CN101543881A - 双断面组合连铸工艺 - Google Patents

双断面组合连铸工艺 Download PDF

Info

Publication number
CN101543881A
CN101543881A CN200910014850A CN200910014850A CN101543881A CN 101543881 A CN101543881 A CN 101543881A CN 200910014850 A CN200910014850 A CN 200910014850A CN 200910014850 A CN200910014850 A CN 200910014850A CN 101543881 A CN101543881 A CN 101543881A
Authority
CN
China
Prior art keywords
sections
section
districts
continuous casting
interior outer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN200910014850A
Other languages
English (en)
Other versions
CN101543881B (zh
Inventor
吕铭
王键
吕长海
刘平
侯光合
陈良
张永青
费燕
陈军胜
谢韵平
焦玉莉
朱士将
范斌
朱波
尹崇丽
魏潇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shandong Iron and Steel Group Co Ltd SISG
Original Assignee
Laiwu Iron and Steel Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Laiwu Iron and Steel Co Ltd filed Critical Laiwu Iron and Steel Co Ltd
Priority to CN2009100148506A priority Critical patent/CN101543881B/zh
Publication of CN101543881A publication Critical patent/CN101543881A/zh
Application granted granted Critical
Publication of CN101543881B publication Critical patent/CN101543881B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

双断面组合连铸工艺，属于钢铁生产连铸技术领域。工艺如下：1)多机多流连铸机按机流数分成两个工作断面，即A断面和B断面，两组断面采用不同规格的结晶器、扇形段、喷嘴和不同的工艺参数；2)出坯系统采用分钢机拨爪从中间向两侧双向出坯，两组断面的铸坯通过两架行车单独码垛。拉速的设定与开启的机流数，按照两断面总过钢量基本平衡的原则，两断面通钢量偏差控制在±8％之内。本发明具有生产效率高、可以轧制不同规格轧材、低能耗的优点。

Description

双断面组合连铸工艺
技术领域
本发明涉及一种双断面组合连铸工艺，属于钢铁生产连铸技术领域。
背景技术
目前国内外新建的钢铁企业转炉、连铸发生了很大的变化，原来的转炉容积一般都在60t以下，而现在新建的钢铁企业转炉容积一般都在100t以上，与之相匹配的连铸机也发生了很大的变化，由原来的3个流、4个流到了现在的6个流、8个流甚至更多流。大转炉配多流连铸机的生产格局已经初步形成，目前大多数铸机产能比原来提高一倍，设备检修维护时间也相应比原来延长了一倍。为了使目前的生产工艺流程更趋合理，生产组织模式更加高效灵活，在提高企业利润的同时，不断降低生产经营成本，出现了连铸工艺。
传统连铸机在设计时一般都会设计两个以上不同的断面，以满足后道轧材工序生产不同规格的钢材需要。轧制不同规格的钢材需要不同断面的连铸坯，传统的生产组织模式是按照相同断面规格的铸坯安排在一个浇次组织生产，其他断面的铸坯安排在另一个浇次组织生产，这样的生产组织模式导致轧材工序如大型轧材车间和中小型轧材车间中总有1个轧材车间出现停机待料的现象。断面规格不同，钢种相同的计划，要分别安排生产，一个断面生产完成后，连铸机停4～12小时，来更换连铸设备如：引锭头、结晶器和扇形段等，既影响生产效率又增加连铸成本，同时轧材生产线与连铸的产能不匹配，大量热态铸坯需落地存放，以保证连铸机停产检修、更换断面时能保证连续生产。该生产组织模式不仅不能实现铸坯的热送热装，造成能源的极大浪费，而且很多时候轧材工序会出现停机待料现象，制约轧材产能的提升。
发明内容
为克服现有技术的不足，本发明提供一种生产效率高、可以轧制不同规格轧材、低能耗的双断面组合连铸工艺。
双断面组合连铸工艺与传统连铸工艺相比较，首先能同时生产两种不同断面规格的连铸坯，满足轧材工序即时轧制不同规格的需要，避免了停机待料现象的发生，提升了轧材工序的产能，提高对市场化定单的响应速度，缩短供货周期，大大提高客户满意度；其次提高铸机和轧机的生产效率，减少更换断面的时间和停机待料时间；第三有效的降低了连铸机和轧机的生产成本，提高了吨钢赢利能力。
本发明的目的是这样实现的：
1)多机多流连铸机按机流数分成两个工作断面，即A断面和B断面，两组断面采用不同规格的结晶器、扇形段、喷嘴和不同的工艺参数：
2)出坯系统采用分钢机拨爪从中间向两侧双向出坯，两组断面的铸坯通过两架行车单独码垛。
拉速的设定与开启的机流数，按照两断面总过钢量基本平衡的原则，两断面通钢量偏差控制在±8％之内。
所述的不同规格的结晶器、扇形段、喷嘴是指：
A断面结晶器260×300-R12，扇形段辊距为308.5mm，喷嘴根据铸坯的表面温度在整个二冷区冷却过程中的变化，分成五个冷却段即五个区：一区：内外弧、侧弧3/8PZ3575B10，二区：内外弧HPZ2.0-7030J，侧弧HPZ1.7-7030J；三区：内外弧HPZ1.3-7030J，侧弧HPZ1.0-7030J；四、五区：内外弧、侧弧HPZ0.8-70QZ2。
B断面结晶器180×220-R12，扇形段辊距为226.5mm，喷嘴根据铸坯的表面温度在整个二冷区冷却过程中的变化，分成五个冷却段即五个区：一区：内外弧、侧弧3/8PZ3575B10，二区：内外弧HPZ1.8-7030J，侧弧HPZ1.5-7030J；三区：内外弧HPZ1.2-7030J，侧弧HPZ1.0-7030J；四、五区：内外弧、侧弧HPZ0.8-70QZ2。
所述的不同的工艺参数是指：
A断面的工艺参数为：拉速：0.6-0.8m/min，结晶器水流量为148-155m3/h，二冷动态配水量：16-18m3/h，电磁搅拌参数：电流380A，频率3HZ，振动参数：振幅2.2-2.4mm，振频83-90HZ。
B断面的工艺参数为：拉速1.2-1.5m/min、结晶器水流量为138-145m3/h，二冷动态配水量：21-23m3/h、电磁搅拌参数、电流400A，频率3.5HZ，振动参数：振幅2.6-2.8mm，振频118-130HZ。
由于两组不同规格的铸坯同时生产，原有的单向出坯系统，不能实现两种规格分组吊装，无法实现两个不同规格的铸坯同时下线。新设计的出坯系统采用双向出坯模式，由铸机的中间向两侧出坯，以实现不同规格的铸坯能同时分组吊装，从而实现轧材工序能同时生产不同规格的钢材。
本发明的连铸工艺与传统工艺相比较有以下优点：
1、可以提高生产效率，对于钢种相同断面不同的生产计划可以安排在同一个浇次中进行，这样即节省生产时间，提高生产效率，又降低连铸生产成本，能及时满足“小批量、多批次”定单的要求。
2、双断面同时生产，降低了因更换断面占用的生产时间，提高了铸机作业效率。
3、两断面同时生产，能及时满足轧制需求，减少铸坯库存量，提高资金周转率，提高铸坯热装比例，节约能耗。
4、双断面同时生产实现了轧制规格的多样化，满足了客户对不同规格的需求，提高了即时生产的能力，缩短了生产周期，提高了客户的满意度。
附图说明
图1是本发明断面结构示意图。
图2是本发明出坯系统结构示意图。
其中，1、A断面结晶器，2、A断面二冷系统，3、B断面结晶器，4、B断面二冷系统，5、双向出坯系统，6、分钢机拨爪。
具体实施方式
实施例：六机六流的方坯连铸机，生产断面180mm×180mm、240mm×240mm，转炉出钢量120吨/炉。对应的轧材生产线如下：轧钢大型生产线，轧制规格φ75mm～φ150mm，使用240mm×240mm坯料，生产能力1400～1800t/天；中型生产线，轧制规格φ45mm～φ75mm，使用180mm×180mm坯料，生产能力800～1000t/天；小型生产线，轧制规格φ25mm～φ50mm，使用180mm×180mm坯料，生产能力800～1000t/天。连铸机日产3600～4200吨，每断面连续生产3～5天，采用单一断面，任一条生产线都无法及时消化生产的坯料，不能实现铸坯的热送热装，造成能源的极大浪费；同时，需要有大面积的场地存储大量的冷态铸坯，以保证连铸检修或更换断面时能连续生产。
采用本发明技术后，连铸机1～3流采用260mm×300mm结晶器1和相应的二冷系统2，4～6流采用180mm×220mm结晶器3和相应的二冷系统4，出坯系统采用双向出坯系统5，1～3流的拉速控制在0.6m/min～0.9m/min，4～6流的拉速控制在1.2m/min～1.6m/min。1～3流的通钢量平均1.83吨/分，4～6流的通钢量平均1.73吨/分，两断面通钢量差在6％，中间包流场平衡。生产出的铸坯经双向出坯系统5，通过分钢机拨爪6实现分别收集出坯，180mm×220mm每6支一组，260mm×300mm每4支一组，同时下线码坯。每炉钢被分成大小断面各半炉发往轧制不同规格的轧材厂，实现铸坯的即时轧制，提高了快速反应能力，铸坯的装炉温度在400℃以上，节约了能源消耗。
由于双断面同时生产，连铸机每月减少断面更换6次，更换断面每次需10小时，每月节省时间60小时，全年增加作业时间30天，大大提高了铸机的生产效率。
如遇到大型轧材线检修时，连铸机可停开260mm×300mm断面1～2流，减少大断面的产量，减少存坯量；中型或小型轧材线检修时，连铸机可停开180mm断面1～2流，减少小断面的产量，减少存坯量。

Claims (4)

1、一种双断面组合连铸工艺，其特征在于，工艺如下：
1)多机多流连铸机按机流数分成两个工作断面，即A断面和B断面，两组断面采用不同规格的结晶器、扇形段、喷嘴和不同的工艺参数：
2)出坯系统采用分钢机拨爪从中间向两侧双向出坯，两组断面的铸坯通过两架行车单独码垛。
2、如权利要求1所述的双断面组合连铸工艺，其特征在于，拉速的设定与开启的机流数，按照两断面总过钢量基本平衡的原则，两断面通钢量偏差控制在±8％之内。
3、如权利要求1所述的双断面组合连铸工艺，其特征在于，所述的不同规格的结晶器、扇形段、喷嘴是指：
A断面结晶器260×300-R12，扇形段辊距为308.5mm，喷嘴根据铸坯的表面温度在整个二冷区冷却过程中的变化，分成五个冷却段即五个区：一区：内外弧、侧弧3/8PZ3575B10；二区：内外弧HPZ2.0-7030J，侧弧HPZ1.7-7030J；三区：内外弧HPZ1.3-7030J，侧弧HPZ1.0-7030J；四、五区：内外弧、侧弧HPZ0.8-70QZ2；
B断面结晶器180×220-R12，扇形段辊距为226.5mm，喷嘴根据铸坯的表面温度在整个二冷区冷却过程中的变化，分成五个冷却段即五个区：一区：内外弧、侧弧3/8PZ3575B10，二区：内外弧HPZ1.8-7030J，侧弧HPZ1.5-7030J；三区：内外弧HPZ1.2-7030J，侧弧HPZ1.0-7030J；四、五区：内外弧、侧弧HPZ0.8-70QZ2。
4、如权利要求1所述的双断面组合连铸工艺，其特征在于，所述的不同的工艺参数是指：
A断面的工艺参数为：拉速：0.6-0.8m/min，结晶器水流量为148-155m3/h，二冷动态配水量：16-18m3/h，电磁搅拌参数：电流380A，频率3HZ，振动参数：振幅2.2-2.4mm，振频83-90HZ；
B断面的工艺参数为：拉速1.2-1.5m/min、结晶器水流量为138-145m3/h，二冷动态配水量：21-23m3/h、电磁搅拌参数、电流400A，频率3.5HZ，振动参数：振幅2.6-2.8mm，振频118-130HZ。
CN2009100148506A 2009-04-28 2009-04-28 双断面组合连铸工艺 Expired - Fee Related CN101543881B (zh)