一种无砷低铁荧光灯用玻璃，其特征是：所述玻璃含有以下成份(以重量百分比计)：
SiO2        71.7
Al2O3       1.5
Na2O+K2O    17.6
CaO+MgO     7.75
B2O3        1.0
CeO2        0.22
Fe2O3       0.04
CN200810063484A 2008-08-14 2008-08-14 无砷低铁荧光灯用玻璃 Pending CN101628787A (zh)