CN106675483A - Environmental protection type glue and preparation method thereof - Google Patents
Environmental protection type glue and preparation method thereof Download PDFInfo
- Publication number
- CN106675483A CN106675483A CN201510763443.0A CN201510763443A CN106675483A CN 106675483 A CN106675483 A CN 106675483A CN 201510763443 A CN201510763443 A CN 201510763443A CN 106675483 A CN106675483 A CN 106675483A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- glue
- acrylate
- friendlyglue glue
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an environmental protection type glue, which comprises, by weight, 30-40 parts of a prepolymer, 35-55 parts of an acrylate monomer, 5-10 parts of a surfactant, 3-8 parts of a defoamer, 3-5 parts of an initiator, and 45-65 parts of water. According to the present invention, the environmental protection type glue has strong adhesion, can be completely peeled off without any residual glue, completely eliminates the bubble problem occurred in the traditional glue use process, and can be conveniently and rapidly constructed and removed, and the back glue produced by using the formula is conveniently adhered on the surface of the smooth object.
Description
Technical field
The present invention relates to a kind of glue technical field, more particularly, to a kind of Environment-friendlyglue glue and preparation method thereof.
Background technology
At present, field is pasted in paper, most widely used for double faced adhesive tape or latex, latex or double faced adhesive tape easily leave cull, are not easily stripped and are used only once.Such as：China Patent Publication No. is the patent document of CN1057280A, disclose a kind of manufacture method of adhesive for paper-hanging, although the method improves the low-temperature stability that original technique is obtained product, but it is still not fee from and uses to people to this organic substance of all disagreeableness formaldehyde of environment.Preparing the another kind of sticky paper glue is, such as：Chinese patent patent publication No. is CN1261088A, the patent document of a kind of copy for the record or for reproduction adhesive of denomination of invention and its manufacture method, disclosed technical scheme is mainly prepared with EVA resin, chlorinated polypropylene, composite antioxidant, tackifying resin and organic solvent, but its manufacturing process is complex, while the drawbacks of remaining on presence using organic solvents such as toluene.Difficulty of construction is not only increased, and environmental pollution is unfavorable for environmental protection than more serious.
The content of the invention
In order to overcome the deficiencies in the prior art, it is an object of the invention to provide a kind of Environment-friendlyglue glue and preparation method thereof.
The present invention is achieved through the following technical solutions.
A kind of Environment-friendlyglue glue, including following components, and the parts by weight of each component are respectively：
Prepolymer：30-40 parts；
Acrylate monomer：35-55 parts；
Surfactant：5-10 parts；
Defrother：3-8 parts；
Initiator：3-5 parts；
Water：45-65 parts.
Described prepolymer be epoxy acrylate, urethane acrylate, polyether acrylate, any one in polyester acrylate.
Any one in described surfactant fatty acid glyceride, polyalcohol, Pluronic F68.
The defrother is dicarbaldehyde silicone emulsion.
Described initiator is methoxy acetone.
The preparation method of above-mentioned Environment-friendlyglue glue, by prepolymer：30-40 parts；Acrylate monomer：45-55 parts；Surfactant：5-10 parts；Defrother：3-8 parts；Initiator：3-5 parts；Water：45-65 is added in mixer, and 20-30min is mixed under the rotating speed of 300-350r/min, is then stood shaping and is obtained product
The invention has the beneficial effects as follows：Viscosity is strong, can be completely exfoliated and not stay any cull, completely eliminates the air bubble problem that traditional glue occurs in use, can aspect quickly sticking construction and remove, in addition, being easy to be pasted onto smooth object surface using the gum of this kind of formula production.
Specific embodiment
Describe the present invention in detail below in conjunction with specific embodiments.
Embodiment.
In parts by weight：By epoxy acrylate：30 parts；Acrylate monomer：55 parts；Pluronic F68：5 parts；Methoxy acetone：5 parts；Dicarbaldehyde silicone emulsion：3 parts；Water：In 90 parts of addition mixers, 20min is mixed under the mixing speed of 300r/min, then stood after shaping, without shadow gum.
Embodiment
2
。
In parts by weight：By urethane acrylate：35 parts；Acrylate monomer：50 parts；Fatty glyceride：8 parts；Methoxy acetone：4 parts；Dicarbaldehyde silicone emulsion：5 parts；Water：Water：In 50 parts of addition mixers, 25min is mixed under the mixing speed of 320r/min, then stood after shaping, produced without shadow gum.
Embodiment
3
。
In parts by weight：By polyester acrylate：40 parts；Acrylate monomer：45 parts；Polyalcohol：10 parts；Methoxy acetone：3 parts；Dicarbaldehyde silicone emulsion：8 parts；Water：Water：In 65 parts of addition mixers, 30min is mixed under the mixing speed of 350r/min, then stood after shaping, without shadow gum.
Below the present invention disclosed with preferred embodiment, so it is not intended to limiting the invention, the technical scheme that all employing equivalents or equivalent transformation mode are obtained, and is within the scope of the present invention.
Claims (6)
1. a kind of Environment-friendlyglue glue, it is characterised in that including following components, and the parts by weight of each component are respectively：
Prepolymer：30-40 parts；
Acrylate monomer：35-55 parts；
Surfactant：5-10 parts；
Defrother：3-8 parts,
Initiator：3-5 parts；
Water：45-65 parts.
2. according to a kind of Environment-friendlyglue glue of claim 1, it is characterised in that described prepolymer be epoxy acrylate, urethane acrylate, polyether acrylate, any one in polyester acrylate.
3. according to a kind of Environment-friendlyglue glue of claim 1, it is characterised in that any one in described surfactant fatty acid glyceride, polyalcohol, Pluronic F68.
4. according to a kind of Environment-friendlyglue glue of claim 1, it is characterised in that the defrother is dicarbaldehyde silicone emulsion.
5. according to a kind of Environment-friendlyglue glue of claim 1, it is characterised in that described initiator is methoxy acetone.
6. a kind of Environment-friendlyglue glue preparation method of claim 1, it is characterised in that by prepolymer：30-40 parts；Acrylate monomer：45-55 parts；Surfactant：5-10 parts；Defrother：3-8 parts；Initiator：3-5 parts；Water：45-65 is added in mixer, and 20-30min is mixed under the rotating speed of 300-350r/min, is then stood shaping and is obtained product.