CN101591968A - A kind of bamboo floor block and manufacture method thereof that constitutes by clout - Google Patents
A kind of bamboo floor block and manufacture method thereof that constitutes by clout Download PDFInfo
- Publication number
- CN101591968A CN101591968A CNA2008101239777A CN200810123977A CN101591968A CN 101591968 A CN101591968 A CN 101591968A CN A2008101239777 A CNA2008101239777 A CN A2008101239777A CN 200810123977 A CN200810123977 A CN 200810123977A CN 101591968 A CN101591968 A CN 101591968A
- Authority
- CN
- China
- Prior art keywords
- bamboo
- clout
- chip veneer
- bamboo floor
- block
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of bamboo floor block and manufacture method thereof that constitutes by clout, belong to the fitting-out work technical field of building.This bamboo floor comprises the multilayer bamboo chip veneer of arranging mutually from top to bottom, the formation that is laminated between bamboo chip veneer cell block, and four cell block amalgamations constitute bamboo floor block, and the bamboo chip veneer all adopts bamboo floor clout.Its manufacture method comprise get the raw materials ready, cut, polishing, pressing, splicing be shaped.Adopt the bamboo floor clout that serves as discarded object in the process of assembling of to be in behind the present invention originally to process again, make new bamboo floor.And such processing is removed from from the former loaded down with trivial details processing of expecting finished product of bamboo.Simultaneously, newly formed bamboo floor is not only higher for the adaptive capacity of laying, and also has the parquets aesthetic.
Description
Technical field
The present invention relates to house ornamentation bamboo floor in the industry, relate in particular to a kind of bamboo floor block and manufacture method thereof that constitutes by clout, belong to the fitting-out work technical field of building.
Background technology
A few days ago, along with the reinforcement to the forest conservation dynamics, the manufacturing of former wood flooring reduces day by day.Relative, bamboo utilizes bamboo can not destroy the forest reserves because the speed of growth is very fast, and therefore, the floor of adopting the bamboo wood material to make more and more becomes important wood flooring substitute.In existing house ornamentation market, the application on bamboo floor is also comparatively universal.But, because the difference of household area, the bamboo floor is in installing laying, can produce certain floor clout, and these floor clouts often are used as waste material and have directly wasted, having caused enormous economic loss thus, also is to be the price major reason that when the river rises the boat goes up day by day of the tame package material of major ingredient with the floor.And, do not meet present house ornamentation environment protection requirement in the industry.
Summary of the invention
Purpose of the present invention is exactly in order to solve the above-mentioned problems in the prior art, and a kind of bamboo floor block and manufacture method thereof that is made of clout is provided.
Purpose of the present invention is achieved through the following technical solutions:
A kind of bamboo floor block that constitutes by clout, wherein: described bamboo floor block is made of two module unit pieces at least, cell block is made of multilayer bamboo chip veneer vertical press-fit, and the bamboo line direction of adjacent two cell blocks is orthogonal, and the bamboo chip veneer all adopts bamboo floor clout.
Above-mentioned a kind of bamboo floor block that is made of clout, wherein: the bamboo chip veneer of described formation cell block, the bamboo line direction of its adjacent each layer is parallel to each other.
Further, above-mentioned a kind of bamboo floor block that constitutes by clout, wherein: the length of described each bamboo chip veneer, thickness, width are all consistent.
Further, above-mentioned a kind of bamboo floor block that constitutes by clout, wherein: described bamboo chip veneer thickness is 0.3～0.6cm.
Further, above-mentioned a kind of bamboo floor block that constitutes by clout, wherein: described bamboo chip veneer width is 1.5～2.5cm.
Further, above-mentioned a kind of bamboo floor block that constitutes by clout, wherein: described bamboo chip veneer length is 15～17cm.
Again further, above-mentioned a kind of bamboo floor block that constitutes by clout, wherein: the adjacent both sides of described bamboo floor block are public tenon or female tenon.
A kind of manufacture method of the bamboo floor block that constitutes by clout, the method includes the steps of:
Step 1: the bamboo floor clout that quality is identical cuts into the bamboo chip veneer of Len req;
Step 2: with the planing machine cutting burr on the above-mentioned bamboo chip veneer external surface is partly eliminated, make bamboo chip veneer width reach requirement;
Step 3: above-mentioned bamboo chip veneer is dug to desired thickness with the planing machine;
Step 4: the bamboo chip veneer of length, thickness, width unanimity according to three layers of bamboo line direction mode vertical stackings parallel to each other, is heated to 180～220 ℃,, under the pressure of 14～21MPa, it vertically is rolled into cell block with two roller rivet buckers;
Step 5: cell block according to the orthogonal splicing of bamboo line direction, is shaped by pressurized adhesion, constitutes bamboo floor block.
The manufacture method of above-mentioned a kind of bamboo floor block that is made of clout, wherein: the bamboo chip veneer that is positioned at same horizontal plane in the described step 4 when piling up is 4～7.
Further, the manufacture method of above-mentioned a kind of bamboo floor block that constitutes by clout, wherein: scribble epoxy resin or urea formaldehyde resin adhesive piling up in bonding surface and the described step 5 of bamboo chip veneer on the cell block Mosaic face in the described step 4.
The outstanding substantive distinguishing features and the obvious improvement of technical solution of the present invention is mainly reflected in: the bamboo floor clout that serves as discarded object in the process of assembling of will being in is originally processed again, makes new bamboo floor.And such processing is removed from from the former screening of expecting finished product of bamboo, removes surf green, is removed tabasheer, baking process, and processing and making process is easy.Simultaneously, newly formed bamboo floor is higher for the adaptive capacity of laying, anti-skid wearable not only, more have present bamboo floor nearly less than the parquets aesthetic.This shows that the present invention has substantive technical characterstic and significant technological progress, its application prospect is boundless.
Description of drawings
Purpose of the present invention, advantage and characteristics will illustrate by the non-limitative illustration of following preferred embodiment and explain.These embodiment only are the prominent examples of using technical solution of the present invention, and all technical schemes of taking to be equal to replacement or equivalent transformation and forming all drop within the scope of protection of present invention.In the middle of these accompanying drawings,
Fig. 1 is the front schematic view of bamboo floor block;
Fig. 2 is the unitary construction schematic diagram of bamboo floor block.
The implication of each Reference numeral is as follows among the figure:
1 bamboo chip veneer, 2 public tenons
3 female tenons
The specific embodiment
A kind of bamboo floor block that constitutes by clout as shown in Figure 1 and Figure 2, its special feature is: described bamboo floor block is made of two module unit pieces at least, cell block is made of multilayer bamboo chip veneer 1 vertical press-fit, the bamboo line direction of adjacent two cell blocks is orthogonal, and bamboo chip veneer 1 all adopts bamboo floor clout.Further, use needed intensity in order to allow floor after being shaped reach, described multilayer bamboo chip veneer 1, the quality of adjacent each layer is identical, and the bamboo line direction between the cell block is orthogonal.Simultaneously, in order to play certain beauty function, the bamboo line direction of multilayer bamboo chip veneer 1 adjacent each layer is parallel to each other.Consider existing house ornamentation bamboo floor style, and the roughly specification of bamboo floor clout, bamboo chip veneer 1 thickness is 0.3～0.6cm, and width is 1.5～2.5cm, and length is 15～17cm.Certainly, constitute length, thickness, the width unanimity of the bamboo chip veneer 1 of cell block.For the ease of the splicing between the bamboo floor, described bamboo floor edge is a tack.Certainly, consider that the combination between the bamboo floor is stable, the adjacent both sides of bamboo floor block are public tenon 2 or female tenon 3.That is to say, when assembling, public tenon 2 is embedded female tenon 3 get final product.
Again further, manufacture method of the present invention, method comprise following step: at first, the bamboo floor clout that quality is identical cuts into the bamboo chip veneer 1 of Len req.Subsequently, the cutting burr on above-mentioned bamboo chip veneer 1 external surface is partly eliminated, make bamboo chip veneer 1 width reach requirement with the planing machine.Then, with the planing machine above-mentioned bamboo chip veneer 1 is dug to desired thickness equally.Then, 4～7 bamboo chip veneers 1 are piled up three layers according to bamboo line direction mode parallel to each other, scribble adhesive between the bamboo chip veneer 1, be heated to 180～220 ℃ after, apply the pressure of 14～21MPa with two roller rivet buckers, be rolled into cell block.At last, according to the orthogonal splicing of bamboo line direction, adopt epoxy resin or Lauxite cell block, be shaped, constitute bamboo floor block by pressurized adhesion as adhesive.Certainly, consider the aesthetic measure that bamboo floor block is final, can carry out mopping on its surface.
" embodiment one "
A kind of manufacture method of the bamboo floor block that constitutes by clout, roughly process is as follows for it: at first, and the bamboo floor clout that quality is identical, cutting into length is the bamboo chip veneer 1 of 15cm.Subsequently, the cutting burr on above-mentioned bamboo chip veneer 1 external surface is partly eliminated, make the unified 1.5cm of being of width of bamboo chip veneer 1 with the planing machine.Then, with the planing machine above-mentioned bamboo chip veneer 1 is dug thickness to 0.3cm equally.
Then, the bamboo chip veneer 1 that the bamboo floor clout of 4 specification unanimities is constituted piles up according to bamboo line direction mode parallel to each other, and totally three layers, promptly altogether 12.During this period, can smear on the bamboo chip veneer 1 that epoxy resin or Lauxite help between the bamboo chip veneer 1 can smooth bonding shaping.
Subsequently, the bamboo chip veneer 1 after will piling up is heated to 180 ℃, with two roller rivet buckers the pressure that it applies 14MPa is carried out spreading, constitutes cell block.After waiting to make many group cell blocks, with between the cell block according to the orthogonal splicing of bamboo line direction.More firm after the splicing in order to make between the cell block in conjunction with getting, on Mosaic face, scribble epoxy resin or Lauxite as adhesive.And, in splicing, carrying out suitable pressing, the bamboo floor block that order is made of cell block is configured as one.
Because this technology bamboo floor of making derives from the clout on bamboo floor, it is compact therefore to allow the area on bamboo floor trend towards in process, can be suitable for use in the less room of area and lay, and can not produce the secondary clout again.
" embodiment two "
A kind of manufacture method of the bamboo floor block that constitutes by clout, its process is as follows: at first, and the bamboo floor clout that quality is identical, cutting into length is the bamboo chip veneer 1 of 16cm.Subsequently, the cutting burr on above-mentioned bamboo chip veneer 1 external surface is partly eliminated, make the unified 2cm of being of width of bamboo chip veneer 1 with the planing machine.Then, with the planing machine above-mentioned bamboo chip veneer 1 is dug thickness to 0.4cm equally.
Then, the bamboo chip veneer 1 that the bamboo floor clout of 5 specification unanimities is constituted respectively piles up three layers respectively according to bamboo line direction mode parallel to each other, promptly adopts 15 bamboo chip veneers 1 altogether.During this period, can smear on the bamboo chip veneer 1 that epoxy resin or Lauxite help between the bamboo chip veneer 1 can smooth bonding shaping.
Subsequently, the bamboo chip veneer 1 after will piling up is heated to 200 ℃, with two roller rivet buckers the pressure that it applies MPa is carried out spreading, constitutes cell block.After waiting to make many group cell blocks, with between the cell block according to the orthogonal splicing of bamboo line direction.More firm after the splicing in order to make between the cell block in conjunction with getting, on Mosaic face, scribble epoxy resin or Lauxite as adhesive.And, in splicing, carrying out suitable pressing, the bamboo floor block that order is made of cell block firmly is shaped.
There is bigger area on bamboo floor after adopting this technology to make, can be applicable to bigger laying work area, such as parlor etc.
" embodiment three "
A kind of manufacture method of the bamboo floor block that constitutes by clout, roughly process is as follows for it: at first, and the bamboo floor clout that quality is identical, cutting into length is the bamboo chip veneer 1 of 17cm.Subsequently, the cutting burr on above-mentioned bamboo chip veneer 1 external surface is partly eliminated, make the unified 2.5cm of being of width of bamboo chip veneer 1 with the planing machine.Then, with the planing machine above-mentioned bamboo chip veneer 1 is dug thickness to 0.6cm equally.
Then, the bamboo chip veneer 1 that the bamboo floor clout of 7 specification unanimities is constituted respectively piles up three layers respectively according to bamboo line direction mode parallel to each other, promptly adopts 21 bamboo chip veneers 1 altogether.During this period, can smear on the bamboo chip veneer 1 that epoxy resin or Lauxite help between the bamboo chip veneer 1 can smooth bonding shaping.
Subsequently, the bamboo chip veneer 1 after will piling up is heated to 220 ℃, with two roller rivet buckers the pressure that it applies 17MPa is carried out spreading, constitutes cell block.After waiting to make many group cell blocks, with between the cell block according to the orthogonal splicing of bamboo line direction.More firm after the splicing in order to make between the cell block in conjunction with getting, on Mosaic face, scribble epoxy resin or Lauxite as adhesive.And, in splicing, carrying out suitable pressing, the bamboo floor block that order is made of cell block firmly is shaped.At last, offer public tenon 2 or female tenon 3 on the adjacent both sides of floor board block.
By the bamboo floor that above-mentioned technology is made, its area is more moderate, can comparatively be widely used in each place of house ornamentation, and is higher with the matching degree of coverage.
By above-mentioned text description also in conjunction with the accompanying drawings as can be seen, behind employing the present invention, serve as the bamboo floor clout of discarded object in the process of assembling of will being in originally and process again, make new bamboo floor.And such processing is removed from from the former screening of expecting finished product of bamboo, removes surf green, is removed tabasheer, baking process, and processing and making process is easy.Simultaneously, newly formed bamboo floor is higher for the adaptive capacity of laying, anti-skid wearable not only, more have present bamboo floor nearly less than the parquets aesthetic.Thus, the present invention has expanded the space for the technological progress of this area, and implementation result is good.
Claims (10)
1, a kind of bamboo floor block that constitutes by clout, it is characterized in that: described bamboo floor block is made of two module unit pieces at least, cell block is made of multilayer bamboo chip veneer vertical press-fit, and the bamboo line direction of adjacent two cell blocks is orthogonal, and the bamboo chip veneer all adopts bamboo floor clout.
2, a kind of bamboo floor block that is made of clout according to claim 1 is characterized in that: the bamboo chip veneer of described formation cell block, the bamboo line direction of its adjacent each layer is parallel to each other.
3, a kind of bamboo floor block that is made of clout according to claim 1 is characterized in that: the length of described each bamboo chip veneer, thickness, width are all consistent.
4, a kind of bamboo floor block that is made of clout according to claim 1, it is characterized in that: described bamboo chip veneer thickness is 0.3～0.6cm.
5, a kind of bamboo floor block that is made of clout according to claim 1 is characterized in that: described bamboo chip veneer width is 1.5～2.5cm.
6, a kind of bamboo floor block that is made of clout according to claim 1 is characterized in that: described bamboo chip veneer length is 15～17cm.
7, a kind of bamboo floor block that is made of clout according to claim 1 is characterized in that: the adjacent both sides of described bamboo floor block are public tenon or female tenon.
8, a kind of manufacture method of the bamboo floor block that is made of clout is characterized in that the method includes the steps of:
Step 1: the bamboo floor clout that quality is identical cuts into the bamboo chip veneer of Len req;
Step 2: with the planing machine cutting burr on the above-mentioned bamboo chip veneer external surface is partly eliminated, make bamboo chip veneer width reach requirement;
Step 3: above-mentioned bamboo chip veneer is dug to desired thickness with the planing machine;
Step 4: the bamboo chip veneer of length, thickness, width unanimity according to three layers of bamboo line direction mode vertical stackings parallel to each other, is heated to 180～220 ℃,, under the pressure of 14～21MPa, it vertically is rolled into cell block with two roller rivet buckers;
Step 5: cell block according to the orthogonal splicing of bamboo line direction, is shaped by pressurized adhesion, constitutes bamboo floor block.
9, the manufacture method of a kind of bamboo floor block that is made of clout according to claim 8, it is characterized in that: the bamboo chip veneer that is positioned at same horizontal plane in the described step 4 when piling up is 4～7.
10, the manufacture method of a kind of bamboo floor block that is made of clout according to claim 8 is characterized in that: scribble epoxy resin or urea formaldehyde resin adhesive piling up in bonding surface and the described step 5 of bamboo chip veneer on the cell block Mosaic face in the described step 4.