CN101572147B - 声磁防盗硬标签中的偏置磁片的制备方法 - Google Patents

声磁防盗硬标签中的偏置磁片的制备方法 Download PDF

Info

Publication number
CN101572147B
CN101572147B CN2009100788396A CN200910078839A CN101572147B CN 101572147 B CN101572147 B CN 101572147B CN 2009100788396 A CN2009100788396 A CN 2009100788396A CN 200910078839 A CN200910078839 A CN 200910078839A CN 101572147 B CN101572147 B CN 101572147B
Authority
CN
China
Prior art keywords
magnetic
magnetic sheet
sheet
rubber
label
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN2009100788396A
Other languages
English (en)
Other versions
CN101572147A (zh
Inventor
张建国
王志远
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Beijing letter of the letter in the new material technology company
Guangzhou Qida Material Technology Co., Ltd.
Original Assignee
BEIJING SIHAICHENGMING TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BEIJING SIHAICHENGMING TECHNOLOGY Co Ltd filed Critical BEIJING SIHAICHENGMING TECHNOLOGY Co Ltd
Priority to CN2009100788396A priority Critical patent/CN101572147B/zh
Publication of CN101572147A publication Critical patent/CN101572147A/zh
Application granted granted Critical
Publication of CN101572147B publication Critical patent/CN101572147B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及声磁防盗硬标签中的偏置磁片的制备方法。本发明偏置磁片是由钕铁硼粉、改性橡胶粘结剂和加工助剂制成钕铁硼橡塑片，偏置磁片矫顽力800KA/M-1000KA/M，磁场强度8KA/M-16KA/M，详细原料比例及制备方法见说明书。本发明优点是：偏置磁片矫顽力高800KA/M-1000KA/M，这样的声磁防盗标签在重复使用时的解锁过程中，磁力式解锁器的强磁场对本发明的偏置磁片的磁性不产生影响，不破坏防盗标签的报警性能，解决了现有技术硬标签不能用磁力式解锁方式的问题。偏置磁片的用途，用于声磁防盗硬标签或锁扣式声磁防盗硬标签中，以防止被保护商品的被盗。

Description

声磁防盗硬标签中的偏置磁片的制备方法
技术领域
本发明涉及电子商品防盗系统(EAS)，具体地说，本发明涉及声磁防盗硬标签中的制备方法。
背景技术
电子商品防盗系统是广泛应用于超市、商场、图书馆、专卖店为防止零售商品丢失的电子装置。美国专利US4510489公开了一种磁机式电子商品防盗系统及声磁防盗标签。现有技术的防盗标签中偏置磁片是由金属半硬磁材料或铁氧体永磁材料制成。金属半硬磁材料的磁性矫顽力较小，可以通过对偏置磁片充磁或消磁来完成对声磁标签激活与钝化的控制，这种声磁标签称软标签。铁氧体材料的磁性矫顽力较高，一般条件下不能对其进行充消磁，所以铁氧体材料为偏置磁片的声磁标签一直处在激活状态，这样的标签称硬标签。现有技术硬标签是通过一个锁扣装置及锁钉与商品连在一起的，在合法的通过电子商品防盗系统的检测区时要通过解锁器把硬标签从商品上解下来。这样标签可以反复使用。
现有技术硬标签的锁扣装置有机械式和磁力式，相应的解锁器也有机械式和磁力式。磁力式锁扣装置由锁紧钢珠、弹簧及支架组成，加锁过程是把锁钉插入锁扣装置的锁孔，在弹簧的作用下锁紧钢珠锁住锁钉。磁力式解锁器主要部分是一块强磁铁，强磁铁的磁场强度320KA/M-500KA/M，通过强磁吸力抵消弹簧作用使锁紧钢珠松动，拔出锁钉完成开锁过程。在开锁过程中强磁场同时也会对铁氧体材料的偏置磁片产生作用，改变铁氧体材料偏置磁片的磁性，使非晶共振片工作状态漂移，失去报警功能。所以采用磁力式解锁方式的现有技术声磁硬标签在反复解锁的过程中会因开锁器强磁场的作用而失效。
发明内容
本发明的目的在于克服现有技术中存在的不足之处，而提供了一种矫顽力更高、体积更小、更薄和成本更低的新型声磁防盗硬标签中的偏置磁片、制备方法及其用途。
本发明的技术方案如下：本发明声磁防盗硬标签中的偏置磁片是钕铁硼永磁材料的橡塑片，偏置磁片矫顽力800KA/M-1000KA/M，磁场强度8KA/M-16KA/M。
钕铁硼材料橡塑片的制备方法：偏置磁片按重量百分比计，钕铁硼粉为25％-80％， 改性橡胶粘结剂为15％-75％，加工助剂为0-5％，把钕铁硼粉与改性橡胶粘结剂和加工助剂混合，经开炼机混炼均匀，然后在压延机上制成厚度0.2-1.5mm的磁板，剪切成合适的几何尺寸，用于声磁标签中的偏置磁片；
钕铁硼粉粒度15μm-100μm；所述的改性橡胶粘结剂为聚异丁烯橡胶、氯丁橡胶、顺丁橡胶、乙丙橡胶、丁基橡胶、聚氨酯橡胶、硅橡胶中的一种或几种；所述的加工助剂为偶联剂、增塑剂、润滑剂、抗氧化剂。
本发明的偏置磁片的用途，用于声磁防盗硬标签或锁扣式声磁防盗硬标签中，以防止被保护商品的被盗。
本发明与现有技术相比，具有如下的优点：本发明的偏置磁片使用矫顽力非常高的钕铁硼磁性材料，其矫顽力800KA/M-1000KA/M，而现有技术声磁硬标签的偏置磁片为铁氧体材料，其矫顽力144KA/M-176KA/M。现有技术的磁力式解锁器的强磁铁产生的磁场强度是320KA/M-500KA/M，在开锁过程中，因开锁器的磁场强度(320KA/M-500KA/M)远大于铁氧体材料的矫顽力(144KA/M-176KA/M)，强磁场会对现有技术偏置磁片产生作用，改变偏置磁片的磁性，使非晶共振片工作状态漂移，失去报警功能；而本发明的钕铁硼材料偏置磁片其矫顽力(800KA/M-1000KA/M)远高于开锁器的(320KA/M-500KA/M)磁场强度，所以在反复使用的开锁过程中，开锁器的磁场不影响本发明的偏置磁片的磁性，不破坏防盗标签的报警性能，解决了现有技术硬标签不能用磁力式解锁方式的问题。
现有技术的钕铁硼橡塑片(专利200410052150.3)磁场强度很高，并且现有技术钕铁硼永磁材料追求磁性越强越好，包括钕铁硼橡塑板和钕铁硼注塑片，加入钕铁硼永磁粉末比例很高，一般高于85％。本发明的偏置磁片用钕铁硼橡塑片按重量百分比计，钕铁硼粉为25％-80％，磁场强度控制在8KA/M-16KA/M之间。
本发明申请发明专利的同时，亦申请了两个实用新型，发明名称分别为锁扣式声磁防盗硬标签和声磁防盗硬标签，两个实用新型中，阐述了偏置磁片放置在非晶共振片上面，或非晶共振片两端，偏置磁片与非晶共振片之间加0.2mm-0.5mm厚隔膜或不加隔膜。隔膜一般使用非磁性材料例如塑料膜、纸膜等，通过隔膜厚度调整偏置磁片与非晶共振片间的距离，以达到调整非晶共振片工作点的目的。
声磁防盗硬标签通过绳索或带有锁扣装置的护盒与被保护商品连接。
具体实施方式
下面列举2个实施例，对本发明加以进一步说明，但本发明不只限于这2个实施例。
实施例1
偏置磁片由钕铁硼橡塑片制成，橡塑片中按重量百分比计，钕铁硼粉含量60％，改性橡胶粘结剂为聚异丁烯橡胶含量36.5％，硅烷偶联剂1.0％，环氧树脂1.0％，其他加工助剂1.5％。把钕铁硼粉与改性橡胶粘结剂和加工助剂混合，经开炼机混炼均匀，然后在压延机上制成厚度0.4mm的橡塑板，偏置磁片剪切成长26毫米、宽6毫米长方形薄片用于声磁标签中，偏置磁片矫顽力800KA/M，磁场强度12KA/M，偏置磁片与非晶共振片之间加0.30mm厚的PE塑料隔膜。
锁扣装置是磁力式锁扣装置，由锁紧钢珠、弹簧和支架组成，加锁过程是把锁钉插入锁扣装置的锁孔，在弹簧的作用下锁紧钢珠锁住锁钉，完成防盗标签与目标商品的连接。开锁方法是用磁力式解锁器，通过强磁吸力抵消弹簧作用使锁钉松动，拔出锁钉完成开锁过程。
实施例2
用实施例1的方法，不同之处是：偏置磁片由钕铁硼橡塑片制成，按重量百分比计，钕铁硼粉含量25％，改性橡胶粘结剂为聚异丁烯橡胶含量70.5％，加工助剂含量4.5％；加工助剂是硅烷偶联剂、环氧树脂、有机过氧化物；制成厚度1.0mm的橡塑板，剪切成长30毫米、宽6毫米、厚1.0毫米长方形薄片。偏置磁片矫顽力800KA/M，磁场强度9KA/M。其后，在非晶共振片上叠放偏置磁片。偏置磁片与非晶共振片之间不加隔膜。
本发明不仅适用于非晶共振片和偏置磁片的现有尺寸，同样也适用其他尺寸。
本发明不仅适用于钕铁硼橡塑片，同样也适用钕铁硼注塑片。

Claims (2)

1.声磁防盗硬标签中的偏置磁片的制备方法，其特征在于：钕铁硼材料橡塑片的制备方法：偏置磁片按重量百分比计，钕铁硼粉为25％-60％，改性橡胶粘结剂为36.5％-70.5％，加工助剂为3.5％-4.5％，把钕铁硼粉与改性橡胶粘结剂和加工助剂混合，经开炼机混炼均匀，然后在压延机上制成厚度0.2-1.5mm的磁片，剪切成合适的几何尺寸，用于声磁标签中的偏置磁片；偏置磁片是钕铁硼永磁材料橡塑片，偏置磁片矫顽力800KA/M-1000KA/M，磁场强度8KA/M-16KA/M。
2.由权利要求1所述的声磁防盗硬标签中的偏置磁片的制备方法，其特征在于：所述的钕铁硼粉粒度15μm-100μm；所述的改性橡胶粘结剂为聚异丁烯橡胶、氯丁橡胶、顺丁橡胶、乙丙橡胶、丁基橡胶、聚氨酯橡胶、硅橡胶中的一种或几种；所述的加工助剂为偶联剂、增塑剂、润滑剂、抗氧化剂中的一种或几种。
CN2009100788396A 2009-03-04 2009-03-04 声磁防盗硬标签中的偏置磁片的制备方法 Active CN101572147B (zh)