CN101560352A - 一种彩色水泥瓦水性漆 - Google Patents
一种彩色水泥瓦水性漆 Download PDFInfo
- Publication number
- CN101560352A CN101560352A CNA2009101169139A CN200910116913A CN101560352A CN 101560352 A CN101560352 A CN 101560352A CN A2009101169139 A CNA2009101169139 A CN A2009101169139A CN 200910116913 A CN200910116913 A CN 200910116913A CN 101560352 A CN101560352 A CN 101560352A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- water based
- weight
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种彩色水泥瓦水性漆,其特征在于:组分按重量份为:制浆组分按重量份比为:软质水140-160,润湿剂1-2,聚羧酸铵盐分散剂3-5,聚羧酸钠盐分散剂1-3,丙二醇10-20,2-氨基-2-甲基-1-丙醇1-2,铁红粉150-170,水性涂料消泡剂1-3;调漆组分按重量份为:纯丙烯酸乳液550-650,成膜助剂25-35,碱溶性增稠剂3-7,疏水改性碱溶性增稠剂1-5,软质水24-25,水基型杀菌剂1-3。本发明具有较低的吸水率、优异的耐水白性能、优秀的基材附着力,适用于混凝土屋面、彩瓦与水泥瓦、砖石墙面,各类竣桥、体育馆看台等,陶土瓦、石棉瓦等。
Description
技术领域
本发明涉及一种水性漆,具体是一种彩色水泥瓦水性漆。
背景技术
水泥瓦是取代粘土瓦的新型建筑材料,其基本材料为是水泥。彩色水泥瓦是由模压瓦成型主机生产的环保型产品,是通过高压经优质模具压滤而成。因而具有密度大、强度高、防雨抗冻性能好,表面平整、尺寸准确的优点。彩色水泥瓦色彩多样,使用年限长,造价便宜。但是,目前用于彩色水泥瓦表面的涂料耐水性、机械稳定性、柔韧性和表面硬度较差,容易出现脱皮和腿色的现象。
发明内容
本发明提供了一种彩色水泥瓦水性漆,具有良好的机械稳定性、柔韧性和表面硬度,彩色水泥瓦水性漆膜具有较高的透明光泽和优异的耐水性、抗水泛白性和户外耐久性。
本发明的技术方案为:
一种彩色水泥瓦水性漆,其特征在于:组分按重量份为:
制浆组分按重量份为:软质水140-160,润湿剂1-2,聚羧酸铵盐分散剂3-5,,聚羧酸钠盐分散剂1-3,丙二醇10-20,2-氨基-2-甲基-1-丙醇1-2,铁红粉150-170,水性涂料消泡剂1-3;
调漆组分按重量份为:纯丙烯酸乳液550-650,成膜助剂25-35,碱溶性增稠剂3-7,疏水改性碱溶性增稠剂1-5,软质水24-25,水基型杀菌剂1-3;
所述的水性漆为所述的制浆组分与调漆组分的混合物。
水基型杀菌剂为2(羟甲基氨基)乙醇。
一种彩色水泥瓦水性漆,其特征在于:所述的润湿剂选用非离子型表面活性剂,所述的成膜助剂选用2,2,4-三甲基戊二醇-1,3单异丁酸酯。
本发明具有较低的吸水率、优异的耐水白性能、优秀的基材附着力,适用于混凝土屋面、彩瓦与水泥瓦、砖石墙面,各类竣桥、体育馆看台等,陶土瓦、石棉瓦等。
具体实施方式
彩色水泥瓦水性漆的制备步骤如下:
(1)制浆:将制浆组分按重量份(千克)为:软质水140-160,STRS-280润湿剂1-2,聚羧酸铵盐分散剂3-5,,聚羧酸钠盐分散剂1-3,丙二醇10-20,2-氨基-2-甲基-1-丙醇(AMP-95)1-2,铁红粉150-170,水性涂料消泡剂(F111)1-3混合,然后将混合后的制浆组分输送到高速分散釜内进行搅拌、分散30-40分钟,溶解,分散和溶解后的制浆组分输送到砂磨机内进行进行湿式砂磨,分散,得到浆料,浆料研磨两便细度达到小于或等于40微米;
(2)调漆:在制得的浆料中加入调漆组分按重量份(千克)为:纯丙烯酸乳液550-650,STCM-1成膜助剂25-35,STZC-96碱溶性增稠剂3-7,STZC-95疏水改性碱溶性增稠剂1-5,软质水24-25,2(羟甲基氨基)乙醇水基型杀菌剂1-3,然后输送到高速分散釜内进行搅拌、分散和溶解,分散和溶解后组分的输送到砂磨机内进行进行湿式砂磨、分散,得到漆料;
(3)将制得的漆料输送到振动过滤机进行过滤和筛选,然后将过滤后的产品进行包装,入库。
彩色水泥瓦水性漆每片彩瓦喷涂18-25克。
Claims (2)
1、一种彩色水泥瓦水性漆,其特征在于:组分按重量份为:
制浆组分按重量份为:软质水140-160,润湿剂1-2,聚羧酸铵盐分散剂3-5,,聚羧酸钠盐分散剂1-3,丙二醇10-20,2-氨基-2-甲基-1-丙醇1-2,铁红粉150-170,水性涂料消泡剂1-3;
调漆组分按重量份为:纯丙烯酸乳液550-650,成膜助剂25-35,碱溶性增稠剂3-7,疏水改性碱溶性增稠剂1-5,软质水24-25,水基型杀菌剂1-3;
所述的水性漆为所述的制浆组分与调漆组分的混合物。
2、根据权利要求2所述的一种彩色水泥瓦水性漆,其特征在于:所述的润湿剂选用非离子型表面活性剂,所述的成膜助剂选用2,2,2-三甲基-1,3-戊二醇单异丁酸酯。