CN101545301B - Wood-plastic plate internally filled with self-hardening resin light material - Google Patents
Wood-plastic plate internally filled with self-hardening resin light material Download PDFInfo
- Publication number
- CN101545301B CN101545301B CN2009100085969A CN200910008596A CN101545301B CN 101545301 B CN101545301 B CN 101545301B CN 2009100085969 A CN2009100085969 A CN 2009100085969A CN 200910008596 A CN200910008596 A CN 200910008596A CN 101545301 B CN101545301 B CN 101545301B
- Authority
- CN
- China
- Prior art keywords
- wood
- moulded
- plate
- self
- light material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention relates to a wood-plastic plate internally filled with self-hardening resin light material, comprising a wood-plastic plate with an open chamber or a combined wood-plastic plate with an open chamber and a closed chamber, self-hardening resin, a solidifying agent, an accelerating agent, light material, fiber material and auxiliary materials. The external surface of the wood-plastic plate is adhered with a resin film or a metal plate or coated with anticorrosive coating or latex, and the self-hardening resin light material is filled in the open chamber of the wood-plastic plate and organic resin foam material is filled in the closed chamber.
Description
Technical field;
The present invention relates to wallboard, link plate, floor, building roof with the Wood-plastic material manufacturing.
Background technology;
Existing wood is moulded plate and is adopted plastic tree cosmetics and wood powder to make moulding through hot extrusion; The addition of wood powder is controlled between the 40%-80% usually, and it is low, yielding that the wood that adds wood powder is moulded plate intensity; When especially the wood of employing foaming loose structure was moulded plate, its strength problem was more outstanding.Another shortcoming that wood is moulded plate is a temperature when raising, easy firing.The problems referred to above limit is moulded the application of plate.
Expanded perlite granule is a material from acidic volcanic glass matter lava, and expanding through 1200 ℃ of high temperature forms, and has natural fireproof performance; Need not add the safety that any fireproofing agent just can guarantee the highrise building external thermal insulation; Light weight, unit weight are about every cubic metre of 50-150kg, and be nontoxic, can not give off pernicious gas; Tasteless, be natural green material.
Glass bead is a kind of inorganic matter nature of glass mineral material; Be to be ground into ore in sand form, process that product is irregular orbicule particle through special expanded burning method by lava; Inside is cavity structure; Surface vitreous sealing, have light weight, heat-insulating, fire-preventing, high temperature resistant, anti-aging, water absorption rate is little, not hollowing, do not ftracture, intensity is high, adhesion stress is strong, good, the insect protected ant bite and corrosion of anti-sag performance, the easy construction characteristics.
The self-hardening resin comprises: furane resins, urethane resin, phenolic resins three major types self-hardening resin; All has higher temperature tolerance, excellent acid alkalescence; Good anti-corrosion, and adhesive property preferably add after strong acid curing compound and the accelerator self-hardening fast.
Begin furane resins, urethane resin, phenolic resins are combined to be applied in casting industry with sand facies in China from the seventies; The characteristic of self-hardening fast after utilizing furane resins, urethane resin, phenolic resins and modified resin thereof and strong acid curing compound and accelerator combining; Produce have good fluidity, intensity is high, high-temperature shrinkage is little, the resin self-setting sand of quick-hardening; Simplify production technology, improve casting quality, brought remarkable economic efficiency for domestic casting industry.
Specific embodiments:
The objective of the invention is; 1, wood is moulded plate cavity internally filled with self-hardening resin light material, utilizes self-hardening resin light material dimensionally stable, incombustible characteristic, solves wood and moulds the plate problem on deformation, improves wood and moulds plate intensity, heat-insulating property and fireproof performance.2, the advantage that has an aesthetic appearances with Wood-plastic material overcomes the shortcoming of self-hardening resin light material porous surface aesthetic property difference, and with self-hardening resin light material, high temperature is indeformable; The incombustible advantage of naked light overcomes the Wood-plastic material high temperature deformation, and incendive shortcoming is filled into wood through self-hardening resin light material and moulds in the plate chamber; Manufacturing has aesthetic appearances; Indeformable, heatproof, fireproof combination product.3, internally filled with self-hardening resin light material wood is moulded the holddown groove that the adjacent side with body of wall of plate establishes the band butt hook or the inserts of band butt hook, improves the bonding strength that wood is moulded the plate middle part, prevents that wood from moulding the plate chatter and coming off.4, wood is moulded plate and is established in overhanging connection fixed head and the nut storage chamber, connects the head of a nail and is hidden in the nut storage chamber, solves wood and moulds corrosion of plate connected nail place and seepy question, improves wood and moulds plate application life.5, through mould plate external surface or primary coat surfaces coated sunlight control grain coating or antibiotic and antivirus activity material coating at wood, improve self-cleaning function, sterilizing function and anti-aging function that wood is moulded plate.6,, improve wood and mould the anti-aging function of plate through mould plate external surface or primary coat surfaces coated metal scale coating or glass flake coating at wood.7, make surface material and the wooden composite wood-plastic material of core material one of moulding through co-extrusion technology, improve performance, reduce cost.
The wood of the internally filled with self-hardening resin light material that the present invention proposes is moulded plate, comprising: plate moulded by atrium wood or atrium is moulded plate, self-hardening resin, curing compound with the chamber combination wood of remaining silent; Accelerator, light material, fibrous material attaches material; Wood is moulded plate external surface viscosity resin film or sticking metal sheet or is coated with anticorrosive paint or japanning, and wood is moulded and filled in the plate atrium by self-hardening resin, curing compound; Accelerator is filled in self-hardening resin light material that light material is formed or the atrium by self-hardening resin, curing compound; Accelerator, the self-hardening resin light material that light material is formed is filled organic resin foam material in the chamber of remaining silent.The self-hardening resin comprises: furane resins, urethane resin, phenolic resins and and carry out modified resins with epoxy resin or silane resin or polyurethane resin, curing compound comprises: p-methyl benzenesulfonic acid, benzene sulfonic acid, xylitol organic acid esters, glycerine amyl acetate.Light material comprises: closed-cell expanded perlite particle, expanded and vitrified small ball, granular polystyrene, slag, wood powder, fiber powder, glass fiber, fibre.Self-hardening resin light material is made up of with one or more light materials self-hardening resin and curing compound, and the addition of self-hardening resin accounts for the 1%-8% of light material weight, and the addition of curing compound accounts for the 10-120% of self-hardening resin.The organic resin expanded material comprises: polyurethane foam material, polystyrene foamed material, Merlon foamed material, polyimide foam material.
A kind of structure that internally filled with self-hardening resin light material wood is moulded plate is that wood is moulded plate one side and established overhanging connection fixed head; The inboard position link slot of setting of overhanging connection fixed head; Wood is moulded the plate opposite side and is set the position joint tongue; The tenon bottom that is located by connecting is that the head of a nail is hidden gap, and the head of a nail is hidden gap and formed nut between fixed head and store the chamber with adjacent overhanging the connection.During assembling, bolt passes and connects fixed head and wood is moulded plate one end be fixed on body of wall or the steel work, and wood is moulded the plate tenon that is located by connecting and injected adjacent wood and mould plate and be located by connecting and wood moulded the plate other end in the groove and fix, and connects the head of a nail and stays in the nut storage chamber, does not expose.
The another kind of structure that the wood of internally filled with self-hardening resin light material is moulded plate is that wood is moulded plate one side and established overhanging connection fixed head, the inboard position link slot of setting of overhanging connection fixed head, and wood is moulded the plate opposite side and is set a position joint tongue; The tenon bottom that is located by connecting is that the head of a nail is hidden gap; The tenon bottom head of a nail that is located by connecting is hidden gap and is formed nut storage chamber between fixed head with adjacent overhanging the connection, and wood is moulded the holddown groove that the adjacent side of plate and body of wall or ground is established the band butt hook, during assembling; Bolt passes and connects fixed head and wood is moulded plate one end be fixed on body of wall or the steel work; Wood is moulded the plate tenon that is located by connecting and is injected adjacent wood and mould plate and be located by connecting and wood moulded the plate other end in the groove and fix, and the head of a nail is hidden gap and formed nut storage chamber between fixed head with adjacent overhanging the connection, connects the head of a nail and stays nut and store in the chamber; Wood is moulded plate and body of wall or ground sides adjacent; Connect base plate and be fixed on body of wall or the steel work with coupling bar, the hook that connects on the base plate is pressed on the interior butt hook of holddown groove, wood is moulded the plate middle part fix; Improve wood and mould the bonding strength at plate middle part, prevent that wood from moulding plate and coming off.
Mould the decorate properties and the antiseptic property of plate for improving internally filled with self-hardening resin light material wood, wood is moulded the sticking metal sheet in plate surface or is manufactured trapezoidal, rectangle or convex tendon is decorated in the curved surface bar shaped.
For preventing that wood from moulding packing material and wood in the plate cavity and moulding plate and break away from, wood is moulded and is established L shaped in the plate cavity or T shape muscle, packing material be wrapped in L shaped or T shape muscle around.
Mould plate outward appearance and antiseptic property for improving internally filled with self-hardening resin light material wood, reduce internally filled with self-hardening resin light material wood and mould the plate cost, wood is moulded plate and is moulded core material by surface material and wood and resist altogether and process.Wood is moulded core material and is established groove, and the surface material of fusion gets into wood and moulds in the core material groove.
For improving the heat-insulating property that internally filled with self-hardening resin light material wood is moulded plate, combined phase-change energy storage material in the hardening resin light material comprises: compound organic phase change energy storage material in inorganic-phase variable energy storage material and organic phase change energy storage material and the light material.
Wood is moulded antibiotic the moulding with antivirus activity material coating or wood of plate surface or primary coat surfaces coated and is added antibiotic and antivirus activity material in the plate co-extrusion surface material, antibioticly comprises with antivirus activity material: nanometer Ag particle, nano-TiO
2Particle, nano-ZnO particle, nanometer SiO
2Particle, nano SnO
2Particle, nanometer ZrO
2Particle, nanometer Cu particle, nanometer CuO
2Particle, nanometer sodium zirconium phosphate particle.Antibiotic and antivirus activity material coating can make wood mould the function that the plate external surface has killing pathogenic bacteria, the place use that suitable hospital and susceptible viral infect.
Wood is moulded plate surface or primary coat surfaces coated sunlight control grain coating or wood and is moulded interpolation sunlight control particle in the plate co-extrusion surface material, and sunlight control particle comprises: silicon nanocrystal grain, nanometer silicon carbide crystal grain, Nano titanium dioxide, nano mica pearl essence; Nanometer aluminium powder, nanoscale tin ash, nanoscale chromium trioxide, nanoscale metatitanic acid barium; Nanoscale Fe304, nano zine oxide, Nano Silver, nano-graphite; Nano-indium stannum oxide, nano oxidized antimony, oxide nano rare earth, nanometer TCO.Wood is moulded the plate external surface and is coated with interpolation sunlight control grain coating, can make wood mould anti-aging of plate external surface and anti-pollution function.
Mould the curing rate and the ageing resistace of plate external surface solar control coating for improving wood, sunlight control grain coating adds the UV optic-solidified adhesive.
The Wood-plastic material that the present invention proposes can be used the high molecule plastic material substitution.Advantage of the present invention is: 1, wood is moulded plate cavity internally filled with self-hardening resin light material, utilizes self-hardening resin light material dimensionally stable, incombustible characteristic, solves wood and moulds the plate problem on deformation, improves wood and moulds plate intensity, heat-insulating property and fireproof performance.2, the advantage that has an aesthetic appearances with Wood-plastic material overcomes the shortcoming of self-hardening resin light material porous surface aesthetic property difference, and with self-hardening resin light material, high temperature is indeformable; The incombustible advantage of naked light overcomes the Wood-plastic material high temperature deformation, and incendive shortcoming is filled into wood through self-hardening resin light material and moulds in the plate chamber; Manufacturing has aesthetic appearances; Indeformable, heatproof, fireproof combination product.3, internally filled with self-hardening resin light material wood is moulded the holddown groove that the adjacent side with body of wall of plate establishes the band butt hook or the inserts of band butt hook, improves the bonding strength that wood is moulded the plate middle part, prevents that wood from moulding the plate chatter and coming off.4, wood is moulded plate and is established in overhanging connection fixed head and the nut storage chamber, connects the head of a nail and is hidden in the nut storage chamber, solves wood and moulds corrosion of plate connected nail place and seepy question, improves wood and moulds plate application life.5, through mould plate external surface or primary coat surfaces coated sunlight control grain coating or antibiotic and antivirus activity material coating at wood, improve self-cleaning function, sterilizing function and anti-aging function that wood is moulded plate.6,, improve wood and mould the anti-aging function of plate through mould plate external surface or primary coat surfaces coated metal scale coating or glass flake coating at wood.7, make surface material and the wooden composite wood-plastic material of core material one of moulding through co-extrusion technology, improve performance, reduce cost.
The specific embodiment:
Embodiment 1:
It is as shown in Figure 1 that opening wood is moulded plate filling urethane resin light material exterior wall cladding end face structure figure, wherein: the 1st, atrium wood is moulded plate, and the 2nd, interior reinforcing rib; The 3rd, urethane resin cementing agent, the 4th, closed-cell expanded perlite particle, the 5th, interior connection fixed head; The 6th, link slot, the 7th, joint tongue, the 8th, decorating film.At first; Weight ratio 1.5% curing compound p-methyl benzenesulfonic acid and 0.2% silane resin are added in the closed-cell expanded perlite particle 4, in blade mixer, mix after 60 seconds, add 2% urethane resin cementing agent 3; Mixed again 60 seconds; Be filled into atrium wood and mould in the atrium of plate 1, after the curing, urethane resin cementing agent 3 with closed-cell expanded perlite particle 4 with have atrium wood and mould plate 1 bonding being integral.
Embodiment 2:
The interior furane resins light material Wood-plastic floor end face structure figure that fills is as shown in Figure 2, and Fig. 3 is that Fig. 2 assembles end face structure figure, wherein: the 9th, have the atrium Wood-plastic floor, the 10th, interior connection fixed head; The 11st, connect skewed slot, the 12nd, seal strip groove, the 13rd, connect bevelled tenon, the 14th, the head of a nail is hidden gap; The 15th, butt hook, the 16th, Wood-plastic floor atrium, the 17th, furane resins cementing agent; The 18th, phase-change accumulation energy perlite particle, the 19th, nanometer silver antimicrobial grain coating, the 20th, nut storage chamber; The 21st, screw, the 22nd, fluid sealant, the 23rd, ground.At first, weight ratio 45% myristic acid phase-change material is mixed with expanded perlite granule, the myristic acid phase-change material is filled in the expanded perlite granule hole; Manufacture phase-change accumulation energy expanded perlite granule 18; Weight ratio 1.5% curing compound p-methyl benzenesulfonic acid and 0.2% silane resin are added in the phase-change accumulation energy expanded perlite granule 18, in blade mixer, mix after 60 seconds, add 1.5% furane resins cementing agent 17; Mixed again 60 seconds; Be filled into and have in the atrium Wood-plastic floor atrium 16, after the curing, furane resins cementing agent 17 with phase-change accumulation energy expanded perlite granule 18 with have atrium Wood-plastic floor 9 bonding being integral.Nanometer silver antimicrobial grain coating 19 is bonded in Wood-plastic floor 9 surfaces; Make Wood-plastic floor 9 have sterilizing function; During assembling; Screw 21 passes overhanging connection fixed head 10 and will have atrium Wood-plastic floor 9 one ends and be fixed on the ground 23, has the bevelled tenon 13 that is located by connecting on the atrium Wood-plastic floor 9 and injects the adjacent atrium Wood-plastic floor that has and be located by connecting in the skewed slot 11, will have atrium Wood-plastic floor 9 other ends and fix.
The present embodiment advantage is: fill the precious different rock particle Wood-plastic floor of furane resins cementing agent and phase-change accumulation energy expansion and effectively prevent Wood-plastic floor distortion and noise and excellent insulating performance.
Embodiment 3:
It is as shown in Figure 4 that interior filled phenolic type polyurethane light material wood is moulded link plate end face structure figure, and Fig. 5 is Fig. 4 link plate assembling end face structure figure, wherein: the 24th, wood is moulded link plate, and the 25th, overhanging connection fixed head; The 26th, the groove that is located by connecting, the 27th, sealed adhesive slot, the 28th, the tenon that is located by connecting, the 29th, the head of a nail is hidden gap; The 30th, holddown groove, the 31st, butt hook, the 32nd, phenol aldehyde type polyurethane glues, the 33rd, closed-cell expanded perlite particle; The 34th, metal flake anticorrosive paint, the 35th, nut storage chamber, the 36th, screw, the 37th, fluid sealant; The 38th, connect base plate, the 39th, connect the base plate hook, the 40th, connect the base plate hold-down screw, the 41st, the body of wall steel work.At first; Weight ratio 0.2% curing compound p-methyl benzenesulfonic acid and 1% phenolic resins are mixed; Add in the closed-cell expanded perlite particle 33 and mixed 1-2 minute, add 1% different hydrogen acid ether (hydrogen acid ester) resinoid bond and mixed again 1-2 minute, be filled into and have atrium wood and mould in the link plate atrium; After the curing, the closed-cell expanded perlite particle 33 of parcel phenol aldehyde type polyurethane self-hardening sand cementing agent 32 is moulded link plate 24 bonding being integral with atrium wood.During assembling; Screw 36 passes overhanging connection fixed head 25 and wood is moulded link plate 24 1 ends fixes; Connect base plate hold-down screw 40 and will connect base plate 38 and be fixed on the body of wall steel work 41, be moved to the left adjacent wood and mould link plate 24, wood is moulded the adjacent wood of tenon 28 reeves that is located by connecting on the link plate 24 and is moulded link plate and be located by connecting in the groove 26; Wood is moulded link plate 24 other ends to be fixed; Screw 36 is stayed overhanging connection fixed head 25 and is hidden in the gap 29 composition nut storage chambeies 35 with the dowel cap that is located by connecting, and connects base plate hook 39 and is pressed on the holddown groove butt hook 31, wood is moulded link plate 24 middle parts fix.
The present embodiment advantage is: the hook that 1, connects on the base plate is pressed on the holddown groove butt hook, and it is fixing that wood is moulded the link plate middle part, improves the bonding strength that wood is moulded the link plate middle part, prevents that wood from moulding link plate and coming off.2, the metal flake anticorrosive paint prevents that wood from moulding link plate exposed surface corrosion.
It is as shown in Figure 6 that the interior connection atrium and the chamber combination wood of remaining silent are moulded wall central layer end face structure figure, and Fig. 7 is that Fig. 6 wood is moulded filling furane resins light material and polyurethane expanded material end face structure figure in the wall central layer, and Fig. 8 is that Fig. 7 wood is moulded wall central layer interior filling furane resins light material and polyurethane expanded material assembling end face structure figure, wherein: the 42nd, wood is moulded the wall central layer; The 43rd, wall central layer dovetail groove, the 44th, the PVDF surface material, the 45th, overhanging connection fixed head, the 46th, groove is located by connecting down; The 47th, on the groove that is located by connecting, the 48th, right sealed adhesive slot, the 49th, left sealed adhesive slot, the 50th, on the tenon that is located by connecting; The 51st, the tenon that is located by connecting down, the 52nd, the head of a nail is hidden gap, and the 53rd, holddown groove, the 54th, butt hook; The 55th, atrium, the 56th, the chamber of remaining silent, the 57th, polyurethane expanded material, the 58th, furane resins light material; The 59th, nut storage chamber, the 60th, screw, the 61st, fluid sealant, the 62nd, connect base plate; The 63rd, connect the base plate hook, the 64th, connect the base plate hold-down screw, the 65th, the body of wall steel work.PVDF surface material 44 is moulded wall central layer 42 with wood and is adopted co-extrusion technology to manufacture the co-extrusion Wood plastic wall board; Because PVDF surface material 44 cementabilities are poor; Mould at wood and to establish wall central layer dovetail groove 43 on the wall central layer 42; The PVDF surface material 44 of fusion is embedded in wood and moulds on the wall central layer 42 in the wall central layer dovetail groove 43, prevents that PVDF surface material 44 and wood from moulding wall central layer 42 and separating., wood fills polyurethane expanded material 57 in moulding the chamber 56 of remaining silent of wall central layer 42; Filling furane resins light material 58 in wood is moulded the atrium 55 of wall central layer 42, filling; Polyurethane expanded material 57 has good heat-insulating property, and furane resins light material 58 has excellent fireproof performance and non-deformability.At first, weight ratio 1.5% curing compound p-methyl benzenesulfonic acid and 0.2% silane resin are added in the closed-cell expanded glass bead particle, in blade mixer, mix after 60 seconds; Add 1.5% furane resins cementing agent; Mixed again 60 seconds, and manufactured furane resins light material 58, furane resins light material 58 is filled into has atrium wood and mould in the wall central layer atrium 55; After the curing, furane resins light material 58 with have atrium wood and mould wall central layer 42 bonding being integral.During assembling; Screw 60 passes overhanging connection fixed head 45 and wood is moulded wall central layer 42 1 ends fixes; Connection base plate hold-down screw 64 will connect base plate 62 and be fixed on the body of wall steel work 65; Be moved to the left adjacent wood and mould wall central layer 42, wood is moulded be located by connecting on the wall central layer 42 tenon 50 and the tenon 51 that is located by connecting down and is injected adjacent wood respectively and mould on the wall central layer 42 in the link slot 47 and in the following link slot 46, wood is moulded wall central layer 42 other ends fix; Screw cap is stayed overhanging connection fixed head 45 and is hidden in the gap 52 composition nut storage chambeies 59 with the head of a nail; Connect base plate hook 63 and be pressed on the holddown groove butt hook 54, will mould wall central layer 42 middle parts and fix, the gap closing of 42 of wall central layers moulded adjacent wood by fluid sealant 61.
Remain silent to fill in the chamber in polyurethane expanded material and the atrium and fill the furane resins light material, make that combination is wooden moulds the wall central layer and have good heat-insulating property fireproof performance and non-deformability.
Figure is as shown in Figure 9 for Wood plastic wall board corner end face structure, and Figure 10 fills furane resins light material and polyurethane expanded material end face structure figure in Fig. 9 Wood plastic wall board corner, and Figure 11 is Fig. 7 and Fig. 9 Wood plastic wall board and Wood plastic wall board corner assembling end face structure figure, wherein: the 42nd, wood is moulded the wall central layer; The 66th, wood is moulded the corner central layer, and the 67th, wood is moulded corner central layer dovetail groove, and the 68th, PVDF surface material, the 69th, overhanging connection fixed head; The 70th, the groove that is located by connecting down, the 71st, on the groove that is located by connecting, the 72nd, sealed adhesive slot, the 73rd, atrium; The 74th, the chamber of remaining silent, the 75th, polyurethane expanded material, the 76th, furane resins light material, the 77th, nut storage chamber; The 78th, screw, the 79th, connect base plate, the 80th, connect the base plate hook; The 81st, connect the base plate hold-down screw, the 82nd, fluid sealant, the 83rd, body of wall steel work.PVDF surface material 68 is moulded corner central layer 66 with wood and is adopted co-extrusion technology to manufacture co-extrusion Wood plastic wall board corner; Because PVDF surface material 68 cementabilities are poor; Mould at wood and to establish wood on the corner central layer 66 and mould corner central layer dovetail groove 67; The PVDF surface material 68 of fusion is embedded in wooden corner central layer 66 overwoods of moulding and moulds in the corner central layer dovetail groove 67, prevents that PVDF surface material 68 and wood from moulding corner central layer 66 and separating., wood fills polyurethane expanded material 75 in moulding the chamber 74 of remaining silent of corner central layer 66;, wood fills furane resins light material 76 in moulding the atrium 73 of corner central layer 66; Polyurethane expanded material 75 has good heat-insulating property, and furane resins light material 76 has excellent fireproof performance and non-deformability.At first, weight ratio 1.5% curing compound p-methyl benzenesulfonic acid and 0.2% silane resin are added in the closed-cell expanded glass bead particle, in blade mixer, mix after 60 seconds; Add 1.5% furane resins cementing agent; Mixed again 60 seconds, and manufactured furane resins light material 76, furane resins light material 76 is filled into has in the atrium Wood plastic wall board corner opening chamber 73; After the curing, furane resins light material 76 with have atrium wood and mould corner central layer 66 bonding being integral.During assembling; Screw 78 passes wood and moulds corner central layer 66 overhanging connection fixed heads 69 and wood is moulded corner central layer 66 two ends be fixed on the body of wall steel work 83; Move adjacent wood and mould wall central layer 42; Wood is moulded be located by connecting on the wall central layer 42 tenon 50 and the tenon 51 that is located by connecting down and is injected adjacent wood respectively and mould on the corner central layer 66 in the link slot 71 and in the following link slot 70; Wood is moulded wall central layer 42 1 ends fix, screw 78 passes overhanging connection fixed head 45 and wood is moulded wall central layer 42 other ends fixes, and wood is moulded wall central layer 42 middle parts and connected base plate hook 80 and be pressed on the holddown groove butt hook 54; Wood is moulded wall central layer 42 middle parts fix, fluid sealant 82 is moulded wall central layer 42 and the wooden gap closing of moulding 66 of corner central layers with adjacent wood.
It is shown in figure 12 that Fig. 6 wood is moulded plate atrium filling self-hardening furane resins light material end face structure figure, and the 77th, the furane resins light material, furane resins light material 77 blank maps 6 wood are moulded in the plate atrium.The manufacturing of furane resins light material 77 is identical with embodiment 5 methods with filling process.
It is shown in figure 13 that self-hardening furane resins light material end face structure figure is filled in the outer corner opening chamber of Fig. 9 Wood plastic wall board; The 78th, the furane resins light material; The furane resins light material is filled in the outer corner opening chamber of Wood plastic wall board, and the manufacturing of furane resins light material 78 is identical with embodiment 5 methods with filling process.
Wood plastic wall board inside lock atrium is filled self-hardening furane resins light material, and figure is shown in figure 14 with the chamber filling polyurethane expanded material end face structure of remaining silent, wherein: the 79th, wood is moulded the inside lock central layer, and the 80th, wood is moulded corner central layer dovetail groove; The 81st, the PVC surface material; The 82nd, overhanging connection fixed head, the 83rd, the groove that is located by connecting down, the 84th, on the groove that is located by connecting; The 85th, sealed adhesive slot; The 86th, the furane resins light material, the 87th, polyurethane expanded material, polyurethane expanded material 87 filling Wood plastic wall board inside locks 79 are remained silent in the chamber; Furane resins light material 86 is filled in Wood plastic wall board inside lock 79 atriums, and the manufacturing of furane resins light material 86 is identical with embodiment 5 methods with filling process.
It is shown in figure 15 that the atrium filling self-hardening furane resins light material and the chamber filling polyurethane expanded material wood of remaining silent are moulded roofing slab end face structure figure, and Figure 16 is that Figure 15 wood is moulded roofing slab assembling end face structure figure, wherein: the 88th, wood is moulded roofing slab, and the 89th, overhanging connection fixed head; The 90th, the groove that is located by connecting, the 91st, right waterproof platform, the 92nd, right sealed adhesive slot, the 93rd, left waterproof platform; The 94th, left sealed adhesive slot, the 95th, the tenon that is located by connecting, the 96th, the head of a nail is hidden gap, and the 97th, interior link slot; The 98th, butt hook, the 99th, the chamber of remaining silent, the 100th, polyurethane expanded material, the 101st, atrium; The 102nd, self-hardening furane resins light material, the 103rd, nut storage chamber, the 104th, screw, the 105th, sealing joint strip; The 106th, connect base plate, the 107th, connect the base plate hook, the 108th, connect the base plate hold-down screw, the 109th, the roof steel work., wood fills polyurethane expanded material 100 in moulding the chamber 99 of remaining silent of roofing slab 88; Mould the atrium 101 internally filled with self-hardening furane resins light materials 102 of roofing slab 88 at wood; Polyurethane expanded material 100 has good heat-insulating property, and furane resins light material 102 has excellent fireproof performance and non-deformability.At first, weight ratio 1.5% curing compound p-methyl benzenesulfonic acid is added in the closed-cell expanded glass bead particle, in puddle mixer, mix after 60 seconds; Add 1.5% furane resins cementing agent; Mixed again 60 seconds, and manufactured furane resins light material 102, furane resins light material 102 is filled into wood moulds in the roofing slab atrium 101; After the curing, furane resins light material 102 is moulded roofing slab 88 bonding being integral with wood.During assembling; Screw 104 passes overhanging connection fixed head 89 and wood is moulded roofing slab 88 1 ends is fixed on the roof steel work 109; Wood is moulded the tenon 95 of being located by connecting on the roofing slab 88 and is injected adjacent wood and mould roofing slab and be located by connecting in the groove 90, wood is moulded roofing slab 88 other ends fix, and screw 104 is stayed overhanging connection fixed head 89 and hidden gap 96 with the head of a nail and form in the nuts storage chambeies 103; Sealing joint strip 105 is installed in the cavity of being made up of right sealed adhesive slot 92 and left sealed adhesive slot 94; Wood is moulded roofing slab 88 middle parts connection base plate hook 107 and is pressed on the holddown groove butt hook 98, and roofing slab 88 middle parts are fixed, and prevents that wood from moulding roofing slab 88 and roof steel work 109 breaks away from.
Description of drawings:
Below in conjunction with accompanying drawing and embodiment, the present invention is further described.
Fig. 1 is that the opening wood with characteristic of the present invention is moulded plate filling urethane resin light material exterior wall cladding end face structure figure.
Fig. 2 has to fill furane resins light material Wood-plastic floor end face structure figure in the characteristic of the present invention.
Fig. 3 fills furane resins light material Wood-plastic floor assembling end face structure figure in Fig. 2.
Fig. 4 has the interior filled phenolic type polyurethane light material wood of characteristic of the present invention to mould link plate end face structure figure.
Fig. 5 is Fig. 4 link plate assembling end face structure figure.
Fig. 6 is that the interior connection atrium with characteristic of the present invention is moulded wall central layer end face structure figure with the chamber combination wood of remaining silent.
Fig. 7 is that Fig. 6 wood is moulded filling furane resins light material and polyurethane expanded material end face structure figure in the wall central layer.
Fig. 8 is that Fig. 7 wood is moulded filling furane resins light material and polyurethane expanded material assembling end face structure figure in the wall central layer.
Fig. 9 has the outer corner end face structure figure of characteristic Wood plastic wall board of the present invention.
Figure 10 fills furane resins light material and polyurethane expanded material end face structure figure in Fig. 9 Wood plastic wall board corner.
Figure 11 is Fig. 7 and Fig. 9 Wood plastic wall board and the outer corner assembling of Wood plastic wall board end face structure figure.
Figure 12 is that Fig. 6 wood is moulded plate atrium filling self-hardening furane resins light material end face structure figure.
Figure 13 is that self-hardening resin light material end face structure figure is filled in the outer corner opening chamber of Fig. 9 Wood plastic wall board.
Figure 14 has characteristic Wood plastic wall board inside lock of the present invention to fill furane resins light material and polyurethane expanded material end face structure figure.
Figure 15 has characteristic wood of the present invention to mould internally filled with self-hardening resin light material roofing slab end face structure figure.
Figure 16 is that Figure 15 assembles end face structure figure.
Claims (10)
1. an internally filled with self-hardening resin light material wood is moulded plate, comprising: plate moulded by atrium wood or atrium is moulded plate, the self-hardening resin with the chamber combination wood of remaining silent; Curing compound, accelerator, light material; Fibrous material, auxiliary material, wood are moulded plate external surface viscosity resin film or sticking metal sheet or are coated with anticorrosive paint; It is characterized in that: wood is moulded plate atrium internally filled with self-hardening resin light material or atrium internally filled with self-hardening resin light material, fills organic resin foam material in the chamber of remaining silent.
2. internally filled with self-hardening resin light material wood as claimed in claim 1 is moulded plate, and it is characterized in that: the self-hardening resin comprises: furane resins, urethane resin, phenolic resins and carry out modified resins with epoxy resin or silane resin or polyurethane resin.
3. the wood of filling self-hardening resin light material as claimed in claim 1 is moulded plate, and it is characterized in that: light material comprises: closed-cell expanded perlite particle, expanded and vitrified small ball, granular polystyrene, slag, wood powder, fiber powder, glass fiber, fibre.
4. the wood of internally filled with self-hardening resin light material as claimed in claim 1 is moulded plate, it is characterized in that: the organic resin foamed material comprises: polyurethane foam material, polystyrene foamed material, Merlon foamed material, polyimide foam material.
5. the wood of internally filled with self-hardening resin light material as claimed in claim 1 is moulded plate; It is characterized in that: wood is moulded plate one side and is established overhanging connection fixed head; The inboard position link slot of setting of overhanging connection fixed head; Wood is moulded the plate opposite side and is set a position joint tongue, and screw passes overhanging connection fixed head and wood is moulded plate one end fixes, and the other end tenon that is located by connecting injects adjacent wood and moulds plate and be located by connecting fixing in the groove.
6. the wood of internally filled with self-hardening resin light material as claimed in claim 1 is moulded plate, it is characterized in that: wood is moulded the holddown groove that the adjacent side of plate and body of wall or ground is established the band butt hook.
7. the wood of internally filled with self-hardening resin light material as claimed in claim 1 is moulded plate, it is characterized in that: wood is moulded plate and is moulded core material by surface material and wood and be made by co-extrusion to.
8. the wood of internally filled with self-hardening resin light material as claimed in claim 1 is moulded plate, it is characterized in that: the plate surface moulded by wood or the primary coat surfaces coated is antibiotic and the antivirus activity material coating.
9. the wood of internally filled with self-hardening resin light material as claimed in claim 1 is moulded plate, it is characterized in that: wood is moulded plate surface or primary coat surfaces coated sunlight control grain coating.
10. the wood of internally filled with self-hardening resin light material as claimed in claim 1 is moulded plate, it is characterized in that: combined phase-change energy storage material in the self-hardening resin light material comprises: inorganic-phase variable energy storage material and organic phase change energy storage material.