CN101509891B - 一种罐盖料转化膜均匀性检测方法 - Google Patents
一种罐盖料转化膜均匀性检测方法 Download PDFInfo
- Publication number
- CN101509891B CN101509891B CN200910131497XA CN200910131497A CN101509891B CN 101509891 B CN101509891 B CN 101509891B CN 200910131497X A CN200910131497X A CN 200910131497XA CN 200910131497 A CN200910131497 A CN 200910131497A CN 101509891 B CN101509891 B CN 101509891B
- Authority
- CN
- China
- Prior art keywords
- conversion film
- uniformity
- film
- detection method
- anodic oxidation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种罐盖料转化膜均匀性检测方法,该检测方法为阳极氧化法,所述阳极氧化法为将罐盖料进行阳极氧化,然后观察其表面的条纹和颜色,来判断转化膜的均匀性。本发明1)利用铝材在阳极氧化时表面因转化膜的均匀性影响,导致腐蚀、氧化速率不一致,在铝材表面生成的氧化膜不均匀,根据氧化膜颜色的均匀性来判断转化膜的均匀性。氧化膜颜色越均匀表示转化膜越均匀;2)阳极氧化时间、电流、电压和槽液浓度等参数的确定;3)观察判断方法、标准的建立。本发明能快速、准确知道罐盖产品转化膜的均匀性,以便指导生产,控制转化膜的均匀性,保证罐盖料的涂膜性能。
Description
技术领域
本发明涉及一种罐盖料转化膜均匀性检测方法。
背景技术
铝合金罐盖料主要用于易拉盖罐装饮料、食品,如可乐、啤酒、八宝粥、椰奶、王老吉等。技术要求高、生产难度大,属于高附加价值产品。它一方面要求材料(包括铝基材和涂膜)具有优良的加工、冲制性能;另一方面要求涂膜具有优良的耐高温灭菌、耐酸、耐硫性能。
罐盖料生产工艺路线长、工艺复杂,通常罐盖料涂层工艺流程为:开卷--脱脂--水洗-化学转化-涂层-烘烤-冷却-收卷,其中化学转化的目的是在铝材表面形成一层致密的转化膜,目前转化膜的种类有两种:一种是含三价的转化膜;另一种是无铬转化膜,如含锆转化膜。转化膜的主要作用:一是提高涂层与基材的附着力;二是增强涂层的耐高温灭菌、耐酸、耐硫性能。转化膜的膜重(厚度)和均匀性影响最终产品质量。
转化膜的不均匀性是指带材横向方向膜厚不均匀,有些多、有些少或有些无转化膜,最终导致带材横向涂层性能不均匀。
罐盖料转化膜比较薄而致密,目视无颜色。转化膜的重量称取方法目前采用的有化学方法-脱膜称重法和仪器检测法-X射线检测法,可以准确测量单位面积的转化膜重量。但如何检测带材横向方向转化膜的均匀性,查询相关资料,尚未发现检测方法,目前是靠工艺来保证,如:通过控制涂辊表面的均匀性、辊速配比、槽液浓度以及加强管理等方面来保证,但均匀性如何无法判断,生产过程中发生异常,无法准确知道转化膜的质量如何。因此,在生产中经常发现涂膜性能不稳定、带材横向涂膜性能不一致,市场投诉在冲盖中出现涂膜脱落现象,导致电导率超标;在高温灭菌时出现涂膜发白;耐酸、耐硫检测时出现涂膜局部脱落、涂膜出现斑点等缺陷。
发明内容
本发明的目的是提供一种罐盖料转化膜均匀性检测方法,该方法能快速、准确判断转化膜的均匀性,从而指导生产,控制转化膜的均匀性,保证罐盖料的涂膜性能。
为达到上述目的,本发明所提供的技术方案是:一种罐盖料转化膜均匀性检测方法,该检测方法为阳极氧化法,所述阳极氧化法为将罐盖料进行阳极氧化,然后观察其表面的条纹和颜色,来判断转化膜的均匀性:
(1)表面上的颜色均匀,以及无任何条纹,表示转化膜均匀;
(2)表面上有条纹和颜色不均匀,表示转化膜不均匀。
所述阳极氧化法的电解液为:硫酸180-200g/L、铝离子5-20g/L。
所述阳极氧化法的电解条件为:温度15-25℃、电流密度1.5-2.0A/dm2、电压10-22V、时间2-3min。
本发明具有的优点:1)利用铝材在阳极氧化时表面因转化膜的均匀性影响,导致腐蚀、氧化速率不一致,在铝材表面生成的氧化膜不均匀,根据氧化膜颜色的均匀性来判断转化膜的均匀性。氧化膜颜色越均匀表示转化膜越均匀;2)阳极氧化时间、电流、电压和槽液浓度等参数的确定;3)观察判断方法、标准的建立。本发明能快速、准确知道罐盖产品转化膜的均匀性,以便指导生产,控制转化膜的均匀性,保证罐盖料的涂膜性能。
具体实施方式:
下面结合具体实施例对本发明作进一步详细说明,但本发明的内容不限于所举的实施例。
一种罐盖料转化膜均匀性检测方法,本方法通过阳极氧化法来检测罐盖料转化膜均匀性。
1、该阳极氧化法的罐盖料试样要求:应从生产线取成品样,要求平整,无油污和损伤,规格500×板宽。
2、阳极氧化要求:
2.1槽液成分:硫酸(H2SO4):180-200g/L;铝离子(Al3+):20>Al3+>5g/L
2.2配制电解液必须用纯水进行配制,对水的纯度要求是:Cl-<15ppm;Fe3+<1ppm;SO4 2-<30ppm;
2.3电解温度:15-25℃;
2.4电流密度:1.5-2.0A/d m2;
2.5电压:10-22V;
电解电压会受到合金材料、电流密度、电解液浓度、铝离子含量和溶液浓度的影响,且还和电解槽尺寸、形状、极(面积)比、极间距离、搅拌状态和制品形态有关,故在实际操作中一般采用恒电流电解,而电压则应不超过22V为宜。
2.6氧化时间:2-3min;
其中:硫酸电解液在使用过程中,液面经常出现油污和泡沫等悬浮的杂质,应在每次氧化之前将其去掉。对溶液要定期进行化学分析,并根据分析结果添加硫酸,保持规定的浓度。采用下述的中和滴定法:
操作程序:用无刻度吸量管取试样5毫升,放入圆锥形烧杯中(300ml),加入纯水约70毫升和氟化钾溶液(10W/V%)30毫升,充分振荡混合,加3-4滴酚酞溶液(1W/V%),用1N氢氧化钠溶液滴定,把呈红色的点作为滴定终点。按下式求硫酸(g/L):
硫酸浓度(克/升)=9.8×V×F
式中:V=1N氢氧化钠标准溶液的滴定毫升数;
F=1N氢氧化钠标准溶液的系数,此处取1
罐盖料试样经过阳极氧化法后取出、清洗、晾干后观察表面均匀性:
级别 | 条纹程度 | 结论 |
1 | 表面无任何条纹,颜色均匀 | 转化膜非常均匀 |
2 | 表面零星条纹,颜色均匀 | 转化膜较均匀 |
3 | 表面细条纹 | 转化膜均匀 |
4 | 表面条纹粗而多 | 转化膜不均匀 |
利用铝材在阳极氧化时表面因转化膜的均匀性影响,导致腐蚀、氧化速率不一致,在铝材表面生成的氧化膜不均匀,根据氧化膜颜色的均匀性来判断转化膜的均匀性,氧化膜颜色越均匀表示转化膜越均匀。
本发明罐盖料转化膜均匀性检测方法能快速、准确判断转化膜的均匀性,从而严格控制转化膜的均匀性,确保涂膜性能。
以上所述,仅是本发明的较佳实施例,并非对本发明作任何形式上的限制,虽然本发明已以较佳实施例揭露如上,然而并非用以限定本发明,任何熟悉本专业的技术人员,在不脱离本发明技术方案范围内,当可利用上述揭示的技术内容作出些许更动或修饰为等同变化的等效实施例,但凡是未脱离本发明技术方案的内容,依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与修饰,均仍属于本发明技术方案的保护范围内。
Claims (1)
1.一种罐盖料转化膜均匀性检测方法,其特征在于:该检测方法为阳极氧化法,所述阳极氧化法为将罐盖料进行阳极氧化,然后观察其表面的条纹和颜色,来判断转化膜的均匀性:
(1)表面上的颜色均匀,以及无任何条纹,表示转化膜均匀;
(2)表面上有条纹和颜色不均匀,表示转化膜不均匀;
所述阳极氧化法的电解液为:硫酸180-200g/L;铝离子5-20g/L;
所述阳极氧化法的电解条件为:温度15-25℃、电流密度1.5-2.0A/dm2、电压10-22V、时间2-3min。