CN101613552A - 汽车内饰塑料件用涂料及其制备方法 - Google Patents

汽车内饰塑料件用涂料及其制备方法 Download PDF

Info

Publication number
CN101613552A
CN101613552A CN200910013090A CN200910013090A CN101613552A CN 101613552 A CN101613552 A CN 101613552A CN 200910013090 A CN200910013090 A CN 200910013090A CN 200910013090 A CN200910013090 A CN 200910013090A CN 101613552 A CN101613552 A CN 101613552A
Authority
CN
China
Prior art keywords
pigment
weighing
take
acrylic resin
coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN200910013090A
Other languages
English (en)
Other versions
CN101613552B (zh
Inventor
解居会
姚杰
王志宏
宋占伍
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TIELING YONGXIN PAINT CO Ltd
Original Assignee
TIELING YONGXIN PAINT CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TIELING YONGXIN PAINT CO Ltd filed Critical TIELING YONGXIN PAINT CO Ltd
Priority to CN2009100130907A priority Critical patent/CN101613552B/zh
Publication of CN101613552A publication Critical patent/CN101613552A/zh
Application granted granted Critical
Publication of CN101613552B publication Critical patent/CN101613552B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种汽车内饰塑料件用涂料，还公开了该种涂料的制备方法。该涂料由羟基丙烯酸树脂、氯化聚丙烯树脂、醋酸丁酯、助剂、颜料和溶剂组成，各组分重量份比为：羟基丙烯酸树脂∶氯化聚丙烯树脂∶醋酸丁酯∶助剂∶颜料∶溶剂＝45－65∶3－8∶20－30∶0.2－0.8∶6－12∶12－20；所述羟基丙烯酸树脂的粘度为2500－6000cps，固体份为70％，羟值为66±5，酸值＜8mgKOH/g，颜色＜1#，外观清澈透明；所述助剂为高分子分散剂和有机硅类流平剂；所述颜料为着色颜料和耐磨性体质颜料。该涂料具有耐磨性强、耐介质腐蚀的特点。

Description

汽车内饰塑料件用涂料及其制备方法
技术领域
本发明涉及一种涂料，特别是涉及一种用于汽车内饰塑料件涂装用的涂料。本发明还涉及到该涂料的制备方法。
背景技术
随着汽车工业的发展，汽车的重量有轻量化的趋势，因此，各种材质的塑料件被应用在汽车上，汽车的内装饰如驾驶室仪表盘等均采用塑料制品。在当今汽车用塑料件制作行业中，其涂料产品远远满足不了客户提出的新要求，存在耐磨、耐介质性差及不环保问题。
发明内容
本发明要解决的技术问题是提供一种汽车内饰塑料件用涂料，该涂料具有耐磨性强、耐介质腐蚀的特点。
为解决上述技术问题，本发明汽车内饰塑料件用涂料采用的技术方案是：该涂料由羟基丙烯酸树脂、氯化聚丙烯树脂、醋酸丁酯、助剂、颜料和溶剂组成，各组分重量份比为：羟基丙烯酸树脂∶氯化聚丙烯树脂∶醋酸丁酯∶助剂∶颜料∶溶剂＝45-65∶3-8∶20-30∶0.2-0.8∶6-12∶12-20；所述羟基丙烯酸树脂的粘度为2500-6000cps，固体份为70％，羟值为66±5，酸值＜8mgKOH/g，颜色＜1#，外观清澈透明；所述助剂为高分子分散剂和有机硅类流平剂；所述颜料为着色颜料和耐磨性体质颜料。
所述助剂高分子分散剂为SUSPENO 962，有机硅类流平剂为efka3033。
所述着色颜料为碳黑。
所述溶剂为CAC或100#。
所述耐磨性体质颜料为滑石粉、玻璃粉或耐磨粉。
本发明汽车车轮塑料装饰罩用涂料在涂装时与固化剂和配套稀释剂配合使用。固化剂由异氰酸脂固化剂和醋酸丁酯组成，异氰酸脂固化剂和醋酸丁的重量份比为：异氰酸脂固化剂∶醋酸丁酯＝40-55∶40-55：配套稀释剂由CAC、醋酸丁酯和100#组成，各组分重量份比为：CAC∶醋酸丁酯∶100#＝30-40∶20-30∶35-45。
本发明汽车车轮塑料装饰罩用涂料性能优越，见表1。
上述汽车内饰塑料件用涂料的制备方法包括以下步骤：
(1).称取羟基丙烯酸树脂45-65份，称取高分子分散剂0.13份，称取100#10-15份，加入调漆罐中，搅拌使之充分溶解；
(2).称取着色颜料2-3份，称取体质颜料4-9份，加入调漆罐中，搅拌使之分散均匀；
(3).用砂磨机研磨步骤(2)所得浆料，至细度合格；
(4).称取有机硅类流平剂0.1-0.5份，氯化聚丙烯树脂3-8份，CAC 2-5份，加入调漆罐中，搅拌使之分散均匀；
(5).称取醋酸丁酯20-30份，加入调漆罐中，调整粘度至合格；
(7).用200目过滤布过滤，包装。
具体实施方式
以下结合实施例对本发明作进一步地详细描述，在这些实施例中，所有份数均按重量计算。
实施例1
将调漆罐清洗干净，称取羟基丙烯酸树脂50份，高分子分散剂0.15份，100#溶剂12份，混合加入调漆罐中，低速搅拌，使之充分溶解，搅拌时间30分钟；称取炭黑2.6份，SNM-100耐磨粉5份，在搅拌下加入到调漆罐中，搅拌的转数为800转，搅拌时间为30分钟；用砂磨机研磨上面配制好的浆料，至细度合格；称取氯化聚丙烯树脂5份，有机硅类流平剂0.2份，CAC 3份，在搅拌的情况下加入到调漆罐中，搅拌的转数为600转，搅拌的时间为30分钟；最后称取醋酸丁酯24.8份，加入到调漆罐中，调整至粘度合格，搅拌时间20分钟，用200目过滤布过滤，包装。
实施例2～3
按照表2所述物料配比，实施例1所述制法生产汽车内饰塑料件用的涂料，所得产品部分项目性能见表3。
表1：按配方所述重量份比制得涂料的性能指标
Figure G2009100130907D00041
表2：实施例1-3各组分配方
Figure G2009100130907D00051
表3：各实施例部分项目检测结果
  NO  检测项目   实例1   实例2   实例3
  1  光泽％   62   40   40
2  附着力(划格法)   较好   0/100   0/100
  3  耐划痕   较好   OK   OK
4  铅笔硬度(擦伤)   HB   HB   H
  5  耐酸性   合格   合格   合格
  6  耐碱性   合格   合格   合格

Claims (6)

1、一种汽车内饰塑料件用涂料，其特征在于：该涂料由羟基丙烯酸树脂、氯化聚丙烯树脂、醋酸丁酯、助剂、颜料和溶剂组成，各组分重量份比为：羟基丙烯酸树脂∶氯化聚丙烯树脂∶醋酸丁酯∶助剂∶颜料∶溶剂＝45-65∶3-8∶20-30∶0.2-0.8∶6-12∶12-20；所述羟基丙烯酸树脂的粘度为2500-6000cps，固体份为70％，羟值为66±5，酸值＜8mgKOH/g，颜色＜1#，外观清澈透明；所述助剂为高分子分散剂和有机硅类流平剂；所述颜料为着色颜料和耐磨性体质颜料。
2、按照权利要求1所述的涂料，其特征在于：所述助剂高分子分散剂为SUSPENO 962，有机硅类流平剂为efka 3033。
3、按照权利要求1所述的涂料，其特征在于：所述着色颜料为碳黑。
4、按照权利要求1所述的涂料，其特征在于：所述耐磨性体质颜料为滑石粉、玻璃粉或耐磨粉。
5、按照权利要求1所述的涂料，其特征在于：所述溶剂为CAC或100#。
6、一种制备权利要求1所述涂料的方法，其特征在于包括以下步骤：
(1).称取羟基丙烯酸树脂45-65份，称取高分子分散剂0.1-0.3份，称取100#10-15份，加入调漆罐中，搅拌使之充分溶解；
(2).称取着色颜料2-3份，称取耐磨性体质颜料4-9份，加入调漆罐中，搅拌使之分散均匀；
(3).用砂磨机研磨步骤(2)所得浆料，至细度合格；
(4).称取有机硅类流平剂0.1-0.5份，氯化聚丙烯树脂3-8份，CAC 2-5份，加入调漆罐中，搅拌使之分散均匀；
(5).称取醋酸丁酯20-30份，加入调漆罐中，调整粘度至合格；
(7).用200目过滤布过滤，包装。
CN2009100130907A 2009-08-11 2009-08-11 汽车内饰塑料件用涂料及其制备方法 Expired - Fee Related CN101613552B (zh)