CN101617909A - 舍利子制品的制作方法 - Google Patents
舍利子制品的制作方法 Download PDFInfo
- Publication number
- CN101617909A CN101617909A CN200910010807A CN200910010807A CN101617909A CN 101617909 A CN101617909 A CN 101617909A CN 200910010807 A CN200910010807 A CN 200910010807A CN 200910010807 A CN200910010807 A CN 200910010807A CN 101617909 A CN101617909 A CN 101617909A
- Authority
- CN
- China
- Prior art keywords
- buddhist
- relic
- bone
- sharipu
- degree
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明为舍利子制品的制作方法，将人体骨灰、水晶及制品与硅酸盐金属显色料研磨至微细；按比例配合均匀，加水揉捏模压制成舍利子制品湿坯，经干燥、加硅酸盐金属显色料喷涂浸渍、干燥、预热、再经1300度氧化条件下烧结、缓慢冷却至室温印制上图片和箴言；经检验合格即为舍利子制品；它具有优良的物化性能并具有美观的外形。佩戴舍利子佩饰、在家中放置舍利子金字塔、舍利子玉壁对先人和亲人进行纪念是一种体现生态文明的纪念方式。
Description
技术领域
本发明为利用人体骨灰制做舍利子制品的制作方法。
技术背景
1、根据佛教的传统说法；舍利一为：真身舍利，大德之人圆寂火化的灵骨或不腐肉身。二为：碎身舍利即舍利子，大德之人圆寂火化后发现的一种特殊物质；其大小不一、外观圆润、色泽亮丽、表面坚硬。三为：法身舍利即佛教一切大德经典，为留给后人的智慧结晶。相传佛祖释迦牟尼圆寂火化后，炼制出一担六斗约84000颗舍利子；并传四方供人们瞻仰，以弘杨佛法。中国陕西省扶风县法门寺地宫中，发现有珍藏的佛祖释迦牟尼的佛指舍利一尊、影舍利三尊、及大量舍利子；现依然保存在法门寺供奉，而其它地方也相继发现慧能、弘一等法师圆寂火化后的舍利子。
2、舍利子是一种特殊物质，印度语叫驮都，也叫设利罗，梵文(sarira)译成中文叫灵骨、身骨、遗骨。它是大德之人圆寂火化后，留下来的可供人们瞻仰的宝贵的精神载体；在物质层面它光彩照人，它们像玉石、玛瑙、水晶晶莹美观；是一难得的珍品。经研究分析，它的主要化学成分是钙、磷、硅及少量鋁、镁、钾、钠、铁等元素。主要矿物是磷酸盐、鋁硅酸盐、硅酸盐等多种矿物的共融体，
3、舍利子的成因，长期以来人们说法不一；有的认为是结石，有的赋予神密色彩。我们认为舍利子既然是自然界的产物；它就必然是物质的、现实的。经我们长期研究，初步揭示舍利子生成的一些基本条件和原由。
(1)、人的骨骼由三百多块骨头构成，而每块骨头都由致密骨或称皮质骨和松质骨组成。骨基质主要无机成分由羟基磷灰石，阳离子钙、镁、钾、钠、铁等和阴离子酸性氧化物组成，约占百分之七十；钙提供骨骼硬度和压力。骨基质中的有机成分由胶原蛋白和糖蛋白构成，约占百分之三十；提供支撑和张力。通过血管进行营养物质和阴，阳离子输送并保持平衡。一般情况下火化，人体骨经高温有机物质氧化燃烧，无机物磷酸钙和碳酸钙分解形成磷酸钙和氧化钙，冷却后成为灰色低强度的骨灰。
(2)、大德之人的生活环境如能给他们提供硅元素；就具备了生成舍利子可能性。经调查，有一些天然水源及泉水中都含有较高浓度的偏硅酸，每升含50毫克上下；如食物：糙米、粗小麦、玉米、土豆、地瓜等都富含硅元素。他们长期饮食这种水源和食物；身体中会富集硅元素。经研究硅元素对人体具有重要的作用，它有利于人体骨胳和机体的生长发育，有利于心血管系统和免疫系统的完善提高；使人延年益寿，体格强壮。在精神生活方面他们脱离了世俗的影响，胸怀坦荡、高雅厚德；为他们充分吸纳有益于身体健康的矿物质提供了重要的道德和精神层面的有利条件。
(3)、大德之人圆寂火化，在高温条件下他们骨骼中的骨胶原蛋白等有机物燃烧氧化；骨胳中的磷酸钙和碳酸钙分解为磷酸钙和氧化钙。在骨骼中主要富集了的硅元素和少量钾、钠、钙、镁、铝、铁等元素也都形成了氧化物。这些氧化物可分为碱性氧化物、碱土氧化物和酸性氧化物并具有活性；它们可以进行固相反应和化学反应。当温度达到一定时，由碱金属、碱土金属形成的矿物就会以液相的形式出现。液相起到凝结固相充填空隙并促进固相反应和化学反应生成鋁硅酸盐、硅酸盐等多种矿物，与磷酸钙形成共融体；冷却后有玻璃体出现。这些矿物统称为硅酸盐矿物；它们是除磷酸钙之外的主体矿物结构。它们的基本单元是由硅氧四面体构成，硅氧四面体之间通过公共氧原子进行架状结构连接，向形成包围磷酸盐的三维结构发展。而硅氧四面体中的硅原子可以被其它原子、如由鋁原子取代，成为鋁氧四面体；就产生多余的负电荷与金属离子钙、钾、钠、镁、铁等离子结合成为新的硅酸盐矿物。据多相动力机理的传质机理，在特定部位及周边富集了的硅元素和其它元素通过蒸发、凝聚机理，扩散传质机理和粘性流动、塑性流动机理；它们可以向一个特定部位扩散和富集。在这样的情况下，在特定部位生成的液相和矿物的总量会相对增加；从而液相和矿物包裹固相，占据空隙形成结构紧密的实体。这种由磷酸钙，鋁硅酸盐，硅酸盐等多种矿物的共融体就形成了；经冷却固化有玻璃体出现并成颗粒状，球状或其它一些形状。这时如果有各种金属离子存在，就会出现不同色彩；钙的基色为乳白色、三价铁显浅红色、二价铁显黑色或灰色。这样，表面圆润光泽，并具有一定强度的舍利子就呈现在人们的面前。
在这个过程中，存在三个不确定性和一个必然性：一是，磷酸盐与硅酸盐的比例不确定；生成舍利子的条件是硅酸盐矿物从内支撑并逐步形成包裹磷酸盐矿物的过程。如仅形成内支撑，就会形成所谓真身舍利；硅酸盐矿物比例提高，形成外包裹就会生成舍利子。二是，硅酸盐矿物的组成不确定：钾、钠、钙、镁、铝、铁的氧化物都可以与二氧化硅形成硅酸盐矿物，它们之间的比例是变化的，而二氧化硅的比例越高，舍利子越接近玉石、玛瑙、水晶的特性。三是，显色金属是变化的；舍利子的基本色是乳白色，舍利子的色泽是在基本色基础上的复合色。另外一个必然性是：二氧化硅存在的主导地位是必然的必须的也是不可替代的。通过以上情况，可以清楚看到，在自然状态下生成舍利子的条件是综合性的、缺一不可的；因此舍利子的生成几率非常低，这也是它的珍稀宝贵之所在。
(4)、现代社会人们记念先贤和亲人，传统方式是修墓占地、焚香烧纸、这不仅挤占耕地、山林，破坏资源环境；而且造成社会财富和资源的极大浪费。
发明内容
本发明的目的就是提供一种技术先进，工艺合理的方法将人体骨灰制成一种品质优良，高贵典雅的舍利子制品，供人们进行怀念和瞻仰。这是人们在纪念文化方面推进人类、社会、环境的科学持续发展；进而促进社会主义生态文明的可行方法。
本发明的制做方法为：
1、原料：以人体骨灰、水晶石英及制品与硅酸盐显色料为主要原料；人体骨灰、水晶石英及制品经焙烧处理；分别研磨至200目～300目。按人体骨灰：40～55；石英粉：50～35；硅酸盐金属显色料10～25进行重量份数配比。(以下均按重量份数配比)
2、舍利子佩饰成型：(1)将粉磨后的人体骨灰、石英粉和硅酸盐金属显色料按重量配比充分混合，按重量加水15～25，搅拌均匀，进行练制、揉捏。(2)手工或模压制成圆型、梯型、球型、椭圆型、水滴型、及十字架型坯料；一般舍利子佩饰长度30～50毫米、厚度5～10毫米、直径15～40毫米。(3)用毛坯制成玉璧、玉圭形状吊坠、宝石状吊坠、十字架状吊坠、圆球状念珠项链和宝石状戒指等各种舍利子佩饰湿坯。
3、舍利子金字塔成型：(1)用上述原料处理方法制得的泥料经模压制成三角形坯料，(2)用三角形毛坯制成舍利子金字塔湿坯，一般舍利子金字塔的底边100毫米至40毫米，厚度5～10毫米；底角52度，可层层叠加制做若干层。
4、舍利子玉璧成型：用上述原料处理方法制得的泥料经手工模压制作成心形、满月形、扇形、古瓶形、寿桃形、祥云形舍利子玉璧湿坯；一般舍利子玉璧长100～80毫米、宽90～80毫米、厚5～10毫米一套由多个不同形状组成。
5、生坯制作：(1)干燥，将舍利子佩饰、舍利子金字塔、及舍利子玉璧湿坯在20度至250度环境下干燥。(2)喷涂或浸渍，将300目细度的石英粉掺加硅酸盐金属显色料加水，比重1.3～1.8搅拌成浆，在一次干坯上喷涂或浸渍。(3)再干燥，一次干坯经喷涂或浸渍处理后，在20度至250度，环境下干燥形成生坯。
6、烧结制作：(1)预热，将再干燥后的生坯进窑炉250至950度预热。(2)烧结，在窑炉中950至1300度、氧化气氛下烧结。
7、冷却，在窑炉中1300至950度，再经950度缓慢冷却至室温。在制品上印制图片、箴言；即为舍利子制品。
8、将舍利子制品进行检验、测试如内在质量和外在质量均合格，即为合格舍利子制品。
(1)外观检验：外表光泽、无裂纹斑点，尺寸公差不大于0.5毫米。图像清晰。
(2)内质检验：机械强度大于500kg/cm2、热稳定性200度置于20度水中不炸裂、吸水率小于0.5％。
具体实施实例
1、原料，取经处理后的人体骨灰200目450克、石英粉200目450克和硅酸盐金属显色料100克充分混合。
2、成型，混合料加水250克混合均匀后；进行练制、揉捏后手工模压制做成各种不同形状的舍利子佩饰湿坯、舍利子金字塔湿坯和舍利子玉璧湿坯。
3、生坯制作，一次干燥：在20度至250度环境下干燥。浸渍：将300目的石英粉掺加硅酸盐金属显色料加水比重1.5，混合均匀成浆，在一次干坯上浸渍。再干燥：在20度至250度环境下干燥。
4、烧结，将再干燥后的生坯进窑炉250至950度预热。在窑炉中950至1300度，氧化气氛下烧结。
5、冷却，在窑炉中1300至950度，再经950度缓慢冷却至室温，在制品上印制图片、箴言，即为舍利子制品；经检验合格，为合格舍利子制品。
本发明的优点在于，本发明与本人已获专利授权的“舍利子的制作方法”有改进和完善。
(1)、进一步揭示了自然状态下舍利子形成的基本原由；主要组成是人体骨灰和石英经高温反应所得。石英即二氧化硅，它是人们摄取富含偏硅酸的水和富含硅元素的食物而获取的。石英是参加反应的重要角色，通过多相动力传质机理，硅元素和其它元素在特定部位可以扩散富集，生成磷酸盐，鋁硅酸盐，硅酸盐等矿物的共融体。
(2)、舍利子制品的水晶石英原料扩大到制品。
(3)、舍利子制品的制作工艺进一步完善；人体骨灰、水晶石英及制品经处理与硅酸盐金属显色料研磨、混和、揉捏、成型、干燥、浸渍、再干燥、预热、经1300度的高温在氧化条件下烧结，再缓慢冷却制成舍利子制品有利于通过固相反应和化学反应形成紧密的磷酸盐、鋁硅酸盐、硅酸盐等矿物的共融体。在原料配比和喷涂浸渍中增添了硅酸盐金属显色料的组分；使舍利子制品具有更稳定良好的物理化学性能，机械强度大于500kg/cm2；热稳定性200度至20度水中急冷不炸裂；耐酸碱；吸水率小于0.5％；对舍利子制品的品质和色彩又得到进一步的提升，更美观晶莹。
(4)、舍利子制品为舍利子的推广使用创造了有利条件；由于舍利子品质实现了“灵骨化玉”质的转化；可做成玉璧、玉圭形状的吊坠、宝石状吊坠、十字架状吊坠、圆球状念珠项链和宝石状戒指等各种佩饰予以佩戴。我们制作的舍利子玉璧，具有心形、满月形、扇面形、寿桃形、古瓶形、祥云形；秉承的是中华民族古代文明崇尚的祭天礼器。我们制做的舍利子金字塔是按照埃及胡夫金字塔的制式制作的，它体现世界古代文明与中国现代文明互相融合的典范。
Claims (1)
1、舍利子制品的制作方法，其特征在于，
(1)、利用人体骨灰、水晶石英及其制品与硅酸盐金属显色色料为原料制作舍利子制品；
(2)、将处理后的人体骨灰、石英与硅酸盐金属显色料粉磨至200～300目；以下均按重量份数，取粉磨后的人体骨灰40～55、石英50～35与硅酸盐金属显色料10～25配比，混合后加水15～25，混合均匀后进行炼制、揉捏，经手工模压制作成圆形、方形、梯形、三角形、十字架形、球形等舍利子坯料；
(3)、将舍利子坯料制作成玉璧、玉圭状吊坠、宝石状吊坠、十字架吊坠、圆球状念珠项链和宝石状戒指等舍利子佩饰湿坯；
(4)、采用三角形舍利子坯料制作层层叠加的多层舍利子金字塔湿坯；
(5)、采用心形、满月形、扇面形、寿桃形、古瓶形、祥云形等舍利子坯料制作舍利子玉璧湿坯；
(6)、将舍利子制品湿坯在20～250度进行一次干燥后，300目石英粉添加硅酸盐金属显色料加水，比重1.3～1.8，进行喷涂或浸渍；再经20～250度环境下干燥；
(7)、在250～950度预热，经950～1300度在氧化条件下烧结；
(8)、经1300至950度、再950度缓慢冷却至室温后，在舍利子制品上印制图片和箴言；经内外品质检验合格后，即为合格舍利子制品。