CN101613546A - A kind of environment-friendly rust sealed base paint - Google Patents
A kind of environment-friendly rust sealed base paint Download PDFInfo
- Publication number
- CN101613546A CN101613546A CN200810016896A CN200810016896A CN101613546A CN 101613546 A CN101613546 A CN 101613546A CN 200810016896 A CN200810016896 A CN 200810016896A CN 200810016896 A CN200810016896 A CN 200810016896A CN 101613546 A CN101613546 A CN 101613546A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- dop
- acetone
- synolac
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of environment-friendly rust sealed base paint, belong to the anticorrosive metal paint production field, made by following raw material: ethyl acetate, DOP, PS, 200# solvent oil, Synolac, kaolin, barium sulfate, zinc oxide, chlorinated rubber, acetone and an amount of pigment are made; Its preparation process is: ethyl acetate, DOP, Synolac, chlorinated rubber, acetone are added the reactor middling speed of being with high speed shear in proportion carry out the base-material modification; Running adds kaolin, barium sulfate, zinc oxide and pigment behind the 1.5-2.5h, again with 5000-6000 rev/min high speed shear, dispersion, emulsification, when the fineness of material reaches 60 μ m when following, can filter, be packaged as finished product.Compare with the rust-inhibiting paint that prior art is produced, it is good that environment-friendly rust sealed base paint of the present invention has an antiseptic property, strong alkali-acid resistance, anti-bromine, characteristics such as use cost is low.
Description
Technical field
The present invention relates to a kind of anticorrosive metal paint, specifically a kind of environment-friendly rust sealed base paint.
Background technology
The rotproofing of metallic substance is the aspect that pay much attention in the scientific research field.At present, mainly also be to use rust-inhibiting paint that metallic substance is carried out rotproofing.Though rust-inhibiting paint of the prior art can be avoided the chemistry or the galvanic corrosion of atmosphere etc. by the protective money metal surface, but still has the following disadvantages: one, time of drying is long, be sprayed on the metallic surface after, surface drying is wanted 3 hours, does solid work to reach 24 hours; Its two, antiseptic property is not comprehensive, the rust-inhibiting paint of most kinds does not have preservative activity to strong acid, highly basic, seawater, salt fog etc., the corrosion to micro-bromine in the seawater does not have protective effect especially; Its three, poor water resistance; Its four, the unit weight spray area is little, the use cost height.
Summary of the invention
Technical assignment of the present invention is at above-mentioned the deficiencies in the prior art, and the environment-friendly rust sealed base paint that a kind of antiseptic property is good, use cost is low is provided.
Technical assignment of the present invention is realized in the following manner: a kind of environment-friendly rust sealed base paint, make by the following weight proportion raw material:
Ethyl acetate 26-29 part PS 16-23 part 200# solvent oil 26-29 part
DOP 2-5 part Synolac 10-15 part kaolin 5-8 part
Barium sulfate 5-9 part zinc oxide 8-11 part chlorinated rubber 8-13 part
Acetone 8-14 part pigment is an amount of;
Its preparation process is: ethyl acetate, DOP, PS, 200# solvent oil, Synolac, chlorinated rubber, acetone are added in the reactor of being with high speed shear in proportion, carry out the base-material modification with 3800-4000 rev/min rotating speed; Running adds kaolin, barium sulfate, zinc oxide and pigment behind the 1.5-2.5h, again with 5000-6000 rev/min high speed shear, dispersion, emulsification, when the fineness of material reaches 60 μ m when following, can filter, be packaged as finished product.
The raw material preferred weight proportioning of this environment-friendly rust sealed base paint is:
Ethyl acetate 27-28 part PS 18-20 part 200# solvent oil 27-28 part
DOP 3-4 part Synolac 11-13 part kaolin 6-7 part
Barium sulfate 6-8 part zinc oxide 9-10 part chlorinated rubber 10-12 part
Acetone 10-12 part pigment is an amount of.
The optimum feed stock weight proportion of this environment-friendly rust sealed base paint is:
27.5 parts of 19 parts of 200# solvent oils of 27.5 parts of PS of ethyl acetate
6 parts of 12 parts of kaolin of 3 parts of Synolac of DOP
11 parts of 10 parts of chlorinated rubbers of 7 parts of zinc oxide of barium sulfate
11 parts of pigment of acetone are an amount of.
Prepare the used various raw materials of environment-friendly rust sealed base paint of the present invention and be commercial grade.Ethyl acetate, PS, 200# solvent oil are solvent; DOP is dioctyl phthalate (DOP) (softening agent); PS is polystyrene (water-resisting agent); Acetone is quick-drying agent.
Environment-friendly rust sealed base paint of the present invention is compared with rust-inhibiting paint of the prior art, can dissolve a small amount of rust spot after the spraying, and surplus person is sealed, and isolated metal contacts with air, has following outstanding beneficial effect:
1, time of drying
On the surface, environment-friendly rust sealed base paint of the present invention metallize, surface drying 4min does solid work 1h; And the surface drying time of rust-inhibiting paint is 3h, and the time of doing solid work is 24h;
2, erosion resistance relatively
Priming paint of the present invention can anti-strong acid, alkaline corrodes, and also has micro-bromine corrosive function in sea water resistance, anti-salt fog, the anti-seawater; And most rust-inhibiting paints do not have these performances in the prior art, and are incomparable;
3, the comparison of water resistance
Priming paint of the present invention has water-proof PS material, and water resistance is remarkable after the PS film forming, can long period of soaking in water;
4, priming paint of the present invention can spray 40m for one kilogram
2(twice lacquer), and rust-inhibiting paint of the prior art approximately can only spray 4m
2About (twice lacquer), the spraying cost be significantly less than existing rust-inhibiting paint.
Embodiment
Embodiment 1:
Prescription:
Ethyl acetate 27Kg PS 22Kg 200# solvent oil 27Kg
DOP 4Kg Synolac 11Kg kaolin 6Kg
Barium sulfate 6Kg zinc oxide 10Kg chlorinated rubber 10Kg
Acetone 12Kg pigment is an amount of.
Preparation process: according to formula rate, ethyl acetate, DOP, PS, 200# solvent oil, Synolac, chlorinated rubber, acetone are added in the reactor of being with high speed shear in proportion, carry out the base-material modification with 3800 rev/mins rotating speeds; Turning round added kaolin, barium sulfate, zinc oxide and pigment after 2.5 hours, again with 5200 rev/mins high speed shear, dispersion, emulsification, turn round after 2.5 hours, the fineness of material reaches below the 60 μ m, can filter, pack finished product.
Embodiment 2:
Prescription:
Ethyl acetate 28Kg PS 19Kg 200# solvent oil 28Kg
DOP 3Kg Synolac 12Kg kaolin 7Kg
Barium sulfate 8Kg zinc oxide 9Kg chlorinated rubber 12Kg
Acetone 9Kg pigment is an amount of.
The preparation process of preparation process and embodiment 1 is basic identical, and the rotating speed of base-material modifying process high speed emulsification pretreatment machine is 4000 rev/mins, modification time 1.5 hours; The rotating speed of dispersion and emulsion process high speed emulsification pretreatment machine is 5800 rev/mins, and turning round, material reaches below the 60 μ m after 1.5 hours.
Embodiment 3:
Prescription:
Ethyl acetate 27.5Kg PS 19Kg 200# solvent oil 27.5Kg
DOP 3Kg Synolac 12Kg kaolin 6Kg
Barium sulfate 7Kg zinc oxide 10Kg chlorinated rubber 11Kg
Acetone 11Kg pigment is an amount of.
The preparation process of preparation process and embodiment 1 is basic identical, and the rotating speed of base-material modifying process high speed emulsification pretreatment machine is 3900 rev/mins, modification time 2 hours; The rotating speed of dispersion and emulsion process high speed emulsification pretreatment machine is 5500 rev/mins, and turning round, material reaches below the 60 μ m after 2 hours.
Claims (3)
1, a kind of environment-friendly rust sealed base paint is characterized in that it is to be made by the following weight proportion raw material:
Ethyl acetate 26-29 part PS 16-23 part 200# solvent oil 26-29 part
DOP 2-5 part Synolac 10-15 part kaolin 5-8 part
Barium sulfate 5-9 part zinc oxide 8-11 part chlorinated rubber 8-13 part
Acetone 8-14 part pigment is an amount of;
Its preparation process is: ethyl acetate, DOP, PS, 200# solvent oil, Synolac, chlorinated rubber, acetone are added in the reactor of being with high speed shear in proportion, carry out the base-material modification with 3800-4000 rev/min rotating speed; Running adds kaolin, barium sulfate, zinc oxide and pigment behind the 1.5-2.5h, again with 5000-6000 rev/min high speed shear, dispersion, emulsification, when the fineness of material reaches 60 μ m when following, can filter, be packaged as finished product.
2, environment-friendly rust sealed base paint according to claim 1 is characterized in that it is to be made by the following weight proportion raw material:
Ethyl acetate 27-28 part PS 18-20 part 200# solvent oil 27-28 part
DOP 3-4 part Synolac 11-13 part kaolin 6-7 part
Barium sulfate 6-8 part zinc oxide 9-10 part chlorinated rubber 10-12 part
Acetone 10-12 part pigment is an amount of.
3, environment-friendly rust sealed base paint according to claim 1 is characterized in that it is to be made by the following weight proportion raw material:
27.5 parts of 27.5 parts of PS19 parts of ethyl acetate 200# solvent oils
6 parts of 12 parts of kaolin of 3 parts of Synolac of DOP
11 parts of 10 parts of chlorinated rubbers of 7 parts of zinc oxide of barium sulfate
11 parts of pigment of acetone are an amount of.