CN101574731B - 一种反击破板锤双面复合工艺 - Google Patents
一种反击破板锤双面复合工艺 Download PDFInfo
- Publication number
- CN101574731B CN101574731B CN2009100650653A CN200910065065A CN101574731B CN 101574731 B CN101574731 B CN 101574731B CN 2009100650653 A CN2009100650653 A CN 2009100650653A CN 200910065065 A CN200910065065 A CN 200910065065A CN 101574731 B CN101574731 B CN 101574731B
- Authority
- CN
- China
- Prior art keywords
- seconds
- wear
- casting
- temperature
- time
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种反击破板锤双面复合工艺，采用三次复合浇注手段，使两边工作部位的高抗磨性材料与中间部位的强韧性材料熔融为一体，使产品既具备了较高的抗磨性，又有优良的韧性，达到了安全耐磨的效果；其技术方案是：先将板锤的平面造型处理好，同时经过双炉冶炼后，初次浇注耐磨铸铁，当温度达到1350℃-1400℃时，经过15秒-35秒后，再次复合浇注碳素钢，当温度上升到1450℃-1530℃时，经过15秒-35秒后，三次复合浇注耐磨铸铁，然后降温，当温度下降到1350℃-1400℃时，经过15秒-35秒后，做落砂处理，然后进行热处理，最后进行后期清理。
Description
所属领域：
本发明涉及一种复合工艺，尤其是一种反击破板锤双面复合工艺。
背景技术：
目前，国内生产的反击式破碎机耐磨备件板锤，是单金属制品，材质为高锰钢系列，韧性好，但是耐磨性相对较差，故使用寿命较短；如采用高铬铸铁系列，硬度高，耐磨性能好，但是韧性差，易断裂。本发明是将两种不同性能的金属材料有机的复合在一起，其抗磨部分采用高铬抗磨铸铁，机体部分采用高韧性的优质碳素钢，使其达到既有优良的抗磨性能，又具备足够的整体韧性，有效地解决了硬度与韧性二者不可兼得的矛盾，从而延长了使用寿命。现提供以下技术方案；
发明内容：
本发明提供的一种反击破板锤双面复合工艺，采用三次复合浇注手段，使两边工作部位的高抗磨性材料与中间部位的强韧性材料熔融为一体，使产品既具备了较高的抗磨性，又有优良的韧性，达到了安全耐磨的效果；其技术方案是：先将板锤的平面造型处理好，同时经过双炉冶炼后，初次浇注耐磨铸铁，当温度达到1350℃-1400℃时，经过15秒-35秒后，再次复合浇注碳素钢，当温度上升到1450℃-1530℃时，经过15秒-35秒后，三次复合浇注耐磨铸铁，然后降温，当温度下降到1350℃-1400℃时，经过15秒-35秒后，做落砂处理，然后进行热处理，最后进行后期清理，本工艺采用三次复合浇注手段，使两边工作部位的高抗磨性材料与中间部位的强韧性材料熔融为一体，使产品既具备了较高的抗磨性，又有优良的韧性，达到了安全耐磨的效果。
有益效果：将两种不同性能的金属材料有机的复合在一起，其抗磨部分采用高铬抗磨铸铁，使产品既具备了较高的抗磨性，又有优良的韧性，达到了安全耐磨的效果，本工艺提供的韧性材料用在零件的机体部位(中间)，冲击值达到AKV≥30J/cm＊2，高硬度材料用在零件的工作部位(两边)，硬度值达到HRC60-65。
附图说明
下面结合附图对本发明进一步进行说明。
图1是，本发明的工艺流程图。
具体实施方式：
下面结合实施例对本发明进一步进行说明。
实施列1
将板锤的平面造型处理好，同时经过双炉冶炼后，初次浇注耐磨铸铁，当温度达到1350℃时，经过15秒后，再次复合浇注碳素钢，当温度上升到1450℃-时，经过15秒后，三次复合浇注耐磨铸铁，然后降温，当温度下降到1350℃时，经过15秒后，做落砂处理，然后进行热处理，最后进行后期清理，至此，即构成反击破板锤双面复合工艺。
实施列2
将板锤的平面造型处理好，同时经过双炉冶炼后，初次浇注耐磨铸铁，当温度达到1400℃时，经过35秒后，再次复合浇注碳素钢，当温度上升到1530℃时，经过35秒后，三次复合浇注耐磨铸铁，然后降温，当温度下降到1400℃时，经过35秒后，做落砂处理，然后进行热处理，最后进行后期清理，至此，即构成反击破板锤双面复合工艺。
实施列3
将板锤的平面造型处理好，同时经过双炉冶炼后，初次浇注耐磨铸铁，当温度达到1375℃时，经过25秒后，再次复合浇注碳素钢，当温度上升到1490℃时，经过25秒后，三次复合浇注耐磨铸铁，然后降温，当温度下降到1375℃时，经过25秒后，做落砂处理，然后进行热处理，最后进行后期清理，至此，即构成反击破板锤双面复合工艺。
Claims (1)
1.一种反击破板锤双面复合工艺，其特征在于：将板锤的平面造型处理好，同时经过双炉冶炼后，初次浇注耐磨铸铁，当温度达到1350℃-1400℃时，经过15秒-35秒后，再次复合浇注碳素钢，当温度上升到1450℃-1530℃时，经过15秒-35秒后，三次复合浇注耐磨铸铁，然后降温，当温度下降到1350℃-1400℃时，经过15秒-35秒后，做落砂处理，然后进行热处理，最后进行后期清理。