CN101353241A - 一种机制砂清水混凝土拌合物 - Google Patents

一种机制砂清水混凝土拌合物 Download PDF

Info

Publication number
CN101353241A
CN101353241A CNA2008100460724A CN200810046072A CN101353241A CN 101353241 A CN101353241 A CN 101353241A CN A2008100460724 A CNA2008100460724 A CN A2008100460724A CN 200810046072 A CN200810046072 A CN 200810046072A CN 101353241 A CN101353241 A CN 101353241A
Authority
CN
China
Prior art keywords
machine
made sand
concrete
faced concrete
fair
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2008100460724A
Other languages
English (en)
Inventor
高育欣
任治平
向卫平
郑广军
简晓军
修晓明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
China Construction Third Engineering Bureau Co Ltd
China Construction Ready Mixed Concrete Co Ltd
Original Assignee
Concrete Service Station of China Construction Third Bureau Co Ltd Chengdu Branch
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Concrete Service Station of China Construction Third Bureau Co Ltd Chengdu Branch filed Critical Concrete Service Station of China Construction Third Bureau Co Ltd Chengdu Branch
Priority to CNA2008100460724A priority Critical patent/CN101353241A/zh
Publication of CN101353241A publication Critical patent/CN101353241A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种机制砂清水混凝土拌合物，属于新型混凝土材料领域。本发明的清水混凝土拌合物是由水泥100份、矿粉65－150份、硅粉0－10份、聚羧酸减水剂1.7－2.6份、碎石330－530份、机制砂250－410份组成；为了使新拌混凝土及硬化混凝土颜色达到不同程度的浅白色，还可以加入钛白粉0－6份。本发明全部使用机制砂制备混凝土拌合物，有利于节约天然资源，并且，该混凝土具有良好的和易性和保水性能。

Description

一种机制砂清水混凝土拌合物
技术领域
本发明涉及一种用于工业与民用建筑的混凝土拌合物，具体涉及一种机制砂清水混凝土拌合物，属于新型混凝土材料领域。
背景技术
清水混凝土指直接利用混凝土成型后的自然质感效果作为装饰效果的混凝土，近年来，这种混凝土在大型公共建筑和主要的公共设施中得到广泛采用。随着清水混凝土工程在国内大面积推广应用，人们对清水混凝土表观颜色的要求也越来越多样化，很多设计师不再满足于单调的灰色，从而使得彩色、白色等清水混凝土概念不断被提出并得到试验研究。
机制砂近年来在普通混凝土中得到了广泛应用，但是由于其级配以及颗粒粒形都比较差，容易造成新拌混凝土的泌水离析，若用来拌制清水混凝土拌合物，则混凝土硬化体表面容易出现“花面”、“水线”等由于混凝土保水性能不好引起的表观现象，对清水饰面效果的实现产生影响。因此，目前国内一般的清水混凝土工程，基本选用级配好、颗粒粒形好的天然河砂配制。
目前天然砂资源逐渐枯竭，很多地区机制砂逐渐得到推广，机制砂的应用研究，特别是在各种特殊混凝土中的应用研究，逐渐成为一种趋势。
发明内容
本发明的目的是使用机制砂，提供一种适用于清水工程要求的混凝土拌合物。
为实现发明目的，本发明的具体技术方案如下：
按重量份计算，本发明的清水混凝土拌合物是由水泥100份、矿粉65-150份、硅粉0-10份、聚羧酸减水剂1.7-2.6份、碎石330-530份、机制砂250-410份组成。
为了使新拌混凝土及硬化混凝土颜色达到不同程度的浅白色，还可以加入钛白粉0-6份。
所述钛白粉为金红石型R-930。
所述水泥为普通硅酸盐水泥或硅酸盐水泥，其强度等级≥42.5Mpa。
所述矿粉是S95级，比表面积≥430m2/kg，流动度比＞110％；为了使混凝土颜色更浅，矿粉的粉体白度≥80％。
所述聚羧酸减水剂固含量为20％。
所述碎石为5-25mm连续级配，经过水洗，含泥量小于1％。
所述机制砂以卵石为原料破碎而成，细度模数为2.5-3.0，级配达到II区中砂边缘要求，石粉含量8％-10％。
使用时，按照不同的强度等级要求，按照0.28～0.38的水胶比加入水搅拌均匀即得浅白色清水混凝土拌合物。该混凝土具有良好的和易性和保水性能，适用于清水混凝土结构。
与现有技术相比，本发明具有以下独特的性能和优点：
(1)为清水混凝土的颜色实现提供了一种新的选择，其色泽、观感也优于普通清水混凝土。
(2)在颜色改变的前提下，没有改变混凝土的生产工艺，有利于实现大批量生产，推广应用价值高。
(3)本发明全部使用机制砂制备混凝土拌合物，有利于节约天然资源，符合国家资源可持续发展战略。
具体实施方式
实施例一
取水泥300kg，矿粉200kg、钛白粉15kg、机制砂760kg、碎石1000kg、聚羧酸减水剂5.2kg，加水150kg拌合。
其中，水泥强度为42.5Mpa；矿粉级数为S95级、粉体白度≥80％、比表面积450m2/kg、流动比112％；钛白粉为普通钛白粉；机制砂以卵石为原料破碎而成，细度模数为2.8，级配达到II区中砂边缘要求，石粉含量为9％；碎石为5-25mm连续级配，经过水洗，含泥量为0.8％；聚羧酸减水剂固含量为20％。
新拌混凝土及硬化混凝土颜色均为浅白色，3天强度为43.2Mpa，7天强度为60.3Mpa，28天强度为80.5Mpa。
实施例二
取水泥200kg，矿粉180kg、硅粉20kg、钛白粉4kg、机制砂820kg、碎石1060kg、聚羧酸减水剂4kg，加水150kg拌合。
其中，水泥强度为45.6Mpa；矿粉级数为S95级、粉体白度≥80％、比表面积480m2/kg、流动比115％；钛白粉为金红石型R-930；机制砂以卵石为原料破碎而成，细度模数为2.5，级配达到II区中砂边缘要求，石粉含量为8％；碎石为5-25mm连续级配，经过水洗，含泥量为0.9％；聚羧酸减水剂固含量为20％。
新拌混凝土及硬化混凝土颜色均为浅白色，3天强度为25.4Mpa，7天强度为36.2Mpa，28天强度为50.9Mpa。
实施例三
取水泥250kg，矿粉230kg、硅粉20kg、钛白粉15kg、机制砂760kg、碎石1000kg、聚羧酸减水剂5.2kg，加水150kg拌合。
其中，水泥强度为48Mpa；矿粉级数为S95级、粉体白度≥80％、比表面积500m2/kg、流动比121％；钛白粉为金红石型R-930；机制砂以卵石为原料破碎而成，细度模数为3.0，级配达到II区中砂边缘要求，石粉含量为10％；碎石为5-25mm连续级配，经过水洗，含泥量为0.73％；聚羧酸减水剂固含量为20％。
新拌混凝土及硬化混凝土颜色均为浅白色，3天强度为35.5Mpa，7天强度为49.6Mpa，28天强度为72.8Mpa。
实施例四
取水泥200kg，矿粉300kg、硅粉20kg、机制砂760kg、碎石1000kg、聚羧酸减水剂5.2kg，加水150kg拌合。
其中，水泥强度为43.8Mpa；矿粉级数为S95级、粉体白度≥80％、比表面积430m2/kg、流动比117％；钛白粉为金红石型R-930；机制砂以卵石为原料破碎而成，细度模数为2.6，级配达到II区中砂边缘要求，石粉含量为8.8％；碎石为5-25mm连续级配，经过水洗，含泥量为0.7％；聚羧酸减水剂固含量为20％。
3天强度为24.5Mpa，7天强度为35.6Mpa，28天强度为55.8Mpa。
实施例五
取水泥250kg，矿粉250kg、硅粉17.5kg、钛白粉15kg、机制砂700kg、碎石1050kg、聚羧酸减水剂5.3kg，加水150kg拌合。
其中，水泥强度为49Mpa；矿粉级数为S95级、粉体白度≥80％、比表面积490m2/kg、流动比128％；钛白粉为金红石型R-930；机制砂以卵石为原料破碎而成，细度模数为3.0，级配达到II区中砂边缘要求，石粉含量为8％；碎石为5-25mm连续级配，经过水洗，含泥量为0.6％；聚羧酸减水剂固含量为20％。
新拌混凝土及硬化混凝土颜色均为浅白色，3天强度为41.8Mpa，7天强度为55.2Mpa，28天强度为76.7Mpa。

Claims (9)

1、一种机制砂清水混凝土拌合物，其特征在于：按重量份计算，由水泥100份、矿粉65-150份、硅粉0-10份、聚羧酸减水剂1.7-2.6份、碎石330-530份、机制砂250-410份组成。
2、根据权利要求1所述的一种机制砂清水混凝土拌合物，其特征在于：还含有钛白粉0-6份。
3、根据权利要求2所述的一种机制砂清水混凝土拌合物，其特征在于：所述钛白粉为金红石型R-930。
4、根据权利要求1或2任一项所述的一种机制砂清水混凝土拌合物，其特征在于：所述水泥为普通硅酸盐水泥或硅酸盐水泥，其强度等级≥42.5Mpa。
5、根据权利要求1或2任一项所述的一种机制砂清水混凝土拌合物，其特征在于：所述矿粉是S95级，比表面积≥430m2/kg，流动度比＞110％。
6、根据权利要求5所述的一种机制砂清水混凝土拌合物，其特征在于：所述矿粉的粉体白度≥80％。
7、根据权利要求1或2任一项所述的一种机制砂清水混凝土拌合物，其特征在于：所述聚羧酸减水剂固含量为20％。
8、根据权利要求1或2任一项所述的一种机制砂清水混凝土拌合物，其特征在于：所述碎石为5-25mm连续级配，经过水洗，含泥量小于1％。
9、根据权利要求1或2任一项所述的一种机制砂清水混凝土拌合物，其特征在于：所述机制砂以卵石为原料破碎而成，细度模数为2.5-3.0，级配达到II区中砂边缘要求，石粉含量8％-10％。
CNA2008100460724A 2008-09-16 2008-09-16 一种机制砂清水混凝土拌合物 Pending CN101353241A (zh)