CN101613583A - The production technique of back adhesive of shadowless adhesive - Google Patents
The production technique of back adhesive of shadowless adhesive Download PDFInfo
- Publication number
- CN101613583A CN101613583A CN200910183831A CN200910183831A CN101613583A CN 101613583 A CN101613583 A CN 101613583A CN 200910183831 A CN200910183831 A CN 200910183831A CN 200910183831 A CN200910183831 A CN 200910183831A CN 101613583 A CN101613583 A CN 101613583A
- Authority
- CN
- China
- Prior art keywords
- minutes
- adhesive
- percentage composition
- quality percentage
- acrylate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of production technique of back adhesive of shadowless adhesive, comprise step: prepare main polymers-with 1240～1260 rev/mins stirring velocitys stirred main polymers 14～16 minutes-preparation small powder-with small powder weight ratio in accordance with regulations joins in the main polymers and to mix and stirred 44～46 minutes---it is standby to leave standstill moulding in 14～16 minutes.But the back adhesive of shadowless adhesive viscosity of producing by production technique of the present invention is strong, can peel off fully and do not stay any cull aspect sticking construction and removing quickly, utilize the no shadow glue of this kind prescription production can realize two-sided air brushing in addition, be convenient to very much stick on the smooth object surface, the safe ready construction.
Description
Technical field
The present invention relates to a kind of production technique of viscose glue, relate to a kind of production technique of back adhesive of shadowless adhesive concretely, belong to the rubber technology field.
Background technology
We know, advertisement field, the general mode that plasters posters be at first use the air brushing machine with ad content air brushing wherein one deck at printing film on, paste on the wall at common latex of another layer usefulness of printing film or double faced adhesive tape then, billboard etc. is above the carrier, this kind mode is the operational procedure complexity on the one hand, on the other hand when removing advertisement, employed latex or double faced adhesive tape stay cull easily, be difficult for peeling off and can only use once.In addition, aforesaid way can only be realized the single face air brushing, and for transparent glass port, if be that carrier is advertised with it, then need externally constructing operation, like this advertisement picture is had certain influence, operation is difficulty relatively, and is destroyed by the people of process easily, or even tear to pieces, especially advertise than higher glass port at floor, then construction is dangerous more, and can't realize two-sided demonstration effect.
Summary of the invention
In order to overcome the deficiencies in the prior art, the object of the present invention is to provide a kind of viscosity height, can reuse, easily peel off, be difficult for the production technique of residual back adhesive of shadowless adhesive.
The present invention is achieved through the following technical solutions:
A kind of production technique of back adhesive of shadowless adhesive, its step is as follows:
(1) get the raw materials ready: prepare main polymers DICANAL MFR-20 acrylate: with the quality percentage composition is that 45～55% acrylate, quality percentage composition are that 40～50% water and quality percentage composition are that 1～10% interfacial agent mixes;
(2) stir: main polymers DICANAL MFR-20 acrylate is joined in the clean agitation vat, be transported to stirring region, open the gear stirrer and stirred 14～15 minutes, the stirring velocity of stirrer is 1240～1260 rev/mins;
(3) get the raw materials ready: preparation small powder DICANL GX acrylate: with the quality percentage composition is that 15～25% water, quality percentage composition are that 35～45% Malignant azoles quinoline based polyalcohol and quality percentage composition are that 35～45% methoxy propyl enol mixes, and stirs in tempering tank 4～6 minutes with excellent;
(4) mix stirring: open bung, the small powder for preparing above joined in the agitation vat under the stirring velocity of stirrer is 290～310 rev/mins condition mix, the ratio of mixture of main polymers and small powder is 41～42: 1, stirred 9～11 minutes with 1240～1260 rev/mins stirring velocity then, adding 1% pure water then continues to stir 24～26 minutes, and then add 1% pure water, continue again to stir 9～11 minutes;
(5) leave standstill moulding: after stopping to stir, left standstill 14～16 minutes, standby after the moulding.
Utilize above-mentioned production craft step can produce back adhesive of shadowless adhesive, and utilize above-mentioned back adhesive of shadowless adhesive can produce no shadow glue.
The invention has the beneficial effects as follows: but the back adhesive of shadowless adhesive viscosity of producing by production technique of the present invention strong, can peel off fully and not stay any cull aspect sticking construction and removing quickly, utilize the no shadow glue of this kind prescription production can realize two-sided air brushing in addition, be convenient to very much stick on the smooth object surface, the secure context construction.
Embodiment
Describe the present invention below in conjunction with specific embodiments in detail:
Embodiment 1:
A kind of production technique of back adhesive of shadowless adhesive, its step is as follows:
(1) get the raw materials ready: prepare main polymers DICANAL MFR-20 acrylate: with the quality percentage composition is that 45% acrylate, quality percentage composition are that 40% water and quality percentage composition are that 5% interfacial agent mixes;
(2) stir: main polymers DICANAL MFR-20 acrylate is joined in the clean agitation vat, be transported to stirring region, open the gear stirrer and stirred 14 minutes, the stirring velocity of stirrer is 1240 rev/mins;
(3) get the raw materials ready: preparation small powder DICANL GX acrylate: with the quality percentage composition is that 15% water, quality percentage composition are that 40% Malignant azoles quinoline based polyalcohol and quality percentage composition are that 45% methoxy propyl enol mixes, and stirs 4 minutes in tempering tank with rod;
(4) mix stirring: open bung, the small powder for preparing above joined in the agitation vat under the stirring velocity of stirrer is 290 rev/mins condition mix, the ratio of mixture of main polymers and small powder is 41: 1, stirred 9 minutes with 1240 rev/mins stirring velocity then, adding 1% pure water then continues to stir 24 minutes, and then add 1% pure water, continue again to stir 9 minutes;
(5) leave standstill moulding: after stopping to stir, left standstill 14 minutes, standby after the moulding.
Embodiment 2:
A kind of production technique of back adhesive of shadowless adhesive, its step is as follows:
(1) get the raw materials ready: prepare main polymers DICANAL MFR-20 acrylate: with the quality percentage composition is that 50% acrylate, quality percentage composition are that 40% water and quality percentage composition are that 10% interfacial agent mixes;
(2) stir: main polymers DICANAL MFR-20 acrylate is joined in the clean agitation vat, be transported to stirring region, open the gear stirrer and stirred 15 minutes, the stirring velocity of stirrer is 1250 rev/mins;
(3) get the raw materials ready: preparation small powder DICANL GX acrylate: with the quality percentage composition is that 20% water, quality percentage composition are that 45% Malignant azoles quinoline based polyalcohol and quality percentage composition are that 35% methoxy propyl enol mixes, and stirs 5 minutes in tempering tank with rod;
(4) mix stirring: open bung, the small powder for preparing above joined in the agitation vat under the stirring velocity of stirrer is 300 rev/mins condition mix, the ratio of mixture of main polymers and small powder is 41.5: 1, stirred 10 minutes with 1250 rev/mins stirring velocity then, adding 1% pure water then continues to stir 25 minutes, and then add 1% pure water, continue again to stir 10 minutes.
(5) leave standstill moulding: after stopping to stir, left standstill 14 minutes, standby after the moulding.
Embodiment 3:
A kind of production technique of back adhesive of shadowless adhesive, its step is as follows:
(1) get the raw materials ready: prepare main polymers DICANAL MFR-20 acrylate: with the quality percentage composition is that 55% acrylate, quality percentage composition are that 44% water and quality percentage composition are that 1% interfacial agent mixes;
(2) stir: main polymers DICANAL MFR-20 acrylate is joined in the clean agitation vat, be transported to stirring region, open the gear stirrer and stirred 16 minutes, the stirring velocity of stirrer is 1260 rev/mins;
(3) get the raw materials ready: preparation small powder DICANL GX acrylate: with the quality percentage composition is that 25% water, quality percentage composition are that 35% Malignant azoles quinoline based polyalcohol and quality percentage composition are that 40% methoxy propyl enol mixes, and stirs 6 minutes in tempering tank with rod;
(4) mix stirring: open bung, the small powder for preparing above joined in the agitation vat under the stirring velocity of stirrer is 300 rev/mins condition mix, the ratio of mixture of main polymers and small powder is 42: 1, stirred 11 minutes with 1260 rev/mins stirring velocity then, adding 1% pure water then continues to stir 26 minutes, and then add 1% pure water, continue again to stir 11 minutes;
(5) leave standstill moulding: after stopping to stir, left standstill 16 minutes, standby after the moulding.
Be most preferred embodiment wherein with embodiment 2.
Below disclose the present invention with preferred embodiment, so it is not in order to restriction the present invention, and all employings are equal to replaces or technical scheme that the equivalent transformation mode is obtained, all drops within protection scope of the present invention.
Claims (3)
1, a kind of production technique of back adhesive of shadowless adhesive, its step is as follows:
(1) get the raw materials ready: prepare main polymers DICANAL MFR-20 acrylate: with the quality percentage composition is that 45～55% acrylate, quality percentage composition are that 40～50% water and quality percentage composition are that 1～10% interfacial agent mixes;
(2) stir: main polymers DICANAL MFR-20 acrylate is joined in the clean agitation vat, be transported to stirring region, open the gear stirrer and stirred 14～15 minutes, the stirring velocity of stirrer is 1240～1260 rev/mins;
(3) get the raw materials ready: preparation small powder DICANL GX acrylate: with the quality percentage composition is that 15～25% water, quality percentage composition are that 35～45% Malignant azoles quinoline based polyalcohol and quality percentage composition are that 35～45% methoxy propyl enol mixes, and stirs in tempering tank 4～6 minutes with excellent;
(4) mix stirring: open bung, the small powder for preparing above joined in the agitation vat under the stirring velocity of stirrer is 290～310 rev/mins condition mix, the ratio of mixture of main polymers and small powder is 41～42: 1, stirred 9～11 minutes with 1240～1260 rev/mins stirring velocity then, adding 1% pure water then continues to stir 24～26 minutes, and then add 1% pure water, continue again to stir 9～11 minutes;
(5) leave standstill moulding: after stopping to stir, left standstill 14～16 minutes, standby after the moulding.
2, a kind of back adhesive of shadowless adhesive that utilizes claim 1 described production craft step to produce.
3, a kind of no shadow glue that utilizes claim 2 described back adhesive of shadowless adhesive to produce.