CN101624749A - Process for producing high-performance cleaning cloth - Google Patents
Process for producing high-performance cleaning cloth Download PDFInfo
- Publication number
- CN101624749A CN101624749A CN200810124449A CN200810124449A CN101624749A CN 101624749 A CN101624749 A CN 101624749A CN 200810124449 A CN200810124449 A CN 200810124449A CN 200810124449 A CN200810124449 A CN 200810124449A CN 101624749 A CN101624749 A CN 101624749A
- Authority
- CN
- China
- Prior art keywords
- polyester film
- polyester
- cleaning cloth
- polyamide compound
- cloth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a process for producing high-performance cleaning cloth and relates to a process for producing living goods. The process for producing high-performance cleaning cloth comprises the steps of twisting wires, weaving the wires to make cloth and dyeing the cloth, wherein in the step of twisting wires, polyester and polyamide compound fibers are fed into a textured yarn twisting machine in a double-roller mode and coated with a polyester film; the feeding speed of the polyester film is 380 to 420 m/min; the feeding speed of the polyester and polyamide compound fibers is 300 to 340 m/min; and the pressure is 0.8 to 1.2 kg/cm<2>. The process has the advantages that: the polyester and polyamide compound fibers and the polyester film are combined together by coating the polyester film on the polyester and polyamide compound fibers, so the excellent strength, elasticity and wear resistance of the polyester film well adapt the cleaning cloth to stubborn stains when the cleaning cloth cleans articles; and meanwhile, the high water absorptivity of the polyester and polyamide compound fibers well adapt the cleaning cloth to wet environments.
Description
Technical field
The present invention relates to a kind of production technology of daily necessities, relate in particular to a kind of production technology of high-performance cleaning cloth.
Background technology
Cleaning cloth is a decontamination instrument commonly used in people's daily life, often make by polyamide composite filaments or polyester film, polyamide composite filaments has good hand touch, good moisture absorption is loose moist, be applicable in the moist environment, but because of its quality softness, be not suitable for the wiping stain, and the polyester film has good intensity, elasticity and ABRASION RESISTANCE, the stain of going out is comparatively effective, but it is moist relatively poor that its moisture absorption is loose, be not suitable for using in a humid environment, but frequent wiping stain in a humid environment just needs to prepare two cleaning cloths of being made by polyamide composite filaments and polyester film respectively this moment in daily life, uses inconvenience, sometimes also use mistake easily, cause the damage of cleaning cloth.
Summary of the invention
The present invention is directed to above-mentioned defective, purpose is to provide a kind of cleaning cloth of producing to have the production technology of the high-performance cleaning cloth of polyamide composite filaments and polyester film advantage concurrently.
Technical scheme of the present invention is: the present invention includes and twist thread, be woven into cloth, dyeing, the step of twisting thread: adopt two roller modes to feed the pattern twisting machine polyamide composite filaments and polyester film, and make the polyester film envelope polyamide composite filaments, the feeding speed of polyester film is 380m/min-420m/min, the feeding speed of polyamide composite filaments is 300m/min-340m/min, and pressure is 0.8kg/cm2-1.2kg/cm2.
The present invention is combined with each other polyamide composite filaments and polyester film, the polyester film is enveloped polyamide composite filaments, during the wiping object, because the polyester film has good intensity, elasticity and ABRASION RESISTANCE, so it can be good at adapting to stain, utilize the polyamide composite filaments high-hydroscopicity simultaneously, make it can well adapt to wet environment.
The specific embodiment
Embodiment 1
The present invention includes and twist thread, be woven into cloth, dyeing, it is characterized in that, the step of twisting thread: adopt two roller modes to feed the pattern twisting machine polyamide composite filaments and polyester film, and make the polyester film envelope polyamide composite filaments, the feeding speed of polyester film is 380m/min, the feeding speed of polyamide composite filaments is 300m/min, and pressure is 0.8kg/cm2.
Embodiment 2
The present invention includes and twist thread, be woven into cloth, dyeing, it is characterized in that, the step of twisting thread: adopt two roller modes to feed the pattern twisting machine polyamide composite filaments and polyester film, and make the polyester film envelope polyamide composite filaments, the feeding speed of polyester film is 420m/min, the feeding speed of polyamide composite filaments is 340m/min, and pressure is 1.2kg/cm2.
Claims (1)
1, the production technology of high-performance cleaning cloth, comprise and twist thread, be woven into cloth, dyeing, it is characterized in that, the step of twisting thread: adopt two roller modes to feed the pattern twisting machine polyamide composite filaments and polyester film, and make the polyester film envelope polyamide composite filaments, the feeding speed of polyester film is 380m/min-420m/min, and the feeding speed of polyamide composite filaments is 300m/min-340m/min, and pressure is 0.8kg/cm2-1.2kg/cm2.