CN101531372A - 高岭土碱性静态漂白工艺 - Google Patents

高岭土碱性静态漂白工艺 Download PDF

Info

Publication number
CN101531372A
CN101531372A CN200910038467A CN200910038467A CN101531372A CN 101531372 A CN101531372 A CN 101531372A CN 200910038467 A CN200910038467 A CN 200910038467A CN 200910038467 A CN200910038467 A CN 200910038467A CN 101531372 A CN101531372 A CN 101531372A
Authority
CN
China
Prior art keywords
kaoline
alkaline
pulp
static
bleaching
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN200910038467A
Other languages
English (en)
Other versions
CN101531372B (zh
Inventor
王运新
全明华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
MAOMING SILVER FLOWER KAO LIN CLAY CO Ltd
Original Assignee
MAOMING SILVER FLOWER KAO LIN CLAY CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by MAOMING SILVER FLOWER KAO LIN CLAY CO Ltd filed Critical MAOMING SILVER FLOWER KAO LIN CLAY CO Ltd
Priority to CN2009100384674A priority Critical patent/CN101531372B/zh
Publication of CN101531372A publication Critical patent/CN101531372A/zh
Application granted granted Critical
Publication of CN101531372B publication Critical patent/CN101531372B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种高岭土碱性静态漂白工艺，它是将分级后的高岭土矿浆与保险粉混合均匀后，静置，然后加入调节剂，使矿浆pH值控制在3～5，搅拌均匀即得。本发明操作简单，生产中容易实现，且效果明显，可广泛用于高岭土加工企业，具有较大的推广价值和应用前景。

Description

高岭土碱性静态漂白工艺
技术领域
本发明属于高岭土加工领域，具体涉及一种高岭土碱性静态漂白工艺。
背景技术
高岭土的漂白方法大多数是采用还原漂白，就是将高岭土中带色的Fe3+还原成无色的Fe2+，经脱水将Fe2+除去，使高岭土变白。工业生产中用保险粉(学名：连二亚硫酸钠、分子式：Na2S2O4)作还原剂，用硫酸作调整剂。具体办法是用硫酸调节矿浆的PH值至2-3，然后加入保险粉，搅拌30分钟，即完成漂白，生产中是一槽槽间断进行。由于保险粉很不稳定，遇水即水解，水解过程产生还原性，水解速度随PH值降低而加快。在酸性介质中，保险粉的水解速度比高岭土的漂白速度快得多，造成保险粉浪费。在碱性介质中，常温下保险粉的水解速度明显减慢，在正常条件下难以达到漂白效果，由于Fe3+还原成Fe2+的反应是可逆的，如果保险粉的水解速度太慢，介质中没有保持足够的还原能力，部分Fe2+就会氧化成Fe3+，影响漂白效果。在碱性介质中，要加快保险粉的水解速度，可以通过加热的办法，这将消耗大量热量，在生产中是不经济的。因此，发明一种既能达到酸性漂白的效果，又能节约保险粉用量，减少设备腐蚀的碱性静态漂白工艺对高岭土的加工企业具有很大的意义。
发明内容
本发明的目的是提供一种既可以得到理想的漂白效果，又可以节能降耗的高岭土碱性静态漂白工艺。
本发明提供的高岭土碱性静态漂白工艺，它是将分级后的高岭土矿浆与保险粉混合均匀后，静置，然后加入调节剂，使矿浆PH值控制在3～5，搅拌均匀即得。
在矿浆PH值>7，≤9时加入保险粉，保险粉加入量以浓度为10～15％的矿浆计，为0.8～1.5kg/m3矿浆。
所述的调节剂为硫酸和草酸或磷酸，按浓度为98％的硫酸和无水草酸或磷酸计，草酸或磷酸用量为调节剂总重量的15～25％。
静置时间为10～30小时。
调节剂为硫酸和草酸或磷酸，硫酸的作用主要调节矿浆的PH值，草酸或磷酸作为稳定剂使用，作用是与Fe2+形成性质相对稳定的络合物，避免Fe2+氧化成为Fe3+，而造成产品“返黄”从而降低硫酸的用量。
本发明与现有技术相比，具有如下优点和有益效果：
一、由于分级后的矿浆为弱碱性，保险粉的水解速度大大减慢，避免了在酸性介质中保险粉产生的无效水解，而且漂白过程是在矿浆处于静止状态下进行，大大减少Fe2+氧化成Fe3+，从而达到节约保险粉的效果。
二、由于漂白时间很长，对于难漂的高岭土矿，漂白效果比酸性漂白好。
三、漂白过程除了加入保险粉，不需添加其他药剂，只是在漂白过程完成后防止Fe2+氧化成Fe3+而出现“返黄”，需要加入适量酸或其他稳定剂，酸的用量比酸漂工艺要少许多。
本发明的碱性静态漂白工艺与酸性漂白工艺相比，每吨产品可以节约1kg左右保险粉，漂白后矿浆PH值可以提高1个值以上，漂白效果比酸漂稳定，尤其对难漂的矿浆，效果更加明显。而且矿浆在静置过程中能排出一部分水，提高了矿浆浓度，从而提高后续脱水工序的效率。
本发明的高岭土碱性静态漂白工艺，操作简单，生产中容易实现，且效果明显，可广泛用于高岭土加工企业，具有较大的推广价值和应用前景。
具体实施方式
实施例一：
本发明的高岭土碱性静态漂白工艺，将经分级后PH值为7.5的高岭土矿浆直接送入混合池，加入保险粉，保险粉加入量以浓度为10～15％的矿浆计，为0.8～1.5kg/m3矿浆，混合均匀后输送到储浆池，储浆池装满后静置10小时，然后将矿浆排到搅拌池，加入调节剂硫酸和草酸，调节矿浆PH值为3，搅拌均匀即完成整个漂白过程，其中，按浓度为98％的硫酸和无水草酸计，草酸用量为调节剂总重量的15％。
实施例二：
本发明的高岭土碱性静态漂白工艺，将经分级后PH值为8的高岭土矿浆直接送入混合池，加入保险粉，保险粉加入量以浓度为10～15％的矿浆计，为0.8～1.5kg/m3矿浆，混合均匀后输送到储浆池，储浆池装满后静置20小时，然后将矿浆排到搅拌池，加入调节剂硫酸和草酸，调节矿浆PH值为4，搅拌均匀即完成整个漂白过程，其中，按浓度为98％的硫酸和无水草酸计，草酸用量为调节剂总重量的20％。
实施例三：
本发明的高岭土碱性静态漂白工艺，将经分级后PH值为9的高岭土矿浆直接送入混合池，加入保险粉，保险粉加入量以浓度为10～15％的矿浆计，为0.8～1.5kg/m3矿浆，混合均匀后输送到储浆池，储浆池装满后静置30小时，然后将矿浆排到搅拌池，加入调节剂硫酸和草酸，调节矿浆PH值为5，搅拌均匀即完成整个漂白过程，其中，按浓度为98％的硫酸和无水草酸计，草酸用量为调节剂总重量的25％。
具体应用实例：
本发明人在茂名市银华高岭土实业有限公司建造了一套碱性静态漂白工艺，混合池和加酸搅拌池均为两个￠3000×2000mm搅拌池，储浆池为4个各450M3的混凝土浆池。矿浆在混合池内加入定量的保险粉，搅拌3分钟后，用泵输送到储浆池，每个储浆池能容纳12小时的矿浆，储浆池装满后静置20小时，然后排到搅拌池，加入硫酸和稳定剂，矿浆PH值控制在3～5(视原矿质量和稳定剂的选择和加入量而定)，搅拌均匀即完成整个漂白过程。

Claims (4)

1、一种高岭土碱性静态漂白工艺，其特征是它是将分级后的高岭土矿浆与保险粉混合均匀后，静置，然后加入调节剂，使矿浆PH值控制在3～5，搅拌均匀即得。
2、根据权利要求1所述的高岭土碱性静态漂白工艺，其特征是在矿浆PH值>7，≤9时加入保险粉，保险粉加入量以浓度为10～15％的矿浆计，为0.8～1.5kg/m3矿浆。
3、根据权利要求1所述的高岭土碱性静态漂白工艺，其特征是所述的调节剂为硫酸和草酸或磷酸，按浓度为98％的硫酸和无水草酸或磷酸计，草酸或磷酸用量为调节剂总重量的15～25％。
4、根据权利要求1所述的高岭土碱性静态漂白工艺，其特征是静置时间为10～30小时。
CN2009100384674A 2009-04-03 2009-04-03 高岭土碱性静态漂白工艺 Expired - Fee Related CN101531372B (zh)