CN101591974A - A kind of bamboo floor block and manufacture method thereof that adopts clout to constitute - Google Patents
A kind of bamboo floor block and manufacture method thereof that adopts clout to constitute Download PDFInfo
- Publication number
- CN101591974A CN101591974A CNA2008101239762A CN200810123976A CN101591974A CN 101591974 A CN101591974 A CN 101591974A CN A2008101239762 A CNA2008101239762 A CN A2008101239762A CN 200810123976 A CN200810123976 A CN 200810123976A CN 101591974 A CN101591974 A CN 101591974A
- Authority
- CN
- China
- Prior art keywords
- bamboo
- clout
- adopts
- floor block
- bamboo floor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of bamboo floor block and manufacture method thereof that adopts clout to constitute, belong to the fitting-out work technical field of building.Described bamboo floor block piece is made of two module unit pieces at least, and cell block is made of the pressing of multilayer bamboo chip veneer side direction, and the bamboo line direction of adjacent two cell blocks is orthogonal, and the bamboo chip veneer all adopts bamboo floor clout.Its manufacture method comprise get the raw materials ready, cut, polishing, pressing, splicing be shaped.Adopt the bamboo floor clout that serves as discarded object in the process of assembling of to be in behind the present invention originally to process again, make new bamboo floor block, meet the environmental protection demand that house ornamentation is advocated in the industry.And such processing is removed from from the former loaded down with trivial details processing of expecting finished product of bamboo.Simultaneously, newly formed bamboo floor block is not only higher for the adaptive capacity of laying, and also has the parquets aesthetic.
Description
Technical field
The present invention relates to house ornamentation floor board block in the industry, relate in particular to a kind of bamboo floor block and manufacture method thereof that adopts clout to constitute, belong to the fitting-out work technical field of building.
Background technology
Along with the continuous reinforcement of people to environmental consciousness, at present the protection to the forest reserves grows with each passing day, and is that the manufacturing of raw-material former wood flooring reduces day by day with the forest reserves.Relative, because the bamboo speed of growth is very fast, suitably utilize bamboo can not destroy the forest reserves.Therefore, the floor of adopting the bamboo wood material to make has begun to become gradually important wood flooring substitute.
In existing house ornamentation market, the application on bamboo floor is the same with wood flooring to become universal.But,, therefore in the installation on bamboo floor is laid, can produce certain floor clout because the area of household all certainly exists difference.Just at present, these floor clouts often are used as waste disposal, and have directly wasted, and have caused immeasurable economic loss.Moreover such waste does not meet present house ornamentation environment protection requirement in the industry yet.
Summary of the invention
Purpose of the present invention is exactly in order to solve the above-mentioned problems in the prior art, and a kind of bamboo floor block and manufacture method thereof that adopts clout to constitute is provided.
Purpose of the present invention is achieved through the following technical solutions:
A kind of bamboo floor block that adopts clout to constitute, wherein: described bamboo floor block piece is made of two module unit pieces at least, cell block is made of the pressing of multilayer bamboo chip veneer side direction, and the bamboo line direction of adjacent two cell blocks is orthogonal, and the bamboo chip veneer all adopts bamboo floor clout.
Above-mentioned a kind of bamboo floor block that adopts clout to constitute, wherein: described multilayer bamboo chip veneer, the bamboo line direction of adjacent each layer is parallel to each other.
Further, above-mentioned a kind of bamboo floor block that adopts clout to constitute, wherein: the length of described each bamboo chip veneer, thickness, width are all consistent.
Further, above-mentioned a kind of bamboo floor block that adopts clout to constitute, wherein: described bamboo chip veneer thickness is 0.4～0.7cm.
Further, above-mentioned a kind of bamboo floor block that adopts clout to constitute, wherein: described bamboo chip veneer width is 1～2cm.
Further, above-mentioned a kind of bamboo floor block that adopts clout to constitute, wherein: described bamboo chip veneer length is 15～16.5cm.
Again further, above-mentioned a kind of bamboo floor block that adopts clout to constitute, wherein: the adjacent both sides of described bamboo floor block piece are provided with public tenon or female tenon.
A kind of manufacture method that adopts the bamboo floor block of clout formation, wherein: this method comprises following operation:
Step 1: the bamboo floor clout that quality is identical cuts into the bamboo chip veneer of Len req;
Step 2: with the planing machine burr on the above-mentioned bamboo chip veneer external surface is partly eliminated, reach requirement with seasonal bamboo chip veneer width;
Step 3: above-mentioned bamboo chip veneer is dug to desired thickness with the planing machine;
Step 4: with the bamboo chip veneer of length, thickness, width unanimity, arrange, be heated to 160～230 ℃, use the side direction press equipment, under the pressure of 14～21MPa, it is pressed into cell block according to the mode side direction that bamboo line direction is parallel to each other;
Step 5: cell block is spliced mutually according to the vertical mode of bamboo line direction, be shaped, constitute bamboo floor block by pressurized adhesion.
Above-mentioned a kind of manufacture method that adopts the bamboo floor block of clout formation, wherein: the bamboo chip veneer of arranging in same horizontal plane in the described step 4 is 20～30.
Further, above-mentioned a kind of manufacture method that adopts the bamboo floor block of clout formation, wherein: scribble epoxy resin or urea formaldehyde resin adhesive piling up in bonding surface and the described step 5 of bamboo chip veneer on the cell block Mosaic face in the described step 4.
The outstanding substantive distinguishing features and the obvious improvement of technical solution of the present invention is mainly reflected in: the bamboo floor clout that serves as discarded object in the process of assembling of will being in is originally processed again, makes new bamboo floor block, meets the environmental protection demand that house ornamentation is advocated in the industry.And such processing is removed from from the former screening of expecting finished product of bamboo, removes surf green, is removed tabasheer, baking process, and processing and making process is easy, helps promoting.Simultaneously, newly formed bamboo floor block is higher for the adaptive capacity of laying, and can use in a lot of rooms.Anti-skid wearable not only, more have present bamboo floor block nearly less than the parquets aesthetic.This shows that the present invention has substantive technical characterstic and significant technological progress, its application prospect is boundless.
Description of drawings
Purpose of the present invention, advantage and characteristics will illustrate by the non-limitative illustration of following preferred embodiment and explain.These embodiment only are the prominent examples of using technical solution of the present invention, and all technical schemes of taking to be equal to replacement or equivalent transformation and forming all drop within the scope of protection of present invention.In the middle of these accompanying drawings,
Fig. 1 is the unitary construction schematic diagram of bamboo floor block.
The implication of each Reference numeral is as follows among the figure:
1 bamboo chip veneer, 2 public tenons
3 female tenons
The specific embodiment
A kind of bamboo floor block that adopts clout to constitute as shown in Figure 1, its special feature is: described bamboo floor block piece is made of two module unit pieces at least, cell block is made of the 1 side direction pressing of multilayer bamboo chip veneer, the bamboo line direction of adjacent two cell blocks is orthogonal, and bamboo chip veneer 1 all adopts bamboo floor clout.Further, use needed intensity in order to allow floor after being shaped reach, described multilayer bamboo chip veneer 1, the quality of adjacent each layer is identical, and bamboo chip veneer 1 length, thickness, width are all consistent.Simultaneously, in order to play certain beauty function, multilayer bamboo chip veneer 1, the bamboo line direction of adjacent each layer is parallel to each other.Consider existing house ornamentation bamboo floor block style, and the roughly specification of bamboo floor clout, bamboo chip veneer 1 thickness is 0.4～0.7cm, and width is 1～2cm, and length is 15～16.5cm.For the ease of the splicing between the bamboo floor block, described bamboo floor block edge is a tack.Certainly, consider that the combination between the bamboo floor block is stable, can also offer public tenon 2 or female tenon 3 on the adjacent both sides of bamboo floor block piece.That is to say, when assembling, public tenon 2 is embedded female tenon 3 get final product.
Again further, manufacture method of the present invention, method comprise following operation: at first, the bamboo floor clout that quality is identical cuts into the bamboo chip veneer 1 of Len req.Subsequently, the burr on above-mentioned bamboo chip veneer 1 external surface is partly eliminated, make bamboo chip veneer 1 width reach requirement with the planing machine.Then, with the planing machine above-mentioned bamboo chip veneer 1 is dug to desired thickness equally.Then, 20～30 bamboo chip veneers 1 are arranged according to bamboo line direction mode side direction parallel to each other, scribbled adhesive between the bamboo chip veneer 1, after being heated to 160～230 ℃, use the side direction press equipment, under the pressure of 14～21MPa, it is pressed into cell block.At last, cell block is spliced mutually according to the vertical mode of bamboo line direction, adopt epoxy resin or Lauxite, be shaped, constitute bamboo floor block by pressurized adhesion as adhesive.
" embodiment one "
A kind of manufacture method that adopts the bamboo floor block of clout formation, roughly process is as follows for it: at first, the bamboo floor clout that quality is identical cuts into the bamboo chip that length is 15cm.Subsequently, the burr on above-mentioned bamboo chip veneer 1 external surface is partly eliminated, make the unified 1cm of being of width of bamboo chip veneer 1 with the planing machine.Then, with the planing machine above-mentioned bamboo chip veneer 1 is dug thickness to 0.4cm equally.
Then, the bamboo chip veneer 1 that the bamboo floor clout of 20 specification unanimities is constituted is closely arranged according to the mutual side direction of bamboo line direction.During this period, can help bonding shaping between the bamboo chip veneer 1 smearing epoxy resin or Lauxite on the bamboo chip veneer 1.
Subsequently, the bamboo chip veneer 1 after will piling up is heated to 160 ℃, uses the side direction press equipment, under the pressure of 14MPa, it is carried out the side direction pressing, constitutes cell block.After waiting to make many group cell blocks, with between the cell block according to the mutually perpendicular mode of bamboo line direction, splice via same horizontal plane.Certainly, more perfect after the splicing in order to make between the cell block in conjunction with getting, on Mosaic face, scribble epoxy resin or Lauxite as adhesive.And, in splicing, carrying out suitable pressing, the bamboo floor block piece that order is made of cell block is configured as one.
Because the bamboo floor block made of this technology derives from the clout on bamboo floor, it is compact therefore to allow the area of bamboo floor block trend towards in process, can be suitable for use in the less room of area and lay, and can not produce the secondary clout again.
" embodiment two "
A kind of manufacture method that adopts the bamboo floor block of clout formation, its process is as follows: at first, and the bamboo floor clout that quality is identical, being cut to length is the bamboo chip veneer 1 of 16.5cm.Subsequently, the burr on above-mentioned bamboo chip veneer 1 external surface is partly eliminated, make the unified 2cm of being of width of bamboo chip veneer 1 with the planing machine.Then, dig to 0.7cm with the thickness of planing machine equally above-mentioned bamboo chip veneer 1.
Then, according to bamboo line direction mode parallel to each other, side direction is closely arranged mutually with the bamboo chip veneer 1 of 30 specification unanimities after processing.During this period, can on bamboo chip veneer 1, smear epoxy resin or Lauxite and help the shaping of bamboo chip veneer 1 intermediate adhesion.
Subsequently, the bamboo chip veneer 1 after will piling up is heated to 230 ℃, uses the side direction press equipment, under the pressure of 21MPa, it is carried out the side direction pressing, constitutes cell block.After waiting to make many group cell blocks, with between the cell block according to the mutually perpendicular mode of bamboo line direction, splice via same horizontal plane.More perfect after the splicing in order to make between the cell block in conjunction with getting, on Mosaic face, scribble epoxy resin or Lauxite as adhesive.And, in splicing, carrying out suitable pressing, the bamboo floor block piece that order is made of cell block firmly is shaped.
Adopt the bamboo floor block after this technology is made that bigger area is arranged, can be applicable to bigger laying work area, such as parlor etc.
" embodiment three "
A kind of manufacture method that adopts the bamboo floor block of clout formation, roughly process is as follows for it: at first, the bamboo floor clout that quality is identical cuts into the bamboo chip that length is 16cm.Subsequently, the burr on above-mentioned bamboo chip veneer 1 external surface is partly eliminated, make the unified 1.5cm of being of width of bamboo chip veneer 1 with the planing machine.Then, with the planing machine above-mentioned bamboo chip veneer 1 is dug thickness to 0.6cm equally.
Then, the bamboo chip veneer 1 that the bamboo floor clout of 28 specification unanimities is constituted is according to bamboo line direction mode parallel to each other, and side direction is closely arranged mutually.During this period, can on the bonding surface of bamboo chip veneer 1, smear epoxy resin or Lauxite and help the shaping of bamboo chip veneer 1 intermediate adhesion.
Subsequently, the bamboo chip veneer 1 after will piling up is heated to 200 ℃, uses the side direction press equipment, under the pressure of 17MPa, it is carried out the side direction pressing, constitutes cell block.After waiting to make many group cell blocks, with between the cell block according to the mutually perpendicular mode of bamboo line direction, splice via same horizontal plane.More perfect after the splicing in order to make between the cell block in conjunction with getting, on Mosaic face, scribble epoxy resin or Lauxite as adhesive.And, in splicing, carrying out suitable pressing, the bamboo floor block piece that order is made of cell block firmly is shaped.At last, offer public tenon 2 and female tenon 3 on the adjacent both sides of bamboo floor block piece.
By the bamboo floor block that above-mentioned technology is made, its area is more moderate, can comparatively be widely used in each place of house ornamentation, and is higher with the matching degree of coverage.
By above-mentioned text description also in conjunction with the accompanying drawings as can be seen, behind employing the present invention, serve as the bamboo floor clout of discarded object in the process of assembling of will being in originally and process again, make new bamboo floor block, meet the environmental protection demand that house ornamentation is advocated in the industry.And such processing is removed from from the former screening of expecting finished product of bamboo, removes surf green, is removed tabasheer, baking process, and processing and making process is easy, helps promoting.Simultaneously, newly formed bamboo floor block is higher for the adaptive capacity of laying, and can use in a lot of rooms.Anti-skid wearable not only, more have present bamboo floor block nearly less than the parquets aesthetic.Thus, the present invention has expanded the space for the technological progress of this area, and implementation result is good.
Claims (10)
1, a kind of bamboo floor block that adopts clout to constitute, it is characterized in that: described bamboo floor block piece is made of two module unit pieces at least, cell block is made of the pressing of multilayer bamboo chip veneer side direction, and the bamboo line direction of adjacent two cell blocks is orthogonal, and the bamboo chip veneer all adopts bamboo floor clout.
2, a kind of bamboo floor block that adopts clout to constitute according to claim 1, it is characterized in that: described multilayer bamboo chip veneer, the bamboo line direction of adjacent each layer is parallel to each other.
3, a kind of bamboo floor block that adopts clout to constitute according to claim 1 and 2, it is characterized in that: the length of described each bamboo chip veneer, thickness, width are all consistent.
4, a kind of bamboo floor block that adopts clout to constitute according to claim 1, it is characterized in that: described bamboo chip veneer thickness is 0.4～0.7cm.
5, a kind of bamboo floor block that adopts clout to constitute according to claim 1, it is characterized in that: described bamboo chip veneer width is 1～2cm.
6, a kind of bamboo floor block that adopts clout to constitute according to claim 1, it is characterized in that: described bamboo chip veneer length is 15～16.5cm.
7, a kind of bamboo floor block that adopts clout to constitute according to claim 1, it is characterized in that: the adjacent both sides of described bamboo floor block piece are provided with public tenon or female tenon.
8, a kind of manufacture method that adopts the bamboo floor block of clout formation is characterized in that this method comprises following operation:
Step 1: the bamboo floor clout that quality is identical cuts into the bamboo chip veneer of Len req;
Step 2: with the planing machine burr on the above-mentioned bamboo chip veneer external surface is partly eliminated, reach requirement with seasonal bamboo chip veneer width;
Step 3: above-mentioned bamboo chip veneer is dug to desired thickness with the planing machine;
Step 4: with the bamboo chip veneer of length, thickness, width unanimity, arrange, be heated to 160～230 ℃, use the side direction press equipment, under the pressure of 14～21MPa, it is pressed into cell block according to the mode side direction that bamboo line direction is parallel to each other;
Step 5: cell block is spliced mutually according to the vertical mode of bamboo line direction, be shaped by pressurized adhesion;
Step 5: cell block is spliced mutually according to the vertical mode of bamboo line direction, be shaped, constitute bamboo floor block by pressurized adhesion.
9, a kind of manufacture method that adopts the bamboo floor block of clout formation according to claim 8, it is characterized in that: the bamboo chip veneer of arranging in same horizontal plane in the described step 4 is 20～30.
10, a kind of manufacture method that adopts the bamboo floor block of clout formation according to claim 8 is characterized in that: scribble epoxy resin or urea formaldehyde resin adhesive piling up in bonding surface and the described step 5 of bamboo chip veneer on the cell block Mosaic face in the described step 4.