CN101463232A - 粘弹性阻尼专用胶粘剂及施工方法 - Google Patents
粘弹性阻尼专用胶粘剂及施工方法 Download PDFInfo
- Publication number
- CN101463232A CN101463232A CNA2007101511131A CN200710151113A CN101463232A CN 101463232 A CN101463232 A CN 101463232A CN A2007101511131 A CNA2007101511131 A CN A2007101511131A CN 200710151113 A CN200710151113 A CN 200710151113A CN 101463232 A CN101463232 A CN 101463232A
- Authority
- CN
- China
- Prior art keywords
- damping
- adhesive
- elasticity adhesive
- special
- visco
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种粘弹性阻尼专用胶粘剂，其配方组成：氯丁－240、氯丁胶B－30、氧化镁、氧化锌、树脂(说明树脂具体名称)、碳黑、N－苯基－α－萘胺(防老剂A)组成。其制造方法：使用开炼机，开足冷却水，辊距调至最小，放入生胶，薄通塑炼10遍以上，放宽辊距至2～4mm，加入各种配合剂，倒炼3遍，辊距调至1mm左右，打三角包3～6个，下1～2mm厚胶片备用；防止胶片粘接。将胶片裁成胶条，放入溶剂中浸泡24小时以上，搅拌至充分溶解，溶液浓度20～25％，得到粘弹性阻尼专用胶粘剂。主体材料溶解参数相近、内聚强度高、耐海水、耐油、耐燃与被粘结材料如钢板等的互粘性、粘接强度高，以及胶粘剂的初粘性等性能好。
Description
技术领域
本发明属于橡胶粘合剂，特别涉及一种粘弹性阻尼专用胶粘剂及施工方法。
背景技术
已有的粘弹性阻尼胶粘剂性能差：胶粘剂的初粘性等性能差。保证不了胶粘剂的粘合强度，与阻尼胶板粘合剥离强度低，施工复杂。
发明内容
本发明提供一种粘弹性阻尼专用胶粘剂及施工方法。达到与粘弹性阻尼胶板主体材料溶解参数相近、内聚强度高、耐海水、耐油、耐燃等诸项性能与被粘结材料如钢板等的互粘性好、粘接强度高，初粘性性能好。保证胶粘剂具有较高的粘合强度，较好的初粘性和施工性能。
本发明具体方案：
一种粘弹性阻尼专用胶粘剂，其特征在于：
其配方组成：
氯丁—240：20份
氯丁胶B-30：80份
氧化镁：4份
氧化锌：5份
树脂增粘剂：20份
碳黑：15份
N-苯基-α-萘胺(防老剂A)：1份
所述的粘弹性阻尼专用胶粘剂，其制造方法：
使用设备：开炼机，开足开炼机的冷却水，将辊距调至最小，放入生胶，薄通塑炼10遍以上，放宽辊距至2～4mm，加入各种配合剂，倒炼3遍，将辊距调至1mm左右，打三角包3～6个，下1～2mm厚胶片备用；防止胶片粘接；
溶解：将胶片裁成胶条，放入溶剂中浸泡24小时以上，搅拌至充分溶解，溶液浓度20～25％，得到粘弹性阻尼专用胶粘剂。
所述的粘弹性阻尼专用胶粘剂，其施工使用方法：对粘接面进行喷沙打光，在粘接面涂本粘弹性阻尼专用胶粘剂，粘贴胶板，在粘贴胶板面涂粘弹性阻尼专用胶粘剂，在其上制作玻璃钢层。
本发明特点：本粘弹性阻尼专用胶粘剂与粘弹性阻尼胶板主体材料溶解参数相近、内聚强度高、耐海水、耐油、耐燃等诸项性能好的胶种作为胶粘剂的主体材料。
与被粘结材料如钢板等的互粘性、粘接强度高，以及胶粘剂的初粘性等性能好。
主要技术指标：
剥离强度，KN/m(胶板与钢板)：6.7
剥离强度，KN/m(胶板层间)：4
附图说明
图1是粘弹性阻尼专用胶粘剂制作工艺流程图
图2是粘弹性阻尼专用胶粘剂施工方法工艺流程图
具体实施方式
一种粘弹性阻尼专用胶粘剂，其配方组成：
氯丁—240：20份
氯丁胶B-30：80份
氧化镁：4份
氧化锌：5份
树脂：20份
碳黑：15份
N-苯基-α-萘胺(防老剂A)：1份
如图1所示的粘弹性阻尼专用胶粘剂，其制造方法：
使用设备：开炼机，开足开炼机的冷却水，将辊距调至最小，放入生胶，薄通塑炼10遍以上，放宽辊距至2～4mm，加入各种配合剂，倒炼3遍，将辊距调至1mm左右，打三角包3～6个，下1～2mm厚胶片备用；防止胶片粘接。
溶解：将胶片裁成胶条，放入溶剂中浸泡24小时以上，搅拌至充分溶解，溶液浓度20～25％，得到粘弹性阻尼专用胶粘剂。
如图2所示的粘弹性阻尼专用胶粘剂施工使用方法：对粘接面进行喷沙打光，在粘接面涂本粘弹性阻尼专用胶粘剂，粘贴胶板，在粘贴胶板面涂粘弹性阻尼专用胶粘剂，在其上制作玻璃钢层。
施工要点：
1.准备工作
1.1.环境温度高于15℃，相对湿度低于70％
1.2.装备表面喷砂处理要符合有关要求。
1.3.工作环境要保持清洁，操作现场保持隔离，且通风良好。
1.4.预先做好施工粘贴排布方案和胶板排裁方案，严格按工艺程序施工。
1.5.盛装、涂刷胶粘剂的容器、刷子等用具要保持干净，每次取用和收工后要随时盖严所有盛装容器，防止溶剂挥发，并避免引发火灾。
2.操作要点
2.1.在符合要求的装备待敷设阻尼材料表面，按顺序均匀涂刷两遍胶粘剂，在胶板待粘贴表面均匀地涂刷两遍胶粘剂，确认充分干燥后才能涂下一遍。
2.2.胶板粘贴采用对接方式，接口错开，确认装备和胶板上的胶粘剂充分干燥后，找准位置进行粘贴，然后再用压辊从中央向四周将空气赶出、压实，防止窝气。
2.3.对于用窝气或未粘接上的部位应重新粘贴。其程序与新施工一样。
2.4.胶板全部贴好，找平，并经过检查、确认无缺陷和质量问题后，方可进行下一道工序施工，知道玻璃钢约束层的敷设制造。
Claims (3)
1、一种粘弹性阻尼专用胶粘剂，其特征在于：
其配方组成：
氯丁—240：20份
氯丁胶B-30：80份
氧化镁：4份
氧化锌：5份
树脂：20份
碳黑：15份
N-苯基-α-萘胺(防老剂A)：1份
2、根据权利要求1所述的粘弹性阻尼专用胶粘剂，其制造方法：
使用设备：开炼机，开足开炼机的冷却水，将辊距调至最小，放入生胶，薄通塑炼10遍以上，放宽辊距至2～4mm，加入各种配合剂，倒炼3遍，将辊距调至1mm左右，打三角包3～6个，下1～2mm厚胶片备用；防止胶片粘接；
溶解：将胶片裁成胶条，放入溶剂中浸泡24小时以上，搅拌至充分溶解，溶液浓度20～25％，得到粘弹性阻尼专用胶粘剂。
3、根据权利要求1所述的粘弹性阻尼专用胶粘剂，其施工使用方法：对粘接面进行喷沙打光，在粘接面涂本粘弹性阻尼专用胶粘剂，粘贴胶板，在粘贴胶板面涂粘弹性阻尼专用胶粘剂，在其上制作玻璃钢层。