CN101608276A - 阻隔防爆材料 - Google Patents
阻隔防爆材料 Download PDFInfo
- Publication number
- CN101608276A CN101608276A CNA2009101823293A CN200910182329A CN101608276A CN 101608276 A CN101608276 A CN 101608276A CN A2009101823293 A CNA2009101823293 A CN A2009101823293A CN 200910182329 A CN200910182329 A CN 200910182329A CN 101608276 A CN101608276 A CN 101608276A
- Authority
- CN
- China
- Prior art keywords
- proof materials
- block blast
- alloy foil
- manganese
- magnesium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于金属材料领域,特别是一种用在易燃易爆液体或气体储存器内作为填充材料的阻隔防爆材料,由切缝并扩展后的铝合金箔网制成,具有蜂窝状的多孔结构,铝合金箔的化学成分重量百分比为:硅0.2~0.25%,铁0.3~0.7%,铜0.05~0.10%,锰0.05~0.18%,镁1.5~3%,锌0.1~0.2%,钛0.08~0.15%,铬0.1~0.4%,铝为余量。本发明的阻隔防爆材料屈服强度大于130MPa,抗拉强度大于180MPa以上,延伸率大于3%,解决了现有的阻隔防爆材料耐腐蚀性能差、脆性大,延伸率低的技术问题。
Description
技术领域
本发明属于金属材料领域,特别是一种用在易燃易爆液体或气体储存器内作为填充材料的阻隔防爆材料。
背景技术
目前,在汽油、柴油丙烷、乙炔、乙醚等液、气体燃料及易燃、易爆流体储运容器内装设空隙材料后,利用容器内抑爆材料的蜂窝结构,阻隔火焰迅速传播和能量的瞬间释放,利用抑爆材料的热传导效应,破坏燃烧介质的爆炸条件,从而防止爆炸,保证了易燃易爆气态、液态危险品的贮运安全。中国专利CN1029105C公开了一种“用于易燃易爆物品的抑爆材料”,该材料合金成分重量百分比为:硅0.3~0.6,铁0.3~0.7,铜0.1~0.2,锰0.8~1.8,锌0.1%,钛0.1~0.2,铝为余量。这种材料存在脆性大,延伸率低,防锈性能差的缺点,使用中会出现碎片,严重时甚至会造成油路堵塞。特别是在轧制时,箔带边上还可能开裂,影响箔带的防爆性能。
发明内容
本发明要解决的技术问题是:为解决现有的阻隔防爆材料脆性大,延伸率低的技术问题,本发明提供一种防爆性能好,柔性好,屈服强度和抗拉强度高,延伸率高的阻隔防爆材料。
本发明解决其技术问题所采用的技术方案是:一种阻隔防爆材料,由切缝并扩展后的铝合金箔网制成,具有蜂窝状的多孔结构,铝合金箔的化学成分重量百分比为:硅0.2~0.25%,铁0.3~0.7%,铜0.05~0.10%,锰0.05~0.18%,镁1.5~3%,锌0.05~0.2%,钛0.08~0.15%,铬0.1~0.4%,铝为余量。
作为优选,铝合金箔的化学成分重量百分比为:硅0.2~0.25%,铁0.3~0.4%,铜0.05~0.10%,锰0.05~0.18%,镁2~3%,锌0.05~0.2%,钛0.1~0.15%,铬0.3~0.4%,铝为余量。
本发明的有益效果是,本发明的阻隔防爆材料在铝箔合金成分中增加了镁和铬,通过对硅、铁、铜、锰、镁、锌、钛和铬等合金元素含量的合理配比,有效地提高阻隔防爆材料的耐腐蚀性能、屈服强度和抗拉强度,本发明的阻隔防爆材料的屈服强度大于130MPa,抗拉强度可以达到180MPa以上,同时,还可以提高延伸率,延伸率可以达到3%,使阻隔防爆材料在使用时耐腐蚀性能、防爆性能更好,使用安全、可靠。
依据本发明,阻隔防爆材料的合金元素的含量有一定的限制,其原因如下(以下所有成分的百分比均为质量百分比):
1.硅:铝中加入硅有一定的强化作用,但是硅会限制镁的有利作用,硅也会同铁组合形成粗大的AlFeSi颗粒,从而影响阻隔防爆材料的疲劳寿命。为避免造成强化元素镁作用的损失,因此本发明将硅含量控制在0.2~0.25%。
2.铜:有一定的固溶强化效果,铜含量高会造成本发明阻隔防爆材料的耐蚀性的极大恶化。因此,本发明将铜含量控制在0.05~0.10%。
3.锰:锰能阻止铝合金的再结晶过程,提高再结晶温度,能显著细化再结晶晶粒,并通过MnAl6溶解杂质铁,减小铁的有害影响。锰与镁相配合,锰可提高阻隔防爆材料的强度。但是过高的锰含量过高,会影响阻隔防爆材料的延伸率,因此本发明将锰含量控制在0.05~0.18%。
4.镁:镁对铝的强化作用是明显的,每增加1%的镁,抗拉强度大约升高34MPa,但镁含量过高,会使材料脆性大,轧制时,铝箔带边上易开裂,影响阻隔防爆材料的防爆性能。
5.铬:铬阻碍再结晶的形核和长大过程,对合金有一定的强化作用,还能改善合金韧性,提高阻隔防爆材料的耐腐蚀性能和抗氧化性能。
具体实施方式
下面结合实施例对本发明作进一步地说明。
实施例1:
一种阻隔防爆材料,由切缝并扩展后的铝合金箔网制成,具有蜂窝状的多孔结构,铝合金箔的化学成分重量百分比为:硅0.2%,铁0.4%,铜0.10%,锰0.15%,镁3%,锌0.2%,钛0.15%,铬0.4%,铝为余量。
实施例2
一种阻隔防爆材料,由切缝并扩展后的铝合金箔网制成,具有蜂窝状的多孔结构,铝合金箔的化学成分重量百分比为:硅0.25%,铁0.5%,铜0.08%,锰0.18%,镁2%,锌0.15%,钛0.10%,铬0.3%,铝为余量。
实施例3
一种阻隔防爆材料,由切缝并扩展后的铝合金箔网制成,具有蜂窝状的多孔结构,铝合金箔的化学成分重量百分比为:硅0.25%,铁0.6%,铜0.10%,锰0.1%,镁2.5%,锌0.1%,钛0.15%,铬0.2%,铝为余量。
Claims (2)
1.一种阻隔防爆材料,由切缝并扩展后的铝合金箔网制成,具有蜂窝状的多孔结构,其特征在于:铝合金箔的化学成分重量百分比为:硅0.2~0.25%,铁0.3~0.7%,铜0.05~0.10%,锰0.05~0.18%,镁1.5~3%,锌0.1~0.2%,钛0.08~0.15%,铬0.1~0.4%,铝为余量。
2.根据权利要求1所述的阻隔防爆材料,其特征在于:铝合金箔的化学成分重量百分比为:硅0.2~0.25%,铁0.3~0.4%,铜0.05~0.10%,锰0.05~0.18%,镁2~3%,锌0.05~0.2%,钛0.1~0.15%,铬0.3~0.4%,铝为余量。