CN101538763A - Production method of wear and flame resistance sofa fabric - Google Patents
Production method of wear and flame resistance sofa fabric Download PDFInfo
- Publication number
- CN101538763A CN101538763A CN200910097544A CN200910097544A CN101538763A CN 101538763 A CN101538763 A CN 101538763A CN 200910097544 A CN200910097544 A CN 200910097544A CN 200910097544 A CN200910097544 A CN 200910097544A CN 101538763 A CN101538763 A CN 101538763A
- Authority
- CN
- China
- Prior art keywords
- retardant
- lining
- yarn
- production method
- flame
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a production method of wear and flame resistance sofa fabric and aims at providing the production method of the sofa fabric which has the advantages of beautiful color, good durability, resistance to pilling and flame retardant function. Wool is adopted as raw material, the fineness of which is 25.1-31.1um and the length of which is 45-70mm. the production process successively comprises wool mixing, carding roving, ring yarn, warping, weaving, felting, braying, dehydrating, dyeing, dehydrating, drying, shearing, setting, final examination, packaging and warehousing. The production method is characterized in that the coefficient of twist in the ring yarn process is 180-200 per meter; yarn steaming process is arranged between the ring yarn and the warping. Processes of flame resistance treatment and dehydration are arranged between the dehydrating and the drying. Therefore, the strength, the wear resistance and the compactness of the produced fabric are all higher than that of common all woolen fabric. And with fireproof performance, the all woolen fabric can be applied to a plurality of sofa fabrics.
Description
Technical field
The present invention relates to textile product, relate in particular to a kind of production method of wear-resisting, flame-retardant sofa lining.
Background technology
It is good to make sofa fabric requirement ABRASION RESISTANCE, outward appearance is beautiful, traditional sofa fabric is based on leather fabric, artificial leather lining, chemical fiber plus material, cotton fabric, chemical fibre and cotton blended spinning face fabric, though leather fabric, artificial leather lining ABRASION RESISTANCE is good but profile is stiff, poor visual effect, though chemical fiber plus material, cotton fabric, blended yarn woven fabric is good-looking but the easy balling-up of these linings, not wear-resisting, poor fire are of low grade.Though the high-grade fabric of all woolen that wool is made into is arranged, and the lining density of common all woolen is poor, easy deformation is not durable, can only be as tractive and the little garment material of wearing and tearing.
Summary of the invention
The object of the present invention is to provide a kind of color and luster beautiful, durability well can surperficial balling-up yet and the production method of the sofa fabric of anti-flaming function is arranged.
Above-mentioned requirements is wear-resisting in order to reach, the production method of flame-retardant sofa lining: selecting fineness 25.1-31.1um, the length of raw material for use is the wool of 45-70mm, the technology of producing is successively: and hair → carding rove → ring spindle yarn → warping → weave → give birth to and repair → braying → fulling → braying → dehydration → dyeing → dehydration → oven dry → cropping → typing → finished product inspection → packing → warehouse-in, it is characterized in that the twist factor in the ring spindle yarn operation is between every meter of 180-200; Yarn steaming technology is arranged between ring spindle yarn and warping.
The technology that flame treatment and dehydration are arranged between dehydration and stoving process.
Wear-resisting, the flame-retardant sofa lining that obtain according to said method, twist factor in the ring spindle yarn operation is far above every meter of the twist factor 100-140 of common all woolen woven yarn, owing to adopted high twist factor, in normal conditions yarn can take place reverses, adopted yarn steaming technology for this reason, made yarn setting and prevent to reverse.In addition the lining that is made into is carried out flame treatment, increased the fire-proof function of lining.Therefore its intensity of lining, ABRASION RESISTANCE and the compactedness of producing thus all is higher than common all-wool fabric and can prevents fires again, is suitable as all kinds of sofa fabrics.
The specific embodiment
The invention will be further described below in conjunction with embodiment.
Embodiment 1
It selects fineness 25.1-31.1um, the length of raw material for use is the wool of 45-70mm, and the technology of production is successively: and hair → carding rove → ring spindle yarn → yarn steaming → warping → weave → give birth to and repair → braying → fulling → braying → dehydration → dyeing → dehydration → oven dry → cropping → typing → finished product inspection → packing → warehouse-in.Twist factor in this production technology in the division ring ingot spinning process is between every meter of 180-200 and to have increased outside the yarn steaming technology other technologies identical with the production technology of producing traditional slubbing lining, belongs to prior art and omits at this.
Above-mentioned yarn steaming technology is: yarn is placed in the yarn steaming machine, preheating after 3 minutes humidification heat up, in the condition of 80 ℃ of humidity 80% and temperature, kept 50 minutes, dry 5 minutes again to humidity 35%, after be put into the outdoor natural temperature that is cooled to.
Embodiment 2
It selects fineness 25.1-31.1um, the length of raw material for use is the wool of 45-70mm, and the technology of production is successively: and hair → carding rove → ring spindle yarn → yarn steaming → warping → weave → give birth to and repair → braying → fulling → braying → dehydration → dyeing → dehydration → flame treatment → dehydration → oven dry → cropping → typing → finished product inspection → packing → warehouse-in.Twist factor in this production technology in the division ring ingot spinning process is between every meter of 180-200 and has increased outside yarn steaming technology and the flame treatment that other technologies are identical with the production technology of producing traditional slubbing lining, belongs to prior art and omits at this, no longer repeats.
Described yarn steaming technology is: yarn is placed in the yarn steaming machine, preheating after 4 minutes humidification heat up, in the condition of 85 ℃ of humidity 85% and temperature, kept 60 minutes, dry 6 minutes again to humidity 33%, after be put into the outdoor natural temperature that is cooled to.
Described fire retardant treatment process is successively:
(1) preparation of fire-retardant treatment liquid: in 25 ℃ warm water, add hair durable fire retardant QY-407B earlier, the weight ratio of hair durable fire retardant QY-407B and warm water is 1: 3, and fully stirring makes a mao durable fire retardant QY-407B dissolving, is mixed with the QY-407B dilution; Add hair durable fire retardant QY-407A again in 50 ℃ hot water, the weight ratio of hair durable fire retardant QY-407A and hot water is 1: 3, and stirs and make the QY-407A dilution; By the weight ratio of QY-407A dilution and QY-407B dilution is to mix at 1: 2 to make fire-retardant treatment liquid;
(2) soak material: the lining after will dewatering adds cold water after putting into dyeing machine, and the weight ratio of lining and cold water is 1: 14, is warming up to 35 ℃, add formic acid, be adjusted to pH value 2, add fire-retardant treatment liquid again, the weight ratio of fire-retardant treatment liquid and lining is 1: 3, is warming up to 70 ℃ of insulations 40 minutes again;
(3) clean: lining is put into clear water wash 3 times, the pH value 6.2 of lining.
Embodiment 3
It selects fineness 25.1-31.1um, the length of raw material for use is the wool of 45-70mm, and the technology of production is successively: and hair → carding rove → ring spindle yarn → yarn steaming → warping → weave → give birth to and repair → braying → fulling → braying → dehydration → dyeing → dehydration → flame treatment → dehydration → oven dry → cropping → typing → finished product inspection → packing → warehouse-in.Twist factor in this production technology in the division ring ingot spinning process is between every meter of 180-200 and has increased outside yarn steaming technology and the flame treatment that other technologies are identical with the production technology of producing traditional slubbing lining, belongs to prior art and omits at this, no longer repeats.
Described yarn steaming technology is: yarn is placed in the yarn steaming machine, preheating after 4 minutes humidification heat up, in the condition of 85 ℃ of humidity 90% and temperature, kept 65 minutes, dry 7 minutes again to humidity 31%, after be put into the outdoor natural temperature that is cooled to.
Described fire retardant treatment process is successively:
(1) preparation of fire-retardant treatment liquid: in 30 ℃ warm water, add hair durable fire retardant QY-407B earlier, the weight ratio of hair durable fire retardant QY-407B and warm water is 1: 3.5, and fully stirring makes a mao durable fire retardant QY-407B dissolving, is mixed with the QY-407B dilution; Add hair durable fire retardant QY-407A again in 55 ℃ hot water, the weight ratio of hair durable fire retardant QY-407A and hot water is 1: 3.5, and stirs and make the QY-407A dilution; By the weight ratio of QY-407A dilution and QY-407B dilution is to mix at 1: 2 to make fire-retardant treatment liquid;
(2) soak material: the lining after will dewatering adds cold water after putting into dyeing machine, and the weight ratio of lining and cold water is 1: 15, is warming up to 40 ℃, add formic acid, be adjusted to pH value 2.6, add fire-retardant treatment liquid again, the weight ratio of fire-retardant treatment liquid and lining is 1: 4, is warming up to 75 ℃ of insulations 50 minutes again;
(3) clean: lining is put into clear water wash 2 times, the pH value that makes lining is greater than 5.2.
Embodiment 4
It selects fineness 25.1-31.1um, the length of raw material for use is the wool of 45-70mm, and the technology of production is successively: and hair → carding rove → ring spindle yarn → yarn steaming → warping → weave → give birth to and repair → braying → fulling → braying → dehydration → dyeing → dehydration → flame treatment → dehydration → oven dry → cropping → typing → finished product inspection → packing → warehouse-in.Twist factor in this production technology in the division ring ingot spinning process is between every meter of 180-200 and has increased outside yarn steaming technology and the flame treatment that other technologies are identical with the production technology of producing traditional slubbing lining, belongs to prior art and omits at this, no longer repeats.
Described yarn steaming technology is: yarn is placed in the yarn steaming machine, preheating after 5 minutes humidification heat up, in the condition of 90 ℃ of humidity 95% and temperature, kept 75 minutes, dry 8 minutes again to humidity 30%, after be put into the outdoor natural temperature that is cooled to.
Described fire retardant treatment process is successively:
(1) preparation of fire-retardant treatment liquid: in 35 ℃ warm water, add hair durable fire retardant QY-407B earlier, the weight ratio of hair durable fire retardant QY-407B and warm water is 1: 4, and fully stirring makes a mao durable fire retardant QY-407B dissolving, is mixed with the QY-407B dilution; Add hair durable fire retardant QY-407A again in 60 ℃ hot water, the weight ratio of hair durable fire retardant QY-407A and hot water is 1: 4, and stirs and make the QY-407A dilution; By the weight ratio of QY-407A dilution and QY-407B dilution is to mix at 1: 2 to make fire-retardant treatment liquid;
(2) soak material: the lining after will dewatering adds cold water after putting into dyeing machine, and the weight ratio of lining and cold water is 1: 16, is warming up to 35-45 ℃, add hydrochloric acid, be adjusted to pH value 3, add fire-retardant treatment liquid again, the weight ratio of fire-retardant treatment liquid and lining is 1: 5, is warming up to 80 ℃ of insulations 60 minutes again;
(3) clean: lining is put into clear water wash 3 times, the pH value that makes lining is greater than 5.8.
The hair durable fire retardant QY-407A of above-mentioned use and hair durable fire retardant QY-407B unite two groups of use among mao durable fire retardant QY-407, composite flame-retardant agent for fluorine-containing, titanium, zr element, be used for the wool fabric flame treatment of (comprising other animal fiber), be efficient flame-retarding agent with durability, on sale on market.Fabric through this product flame treatment does not influence feel.Certainly except the hair durable fire retardant QY-407 of above-mentioned use, also can use the hair of other kinds to handle with durable fire retardant.
Claims (4)
1, the production method of wear-resisting, flame-retardant sofa lining, selecting fineness 25.1-31.1um, the length of raw material for use is the wool of 45-70mm, the technology of producing is successively: and hair → carding rove → ring spindle yarn → warping → weave → give birth to and repair → braying → fulling → braying → dehydration → dyeing → dehydration → oven dry → cropping → typing → finished product inspection → packing → warehouse-in, it is characterized in that the twist factor in the ring spindle yarn operation is between every meter of 180-200; Yarn steaming technology is arranged between ring spindle yarn and warping.
2, the production method of wear-resisting, flame-retardant sofa lining according to claim 1, it is characterized in that described yarn steaming technology is: yarn is placed in the yarn steaming machine, humidification heats up after preheating 3-5 minute, in the condition of humidity 80-95% and temperature 80-90 ℃, kept 40-80 minute, dry again to humidity 30-35%, after be put into the outdoor natural temperature that is cooled to.
3, the production method of wear-resisting, flame-retardant sofa lining according to claim 1 is characterized in that having the technology of flame treatment and dehydration between dehydration and stoving process.
4, the production method of wear-resisting, flame-retardant sofa lining according to claim 3 is characterized in that described fire retardant treatment process is successively:
(1) preparation of fire-retardant treatment liquid: in 25-35 ℃ warm water, add hair durable fire retardant QY-407B earlier, the weight ratio of hair durable fire retardant QY-407B and warm water is 1: 3-4, and fully stirring makes a mao durable fire retardant QY-407B dissolving, is mixed with the QY-407B dilution; Add hair durable fire retardant QY-407A again in 50-60 ℃ hot water, the weight ratio of hair durable fire retardant QY-407A and hot water is 1: 3-4, and stir and make the QY-407A dilution; By the weight ratio of QY-407A dilution and QY-407B dilution is to mix at 1: 2 to make fire-retardant treatment liquid;
(2) soak material: the lining after will dewatering adds cold water after putting into dyeing machine, the weight ratio of lining and cold water is 1: 14-16, be warming up to 35-45 ℃, add formic acid or hydrochloric acid, be adjusted to pH value 2～3, add fire-retardant treatment liquid again, the weight ratio of fire-retardant treatment liquid and lining is 1: 3～5, is warming up to 70-80 ℃ of insulation 40-60 minute again;
(3) clean: lining is put into clear water wash 2-3 time, the pH value that makes lining is greater than 5.