CN101608404A - The preparation technology of coated fabric with glaring and charming visual effect - Google Patents
The preparation technology of coated fabric with glaring and charming visual effect Download PDFInfo
- Publication number
- CN101608404A CN101608404A CNA2009100998411A CN200910099841A CN101608404A CN 101608404 A CN101608404 A CN 101608404A CN A2009100998411 A CNA2009100998411 A CN A2009100998411A CN 200910099841 A CN200910099841 A CN 200910099841A CN 101608404 A CN101608404 A CN 101608404A
- Authority
- CN
- China
- Prior art keywords
- fabric
- coated
- coating
- temperature
- preparation technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of preparation technology of coated fabric with glaring and charming visual effect belongs to the fabricating technology field of coated fabric.It is characterized in that: this preparation technology comprises the steps: that a. will carry out coating through the fabric of pre-treatment, dyeing or dyeing and printing, pre-setting, and coating procedure is divided into two parts: (1) primary coat: primary coat adopts the PA transparent adhesive tape to carry out dry coating; (2) face is coated with: face is coated with and adopts PA glue to sneak into the illusion-colour pearl essence or the color pearl powder carries out dry coating, puts in order behind the b.: postfinishing process is, earlier stiffening the and water repellent finish liquid of preparation fabric, the fabric after padding coating on the setting machine of band groove then.With the fabric of this prepared, not only can give out pearly luster, have dazzling, charming visual effect, and have stiffening, as to refuse water function, particularly suitable is made products such as umbrella cover, curtain, shower curtain, applied range; In addition, this preparation technology saves material, energy efficient.
Description
Technical field
The invention belongs to the fabricating technology field of coated fabric, be specifically related to a kind of preparation technology of coated fabric with glaring and charming visual effect.
Background technology
Along with improving constantly of people's living standard, the fabric that has certain function separately is the needs that textiles can not satisfy people, and top finish is at the uniform coated material of fabric face, gives fabric certain function, changes the look and feel of fabric.As publication number: CN10144056, open day: 2009.05.27, application number is: 200810244103.7 " a kind of manufacture method of pearly-lustre illusion-colour coated fabric " patent application, on fabric, apply pearicoat exactly, make fabric can give out the gloss of pearl.But there is following disadvantage in above-mentioned patent application: the one, need three layers of coating of coated, and promptly on base cloth, apply the slurry of subcoat earlier, drying is handled, and forms subcoat; At the slurry of subcoat coating epithelial membrane coating, dried forms epithelial membrane coating more then; At the slurry of epithelial membrane coating coating pearicoat, dried forms pearicoat more then.Each layer coating all needs the slurry of one deck, all needs dried again, so the cost height; The 2nd, in the slurry of epithelial membrane coating, the solvent that is adopted also has butanone except toluene, the two volatilization temperature of butanone, toluene is inconsistent, if under certain temperature condition, the inconsistent meeting of the speed of two kinds of solvent evaporates causes the residual of a certain solvent in the fabric, easily causes the variation of fabric coloured light.Three is that the 3rd time coating adopts add the method that colouring agent and pearl essence mix in slurry, the therefore color of no pearl essence self on fabric, and the effect that sets off pearl essence is affected.The 4th, the fabric that makes according to the method for above-mentioned patent application, only has the nacreous effect of the illusion-colour of distributing, there is no stiffening, as to refuse water effect, so can not be used as the fabric that umbrella cover, curtain, shower curtain, interior decoration, tent, automobile interior trim etc. are adopted, range of application is placed restrictions on.
Summary of the invention
The objective of the invention is to provide a kind of preparation technology of coated fabric with glaring and charming visual effect,, not only can give out pearly luster, have dazzling, charming visual effect, and have stiffening, as to refuse water function with the fabric of this prepared; In addition, this preparation technology saves material, energy efficient.
Above-mentioned goal of the invention is achieved through the following technical solutions, and a kind of preparation technology of coated fabric with glaring and charming visual effect, its main points are that this preparation technology comprises the steps:
A. will carry out coating through the fabric of pre-treatment, dyeing or dyeing and printing, pre-setting, coating procedure is divided into two parts: (1). and primary coat: primary coat adopts the PA transparent adhesive tape to carry out dry coating, prescription is: PA glue 80～90%, bridging agent 1.0～2.0%, antiplastering aid 0.1～0.5%, toluene 18.9～7.5%; Primary coat technology is: primary coat consumption 20～25g/m
2, bake out temperature can be with the baking oven joint number raises successively, and promptly with being increased to 140 ℃ by the joint baking oven from 120 ℃, the speed of a motor vehicle is 60～70m/min;
(2). face is coated with: face is coated with and adopts PA glue to sneak into the illusion-colour pearl essence or the color pearl powder carries out dry coating, face gluing prescription is: PA glue 60～70%, bridging agent 2.0～3.0%, antiplastering aid 1.0～2.2%, illusion-colour pearl essence or color pearl powder 15～18%, toluene 22～6.8%, face are coated with technology: face is coated with consumption 10～15g/m
2, bake out temperature still raises successively with the baking oven joint number, and promptly with being increased to 140 ℃ by the joint baking oven from 125 ℃, the speed of a motor vehicle is 60～70m/min;
B. back arrangement: postfinishing process is, the preparation fabric is endured with all one's will and water repellent finish liquid earlier, be that the hard finishing agent concentration is that 15～25g/L, water repellent finish agent concentration are that 10～25g/L, softer consistency are the dressing liquid of 8～12g/L, the fabric after padding coating on the setting machine of band groove then, nip pressure is 3～4 kilograms, baking temperature is: 185～190 ℃, the speed of a motor vehicle is 8～100m/min;
Make fabric have dazzling charming visual effect and endure with all one's will, refuse the water effect by above-mentioned preparation technology.
The preparation technology of above-mentioned coated fabric with glaring and charming visual effect, one of its technical scheme is that fabric is a dacron, the technology of its pre-treatment is: one (caustic soda 1～5g/L, 80～100 ℃ of temperature), two roads (209 detergents, 3～6g/L, 80～100 ℃ of temperature), three roads (penetrating agent JFC 1～5g/L, 95～100 ℃ of temperature), four roads (penetrating agent JFC 1～5g/L, caustic soda 1～5g/L, 95～100 ℃ of temperature), five roads (the spirit 0.3～1g/L that deoils, 50～70 ℃ of temperature), each one of back hot water, cold wash; The purpose of fabric pretreatment mainly is to remove the slurry on the polyster fibre and remain in finish on the fabric when weaving, in order to avoid the dyeing flower phenomenon occurs.
The preparation technology of above-mentioned coated fabric with glaring and charming visual effect, one of its technical scheme is the process of the process using High Temperature High Pressure dye gigging of dyeing, get final product in 125～135 ℃ of insulation 2～3 roads, and accumulate in dyestuff on the fiber surface with removal carrying out reduction cleaning after the dyeing; Carry out pre-setting after the dyeing, the purpose of pre-setting be for the cloth cover that makes dacron smooth, door width of cloth unanimity so that the carrying out of back stamp and top finish, presetting technology is: 185～190 ℃ of temperature, the speed of a motor vehicle 85～95m/min; Or in groove, add a spot of waterproof and soft finishing agent, so that coating, back arrangement are carried out more smoothly.
The preparation technology of above-mentioned coated fabric with glaring and charming visual effect, one of its technical scheme is that printing technology adopts DISPERSE DYES to carry out stamp, mix up required printing paste according to printing color before the seal, printing paste prescription by weight is: DISPERSE DYES 2～5%, synthetic thickening agent 98～95%, stamp is carried out according to the colored type that designs in the back on printing machine, and 100～120 ℃ of oven dry down, adopt saturated vapour decatize 25～35min down at 125～135 ℃ again, synthetic thickening agent remaining on the fabric is removed in the after washing oven dry.
Beneficial effect of the present invention: the one, only need two layers of coating of coated, can give out pearly luster, have dazzling, charming visual effect, reduce one deck epithelial membrane coating than above-mentioned background technology, therefore, this preparation technology saves material, and saves energy.The 2nd, directly in coating adhesive, reach colored dazzling charming effect by adding illusion-colour pearl essence or color pearl powder, rather than colouring agent is mixed in the coating adhesive, thereby make illusion-colour pearl essence or color pearl powder that the color of self be arranged on fabric, dazzling dazzling charming effect is more arranged.The 3rd, there is not epithelial membrane coating among the preparation technology of the present invention, so do not exist toluene, butanone volatilization temperature inconsistent, cause the residual of a certain solvent in the fabric, easily cause the disadvantage of the variation of fabric coloured light.The 4th, the fabric that the present invention makes, not only have the nacreous effect of the illusion-colour of distributing, but also have stiffening effect, refuse the function of water, can be used as the fabric that umbrella cover, curtain, shower curtain, interior decoration, tent, automobile interior trim etc. are adopted, applied range.
The specific embodiment
Embodiment one
The preparation technology of present embodiment---coated fabric with glaring and charming visual effect may further comprise the steps:
Selecting Density for use is the dacron of 190T, and the technology of its pre-treatment is: (caustic soda 2g/L, 80 ℃ of temperature) together, two roads (209 detergent 4g/L, 80 ℃ of temperature), three roads (penetrating agent JFC 2g/L, 95 ℃ of temperature), four roads (penetrating agent JFC 2g/L, caustic soda 2g/L, 95 ℃ of temperature), (clever 0.5g/L deoils in five roads, 55 ℃ of temperature), back hot water, cold wash are each one.
The process of the process using High Temperature High Pressure dye gigging of its dyeing gets final product in 125 ℃ of insulation 3 roads, and accumulates in dyestuff on the fiber surface with removal carrying out reduction cleaning after the dyeing; Carry out pre-setting after the dyeing, presetting technology is: 185 ℃ of temperature, speed of a motor vehicle 85m/min; Or in groove, add a spot of waterproof and soft finishing agent, so that coating, back arrangement are carried out more smoothly.
Its printing technology adopts DISPERSE DYES to carry out stamp, mix up required printing paste according to printing color before the seal, printing paste prescription by weight is: DISPERSE DYES 2%, synthetic thickening agent 98%, stamp is carried out according to the colored type that designs in the back on printing machine, and, adopting saturated vapour decatize 25min down at 125 ℃ again 100 ℃ of oven dry down, synthetic thickening agent remaining on the fabric is removed in the after washing oven dry.
Above-mentioned stamp dacron is carried out pre-setting again.
A. the fabric with above-mentioned stamp terylene pre-setting carries out coating, and coating procedure is divided into two parts:
(1). primary coat: primary coat adopts the PA transparent adhesive tape to carry out dry coating; Prescription is: PA (35C) glue 120kg, bridging agent L-75 3kg, antiplastering aid KC-650 0.6kg, toluene 20kg; Primary coat technology is: primary coat consumption 20g/m
2, bake out temperature raises successively with the baking oven joint number, and promptly with being increased to 140 ℃ by the joint baking oven from 120 ℃, the speed of a motor vehicle is 60m/min;
(2). face is coated with: face is coated with and adopts PA (35C) glue to sneak into the color pearl powder to carry out dry coating, and face gluing prescription is: PA (35C) glue 42lg, bridging agent L-752kg, antiplastering aid KC-650 4kg, color pearl powder FWD50210.6kg, toluene 8kg, face are coated with technology and are: face is coated with consumption 10～15g/m
2, bake out temperature still raises successively with the baking oven joint number, and promptly with being followed successively by 125 ℃, 130 ℃, 135 ℃, 140 ℃ by the joint baking oven, the speed of a motor vehicle is 65m/min;
B. back arrangement: postfinishing process is, the preparation fabric is endured with all one's will and water repellent finish liquid earlier, be that cloth hard finishing agent TR260D concentration is that 25g/L, stiffening catalyst TF-630C concentration are that 6.5g/L, water repellent finishing agent DS-3643 concentration are that 20g/L, soft finishing agent TF-437 concentration are 10g/L, the fabric after padding coating on the setting machine of band groove then, nip pressure is 3 kilograms, baking temperature is: 190 ℃, the speed of a motor vehicle is 95m/min.
Embodiment two:
It is the dacron of 190T for density still that present embodiment is selected fabric for use, and its pre-treatment, dyeing and printing, presetting technology are same as embodiment one;
A. the fabric with above-mentioned stamp terylene pre-setting carries out coating, and coating procedure is divided into two parts:
(1). primary coat: primary coat adopts the PA transparent adhesive tape to carry out dry coating; Prescription is: PA (2820C) glue 120kg, bridging agent L-75 1.8kg, antiplastering aid KC-6500.4kg, toluene 20kg; Primary coat technology is: primary coat consumption 20g/m
2, bake out temperature raises successively with the baking oven joint number, and promptly with being increased to 140 ℃ by the joint baking oven from 120 ℃, 130 ℃, 135 ℃, the speed of a motor vehicle is 60m/min;
(2). face is coated with: face is coated with and adopts PA (35C) glue to sneak into the color pearl powder to carry out dry coating, and face gluing prescription is: PA (35C) glue 42kg, bridging agent L-75 2kg, antiplastering aid KC-650 4kg, toluene 8kg, color pearl powder FWD502 10.6kg; Face is coated with technology: face is coated with consumption 15g/m
2, bake out temperature still raises successively with the baking oven joint number, and promptly with being followed successively by 125 ℃, 130 ℃, 135 ℃, 140 ℃ by the joint baking oven, the speed of a motor vehicle is 65m/min;
B. back arrangement: postfinishing process is, the preparation fabric is endured with all one's will and water repellent finish liquid earlier, be that cloth hard finishing agent TR260D concentration is that 10g/L, stiffening catalyst TF-630C concentration are that 2g/L, water repellent finishing agent DS-3643 concentration are that 15g/L, soft finishing agent TF-437 concentration are 10g/L, the fabric after padding coating on the setting machine of band groove then, nip pressure is 3 kilograms, baking temperature is 190 ℃, and the speed of a motor vehicle is 95m/min.
Embodiment three:
It is the dacron of 190T for density still that present embodiment is selected fabric for use, and its pre-treatment, dyeing, presetting technology are same as embodiment one
A. the fabric with above-mentioned dyeing terylene pre-setting carries out coating, and coating procedure is divided into two parts:
(2). primary coat: primary coat adopts the PA transparent adhesive tape to carry out dry coating; Prescription is: PA (16+20C) 120kg, bridging agent L-751.8kg, antiplastering aid KC-6500.4kg, toluene 20kg; Primary coat technology is: primary coat consumption 20g/m
2, bake out temperature raises successively with the baking oven joint number, and promptly with being increased to 140 ℃ by the joint baking oven from 120 ℃, 130 ℃, 135 ℃, the speed of a motor vehicle is 60m/min;
(2). face is coated with: face is coated with and adopts PA (20C) glue to sneak into the color pearl powder to carry out dry coating, and face gluing prescription is: PA (20C) glue 42kg, bridging agent L-75 1.8kg, antiplastering aid KC-650 1kg, toluene 8kg, illusion-colour look pearl essence (12#) 10.6kg, face is coated with technology and is: face is coated with consumption 15g/m
2, bake out temperature still raises successively with the baking oven joint number, and promptly with being followed successively by 125 ℃, 130 ℃, 135 ℃, 140 ℃ by the joint baking oven, the speed of a motor vehicle is 65m/min;
B. back arrangement: postfinishing process is, the preparation fabric is endured with all one's will and water repellent finish liquid earlier, be that cloth hard finishing agent TR260D concentration is that 20g/L, stiffening catalyst TF-630C concentration are that 4g/L, water repellent finishing agent DS-3643 concentration are that 15g/L, soft finishing agent TF-437 concentration are 10g/L, the fabric after padding coating on the setting machine of band groove then, nip pressure is 3 kilograms, baking temperature is: 190 ℃, the speed of a motor vehicle is 95m/min.
The performance indications of the coated fabric with glaring and charming visual effect that above-mentioned three embodiment prepare are as follows: fabric water pressure resistance＞500mmH
2O; Boardness＞35CZ/mm; Fabric fastness to rubbing: dry friction 〉=4-5 level, wet friction 〉=4-5 level; WASHING COLOR FASTNESS 〉=4 grade.Wherein the water pressure resistance test is according to GB/T4744-1997 (hydrostatic test) testing standard; The stiffness test is according to the GB/T18318 testing standard; Crock fastness is according to the AATCC8 standard; WASHING COLOR FASTNESS is according to the AATCC61-2A standard.
Claims (4)
1. the preparation technology of a coated fabric with glaring and charming visual effect is characterized in that this preparation technology may further comprise the steps:
A. will carry out coating through the fabric of pre-treatment, dyeing or dyeing and printing, pre-setting, coating procedure is divided into two parts: (1). and primary coat: primary coat adopts the PA transparent adhesive tape to carry out dry coating, prescription is: PA glue 80～90%, bridging agent 1.0～2.0%, antiplastering aid 0.1～0.5%, toluene 18.9～7.5%; Primary coat technology is: primary coat consumption 20～25g/m
2, bake out temperature can be with the baking oven joint number raises successively, and promptly with being increased to 140 ℃ by the joint baking oven from 120 ℃, the speed of a motor vehicle is 60～70m/min;
(2). face is coated with: face is coated with and adopts PA glue to sneak into the illusion-colour pearl essence or the color pearl powder carries out dry coating, face gluing prescription is: PA glue 60～70%, bridging agent 2.0～3.0%, antiplastering aid 1.0～2.2%, illusion-colour pearl essence or color pearl powder 15～18%, toluene 22～6.8%, face are coated with technology: face is coated with consumption 10～15g/m
2, bake out temperature still raises successively with the baking oven joint number, and promptly with being increased to 140 ℃ by the joint baking oven from 125 ℃, the speed of a motor vehicle is 60～70m/min;
B. back arrangement: postfinishing process is, the preparation fabric is endured with all one's will and water repellent finish liquid earlier, be that the hard finishing agent concentration is that 15～25g/L, water repellent finish agent concentration are that 10～25g/L, softer consistency are the dressing liquid of 8～12g/L, the fabric after padding coating on the setting machine of band groove then, nip pressure is 3～4 kilograms, baking temperature is: 185～190 ℃, the speed of a motor vehicle is 8～100m/min;
Make fabric have dazzling charming visual effect and endure with all one's will, refuse the water effect by above-mentioned preparation technology.
2. the preparation technology of coated fabric with glaring and charming visual effect according to claim 1, it is characterized in that fabric is a dacron, the technology of its pre-treatment is: one (caustic soda 1～5g/L, 80～100 ℃ of temperature), two roads (209 detergents, 3～6g/L, 80～100 ℃ of temperature), three roads (penetrating agent JFC 1～5g/L, 95～100 ℃ of temperature), four roads (penetrating agent JFC 1～5g/L, caustic soda 1～5g/L, 95～100 ℃ of temperature), five roads (the spirit 0.3～1g/L that deoils, 50～70 ℃ of temperature), each one of back hot water, cold wash; The purpose of fabric pretreatment mainly is to remove the slurry on the polyster fibre and remain in finish on the fabric when weaving, in order to avoid the dyeing flower phenomenon occurs.
3. the preparation technology of coated fabric with glaring and charming visual effect according to claim 2, the process that it is characterized in that the process using High Temperature High Pressure dye gigging of dyeing, get final product in 125～135 ℃ of insulation 2～3 roads, and accumulate in dyestuff on the fiber surface with removal carrying out reduction cleaning after the dyeing; Carry out pre-setting after the dyeing, the purpose of pre-setting be for the cloth cover that makes dacron smooth, door width of cloth unanimity so that the carrying out of back stamp and top finish, presetting technology is: 185～190 ℃ of temperature, the speed of a motor vehicle 85～95m/min; Or in groove, add a spot of waterproof and soft finishing agent, so that coating, back arrangement are carried out more smoothly.
4. the preparation technology of coated fabric with glaring and charming visual effect according to claim 3, it is characterized in that printing technology adopts DISPERSE DYES to carry out stamp, mix up required printing paste according to printing color before the seal, printing paste prescription by weight is: DISPERSE DYES 2～5%, synthetic thickening agent 98～95%, stamp is carried out according to the colored type that designs in the back on printing machine, and 100～120 ℃ of oven dry down, adopt saturated vapour decatize 25～35min down at 125～135 ℃ again, synthetic thickening agent remaining on the fabric is removed in the after washing oven dry.