CN101509059B - 多连杆压力机偏心体的热处理方法 - Google Patents
多连杆压力机偏心体的热处理方法 Download PDFInfo
- Publication number
- CN101509059B CN101509059B CN2008101582165A CN200810158216A CN101509059B CN 101509059 B CN101509059 B CN 101509059B CN 2008101582165 A CN2008101582165 A CN 2008101582165A CN 200810158216 A CN200810158216 A CN 200810158216A CN 101509059 B CN101509059 B CN 101509059B
- Authority
- CN
- China
- Prior art keywords
- link lever
- centering body
- lever press
- hours
- incubated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种多连杆压力机偏心体的热处理方法，包括如下具体步骤：将多连杆压力机偏心体放置在加热炉中，加温至550-570℃，并保温4-6小时；然后放到加热炉中，炉温需小于400℃，保温2小时，升温至600-650℃，保温2小时，再升温至880-900℃保温，保温5-7小时后出炉，用压缩气体冷却至室温；最后放到加热炉中，炉温需小于400℃，保温2小时，升温至回火温度550-570℃，保温5-7小时，然后出炉，自然冷却即可。本发明取得的有益效果是：(1)降低了多连杆压力机偏心体开裂的比率，提高了合格率；(2)提高了多连杆压力机偏心体的强度和硬度，满足了生产实际需要。
Description
技术领域
本发明涉及一种偏心体的热处理方法，特别是一种多连杆压力机偏心体的热处理方法。
背景技术
目前，多年杆压力机偏心体经过通常的正火工艺处理后，容易开裂，究其原因，是因为偏心体的结构复杂，有效厚度大，壁厚不均匀，铸造过程流动性差，在零件的局部存在缺陷造成很大的应力，正火冷却过程中无法完全均匀，一旦超过有缺陷铸件的实际抗拉极限时就会产生裂纹直至零件开裂。
发明内容
本发明要解决的问题是：提供一种多连杆压力机偏心体的热处理方法，通过该热处理方法处理后，大大降低了多连杆压力机偏心体开裂的比率，提高了合格率，提高了多连杆压力机偏心体的强度和硬度。
为了解决上述技术问题，本发明的多连杆压力机偏心体的热处理方法，包括如下具体步骤：
1)对多连杆压力机偏心体进行时效处理：将多连杆压力机偏心体放置在加热炉中，加热至550-570℃，并保温4-6小时；
2)对多连杆压力机偏心体进行正火处理：将时效处理过的多连杆压力机偏心体放到加热炉中，炉温需小于400℃，保温2小时，然后升温至600-650℃，保温2小时，再升温至880-900℃保温，保温5-7小时后出炉，最后用压缩气体将多连杆压力机偏心体冷却至室温；
3)对多连杆压力机偏心体进行回火处理：将多连杆压力机偏心体放到加热炉中，炉温需小于400℃，保温2小时，升温至回火温度550-570℃，保温5-7小时，然后出炉，自然冷却即可。
本发明取得的有益效果是：(1)降低了多连杆压力机偏心体开裂的比率，提高了合格率；(2)提高了多连杆压力机偏心体的强度和硬度，满足了生产实际需要。
具体实施方式
本发明的多连杆压力机偏心体的热处理方法，包括如下具体步骤：
第一步，对多连杆压力机偏心体进行时效处理：将多连杆压力机偏心体放置在加热炉中，加热至550-570℃，并保温4-6小时。
第二步，对多连杆压力机偏心体进行正火处理：将时效处理过的多连杆压力机偏心体放到加热炉中，炉温需小于400℃，保温2小时，然后升温至600-650℃，保温2小时，再升温至880-900℃保温，保温5-7小时后出炉，最后用压力为0.2-0.5Mpa的压缩气体将多连杆压力机偏心体冷却至室温。
第三步，对多连杆压力机偏心体进行回火处理：将多连杆压力机偏心体放到加热炉中，炉温需小于400℃，保温2小时，升温至回火温度550-570℃，保温5-7小时，然后出炉，目然冷却即可。
表1是2003-2007年度多连杆压力机偏心体热处理情况的统计数据，其中2003和2004年度未采用本发明方法，2005-2007年度采用了本发明方法。
表1
| 年份 | 总工件数 | 合格数量 | 不合格数量(开裂) | 合格率 | 是否采用本发明方法 |
| 2003 | 95 | 83 | 12 | 87.40％ | 否 |
| 2004 | 49 | 44 | 5 | 89.80％ | 否 |
| 2005 | 51 | 49 | 2 | 96.10％ | 是 |
| 2006 | 92 | 88 | 4 | 95.70％ | 是 |
| 2007 | 61 | 60 | 1 | 98.40％ | 是 |
通过表1可以看出，采用本发明方法后，多连杆压力机偏心体的开裂几率大幅度减少，合格率得到大幅度提升；另外，采用本发明方法后，零件铸态硬度大于180HB，正火后偏心体外圆硬度为220-280HB，零件的拉伸强度σb≥700MPa，延伸率δ≥2％，远远能满足生产实际的需要。
Claims (1)
1.一种多连杆压力机偏心体的热处理方法，其特征在于：包括如下具体步骤：
1)对多连杆压力机偏心体进行时效处理：将多连杆压力机偏心体放置在加热炉中，加温至550-570℃，并保温4-6小时；
2)对多连杆压力机偏心体进行正火处理：将时效处理过的多连杆压力机偏心体放到加热炉中，炉温需小于400℃，保温2小时，然后升温至600-650℃，保温2小时，再升温至880-900℃保温，保温5-7小时后出炉，最后用压缩气体将多连杆压力机偏心体冷却至室温；
3)对多连杆压力机偏心体进行回火处理：将多连杆压力机偏心体放到加热炉中，炉温需小于400℃，保温2小时，再升温至回火温度550-570℃，保温5-7小时，然后出炉，自然冷却即可。