CN101434479B - 环保粉粒建筑材料 - Google Patents
环保粉粒建筑材料 Download PDFInfo
- Publication number
- CN101434479B CN101434479B CN2008101802610A CN200810180261A CN101434479B CN 101434479 B CN101434479 B CN 101434479B CN 2008101802610 A CN2008101802610 A CN 2008101802610A CN 200810180261 A CN200810180261 A CN 200810180261A CN 101434479 B CN101434479 B CN 101434479B
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- cement
- protective
- construction material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种不含石灰的环保粉粒建筑材料，主要用于贴砖、砌筑、粉糊抹面、地面找平、缝隙灌浆工程等相关领域；其配料主要由水泥、粉煤灰、干式电石渣、烟气脱硫石膏、减水剂组成，其特点是：克服了传统砂浆和易性差、凝固时间长、成本高等不足之处，同时具有成本低、使用方便、抗渗防潮、环保、易生产等优点。
Description
技术领域
本发明涉及一种新型粉粒建筑材料，属于建筑用材料领域。特别的涉及一种不使用普通石灰(或碳烧石灰产品)，固定袋装，使用非常方便，加水调拌即可使用的搅拌灰浆产品。
背景技术
目前，在建筑领域，传统的现场搅拌灰浆存在以下缺陷：
1、由于现场配料、现场目测或评经验计量、现场环境、现场设备、现场质量监督跟不上等因素，制约了质量得不到保证，并造成环境二次污染和材料浪费。
2、传统水泥石灰砂浆有很多不足至今未得到理想解决：①成本高：煤矿产资源是有限的，煤的涨价导致生石灰价格比水泥高，有的地方高出两倍；②小型石灰窑过多，煅烧石灰造成环境的严重污染和造成能源的浪费；③到处乱开乱采石灰岩，造成水土流失，气候恶变；④用于墙体材料不加石灰的水泥砂浆只能用到砌筑上；而贴砖、装修、抹面一般都又不易直接使用；⑤普通掺入石灰的水泥砂浆凝固周期长，加上和易性差，容易产生龟裂和空鼓，日常生活中常发现粘贴到墙面上的瓷砖拉裂、脱落或用手敲打时发出空响声，此现象在本发明前没有得到解决；⑥传统水泥砂浆找平地面作为竹木地板垫层，容易产生地露使木质地板腐蚀生虫、桥拱变形等；⑦从物理力学来说：任何物体都有它的韧性和弹性，建筑材料也如此，如瓷砖、地板砖、大理石等贴材，在日常建筑中，传统的砂浆用来贴墙砖、大理石等装饰材料后，都会发现有线条不平整，60％的瓷砖中部外凸成球面状，用手去敲，有的会发出空响声，有的一两个月后就产生裂纹或者脱落，其实这就是传统的水泥石灰浆所造成的，谁都知道，在贴砖时必须先用水渗透瓷砖，不渗透贴上去不稳固。然而，由于瓷砖本身有一定的弹性，渗水后用传统的水泥石灰浆去粘贴，由于石灰浆的和易性差，加上凝固期长，贴在墙面上的瓷砖与墙面、水泥石灰浆三者之间在凝固期间产生不一致的物理运动，物理运动后产生以上现象。在它们三者之间水泥石灰浆处于中间，所以必须用中间的粘合材料来解决它们之间的物理运动矛盾，要大大增加中间粘合材料的和易性。
本发明科学地利用发电、冶炼等工业排放废料所具有的特定特性，并与普通硅酸盐水泥巧妙地配比起来，改善传统砂浆的不足之处；同时具有有成本低、易生产，废料利用率高、和易性好、节能环保、质量稳定、造价低、使用方便、便于工程质量监督管理、抗渗、防潮、粘性好、易上墙、方便搬运、不易产生二次污染、不易产生龟裂和空鼓等优点。它完全取代了传统的现场手拌灰浆和填补了传统灰浆长期以来的历史性缺陷。
发明内容
本发明提供一种环保粉粒建筑材料，该粉粒材料组份包含普通硅酸盐水泥和粉煤灰，还包含干式电石渣和工业聚合物粉尘和减水剂和/或烟气脱硫石膏，其配制成份和重量份数为：水泥20～60份；粉煤灰30～60份(含水量＜1％，细度50-200目)；干式电石渣5～20(水份≤2％，细度50-500目)；烟气脱硫石膏0～5(含水量≤2％，细度50-150目)；工业聚合物粉尘3～15份；减水剂1～3；加入掺和配料，机械封闭式搅拌得到产品。固定包装入库。
上述原料按计量配比加入封闭式机械搅拌机搅拌3～8分钟，使其搅拌均匀后得产品装袋。现场使用时用上述产品配以重量份数1∶2～1∶6的砂(细度在5mm以下，含泥量小于5％)加适量水调匀即可使用。或上述产品配以重量份数1∶3～5的砂(山砂烘干，水份小于2％，细度在5mm以下，含泥量小于5％)，加入封闭式机械搅拌机搅拌5分钟，使其搅拌均匀后得产品(干料)装袋，现场直接加适量水调匀即可使用。
本发明的有益效果是，在改善传统砂浆不足之处的同时，大大提高了工业废渣费料的循环利用率，保持了水土，节约了能源，优化了“三废”及其矿产资源的利用效益，同时也保护了环境。
具体实施方式
实施例1：
用于粘贴普通墙砖等的粉粒状建筑材料，其配制成份及重量份数为：
水泥： 35～50
粉煤灰： 45～60(细度100～250目，水份＜1％)
干式电石渣： 10～20(细度50～250目，水份＜2％)
烟气脱硫石膏： 1～5(水份＜2％)
工业聚合物粉尘(电除尘)： 3～15(细度100～300目)
减水剂：： 1～3
上述原料按计量配比加入封闭式机械搅拌机搅拌3～8分钟，使其搅拌均匀后得产品以25公斤或50公斤装袋；现场直接加适量水调匀即可使用。
实施例2：
用于室内装潢的竹、木地板垫层或粘贴地板砖等的粉粒状建筑材料，其配制成份及重量份数为：
水泥： 30～45
粉煤灰： 50～60(细度100～250目，水份＜1％)
干式电石渣： 5～10(细度50～250目，水份＜2％)
烟气脱硫石膏： 1～5(水份＜2％)
工业聚合物粉尘(电除尘)： 3～15(细度100～300目)
减水剂：： 1～3
上述原料按计量配比加入封闭式机械搅拌机搅拌3～8分钟，使其搅拌均匀后得产品装袋。现场使用时用上述产品配以重量份数1∶3～1∶5的山砂(细度在5mm以下，含泥量小于5％)加适量水调匀即可使用。或上述产品配以重量份数1∶3～5的山砂(烘干，水份小于2％，细度在5mm以下，含泥量小于5％)，加入封闭式机械搅拌机搅拌5分钟，使其搅拌均匀后得产品(干料)以25公斤或50公斤装袋，现场直接加适量水调匀即可使用。
实施例3：
用于墙体粉糊、抹面及勾缝等的粉粒状建筑材料，其配制成份及重量份数为：
水泥： 35～50
粉煤灰： 45～50(细度100～250目，水份＜1％)
干式电石渣： 10～20(细度50～250目，水份＜2％)
烟气脱硫石膏： 3～5(水份＜2％)
工业聚合物粉尘(电除尘)： 5～10(细度100～300目)
减水剂：： 1～3
上述原料按计量配比加入封闭式机械搅拌机搅拌3～8分钟，使其搅拌均匀后得产品装袋。现场使用时用上述产品配以重量份数1∶3～1∶5的山砂(细度在4mm以下，含泥量小于5％)加适量水调匀即可使用。或上述产品配以重量份数1∶3～1∶5的山砂(山砂烘干，水份小于2％，细度在5mm以下，含泥量小于5％)，加入封闭式机械搅拌机搅拌5分钟，使其搅拌均匀后得产品(干料)以25公斤或50公斤装袋，现场直接加适量水调匀即可使用。用于墙面跑光时用上述产品直接加适量水调匀即可使用。
实施例4
用于砌筑的粉粒状建筑材料，其配制成份及重量份数为：
水泥： 20～40
粉煤灰： 50～60(细度100～250目，水份＜1％)
干式电石渣： 10～15(细度50～250目，水份＜2％)
工业聚合物粉尘(电除尘)： 5～10(细度100～300目)
减水剂：： 1～3
上述原料按计量配比加入封闭式机械搅拌机搅拌3～8分钟，使其搅拌均匀后得产品装袋。现场使用时用上述产品配以重量份数1∶4～6的山砂(该山砂细度在6mm以下，含泥量小于5％)加适量水调匀即可使用。
实施例5：
用于填筑及灌浆工程等的粉粒状建筑材料，其配制成份及重量份数为：
水泥： 50～60
粉煤灰： 30～35(细度100～250目，水份＜1％)
烟气脱硫石膏： 1～2(水份＜2％)
干式电石渣： 1～10(细度50～250目，水份＜2％)
工业聚合物粉尘(电除尘)： 10～15(细度100～300目)
减水剂：： 2～3
上述原料按计量配比加入封闭式机械搅拌机搅拌3～8分钟，使其搅拌均匀后得产品装袋；现场直接加适量水调匀即可使用(用于灌浆)。或使用时用上述产品配以重量份数1∶2～3的山砂(细度在4mm以下，含泥量小于5％)加适量水调匀即可使用。或上述产品配以重量份数1∶2～3的山砂(烘干，水份小于2％，细度在4mm以下，含泥量小于5％)，加入封闭式机械搅拌机搅拌5分钟，使其搅拌均匀后得产品(干料)以25公斤或50公斤装袋，现场直接加适量水调匀即可使用。
本发明所有原料均可从市面购买得到。例如：
1、水泥可以使用市面上常见的Po425普通硅酸盐水泥。
2、粉煤灰来自于300MW及以上火力发电机组干式除灰系统的电除尘灰，执行国标：GB/T1596-2005；达到I～III级技术标准均可使用。它具有“形态和易性效应”、“活性效应”、“微粒填充抗渗效应“和”吸附净化防潮效应“。
3、干式电石渣来自于电石生产厂的排放废物；或使用电石生产乙炔气体产生的废渣烘干后磨细。干式电石渣主要成份为Ca(OH)2，其为碱性物质，它与粉煤灰中的sio 2 tAl 2 O 3在潮湿的环境中发生化学反应，生成水化硅酸钙、钙矾石等物质，使灰浆质量稳定且后期强度明显增加。
4、工业聚合物粉尘来自于冶金企业烟气电除尘收集的粉尘。工业聚合物粉尘属于含硅铝成份的尾矿类固体废弃物，它可用作无机聚合物的原料，无机聚合物也称地质聚合物，是一种新型的工程及建筑材料；地质聚合物具有：耐酸、耐碱、耐高温、不燃烧等优良性质和较高的机械强度；能增加灰浆的抗压能力。
5、烟气脱硫石膏来自于火力发电厂烟气石灰石——石膏湿法脱硫的附产物，采用自然风干的方式得到的石膏粉沫。烟气脱硫石膏主要成份为CaSO 3和CaSO 4，它能起到使灰浆缓凝和稳定的作用。
6、减水剂使用市面销售的混凝土减水剂，增加灰浆的和易性。
Claims (8)
1.一种环保粉粒建筑材料，其特征在于，该粉粒材料组份包含普通硅酸盐水泥和粉煤灰，还包含干式电石渣和工业聚合物粉尘和减水剂和/或烟气脱硫石膏，各组份的重量配比为：水泥20～60份，粉煤灰30～60份，干式电石渣5～20份，烟气脱硫石膏0～5份，工业聚合物粉尘3～15份，减水剂1～3份。
2.如权利要求1所述的环保粉粒建筑材料，其特征在于，各组份的重量配比为：水泥35～50份，粉煤灰45～60份，干式电石渣10～20份，烟气脱硫石膏1～5份，工业聚合物粉尘3～15份，减水剂1～3份。
3.如权利要求1所述的环保粉粒建筑材料，其特征在于，其配制成份及重量份数为：水泥30～45份，粉煤灰50～60份，干式电石渣5～10份，烟气脱硫石膏1～5份，工业聚合物粉尘3～15份，减水剂1～3份。
4.如权利要求1所述的环保粉粒建筑材料，其特征在于，其配制成份及重量份数为：水泥35～50份，粉煤灰45～50份，干式电石渣10～20份，烟气脱硫石膏3～5份，工业聚合物粉尘5～10份，减水剂1～3份。
5.如权利要求1所述的环保粉粒建筑材料，其特征在于，其配制成份及重量份数为：水泥20～40份，粉煤灰50～60份，干式电石渣10～15份，工业聚合物粉尘5～10份，减水剂1～3份。
6.如权利要求1所述的环保粉粒建筑材料，其特征在于，其配制成份及重量份数为：水泥50～60份，粉煤灰30～35份，干式电石渣10～20份，烟气脱硫石膏1～2份，工业聚合物粉尘10～15份，减水剂2～3份。
7.如权利要求1所述的环保粉粒建筑材料，其特征在于，还在所述环保粉粒建筑材料内配以重量份数1；2～1；6的砂。
8.如权利要求1-7任一项所述的环保粉粒建筑材料，其特征在于，所述各原料按计量配比加入封闭式机械搅拌机搅拌数分钟，搅拌均匀后，即得所述环保粉粒建筑材料。