CN101477901A - 一种阻燃电解液及其制备方法 - Google Patents
一种阻燃电解液及其制备方法 Download PDFInfo
- Publication number
- CN101477901A CN101477901A CNA2008102080344A CN200810208034A CN101477901A CN 101477901 A CN101477901 A CN 101477901A CN A2008102080344 A CNA2008102080344 A CN A2008102080344A CN 200810208034 A CN200810208034 A CN 200810208034A CN 101477901 A CN101477901 A CN 101477901A
- Authority
- CN
- China
- Prior art keywords
- weight
- electrolyte
- flame
- percentage
- percent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种阻燃电解液及其制备方法，包括：乙二醇、聚乙烯醇、硼酸、四硼酸铵、甘露糖醇，其重量百分比分别为：56％－75％∶0.5％－2.5％∶6％－10％∶10％－15％∶8％－15％，另外再添加0.5～1.5％的O－硝基茴香醚。本发明的电解液既耐高温高压，又减少氢气量，制成的铝电解电容器使用寿命95℃，2000小时，耐高压达到450V，可降低电解液蒸汽压，具有阻燃性。
Description
技术领域
本发明属电解液及其制备领域，特别是涉及一种阻燃电解液及其制备方法。
背景技术
电解液是铝电解电容器的阴极，其性能对铝电解电容器的性能有一定的影响，现有的电解液配方主要由溶质和溶剂组成。中国专利99121506.0(铝电解电容器)发明的一种无闪点的，即使在高温下长时间使用其外观变化和特性劣化也很少的，可靠性高的铝电解电容器，其电解液的含水率为20～90重量％，电解液中含有选自甲酸铵、乙酸铵、乳酸铵、乙醇酸铵、草酸铵、琥珀酸铵、丙二酸铵、己二酸铵、苯甲酸铵、戊二酸铵、壬二酸铵中一种以上的化合物作为主电解质，另外含有1重量％以上选自特定结构的有机羧酸或其铵盐中一种以上的化合物，上述电解液的凝固点在-10℃以下，改善了其耐电压、高温性能，但未能抑制氢气的产生。
中国专利02805612.4(电解电容器和电解电容器驱动用电解液)公开了吸收铝电极箔和电解液反应生成的氢气，添加含有不饱和键的化合物，制成电解电容器的电特性和在高温放置条件下的特性良好的电容器，提供在内部含有引起加氢反应的不饱和化合物的电解电容器，和相对于含有溶剂是由10～80重量％的有机溶剂和90～20重量％的水构成的溶剂，和选自羧酸或其盐和无机酸或其盐的至少1种电解质的电解液，含有1种或以上在水溶性或极性溶剂和质子系极性溶剂中可溶的不饱和化合物构成的电解液，此配方虽能减少氢气量，但对改善耐高温和高压等性能效果不明显。
发明内容
本发明所要解决的技术问题是提供一种阻燃电解液及其制备方法，该电解液既耐高温，高压又减少氢气量。
本发明的一种阻燃电解液，包括：乙二醇、聚乙烯醇、硼酸、四硼酸铵、甘露糖醇，其重量百分比分别为：56％-75％：0.5％-2.5％：6％-10％：10％-15％：8％-15％，另外再添加0.5～1.5％的O-硝基茴香醚。
本发明的一种阻燃电解液的制备方法，包括：
(1)将(56-75)重量％乙二醇加热到120～125℃，然后把(6-10)重量％硼酸、(10-15)重量％四硼酸铵、(8-15)重量％甘露糖醇依此加入，搅拌直到完全溶解；
(2)将步骤(1)混合液升温到135-150℃，再把(0.5-2.5)重量％聚乙烯醇加入，不断搅拌，直到电解液完全澄清为止；
(3)将步骤(2)的混合液冷却到85℃，加入(0.5～1.5)重量％O-硝基茴香醚，自然冷却，即得阻燃电解液。
有益效果
(1)本发明的电解液既耐高温高压，又减少氢气量；
(2)制成铝电解电容器使用寿命95℃，2000小时，耐高压达到450V，可降低电解液蒸汽压，具有阻燃性。
具体实施方式
下面结合具体实施例，进一步阐述本发明。应理解，这些实施例仅用于说明本发明而不用于限制本发明的范围。此外应理解，在阅读了本发明讲授的内容之后，本领域技术人员可以对本发明作各种改动或修改，这些等价形式同样落于本申请所附权利要求书所限定的范围。
实施例1
一种电解液配比：乙二醇58重量％，聚乙烯醇2.5重量％，硼酸10重量％，四硼酸铵15重 量％，甘露糖醇14重量％，O-硝基茴香醚0.5重量％。
其制备：
(1)将58重量％乙二醇加热到120～125℃，然后把10重量％硼酸、15重量％四硼酸铵、14重量％甘露糖醇依此加入，搅拌直到完全溶解；
(2)将步骤(1)混合液升温到135℃，再把2.5重量％聚乙烯醇加入，不断搅拌，直到电解液完全澄清为止；
(3)将步骤(2)的混合液冷却到85℃，加入0.5重量％O-硝基茴香醚，自然冷却，即得阻燃电解液。
实施例2
一种电解液配比：乙二醇68重量％，聚乙烯醇1.5重量％，硼酸7重量％，四硼酸铵11重量％，甘露糖醇11.5重量％，O-硝基茴香醚1.0重量％。
实施例3
一种电解液配比：乙二醇70.5重量％，聚乙烯醇1重量％，硼酸8重量％，四硼酸铵7重量％，甘露糖醇12重量％，O-硝基茴香醚1.5重量％。
Claims (3)
1.一种阻燃电解液，包括：乙二醇、聚乙烯醇、硼酸、四硼酸铵、甘露糖醇，其重量百分比分别为：56％-75％：0.5％-2.5％：6％-10％：10％-15％：8％-15％，另外再添加0.5～1.5％的O-硝基茴香醚。
2.根据权利要求1所述的一种阻燃电解液，其特征在于：所述的由上述电解液制成铝电解电容器使用寿命95℃，2000小时，耐高压达到450V，降低电解液蒸汽压，具有阻燃性。
3.一种阻燃电解液的制备方法，包括：
(1)将重量百分比为56％-75％乙二醇加热到120～125℃，然后把重量百分比为6％-10％硼酸、重量百分比为10％-15％四硼酸铵、重量百分比为8％-15％甘露糖醇依此加入，搅拌直到完全溶解；
(2)将步骤(1)混合液升温到135-150℃，再把重量百分比为0.5％-2.5％聚乙烯醇加入，不断搅拌，直到电解液完全澄清为止；
(3)将步骤(2)的混合液冷却到85℃，加入重量百分比为0.5～1.5％O-硝基茴香醚，自然冷却，即得阻燃电解液。